Corrosion behavior of high-strength spring steel for high-speed railway

The corrosion resistance and evolution of corrosion products in medium-carbon high-strength spring steels were investigated in a neutral salt spray(5 wt% Na Cl solution). A formation model of γ-Fe OOH and a transformation model describing the conversion of γ-Fe OOH to α-Fe OOH were constructed. The results indicated that, at the initial corrosion stage, the corrosion resistance was gradually improved with the addition of Cr; however, with the addition of alloying element V, the corrosion resistance decreased. These results were attributed mainly to the initial corrosion stage being closely related to the matrix microstructure parameters such as grain-boundary character and dislocation density. After the rust layer was formed at a later corrosion stage, the corrosion resistance was reinforced with the addition of Cr and V because Cr strongly influenced the composition, structure, and morphology of the corrosion products. The results presented herein show that Cr was conducive to the transformation of γ-Fe OOH into α-Fe OOH. Moreover, V and Cr exhibited obvious synergy and were enriched in the inner layer of the corrosion products.

Flow characteristics and hot workability of a typical low-alloy high-strength steel during multi-pass deformation

Heavy components of low-alloy high-strength(LAHS) steels are generally formed by multi-pass forging. It is necessary to explore the flow characteristics and hot workability of LAHS steels during the multi-pass forging process, which is beneficial to the formulation of actual processing parameters. In the study, the multi-pass hot compression experiments of a typical LAHS steel are carried out at a wide range of deformation temperatures and strain rates. It is found that the work hardening rate of the experimental material depends on deformation parameters and deformation passes, which is ascribed to the impacts of static and dynamic softening behaviors. A new model is established to describe the flow characteristics at various deformation passes. Compared to the classical Arrhenius model and modified Zerilli and Armstrong model, the newly proposed model shows higher prediction accuracy with a confidence level of 0.98565. Furthermore, the connection between power dissipation efficiency(PDE) and deformation parameters is revealed by analyzing the microstructures. The PDE cannot be utilized to reflect the efficiency of energy dissipation for microstructure evolution during the entire deformation process, but only to assess the efficiency of energy dissipation for microstructure evolution in a specific deformation parameter state.As a result, an integrated processing map is proposed to better study the hot workability of the LAHS steel, which considers the effects of instability factor(IF), PDE, and distribution and size of grains. The optimized processing parameters for the multi-pass deformation process are the deformation parameters of 1223–1318 K and 0.01–0.08 s^(-1). Complete dynamic recrystallization occurs within the optimized processing parameters with an average grain size of 18.36–42.3 μm. This study will guide the optimization of the forging process of heavy components.

Effect of traveling-wave magnetic field on dendrite growth of high-strength steel slab: Industrial trials and numerical simulation

The dendrite growth behavior of high-strength steel during slab continuous casting with a traveling-wave magnetic field was studied in this paper. The morphology of the solidification structure and composition distribution were analyzed. Results showed that the columnar crystals could deflect and break when the traveling-wave magnetic field had low current intensity. With the increase in current intensity, the secondary dendrite arm spacing and solute permeability decreased, and the columnar crystal transformed into an equiaxed crystal. The electromagnetic force caused by the traveling-wave magnetic field changed the temperature gradient and velocity magnitude and promoted the breaking and fusing of dendrites. Dendrite compactness and composition uniformity were arranged in descending order as follows:columnar-toequiaxed transition (high current intensity), columnar crystal zone (low current intensity), columnar-to-equiaxed transition (low current intensity), and equiaxed crystal zone (high current intensity). Verified numerical simulation results combined with the boundary layer theory of solidification front and dendrite breaking–fusing model revealed the dendrite deflection mechanism and growth process. When thermal stress is not considered, and no narrow segment can be found in the dendrite, the velocity magnitude on the solidification front of liquid steel can reach up to 0.041 m/s before the dendrites break.

Effects of Chromium,Vanadium and Austenite Deformation on Transformation Behaviors of High-strength Spring Steels

The phase transformation behavior during continuous cooling of high-strength spring steels containing different amounts of Cr was studied.Furthermore,the effects of combining Cr with V as well as austenite deformation on the transformation kinetics were investigated in the method of dilatometry and metallography hardness.The results showed that,with the increase of Cr,the pearlite transformation field was enlarged,the ferrite transformation field was narrowed,and the entire phase field shifted to the right.With the addition of V,the start transformation temperature of undercooling austenite( A_(r3))was gradually increased,but the ferrite and pearlite transformation fields were not affected.Besides,the minimum critical cooling rate of martensitic transformation was also reduced.In addition,the dynamic continuous cooling transformation( CCT) curve moves to the top left compared with the static CCT curve.The transformed microstructures showed that the addition of V and the deformation not only refined the overall transformed microstructures but also reduced the lamellar spacing of pearlite.The alloying elements Cr and V promoted the Vickers hardness.However,the effect of Cr on the Vickers hardness of martensite was stronger and the influence of V on that of pearlite was stronger.Moreover,the Vickers hardness affected by the austenite deformation was more complex and strongly depended on the transformed microstructures.

