Synergistic effect of Zr and Mo on precipitation and high-temperature properties of Al-Si-Cu-Mg alloys

This study focuses on finding a solution to the sharp decline in mechanical properties of Al-Si-Cu-Mg alloys due to rapid coarsening of traditional intermediate phases at high temperature.A new type of modified al oy,to be used in automobile engines at high temperatures,was prepared by adding Zr and Mo into Al-Si-Cu-Mg alloy.The synergistic effects of Zr and Mo on the microstructure evolution and high-temperature mechanical properties were studied.Results show that the addition of Zr and Mo generates a series of intermetallic phases dispersed in the alloy.They can improve the strength of the alloy by hindering dislocation movement and crack propagation.In addition,some nano-strengthened phases show coherent interfaces with the matrix and improve grain refinement.The addition of Mo greatly improves the heat resistance of the alloy.The extremely low diffusivity of Mo enables it to improve the thermal stability of the intermetallic phases,inhibit precipitation during aging,reduce the size of the precipitates,and improve the heat resistance of the alloy.

The Research for Surface Properties of Steel Slag Powder and High-Temperature Rheological Properties of Asphalt Mortar

In order to evaluate the feasibility of steel slag powder as filler,the coating properties of steel slag and limestone aggregate were compared by water boiling test,the micro morphology difierences between steel slag powder and mineral powder(limestone powder)were compared by scanning electron microscope(SEM),and the high-temperature rheological properties of asphalt mortar with difierent ratio of filler quality to asphalt quality(F/A)and difierent substitution rates of mineral powder(S/F)were studied by dynamic shear rheological test.The results show that the surface microstructure of steel slag powder is more abundant than that of mineral powder,and the adhesion of steel slag to asphalt is better than that of limestone.At the same temperature,the lower the ratio of S/F is,the greater the rutting factor and complex modulus will be.In addition,the complex modulus and rutting factor of the asphalt mortar increase with the increase of F/A,and the filler type and F/A have a negligible efiect on the phase angle.

Temperature dependence of anisotropic stress-rupture properties of nickel-based single crystal superalloy SRR99

In order to reveal the temperature dependence of anisotropic stress？rupture behavior of SRR99 single crystal superalloys under conditions of temperature ranging from 650 to 1 040 °C and typical stresses,fracture morphologies and microstructure evolution were investigated by SEM and TEM.From the Larson-Miller curves,it is found that single crystal with [001] orientation has the optimum stress rupture property in comparison with [011] and [111] orientations at lower and intermediate temperature.With increasing temperature to 1 040 °C,stress-rupture properties of single crystals with three principal orientations tend to be equivalent.Based on the fracture surface and microstructural observations,superior stress？rupture behavior of single crystal with [001] orientation was rationalized and the effect of misorientation of single crystal on stress rupture property was also discussed.

Effect of extrusion process on microstructure and mechanical properties of Ni_3Al-B-Cr alloy during self-propagation high-temperature synthesis

The well-densified Ni3Al-0.5B-5Cr alloy was fabricated by self-propagation high-temperature synthesis and extrusion technique. Microstructure examination shows that the synthesized alloy has fine microstructure and contains Ni3Al, Al2O3, Ni3B and Cr3Ni2 phases. Moreover, the self-propagation high-temperature synthesis and extrusion lead to great deformation and recrystallization in the alloy, which helps to refine the microstructure and weaken the misorientation. In addition, the subsequent extrusion procedure redistributes the Al2O3 particles and eliminates the γ-Ni phase. Compared with the alloy synthesized without extrusion, the Ni3Al-0.5B-5Cr alloy fabricated by self-propagation high-temperature synthesis and extrusion has better room temperature mechanical properties, which should be ascribed to the microstructure evolution.

Effects of Sn element on microstructure and properties of Zn-Cu-Bi-Sn high-temperature solder

The microstructures and properties of the Zn-Cu-Bi-Sn(ZCBS) high-temperature solders with various Sn contents were studied using differential scanning calorimetry(DSC),scanning electron microscopy(SEM) and X-ray diffraction(XRD).The results indicate that the increase of Sn content can both decrease the melting temperature and melting range of ZCBS solders and it can also effectively improve the wettability on Cu substrate.The shear strength of solder joints reaches a maximum value with the Sn addition of 5%(mass fraction),which is attributed to the formation of refined β-Sn and primary ε-CuZn_5 phases in η-Zn matrix.However,when the content of Sn exceeds 5%,the shear strength decreases due to the formation of coarse β-Sn phase,which is net-shaped presented at the grain boundary.

