Hot deformation of sintered billets by powder metallurgy(PM)is an effective preparation technique for titanium alloys,which is more significant for high-alloying alloys.In this study,Ti–6.5Al–2Zr–Mo–V(TA15)titaniu...Hot deformation of sintered billets by powder metallurgy(PM)is an effective preparation technique for titanium alloys,which is more significant for high-alloying alloys.In this study,Ti–6.5Al–2Zr–Mo–V(TA15)titanium alloy plates were prepared by cold press-ing sintering combined with high-temperature hot rolling.The microstructure and mechanical properties under different process paramet-ers were investigated.Optical microscope,electron backscatter diffraction,and others were applied to characterize the microstructure evolution and mechanical properties strengthening mechanism.The results showed that the chemical compositions were uniformly dif-fused without segregation during sintering,and the closing of the matrix craters was accelerated by increasing the sintering temperature.The block was hot rolled at 1200℃ with an 80%reduction under only two passes without annealing.The strength and elongation of the plate at 20–25℃ after solution and aging were 1247 MPa and 14.0%,respectively,which were increased by 24.5%and 40.0%,respect-ively,compared with the as-sintered alloy at 1300℃.The microstructure was significantly refined by continuous dynamic recrystalliza-tion,which was completed by the rotation and dislocation absorption of the substructure surrounded by low-angle grain boundaries.After hot rolling combined with heat treatment,the strength and plasticity of PM-TA15 were significantly improved,which resulted from the dense,uniform,and fine recrystallization structure and the synergistic effect of multiple slip systems.展开更多
With the intensification of market competition in the aluminum alloy strip processing industry,it is dif-ficult to control the mass production of the same specifications,which is bound to affect the hot rolling produc...With the intensification of market competition in the aluminum alloy strip processing industry,it is dif-ficult to control the mass production of the same specifications,which is bound to affect the hot rolling production.This paper studied the effect of the hot rolling order of aluminum alloy on the surface quality of strip,such as roll printing,color difference,anodic oxidation,etc.,reasonable discharge sequence and corresponding optimization measures were formulated.展开更多
It was discovered the application of Al_(2)O_(3) nanofluid as lubricant for steel hot rolling could synchronously achieve oxidation protection of strips surface.The underlying mechanism was investigated through hot ro...It was discovered the application of Al_(2)O_(3) nanofluid as lubricant for steel hot rolling could synchronously achieve oxidation protection of strips surface.The underlying mechanism was investigated through hot rolling tests and molecular dynamics (MD) simulations.The employment of Al_(2)O_(3) nanoparticles contributed to significant enhancement in the lubrication performance of lubricant.The rolled strip exhibited the best surface topography that the roughness reached lowest with the sparsest surface defects.Besides,the oxide scale generated on steel surface was also thinner,and the ratio of Fe_(2)O_(3) among various iron oxides became lower.It was revealed the above oxidation protection effect of Al_(2)O_(3) nanofluid was attributed to the deposition of nanoparticles on metal surface during hot rolling.A protective layer in the thickness of about 193 nm was formed to prevent the direct contact between steel matrix and atmosphere,which was mainly composed of Al_(2)O_(3) and sintered organic molecules.MD simulations confirmed the diffusion of O_(2) and H_(2)O could be blocked by the Al_(2)O_(3) layer through physical absorption and penetration barrier effect.展开更多
Based on the important boundary conditions of rolling simulation including friction, heat conduction and interactionsof the workpiece and rolls, the hot continuous rolling processes of large-diameter mandrel round bar...Based on the important boundary conditions of rolling simulation including friction, heat conduction and interactionsof the workpiece and rolls, the hot continuous rolling processes of large-diameter mandrel round bar (200 mm indiameter) in 6VH-stand hot tandem mill are successfully simulated by three-dimensional coupled thermomechanicalelastoplastic finite element method (FEM). The distributions of stress, strain, temperature and the rolling force andtorque for the two-pass and four-pass continuous rolling are calculated respectively. Thus, the two and four-passroll schedules are verified, respectively. The simulation results show that it is safe to produce 200 mm round barby the two-pass (oval pass and round pass) continuous rolling on the existing equipment compared to the four-passcontinuous rolling. There are concave surfaces and increased widths occurring at the end of rolled billet due touneven deformations between the outside and inside of the workpiece as well as the free spreading close to the rollgap of the final pass.展开更多