Effect of Boron on Delayed Fracture Resistance of Medium-Carbon High Strength Spring Steel

The delayed fracture behavior of medium-carbon high strength spring steel containing different amounts of boron (0.000 5%, 0.001 6%) was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron content from 0.000 5% to 0.001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350 ℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initiation area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3(C, B) phase.

In-depth analysis of the fatigue mechanism induced by inclusions for high-strength bearing steels

A numerical study of stress distribution and fatigue behavior in terms of the effect of voids adjacent to inclusions was conducted with finite element modeling simulations under different assumptions.Fatigue mechanisms were also analyzed accordingly.The results showed that the effects of inclusions on fatigue life will distinctly decrease if the mechanical properties are close to those of the steel matrix.For the inclusions,which are tightly bonded with the steel matrix,when the Young’s modulus is larger than that of the steel matrix,the stress will concentrate inside the inclusion;otherwise,the stress will concentrate in the steel matrix.If voids exist on the interface between inclusions and the steel matrix,their effects on the fatigue process differ with their positions relative to the inclusions.The void on one side of an inclusion perpendicular to the fatigue loading direction will aggravate the effect of inclusions on fatigue behavior and lead to a sharp stress concentration.The void on the top of inclusion along the fatigue loading direction will accelerate the debonding between the inclusion and steel matrix.

Development of a New Kind of High Strength Spring Steel

A new kind of high strength, high toughness and high plasticity spring steel has been developed. The strength, the reduction of area and the elongation of the steel are all higher than those of the steel 60Si2CrVA. The decarburization resistance and the sag resistance are also higher than those of the steel 60Si2CrVA. It has good hardenability, and is suitable for making springs with big cross section. The bogie springs made of this kind of steel have passed 2×106 cycles without broken under the conditions of maximum stress of 906 MPa and the minimum stress of 388 MPa.

Effect of in-situ nanoparticles on the mechanical properties and hydrogen embrittlement of high-strength steel

We investigated the critical influence of in-situ nanoparticles on the mechanical properties and hydrogen embrittlement(HE)of high-strength steel.The results reveal that the mechanical strength and elongation of quenched and tempered steel(919 MPa yield strength,17.11%elongation)are greater than those of hot-rolled steel(690 MPa yield strength,16.81%elongation)due to the strengthening effect of insitu Ti_(3)O_(5)–Nb(C,N)nanoparticles.In addition,the HE susceptibility is substantially mitigated to 55.52%,approximately 30%lower than that of steels without in-situ nanoparticles(84.04%),which we attribute to the heterogeneous nucleation of the Ti_(3)O_5 nanoparticles increasing the density of the carbides.Compared with hard TiN inclusions,the spherical and soft Al_(2)O_(3)–MnS core–shell inclusions that nucleate on in-situ Al_(2)O_(3) particles could also suppress HE.In-situ nanoparticles generated by the regional trace-element supply have strong potential for the development of high-strength and hydrogen-resistant steels.

Effect of nanosized NbC precipitates on hydrogen-induced cracking of high-strength low-alloy steel

We investigated the effect of nanosized NbC precipitates on hydrogen-induced cracking(HIC)of high-strength low-alloy steel by conducting slow-strain-rate tensile tests(SSRT)and performing continuous hydrogen charging and fracture analysis.The results reveal that the HIC resistance of Nb-bearing steel is obviously superior to that of Nb-free steel,with the fractured Nb-bearing steel in the SSRT exhibiting a smaller ratio of elongation reduction(Iδ).However,as the hydrogen traps induced by NbC precipitates approach hydrogen saturation,the effect of the precipitates on the HIC resistance attenuate.We speculate that the highly dispersed nanosized NbC precipitates act as irreversible hydrogen traps that hinder the accumulation of hydrogen at potential crack nucleation sites.In addition,much like Nb-free steel,the Nb-bearing steel exhibits both H-solution strengthening and the resistance to HIC.