A high-temperature resistant and high-density polymeric saturated brine-based drilling fluid

Three high-temperature resistant polymeric additives for water-based drilling fluids are designed and developed:weakly cross-linked zwitterionic polymer fluid loss reducer(WCZ),flexible polymer microsphere nano-plugging agent(FPM)and comb-structure polymeric lubricant(CSP).A high-temperature resistant and high-density polymeric saturated brine-based drilling fluid was developed for deep drilling.The WCZ has a good anti-polyelectrolyte effect and exhibits the API fluid loss less than 8 mL after aging in saturated salt environment at 200°C.The FPM can reduce the fluid loss by improving the quality of the mud cake and has a good plugging effect on nano-scale pores/fractures.The CSP,with a weight average molecular weight of 4804,has multiple polar adsorption sites and exhibits excellent lubricating performance under high temperature and high salt conditions.The developed drilling fluid system with a density of 2.0 g/cm^(3)has good rheological properties.It shows a fluid loss less than 15 mL at 200°C and high pressure,a sedimentation factor(SF)smaller than 0.52 after standing at high temperature for 5 d,and a rolling recovery of hydratable drill cuttings similar to oil-based drilling fluid.Besides,it has good plugging and lubricating performance.

Magnetic properties of La-Zn substituted Sr-hexaferrites by self-propagation high-temperature synthesis

The La-Zn substituted SrM-type ferrites with the composition of Sr1-xLaxFe12-xZnxO19 （x=0-0.4） were prepared by self-propagating high-temperature synthesis （SHS）. The single SrM phase was detected by XRD in the as-received samples by controlling the Fe contents in the reagents. The substitution of La^3＋and Zn^2＋ obviously increased the magnetic properties of the as-prepared samples. The maximum improvements of Br, Hcb and （BH）m were 14.4%, 15.3% and 30.7%, respectively compared with that of the samples without La-Zn substitution. Microstructure observation by SEM showed that the SHS method benefited forming the better particle features and achieving the higher Hcj in comparison with the traditional firing method.

Microstructure and high-temperature mechanical properties of laser beam welded TC4/TA15 dissimilar titanium alloy joints

The microstructure evolution and high-temperature mechanical properties of laser beam welded TC4/TA15 dissimilar titanium alloy joints under different welding parameters were studied.The results show that the weld fusion zone of TC4/TA15 dissimilar welded joints consists of coarsenedβcolumnar crystals that contain mainly acicularα’martensite.The heat affected zone is composed of the initialαphase and the transformedβstructure,and the width of heat affected zone on the TA15 side is narrower than that on the TC4 side.With increasing temperature,the yield strength and ultimate tensile strength of the TC4/TA15 dissimilar welded joints decrease and the highest plastic deformation is obtained at 800°C.The tensile strength of the dissimilar joints with different welding parameters and base material satisfies the following relation(from high to low):TA15 base material>dissimilar joints>TC4 base material.The microhardness of a cross-section of the TC4/TA15 dissimilar joints reaches a maximum at the centre of the weld and is reduced globally after heat treatment,but the microhardness distribution is not changed.An elevated temperature tensile fracture of the dissimilar joints is located on the side of the TC4 base material.Necking occurs during the tensile tests and the fracture characteristics are typical when ductility is present in the material.

High-temperature mechanical properties of aluminium alloys reinforced with titanium diboride (TiB_2) particles

The physical and mechanical properties of metal matrix composites were improved by the addition of reinforcements. The mechanical properties of particulate-reinforced metal-matrix composites based on aluminium alloys （6061 and 7015） at high temperatures were studied. Titanium diboride （TiB2） particles were used as the reinforcement. All the composites were produced by hot extrusion. The tensile properties and fracture characteristics of these materials were investigated at room temperature and at high temperatures to determine their ultimate strength and strain to failure. The fracture surface was analysed by scanning electron microscopy. TiB2 particles provide high stability of the alumin- ium alloys （6061 and 7015） in the fabrication process. An improvement in the mechanical behaviour was achieved by adding TiB2 particles as reinforcement in both the aluminium alloys. Adding TiB2 particles reduces the ductility of the aluminium alloys but does not change the microscopic mode of failure, and the fracture surface exhibits a ductile appearance with dimples formed by coalescence.

Enhanced thermal stability and mechanical properties of high-temperature resistant Al-Cu alloy with Zr and Mn micro-alloying

The high temperature(HT)thermal stability and mechanical properties of Al-5%Cu(AC)and Al-5%Cu-0.2%Mn-0.2 Zr%(ACMZ)alloys from 573 to 673 K were systematically studied.The results displayed that micro-alloying additions of Zr and Mn elements have presented a significant role in stabilizing the main strengthening metastableθ′precipitates at a temperature as high as 573 K.Simultaneously,the HT tensile test demonstrated that ACMZ alloy retained their strength of(88.6±8.8)MPa,which was much higher than that of AC alloy((32.5±0.8)MPa)after the thermal exposure at 573 K for 200 h.Finally,the underlying mechanisms of strength and ductility enhancement mechanism of the ACMZ alloy at HT were discussed in detail.