A three-dimensional model for strip hot rolling was developed, in which the plastic deformation of strip, the thermal crown of rolls, roll deflection and flattening were calculated by rigid-plastic finite element meth...A three-dimensional model for strip hot rolling was developed, in which the plastic deformation of strip, the thermal crown of rolls, roll deflection and flattening were calculated by rigid-plastic finite element method, finite difference method, influential function method and elastic finite element method respectively. The roll wear was taken into consideration. The model can provide detailed information such as rolling pressure distribution, contact pressure distribution between backup rolls and work rolls, deflection and flattening of work rolls, lateral distribution of strip thickness, and lateral distribution of front and back tensions. The finish rolling on a 1 450 mm hot strip mill was simulated.展开更多
In the present study,the texture evolution and mechanical anisotropy in a typical Mg–Zn–Ca alloy through hot cross rolling(CR)and unidirectional rolling(UR)were systematically studied.The results show that the rolli...In the present study,the texture evolution and mechanical anisotropy in a typical Mg–Zn–Ca alloy through hot cross rolling(CR)and unidirectional rolling(UR)were systematically studied.The results show that the rolling path greatly affects the annealed texture.The UR develops a texture with basal poles mainly distributing along the transverse direction(TD).By contrast,an ellipse-like(0002)texture with basal pole inclining largely away from the normal direction(ND)is developed after hot cross rolling and annealing.Therefore,the CR is an effective method to tailor the texture of the experimental alloy.Unfortunately,this ellipse-like texture could not reserve during the subsequent unidirectional hot rolling and annealing.Both UR and CR plates exhibit a strong planar mechanical anisotropy compared with the traditional unidirectional rolled plate.展开更多
The thermoplasticity of duplex stainless steel 2205(DSS2205) is better than that of lean duplex steel 2101(LDX2101), which undergoes severe cracking during hot rolling. The microstructure, microhardness, phase rat...The thermoplasticity of duplex stainless steel 2205(DSS2205) is better than that of lean duplex steel 2101(LDX2101), which undergoes severe cracking during hot rolling. The microstructure, microhardness, phase ratio, and recrystallization dependence of the deformation compatibility of LDX2101 and DSS2205 were investigated using optical microscopy(OM), electron backscatter diffraction(EBSD), Thermo-Calc software, and transmission electron microscopy(TEM). The results showed that the phase-ratio transformations of LDX2101 and DSS2205 were almost equal under the condition of increasing solution temperature. Thus, the phase transformation was not the main cause for the hot plasticity difference of these two steels. The grain size of LDX2101 was substantially greater than that of DSS2205, and the microhardness difference of LDX2101 was larger than that of DSS2205. This difference hinders the transfer of strain from ferrite to austenite. In the rolling process, the ferrite grains of LDX2101 underwent continuous softening and were substantially refined. However, although little recrystallization occurred at the boundaries of austenite, serious deformation accumulated in the interior of austenite, leading to a substantial increase in hardness. The main cause of crack formation is the microhardness difference between ferrite and austenite.展开更多
A recrystallization model for hot rolling of 5182 aluminum alloy was presented by means of the fractional softening during double interval deformation. It is found that the recrystallization rate depends on strain rat...A recrystallization model for hot rolling of 5182 aluminum alloy was presented by means of the fractional softening during double interval deformation. It is found that the recrystallization rate depends on strain rate more sensitively than deformation temperature, and the time for full recrystallization is very short as strain rate is greater than 1?s -1 . Using the recrystallization—time—temperature curves, the desirable hot rolled microstructure can be obtained by controlling the rolling speed, temperature and cooling rate before cooling during the last pass in reversing mill.[展开更多