DEVELOPMENT OF EFFECTIVE TECHNOLOGICAL PROCESSES OF HIGH-STRENGTH STEEL WELDING

Composition and service properties of high - strength low-alloyed steels with 590-980 MPa yield strength,which find an application in Russia, Belorus,Ukraine and other countries of the former USSR in manufacture of welded structures of a powerful mining and transport machinery, are given. Electrodes and wires for main processes of arc welding of these steels have been devel- oped on the basis of a rational use of different systems of alloying (08KhN2GM,08KhNG2M, and also economical systems of type 10G25, ect. ). Main approaches to the technological provess- es of manufacture of structures of high - strength steels are formulated.They are mainly directed to the weakening of de offect of the factors which contribute to a delayed fracture of joints (diffusive hydrogen,unfavourable rates of cooling,level of residual stresses). When there are no stress concentrators (and at a low level of residual stresses) the welded joints of these steels have a good resistance to fatigue and brittle fractures.As a rule, they are prevented with the help of the known approaches.It is shown that in addition to them and due to a proper selection of conditions of welding the life of welded joints of the high - strength steels can be 1. 2 - 1. 4 times in- creased.

Experimental and Numerical Analysis of High-Strength Concrete Beams Including Steel Fibers and Large-Particle Recycled Coarse Aggregates

In order to study the performances of high-strength concrete beams including steel fibers and large-particle recycled aggregates,four different beams have been designed,tested experimentally and simulated numerically.As varying parameters,the replacement rates of recycled coarse aggregates and CFRP(carbon fiber reinforced polymer)sheets have been considered.The failure mode of these beams,related load deflection curves,stirrup strain and shear capacity have been determined through monotonic loading tests.The simulations have been conducted using the ABAQUS finite element software.The results show that the shear failure mode of recycled concrete beams is similar to that of ordinary concrete beams.The shear carrying capacity of high-strength concrete beams including steel fibers and large-particle recycled coarse aggregates grows with an increase in the replacement rate of recycled coarse aggregates.Reinforcement with CFRP sheets can significantly improve the beam’s shear carrying capacity and overall resistance to deformation.

Forming condition and control strategy of ferrite decarburization in 60Si2MnA spring steel wires for automotive suspensions

The ferrite decarburization behavior of 60Si2MnA spring steel wires for automotive suspensions, including the forming condition and the influence of heating time and cooling rate after hot rolling, was investigated comprehensively. Also, a control strategy during the reheating process and cooling process after rolling was put forward to protect against ferrite decarburization. The results show that ferrite decarburization, which has the strong temperature dependence due to phase transformation, is produced between 675 and 875°C. The maximum depth is found at 750°C. Heating time and cooling rate after rolling have an important influence on decarburization. Reasonable preheating temperature in the billet reheating process and austenitizing temperature in the heat-treatment process are suggested to protect against ferrite decarburization.

Surface decarburization characteristics and relation between decarburized types and heating temperature of spring steel 60Si2MnA

The characteristics of complete and partial decarburizations in spring steel 60Si2MnA were systematically investigated,including the microstructure,the hardness gradient,and the formation mechanism.The relation between decarburized types and heating temperature of the steel was comprehensively discussed.It is found that heating temperature has an important influence on the decarburized types.With the rise of heating temperature,the decarburized types change from no decarburization to complete decarburization,complete and partial decarburizations,partial decarburization,and no decarburization.

Determining role of heterogeneous microstructure in lowering yield ratio and enhancing impact toughness in high-strength low-alloy steel

Here we present a novel approach of intercritical heat treatment for microstructure tailoring,in which intercritical annealing is introduced between conventional quenching and tempering.This induced a heterogeneous microstructure consisting of soft intercritical ferrite and hard tempered martensite,resulting in a low yield ratio(YR)and high impact toughness in a high-strength low-alloy steel.The initial yielding and subsequent work hardening behavior of the steel during tensile deformation were modified by the presence of soft intercritical ferrite after intercritical annealing,in comparison to the steel with full martensitic microstructure.The increase in YR was related to the reduction in hardness difference between the soft and hard phases due to the precipitation of nano-carbides and the recovery of dislocations during tempering.The excellent low-temperature toughness was ascribed not only to the decrease in probability of microcrack initiation for the reduction of hardness difference between two phases,but also to the increase in resistance of microcrack propagation caused by the high density of high angle grain boundaries.

Deformation-softening behaviors of high-strength and high-toughness steels used for rock bolts

In deep ground engineering,the use of high-strength and high-toughness steels for rock bolt can significantly improve its energy absorption capacity.However,the mechanisms and effects of rock loading conditions on this kind of high energy-absorbing steel for rock bolt remain immature.In this study,taking Muzhailing highway tunnel as the background,physically based crystal plasticity simulations were performed to understand the effect of rock loading rate and pretension on the deformation behaviors of twinning induced plasticity(TWIP)steel used for rock bolt.The material physical connecting to the underlying microscopic mechanisms of dislocation glide and deformation twinning were incorporated in numerical modeling.The rock loading conditions were mimicked by the real-time field monitoring data of the NPR bolt/cable equipment installed on the tunnel surrounding rock surface.The results indicate that the bolt rod exhibits pronounced deformation-softening behavior with decrease of the loading rate.There is also a sound deformation-relaxation phenomenon induced by the dramatic decrease of loading rate after pre-tensioning.The high pretension(>600 MPa or 224 k N)can help bolt rod steel resist deformation-softening behavior,especially at low loading rate(<10~(-1)MPa/s or 10~(-2)kN/s).The loading rate was found to be a significant factor affecting deformation-softening behavior while the pretension was found to be the major parameter accounting for the deformation-relaxation scenario.The results provide the theoretical basis and technical support for practical applications.