Microstructure and high-temperature mechanical properties of near net shaped Ti−45Al−7Nb−0.3W alloy by hot isostatic pressing process

Near net shaped Ti−45Al−7Nb−0.3W alloy(at.%)parts were manufactured by hot isostatic pressing(HIP).The microstructure and high-temperature mechanical properties of the alloy were investigated by X-ray diffractometry(XRD),scanning electron microscopy(SEM)and transmission electron microscopy(TEM).The results show that at a temperature of 700℃,the peak yield stress(YS)and ultimate tensile stress(UTS)of alloy are 534 and 575 MPa,respectively,and the alloy shows satisfactory comprehensive mechanical properties at 850℃.The alloy exhibits superplastic characteristics at 1000℃ with an initial strain rate of 5×10^−5 s^−1.When the tensile temperature is below 750℃,the deformation mechanisms are dislocation movements and mechanical twinning.Increasing the tensile temperature above 800℃,grain boundary sliding and grain rotation occur more frequently due to the accumulation of dislocations at grain boundary.

A High-Temperature β-Phase NaMnO2 Stabilized by Cu Doping and Its Na Storage Properties

The high-temperature β-phase NaMnO2 is a promising material for Na-ion batteries（NIBs） due to its high capacity and abundant resources. However, the synthesis of phase-pure -NaMnO2 is burdensome and costineffective because it needs to be sintered under oxygen atmosphere at high temperature and followed by a quenching procedure. Here we first report that the pure β phase can be stabilized by Cu-doping and easily synthesized by replacing a proportion of Mn with Cu via a simplified process including sintering in air and cooling to room temperature naturally. Based on the first-principle calculations, the band gap decreases from 0.7 eV to 0.3 eV, which indicates that the electronic conductivity can be improved by Cu-doping. The designed -NaCu（0.1）Mn（0.9）O2 is applied as cathode in NIBs, exhibiting an energy density of 419 Wh/kg and better performance in terms of rate capability and cycling stability than those in the undoped case.

Effect of boron addition on the microstructure and stress-rupture properties of directionally solidified superalloys

This study is focused on the effect of boron addition, in the range of 0.0007wt% to 0.03wt%, on the microstructure and stress-rupture properties of a directionally solidified superalloy. With increasing boron content in the as-cast alloys, there is an increase in the fraction of the γ′/γ eutectic and block borides precipitate around the γ′/γ eutectic. At a high boron content of 0.03wt%, there is precipitation of lamellar borides. Upon heat treatment, fine block borides tend to precipitate at grain boundaries with increasing boron content. Overall, the rupture life of the directionally solidified superalloy is significantly improved with the addition of nominal content of boron. However, the rupture life decreases when the boron content exceeds 0.03wt%.

Carbides Formation in MarM247 Directional Solidified during Stress-Rupture Test at High Temperature

In our study, stress-rupture tests were conducted at elevated temperatures to examine the impact of high temperature on MarM247 LC (low carbon). Our main objective was to investigate the alterations in the microstructure, particularly the carbon precipitation, during long-term stress-rupture tests. It was observed that cracks developed near the sample neck, following the path of the carbides and the gamma matrix, rather than occurring in the gamma-gamma prime eutectic. This occurred despite the formation of carbides because of prolonged exposure to high temperature and load, and the crack propagation did not follow that path. Based on these findings, we suggest that a reduction in the carbon content of Mar-M247 LC can enhance the sample's lifespan when subjected to temperatures below 760˚C and a stress of 690 MPa.

Experimental Evaluation of the Mechanical Properties of Cement Sheath under High-Temperature Conditions

The sealing integrity of cement sheath in offshore wells is seriously threatened under high-temperature conditions,resulting in gas channeling and other problems.Given the lack of experimental results,in this study relevant samples of a cement slurry sealing section of a typical offshore high-temperature well have been prepared and analyzed.In particular,the mechanical properties have been assessed with a triaxial pressure servo instrument and a high-temperature curing kettle.The density and the Poisson’s ratio of the samples have also been tested.The stress-strain curve has been drawn to obtain the elastic modulus and the compressive strength.The rock brittleness index has been calculated according to the measured elastic modulus and the Poisson’s ratio,together with the brittleness and the compressibility of the cement samples.The test results show that the mechanical properties and bonding strength of the cement samples are optimal at 130°C,medium at 150°C,and poor at 180°C.