A series of simple axisymmetric compression tests were carried out on the computer servo controlled Gleeble 1 500 machine when strain rates ranged between 0.05 25 s -1 and deformation temperature 300 500 ℃. The resul...A series of simple axisymmetric compression tests were carried out on the computer servo controlled Gleeble 1 500 machine when strain rates ranged between 0.05 25 s -1 and deformation temperature 300 500 ℃. The results show that flow stress is related to the Zener Hollonom parameter Z and strain, as well as the static recrystallization fraction between passes during multipass hot deformation of 5182 aluminum alloy. Hence, a modified exponential flow stress equation was presented by considering the values of ln A and β as functions of strain, and by using the uniform softening method and incorporating the static recrystallization fraction between passes to consider the effects of residual strain during multipass hot rolling of 5182 aluminum alloy. The validity of the equation was examined by a typical non isothermal multipass deformation test.展开更多
In order to improve the quality of the strip for the hot continuous rolling, the high accuracy set-up control must be applied to production. In the paper, we analyze the RFC (profile and flatness control) system and s...In order to improve the quality of the strip for the hot continuous rolling, the high accuracy set-up control must be applied to production. In the paper, we analyze the RFC (profile and flatness control) system and simulate the set-up process. Calculation results are in agreement to the actual measurements. It is the basis on the developing model.展开更多
Al Pb alloy strips and hot dip aluminized steel sheets were successfully bonded together by hot rolling, and the interfacial bonding strengths after rolling was evaluated by a new method. The bonding modes were studie...Al Pb alloy strips and hot dip aluminized steel sheets were successfully bonded together by hot rolling, and the interfacial bonding strengths after rolling was evaluated by a new method. The bonding modes were studied by optical and scanning electron microscope and energy dispersive X ray analysis, and the effects of the thickness of the intermetallic layers and the Si content in hot dip aluminized layers on the interfacial bonding strength were also investigated respectively. It is found that the hot dipped steel and Al Pb alloy are bonded through blank interface bonding and block interface bonding, and the total bonding strength mainly depends on that of blank interfaces and the fraction of blank interfaces. There is a linear relationship between the total bonding strength F and the fraction of blank interfaces K b. The bonding strength varies with the Si content in the hot dipped aluminized layers on the surface of steel sheets, the fraction of blank interfaces and the rotation of the intermetallic blocks. [展开更多
Deep rolling is one of the most widely used surface mechanical treatments among several methods used to generate compressive residual stress. This process is usually used for axisymmetric components and can lead to im...Deep rolling is one of the most widely used surface mechanical treatments among several methods used to generate compressive residual stress. This process is usually used for axisymmetric components and can lead to improvements of the surface quality, dimensional accuracy, and mechanical properties. In this study, we deduced the appropriate deep rolling parameters for Al-3vol%Si C nanocomposite samples using roughness and microhardness measurements. The nanocomposite samples were fabricated using a combination of mechanical milling, cold pressing, and hot extrusion techniques. Density measurements indicated acceptable densification of the samples, with no porosity. The results of tensile tests showed that the samples are sufficiently strong for the deep rolling process and also indicated near 50% improvement of tensile strength after incorporating Si C nanoparticle reinforcements. The effects of some important rolling parameters, including the penetration depth, rotation speed, feed rate, and the number of passes, on the surface quality and microhardness were also investigated. The results demonstrated that decreasing the feed rate and increasing the number of passes can lead to greater surface hardness and lower surface roughness.展开更多
