Novel hollow Fe3O4 nanoparticles for drug delivery were synthesized via a one-step template- free approach. These nanoparticles were obtained by modifing the Fe3O4 nanoparticles with 3-aminopropyltrimethoxy silane, an...Novel hollow Fe3O4 nanoparticles for drug delivery were synthesized via a one-step template- free approach. These nanoparticles were obtained by modifing the Fe3O4 nanoparticles with 3-aminopropyltrimethoxy silane, and then grafting alginate onto the surface of amine magnetic. The hollow structure of Fe3O4 spheres was characterized by TEM, XRD, and XPS. The M-H hysteresis loop indicated that the magnetic spheres exhibit snperparamagnetic characteristics at room temperature. Daunorubicin acting as a model drug was loaded into the carrier, and the maximum percent of envelop and load were 28.4% and 14.2% respectively. The drug controlled releasing behaviors of the carriers were compared in different pH media.展开更多
Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. T...Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. The product was characterized by IR,XRD,TEM,Vibrating Sample Magnetometer (VSM),TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe3O4 nanoparticles is also suggested.展开更多
文摘Novel hollow Fe3O4 nanoparticles for drug delivery were synthesized via a one-step template- free approach. These nanoparticles were obtained by modifing the Fe3O4 nanoparticles with 3-aminopropyltrimethoxy silane, and then grafting alginate onto the surface of amine magnetic. The hollow structure of Fe3O4 spheres was characterized by TEM, XRD, and XPS. The M-H hysteresis loop indicated that the magnetic spheres exhibit snperparamagnetic characteristics at room temperature. Daunorubicin acting as a model drug was loaded into the carrier, and the maximum percent of envelop and load were 28.4% and 14.2% respectively. The drug controlled releasing behaviors of the carriers were compared in different pH media.
文摘Nano-sized Fe3O4 powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe3O4 powders through Microlatex-Crosslinking Method. The product was characterized by IR,XRD,TEM,Vibrating Sample Magnetometer (VSM),TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe3O4 nanoparticles is also suggested.