Effect of hot isostatic pressure on the microstructure and tensile properties of γ'-strengthened superalloy fabricated through induction-assisted directed energy deposition

The microstructure characteristics and strengthening mechanism of Inconel738LC(IN-738LC) alloy prepared by using induction-assisted directed energy deposition(IDED) were elucidated through the investigation of samples subjected to IDED under 1050℃ preheating with and without hot isostatic pressing(HIP,1190℃,105 MPa,and 3 h).Results show that the as-deposited sample mainly consisted of epitaxial columnar crystals and inhomogeneously distributed γ’ phases in interdendritic and dendritic core regions.After HIP,grain morphology changed negligibly,whereas the size of the γ’ phase became increasingly even.After further heat treatment(HT,1070℃,2 h + 845℃,24 h),the γ’ phase in the as-deposited and HIPed samples presented a bimodal size distribution,whereas that in the as-deposited sample showed a size that remained uneven.The comparison of tensile properties revealed that the tensile strength and uniform elongation of the HIP + HTed sample increased by 5% and 46%,respectively,due to the synergistic deformation of bimodal γ’phases,especially large cubic γ’ phases.Finally,the relationship between phase transformations and plastic deformations in the IDEDed sample was discussed on the basis of generalized stability theory in terms of the trade-off between thermodynamics and kinetics.

Creep rupture properties and microstructure stability of the GH984G alloy tube

GH984G alloy is a significant candidate material for 650-700℃ ultra-supercritical coal-fired generating units.In this paper,creep rupture properties and microstructure stability of the GH984G alloy tube were studied,and the findings indicated excellent creep rupture properties at 700℃.Furthermore,the extrapolated strength for 100000 h was found to be 153.8 MPa,which satisfies the requirements for the long-term performance of high-temperature materials in power stations.Aging at 700℃ with the extension of time,the grain boundary carbides and the particle size of the γ′phase on the matrix gradually coarsen,but its spherical morphology remains uniformly distributed.However,no harmful phase precipitates were found even after aging at 700℃ for up to 19144 h.Excellent microstructure stability guarantees the 700℃ creep rupture properties of the GH984G alloy tube.

Effects of Bi and rare earth metal on the microstructure and properties of Zn-based high-temperature solder

A novel Zn-based high-temperature solder was developed to join copper/steel at moderate temperature. The effects of Bi and rare earth metal on the microstructures , wettability of solders as well as the mechanical properties of solder joints were investigated. The results indicated that with the addition of Bi into Zn-Cu-Sn （ZCS） alloy, significant improvement in wettability is realized. When the content of Bi element is 1.5 wt. % in the solder, the spreading area researched over 200 mm^2. Furthermore, with the addition of RE, refined primary ε-CuZn5 phases were formed and the shear strength of the solder joint was largely improved.

Reaction mechanism of metal and pyrite under high-pressure and high-temperature conditions and improvement of the properties

Pyrite tailings are the main cause of acid mine wastewater.We propose an idea to more effectively use pyrite,and it is modified by exploiting the reducibility of metal represented by Al under high-pressure and high-temperature(HPHT)conditions.Upon increasing the Al addition,the conductivity of pyrite is effectively improved,which is nearly 734 times higher than that of unmodified pyrite at room temperature.First-principles calculations are used to determine the influence of a high pressure on the pyrite lattice.The high pressure increases the thermal stability of pyrite,reduces pyrite to highconductivity Fe7S8(pyrrhotite)by Al.Through hardness and density tests the influence of Al addition on the hardness and toughness of samples is explored.Finally we discuss the possibility of using other metal-reducing agents to improve the properties of pyrite.

Research on microstructure and high-temperature friction and wear properties of a cobalt-based alloy for hot extrusion die

The hot extrusion die is a key tool for determining the surface quality and dimensional accuracy of extruded products.Because its service process is subject to high temperature,high pressure,and wear,it must be resistant to these conditions.In this paper,the high-temperature friction and wear properties of a cobalt(Co)-based alloy were investigated and compared with those of a titanium carbide(TiC)cemented material.The results show that the high-temperature wear performance of the Co-based alloy is better than that of the TiC cemented material,and that Co-based materials have the potential for replacing TiC cemented materials as hot-extrusion-die materials.Due to the high density and good combination of the matrix and carbide,the carbides do not easily peel off from the matrix during the wear process.Due to the higher impact toughness of the Co-based alloys,microcracks that can cause worn-surface peeling are not easily generated.As a result,the high-temperature wear performance of Co-based alloys is found to be better than that of TiC cemented materials.