Mg-6Al-0.3Mn-xY(x=0,0.3,0.6 and 0.9,mass fraction,%) magnesium alloys were prepared by casting and hot rolling process.The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium...Mg-6Al-0.3Mn-xY(x=0,0.3,0.6 and 0.9,mass fraction,%) magnesium alloys were prepared by casting and hot rolling process.The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium alloy was investigated.The results reveal that with increasing the yttrium content,Al2Y precipitates form and the grain size is reduced.The ultimate strength,yield strength and elongation at room temperature are 192 MPa,62 MPa and 12.6%,respectively,for the as-cast Mg-6Al-0.3Mn-0.9Y alloy.All these properties are improved obviously by hot rolling,and the values are up to 303 MPa,255 MPa and 17.1%,respectively,for the rolled Mg-6Al-0.3Mn-0.9Y alloy.The improvement of mechanical properties is attributed to continuous dynamic recrystallization and the existence of highly thermal stable Al2Y precipitate which impedes the movement of dislocation effectively.展开更多
Multi-pass hot-rolling technique was used to fabricate W80Cu20 alloy,and its properties were characterized in this paper.Results show that the W-Cu alloy sheets with a thickness of 0.5 mm and a relative density of99.8...Multi-pass hot-rolling technique was used to fabricate W80Cu20 alloy,and its properties were characterized in this paper.Results show that the W-Cu alloy sheets with a thickness of 0.5 mm and a relative density of99.87%can be successfully made using this new technique at 800℃.In hot-rolling process,Cu phases are closely surrounded by W particles under the rolling stress to form a network microstructure,thus making significant increase in electrical and thermal conductivity up to53.00%and 24.44%,respectively.Transverse and longitudinal hardness of the W–Cu sheets significantly increase due to the enhanced densification and deformation strength.Similar to that of the raw materials,three fracture types were observed in the hot-rolled materials,i.e.,ductile fracture of Cu binding phases,trans-granular fracture of W phases,and W–W interfacial fracture.展开更多
AZ91 magnesium alloy was prepared by spray forming. The spray-deposited alloy was subsequently hot-rolled with a 80% reduction at 350 ℃. The microstructural features of the as-spray-deposited and hot-rolled alloy wer...AZ91 magnesium alloy was prepared by spray forming. The spray-deposited alloy was subsequently hot-rolled with a 80% reduction at 350 ℃. The microstructural features of the as-spray-deposited and hot-rolled alloy were examined by optical microscopy, scanning electron microscopy and X-ray diffractometry. The results show that the spray-formed AZ91 magnesium alloy has, compared with the as-cast ingot, a finer microstructure with less intermetallic phase Mg17Al12 dispersed in the matrix due to fast cooling and solidification rates of spray forming process, and, therefore showing excellent workability. It can be hot-rolled with nearly 20% reduction for one pass at lower temperatures (330-360℃), and the total reduction can reach 50% prior to annealing. After proper thermo-mechanical treatment, the spray-formed AZ91 magnesium alloy exhibits outstanding mechanical properties.展开更多
A 3D rigid-plastic and coupled thermo-mechanical FE model for hot ring rolling(HRR) was developed based on DEFORM 3D software,then coupled heat transferring,material flow and temperature distribution of the ring in HR...A 3D rigid-plastic and coupled thermo-mechanical FE model for hot ring rolling(HRR) was developed based on DEFORM 3D software,then coupled heat transferring,material flow and temperature distribution of the ring in HRR were simulated and the effects of process parameters on them were analyzed.The results show that the deformation nonuniformity of ring blank increases with the increase of the rotational speed of driver roll and friction factor or the decrease of the feed rate of idle roll and initial temperature of ring blank.The temperature nonuniformity of ring blank decreases with the increase of the feed rate of idle roll or the decrease of initial temperature of ring blank and friction factor.There is an optimum rotational speed of driver roll under which the temperature distribution of ring blank is the most uniform.The results obtained can provide a guide for forming parameters optimization and quality control.展开更多
Numerical simulation on microstructural evolution during multipass hot rolling of aluminum alloys was performed by using DEFORM TM software and incorporating Zener Hollomon parameter Z . The distributions of equivalen...Numerical simulation on microstructural evolution during multipass hot rolling of aluminum alloys was performed by using DEFORM TM software and incorporating Zener Hollomon parameter Z . The distributions of equivalent stress, equivalent strain, equivalent strain rate and temperature, as well as the distribution of recrystallization fraction through the thickness of deformed specimen during multipass hot rolling of 5182 aluminum alloy, were all calculated. The results agree well with the metallographic examination of the deformed specimen on Gleeble 1500. [展开更多
