Holding temperature and holding thickness are main parameters for two-phase controlled rolling on plate mill. The optimization of holding temperature and holding thickness for pass schedule calculation of two-phase co...Holding temperature and holding thickness are main parameters for two-phase controlled rolling on plate mill. The optimization of holding temperature and holding thickness for pass schedule calculation of two-phase controlled rolling on plate mill was presented and its feature is as follows： （1） Determination of holding thickness can be automatically obtained based on the influence of mill safety limits, tracking zone length and holding time on holding thickness; （2） Determination of holding temperature can be automatically obtained and the holding time can be reduced as much as possible; （3） Algorithm can modify the holding temperature and thickness depending on slab size and product size.展开更多
采用1 mm Al+3 mm Mg+1 mm Al的组坯方式,轧制温度为400℃,压下率为35%,热轧得到6061/AZ31B/6061复合板。在退火温度为200℃的条件下,研究了不同退火时间对复合板拉伸性能、界面结合、微观组织以及表面残余应力的影响。在保温时间分别为...采用1 mm Al+3 mm Mg+1 mm Al的组坯方式,轧制温度为400℃,压下率为35%,热轧得到6061/AZ31B/6061复合板。在退火温度为200℃的条件下,研究了不同退火时间对复合板拉伸性能、界面结合、微观组织以及表面残余应力的影响。在保温时间分别为0、0.5、1和1.5 h情况下,分别进行拉伸实验、能谱分析、微观组织观察和残余应力测试。结果表明,当轧制压下率为35%时,6061铝合金和AZ31B镁合金能够通过热轧方法得到很好的复合;随着退火时间的增加,6061/AZ31B/6061复合板的拉伸强度、伸长率和界面扩散厚度显著增加,且铝合金表面残余应力也增大。展开更多
文摘Holding temperature and holding thickness are main parameters for two-phase controlled rolling on plate mill. The optimization of holding temperature and holding thickness for pass schedule calculation of two-phase controlled rolling on plate mill was presented and its feature is as follows： （1） Determination of holding thickness can be automatically obtained based on the influence of mill safety limits, tracking zone length and holding time on holding thickness; （2） Determination of holding temperature can be automatically obtained and the holding time can be reduced as much as possible; （3） Algorithm can modify the holding temperature and thickness depending on slab size and product size.
文摘采用1 mm Al+3 mm Mg+1 mm Al的组坯方式,轧制温度为400℃,压下率为35%,热轧得到6061/AZ31B/6061复合板。在退火温度为200℃的条件下,研究了不同退火时间对复合板拉伸性能、界面结合、微观组织以及表面残余应力的影响。在保温时间分别为0、0.5、1和1.5 h情况下,分别进行拉伸实验、能谱分析、微观组织观察和残余应力测试。结果表明,当轧制压下率为35%时,6061铝合金和AZ31B镁合金能够通过热轧方法得到很好的复合;随着退火时间的增加,6061/AZ31B/6061复合板的拉伸强度、伸长率和界面扩散厚度显著增加,且铝合金表面残余应力也增大。