Kinetic analysis of austenite transformation for B1500HS high-strength steel during continuous heating

The dilatometric curves of B1500HS high-strength steel at different heating rates were measured by a Gleeble-3800 thermal simulator and analyzed to investigate the effect of heating rate on austenitization.Results show that the value of starting temperature and ending temperature of austenite transformation increase with the rise of heating rates,whereas the temperature interval of austenite formation decreases.The kinetic equation of austenite transformation was solved using the Johnson–Mehl–Avrami model,and the related parameters of the equation were analyzed by the Kissinger method.For those calculations,the activation energy of austenite transformation is 1.01×10^6 J/mol,and the values of kinetic parameters n and ln k0 are 0.63 and 103.03,respectively.The relationship between the volume fraction of austenite and the heating time at different heating rates could be predicted using the kinetic equation.The predicted and experimental results were compared to verify the accuracy of the kinetic equation.The microstructure etched by different corrosive solutions was analyzed,and the reliability of kinetic equation was further verified from the microscopic perspective.

Analysis of vibration reduction characteristics and applicability of steel-spring floating-slab track

A coupled dynamics computation model for metro vehicles,along with a steel-spring floating-slab track,is developed based on the theory of vehicle-track coupled dynamics.Using the developed model,the influences of the thickness,length and mass of floating-slab,spring rate and its arrangement space,running speed,etc.on the time and frequency domain characteristics of steel-spring fulcrum force are analyzed.The applicability of steel-spring floating-slab track is discussed through two integrated example cases of metro and buildings possessing distinct natural vibra-tion characteristics.It is concluded that,it is quite significant,in the optimization modular design of the parameters of steel-spring floating-slab track,to take the matching relationship of both the amplitude-frequency characteristics of steel-spring fulcrum force and natural vibration characteristics of integrated structures into comprehensive considera-tion.In this way the expensive steel-spring floating-slab track can be economically and efficiently utilized according to the site condition,and at the same time,the economic losses and bad social impact resulted from the resonance during usage of steel-spring floating-slab track can be avoided.

Development of low-cost high-strength stainless steel for new-energy bus frames

Along with strict environmental regulation,new-energy vehicles are becoming increasingly popular due to their low emissions,and they will inevitably replace existing fossil-fuel-based buses in China. To achieve a lightw eight bus body,high-strength steels are commonly used for the bus frame,but these grades are susceptible to corrosion. From the perspective of "lower life-cycle cost ",high-strength stainless steel is a better bus structure choice than high-strength carbon steels,since stainless steel bus frames last 10-15 years without requiring any maintenance. The low-cost high-strength stainless steels developed by Baosteel are introduced,the yield and tensile strengths of which can be controlled to within the range of 350-700 MPa and 900-1 200 MPa,respectively,and the elongation values are above 30%. Measurements of the toughness and fatigue resistance of these high-strength stainless steels and their joints indicate that the structural integrity requirements for bus frames can be met. The results of salt spray corrosion studies indicate that stainless steels will substantially increase the service life of bus frames in wet and icy winter conditions w here deicing with Ca Cl_2 is necessary for road safety. The results of our investigation clearly indicate that high-strength stainless steel is a potential bus-frame material that makes it possible to achieve substantial weight savings,excellent corrosion resistance,and prolonged operational life.

Finite element analysis of the end cutting process for U-section parts with high-strength steel

This paper presents a constitutive framework for finite element analysis of the truck beam end cutting process.For this purpose,a finite strain anisotropic elasto-plastic model,which takes nonlinear kinematic and isotropic hardening into account,is presented.Three factors are investigated to determine the effect on cutting quality:radius of cutting tools,strength of materials and relative clearance in cutting.The recommendations made herein are based on the simulation results.

Inclusion control of automotive spring steel in the basic oxygen furnace and ingot casting process

The process of automotive spring steel in the basic oxygen furnace and ingot casting(BOF-IC)of Baosteel is described in this paper.High quality spring steel can be obtained through designing reasonable deoxidization and alloying processes,enhancing steel purity and reducing inclusions in steel.