Based on load-oriented manufacturing control theory,different combining modes and slab storage calculation method for continuous casting and hot rolling were discussed.The buffer capacity index of continuous casting-r...Based on load-oriented manufacturing control theory,different combining modes and slab storage calculation method for continuous casting and hot rolling were discussed.The buffer capacity index of continuous casting-rolling was introduced,and the reasonable slab storage under different combining modes was calculated with buffer capacity index of 120.00 hfor CCR,79.20 hfor HCR,19.68 hfor DHCR and 3.84 hfor DR.Thin slab is 1.20 h,and the strip is zero.Theory gist was provided for steel enterprise to decrease storage.展开更多
基金supported by the National Natural Science Foundation of China(No.52274359)Guangdong Basic and Applied Basic Research Foundation,China(No.2022A1515110406)+3 种基金Beijing Natural Science Foundation,China(No.2212035)the Fundamental Research Funds for the Central Universities,China(Nos.FRF-TP-19005C1Z and 00007718)the Aeroengine Group University Research Cooperation Project,China(No.HFZL2021CXY021)the State Key Lab of Advanced Metals and Materials,University of Science and Technology Beijing,China(Nos.2021Z-03 and 2022Z-14).
文摘Hot deformation of sintered billets by powder metallurgy(PM)is an effective preparation technique for titanium alloys,which is more significant for high-alloying alloys.In this study,Ti–6.5Al–2Zr–Mo–V(TA15)titanium alloy plates were prepared by cold press-ing sintering combined with high-temperature hot rolling.The microstructure and mechanical properties under different process paramet-ers were investigated.Optical microscope,electron backscatter diffraction,and others were applied to characterize the microstructure evolution and mechanical properties strengthening mechanism.The results showed that the chemical compositions were uniformly dif-fused without segregation during sintering,and the closing of the matrix craters was accelerated by increasing the sintering temperature.The block was hot rolled at 1200℃ with an 80%reduction under only two passes without annealing.The strength and elongation of the plate at 20–25℃ after solution and aging were 1247 MPa and 14.0%,respectively,which were increased by 24.5%and 40.0%,respect-ively,compared with the as-sintered alloy at 1300℃.The microstructure was significantly refined by continuous dynamic recrystalliza-tion,which was completed by the rotation and dislocation absorption of the substructure surrounded by low-angle grain boundaries.After hot rolling combined with heat treatment,the strength and plasticity of PM-TA15 were significantly improved,which resulted from the dense,uniform,and fine recrystallization structure and the synergistic effect of multiple slip systems.
文摘With the intensification of market competition in the aluminum alloy strip processing industry,it is dif-ficult to control the mass production of the same specifications,which is bound to affect the hot rolling production.This paper studied the effect of the hot rolling order of aluminum alloy on the surface quality of strip,such as roll printing,color difference,anodic oxidation,etc.,reasonable discharge sequence and corresponding optimization measures were formulated.
基金financially supported by the National Natural Science Foundation of China(No.51874036)National Key Research and Development Program of China(No.2021YFB3701305)。
文摘It was discovered the application of Al_(2)O_(3) nanofluid as lubricant for steel hot rolling could synchronously achieve oxidation protection of strips surface.The underlying mechanism was investigated through hot rolling tests and molecular dynamics (MD) simulations.The employment of Al_(2)O_(3) nanoparticles contributed to significant enhancement in the lubrication performance of lubricant.The rolled strip exhibited the best surface topography that the roughness reached lowest with the sparsest surface defects.Besides,the oxide scale generated on steel surface was also thinner,and the ratio of Fe_(2)O_(3) among various iron oxides became lower.It was revealed the above oxidation protection effect of Al_(2)O_(3) nanofluid was attributed to the deposition of nanoparticles on metal surface during hot rolling.A protective layer in the thickness of about 193 nm was formed to prevent the direct contact between steel matrix and atmosphere,which was mainly composed of Al_(2)O_(3) and sintered organic molecules.MD simulations confirmed the diffusion of O_(2) and H_(2)O could be blocked by the Al_(2)O_(3) layer through physical absorption and penetration barrier effect.
文摘Based on the important boundary conditions of rolling simulation including friction, heat conduction and interactionsof the workpiece and rolls, the hot continuous rolling processes of large-diameter mandrel round bar (200 mm indiameter) in 6VH-stand hot tandem mill are successfully simulated by three-dimensional coupled thermomechanicalelastoplastic finite element method (FEM). The distributions of stress, strain, temperature and the rolling force andtorque for the two-pass and four-pass continuous rolling are calculated respectively. Thus, the two and four-passroll schedules are verified, respectively. The simulation results show that it is safe to produce 200 mm round barby the two-pass (oval pass and round pass) continuous rolling on the existing equipment compared to the four-passcontinuous rolling. There are concave surfaces and increased widths occurring at the end of rolled billet due touneven deformations between the outside and inside of the workpiece as well as the free spreading close to the rollgap of the final pass.
基金ItemSponsored by National Natural Science Foundation of China (50275130) Provincial Natural Science Foundation ofHebei Province of China (E200400223)
文摘A three-dimensional model for strip hot rolling was developed, in which the plastic deformation of strip, the thermal crown of rolls, roll deflection and flattening were calculated by rigid-plastic finite element method, finite difference method, influential function method and elastic finite element method respectively. The roll wear was taken into consideration. The model can provide detailed information such as rolling pressure distribution, contact pressure distribution between backup rolls and work rolls, deflection and flattening of work rolls, lateral distribution of strip thickness, and lateral distribution of front and back tensions. The finish rolling on a 1 450 mm hot strip mill was simulated.
基金the National Key Basic Research Program of China(2013CB632204)Natural Science Foundation of China(51671040).
文摘In the present study,the texture evolution and mechanical anisotropy in a typical Mg–Zn–Ca alloy through hot cross rolling(CR)and unidirectional rolling(UR)were systematically studied.The results show that the rolling path greatly affects the annealed texture.The UR develops a texture with basal poles mainly distributing along the transverse direction(TD).By contrast,an ellipse-like(0002)texture with basal pole inclining largely away from the normal direction(ND)is developed after hot cross rolling and annealing.Therefore,the CR is an effective method to tailor the texture of the experimental alloy.Unfortunately,this ellipse-like texture could not reserve during the subsequent unidirectional hot rolling and annealing.Both UR and CR plates exhibit a strong planar mechanical anisotropy compared with the traditional unidirectional rolled plate.
基金financially supported by the National Natural Science Foundation of China (No. 51174026)the National Science and Technology Pillar Program during the Twelfth Five-Year Plan Period (No. 2012BAE04B02)
文摘The thermoplasticity of duplex stainless steel 2205(DSS2205) is better than that of lean duplex steel 2101(LDX2101), which undergoes severe cracking during hot rolling. The microstructure, microhardness, phase ratio, and recrystallization dependence of the deformation compatibility of LDX2101 and DSS2205 were investigated using optical microscopy(OM), electron backscatter diffraction(EBSD), Thermo-Calc software, and transmission electron microscopy(TEM). The results showed that the phase-ratio transformations of LDX2101 and DSS2205 were almost equal under the condition of increasing solution temperature. Thus, the phase transformation was not the main cause for the hot plasticity difference of these two steels. The grain size of LDX2101 was substantially greater than that of DSS2205, and the microhardness difference of LDX2101 was larger than that of DSS2205. This difference hinders the transfer of strain from ferrite to austenite. In the rolling process, the ferrite grains of LDX2101 underwent continuous softening and were substantially refined. However, although little recrystallization occurred at the boundaries of austenite, serious deformation accumulated in the interior of austenite, leading to a substantial increase in hardness. The main cause of crack formation is the microhardness difference between ferrite and austenite.
文摘A recrystallization model for hot rolling of 5182 aluminum alloy was presented by means of the fractional softening during double interval deformation. It is found that the recrystallization rate depends on strain rate more sensitively than deformation temperature, and the time for full recrystallization is very short as strain rate is greater than 1?s -1 . Using the recrystallization—time—temperature curves, the desirable hot rolled microstructure can be obtained by controlling the rolling speed, temperature and cooling rate before cooling during the last pass in reversing mill.[
文摘A series of simple axisymmetric compression tests were carried out on the computer servo controlled Gleeble 1 500 machine when strain rates ranged between 0.05 25 s -1 and deformation temperature 300 500 ℃. The results show that flow stress is related to the Zener Hollonom parameter Z and strain, as well as the static recrystallization fraction between passes during multipass hot deformation of 5182 aluminum alloy. Hence, a modified exponential flow stress equation was presented by considering the values of ln A and β as functions of strain, and by using the uniform softening method and incorporating the static recrystallization fraction between passes to consider the effects of residual strain during multipass hot rolling of 5182 aluminum alloy. The validity of the equation was examined by a typical non isothermal multipass deformation test.
文摘In order to improve the quality of the strip for the hot continuous rolling, the high accuracy set-up control must be applied to production. In the paper, we analyze the RFC (profile and flatness control) system and simulate the set-up process. Calculation results are in agreement to the actual measurements. It is the basis on the developing model.
文摘Al Pb alloy strips and hot dip aluminized steel sheets were successfully bonded together by hot rolling, and the interfacial bonding strengths after rolling was evaluated by a new method. The bonding modes were studied by optical and scanning electron microscope and energy dispersive X ray analysis, and the effects of the thickness of the intermetallic layers and the Si content in hot dip aluminized layers on the interfacial bonding strength were also investigated respectively. It is found that the hot dipped steel and Al Pb alloy are bonded through blank interface bonding and block interface bonding, and the total bonding strength mainly depends on that of blank interfaces and the fraction of blank interfaces. There is a linear relationship between the total bonding strength F and the fraction of blank interfaces K b. The bonding strength varies with the Si content in the hot dipped aluminized layers on the surface of steel sheets, the fraction of blank interfaces and the rotation of the intermetallic blocks. [
文摘Deep rolling is one of the most widely used surface mechanical treatments among several methods used to generate compressive residual stress. This process is usually used for axisymmetric components and can lead to improvements of the surface quality, dimensional accuracy, and mechanical properties. In this study, we deduced the appropriate deep rolling parameters for Al-3vol%Si C nanocomposite samples using roughness and microhardness measurements. The nanocomposite samples were fabricated using a combination of mechanical milling, cold pressing, and hot extrusion techniques. Density measurements indicated acceptable densification of the samples, with no porosity. The results of tensile tests showed that the samples are sufficiently strong for the deep rolling process and also indicated near 50% improvement of tensile strength after incorporating Si C nanoparticle reinforcements. The effects of some important rolling parameters, including the penetration depth, rotation speed, feed rate, and the number of passes, on the surface quality and microhardness were also investigated. The results demonstrated that decreasing the feed rate and increasing the number of passes can lead to greater surface hardness and lower surface roughness.
基金Projects(2006BA104B04-1,2006BAE04B07-3) supported by the National Science and Technology Supporting Program of ChinaProject (2007KZ05) supported by the Science and Technology Supporting Program of Changchun City, ChinaProject supported by "985 Program" of Jilin University,China
文摘Mg-6Al-0.3Mn-xY(x=0,0.3,0.6 and 0.9,mass fraction,%) magnesium alloys were prepared by casting and hot rolling process.The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium alloy was investigated.The results reveal that with increasing the yttrium content,Al2Y precipitates form and the grain size is reduced.The ultimate strength,yield strength and elongation at room temperature are 192 MPa,62 MPa and 12.6%,respectively,for the as-cast Mg-6Al-0.3Mn-0.9Y alloy.All these properties are improved obviously by hot rolling,and the values are up to 303 MPa,255 MPa and 17.1%,respectively,for the rolled Mg-6Al-0.3Mn-0.9Y alloy.The improvement of mechanical properties is attributed to continuous dynamic recrystallization and the existence of highly thermal stable Al2Y precipitate which impedes the movement of dislocation effectively.
基金supported by the National Natural Science Foundation of China (No. 50834003)
文摘Multi-pass hot-rolling technique was used to fabricate W80Cu20 alloy,and its properties were characterized in this paper.Results show that the W-Cu alloy sheets with a thickness of 0.5 mm and a relative density of99.87%can be successfully made using this new technique at 800℃.In hot-rolling process,Cu phases are closely surrounded by W particles under the rolling stress to form a network microstructure,thus making significant increase in electrical and thermal conductivity up to53.00%and 24.44%,respectively.Transverse and longitudinal hardness of the W–Cu sheets significantly increase due to the enhanced densification and deformation strength.Similar to that of the raw materials,three fracture types were observed in the hot-rolled materials,i.e.,ductile fracture of Cu binding phases,trans-granular fracture of W phases,and W–W interfacial fracture.
基金Project(50271076) supported by the National Natural Science Foundation of China
文摘AZ91 magnesium alloy was prepared by spray forming. The spray-deposited alloy was subsequently hot-rolled with a 80% reduction at 350 ℃. The microstructural features of the as-spray-deposited and hot-rolled alloy were examined by optical microscopy, scanning electron microscopy and X-ray diffractometry. The results show that the spray-formed AZ91 magnesium alloy has, compared with the as-cast ingot, a finer microstructure with less intermetallic phase Mg17Al12 dispersed in the matrix due to fast cooling and solidification rates of spray forming process, and, therefore showing excellent workability. It can be hot-rolled with nearly 20% reduction for one pass at lower temperatures (330-360℃), and the total reduction can reach 50% prior to annealing. After proper thermo-mechanical treatment, the spray-formed AZ91 magnesium alloy exhibits outstanding mechanical properties.
基金Project(2006AA04Z135) supported by the National Hi-tech Research and Development Program of ChinaProject(50735005) supported by the National Natural Science Foundation of ChinaProject supported by Northwestern Polytechnical University Foundation for Fundamental Research, China
文摘A 3D rigid-plastic and coupled thermo-mechanical FE model for hot ring rolling(HRR) was developed based on DEFORM 3D software,then coupled heat transferring,material flow and temperature distribution of the ring in HRR were simulated and the effects of process parameters on them were analyzed.The results show that the deformation nonuniformity of ring blank increases with the increase of the rotational speed of driver roll and friction factor or the decrease of the feed rate of idle roll and initial temperature of ring blank.The temperature nonuniformity of ring blank decreases with the increase of the feed rate of idle roll or the decrease of initial temperature of ring blank and friction factor.There is an optimum rotational speed of driver roll under which the temperature distribution of ring blank is the most uniform.The results obtained can provide a guide for forming parameters optimization and quality control.
文摘Numerical simulation on microstructural evolution during multipass hot rolling of aluminum alloys was performed by using DEFORM TM software and incorporating Zener Hollomon parameter Z . The distributions of equivalent stress, equivalent strain, equivalent strain rate and temperature, as well as the distribution of recrystallization fraction through the thickness of deformed specimen during multipass hot rolling of 5182 aluminum alloy, were all calculated. The results agree well with the metallographic examination of the deformed specimen on Gleeble 1500. [
文摘Based on load-oriented manufacturing control theory,different combining modes and slab storage calculation method for continuous casting and hot rolling were discussed.The buffer capacity index of continuous casting-rolling was introduced,and the reasonable slab storage under different combining modes was calculated with buffer capacity index of 120.00 hfor CCR,79.20 hfor HCR,19.68 hfor DHCR and 3.84 hfor DR.Thin slab is 1.20 h,and the strip is zero.Theory gist was provided for steel enterprise to decrease storage.