Influence of hot rolling conditions on the mechanical properties of hot rolled TRIP steel was investigated. Thermomechanical control processing （TMCP） was conducted by using a laboratory hot rolling mill, in which t...Influence of hot rolling conditions on the mechanical properties of hot rolled TRIP steel was investigated. Thermomechanical control processing （TMCP） was conducted by using a laboratory hot rolling mill, in which three different kinds of finish rolling temperatures were applied. The results show that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained by controlled rolling processes. The finer ferrite grain size is produced through the deformation induced transformation during deformation rather than after deformation, which affects the mechanical properties of hot rolled TRIP steel. Mechanical properties increase with decreasing finish rolling temperature due to the stabilization of retained austenite. Ultimate tensile strength （UTS）, total elongation （TEL） and the product of ultimate tensile strength and total elongation （UTS×TEL） reaches optimal values （791 MPa, 36% and 28 476 MPa%, respectively） when the specimen was hot rolled for 50% reduction at finish rolling temperature of 700 ℃.展开更多
Although biopolymers have been widely utilized as triboelectric materials for the construction of self-powered sensing systems,the annihilation of triboelectric charges at high temperatures restricts the output signal...Although biopolymers have been widely utilized as triboelectric materials for the construction of self-powered sensing systems,the annihilation of triboelectric charges at high temperatures restricts the output signals and sensitivity of the assembled sensors.Herein,a novel chitosan/montmorillonite/lignin(CML)composite film was designed and employed as a tribopositive layer in the assembly of a self-powered sensing system for use under hot conditions(25-70℃).The dense contact surface resulting from the strong intermolecular interaction between biopolymers and nanofillers restrained the volatilization of induced electrons.The optimized CML-TENG delivered the highest open-circuit voltage(V_(oc))of 262 V and maximum instantaneous output power of 429 mW/m^(2).Pristine CH-TENG retained only 39%of its initial Voc at 70℃,whereas the optimized CM_(5)L_(3)-TENG retained 66%of its initial Voc.Our work provides a new strategy for suppressing the annihilation of triboelectric charges at high temperatures,thus boosting the development of self-powered sensing devices for application under hot conditions.展开更多
Effects of finishing rolling temperatures and reduction on the mechanical properties of hot rolled multiphase steel were investigated. Thermo-mechanical control processing (TMCP) was conducted by using a laboratory ho...Effects of finishing rolling temperatures and reduction on the mechanical properties of hot rolled multiphase steel were investigated. Thermo-mechanical control processing (TMCP) was conducted by using a laboratory hot rolling mill, in which three different kinds of finishing rolling temperatures and reduction and various austempering times were applied. The results showed that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained by controlled rolling processes, and that the strain-induced transformation to martensite from the retained austenite can occur gradually when the steel is deformed during tensile test. Mechanical properties increase with decreasing finishing rolling temperature and increasing amount of deformation. The most TRIP (transformation induced plasticity) effect, and ultimate tensile strength (UTS), total elongation (TEL) and the product of ultimate tensile strength and total elongation (UTS×TEL) are obtained at 20 min.展开更多
基金the National Natural Science Foundation of China(No.50334010)the Program of Education Branch of Liaoning Province of China(No.2006B075)
文摘Influence of hot rolling conditions on the mechanical properties of hot rolled TRIP steel was investigated. Thermomechanical control processing （TMCP） was conducted by using a laboratory hot rolling mill, in which three different kinds of finish rolling temperatures were applied. The results show that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained by controlled rolling processes. The finer ferrite grain size is produced through the deformation induced transformation during deformation rather than after deformation, which affects the mechanical properties of hot rolled TRIP steel. Mechanical properties increase with decreasing finish rolling temperature due to the stabilization of retained austenite. Ultimate tensile strength （UTS）, total elongation （TEL） and the product of ultimate tensile strength and total elongation （UTS×TEL） reaches optimal values （791 MPa, 36% and 28 476 MPa%, respectively） when the specimen was hot rolled for 50% reduction at finish rolling temperature of 700 ℃.
基金grateful for the financial support from the National Natural Science Foundation of China(Nos.22208038,22278047,and 22208040)the Liaoning Revitalization Talent Program,China(No.XLYC2002024)the Fundamental Research Funds for the Universities of Liaoning Province,China(No.LJBKY2024055).
文摘Although biopolymers have been widely utilized as triboelectric materials for the construction of self-powered sensing systems,the annihilation of triboelectric charges at high temperatures restricts the output signals and sensitivity of the assembled sensors.Herein,a novel chitosan/montmorillonite/lignin(CML)composite film was designed and employed as a tribopositive layer in the assembly of a self-powered sensing system for use under hot conditions(25-70℃).The dense contact surface resulting from the strong intermolecular interaction between biopolymers and nanofillers restrained the volatilization of induced electrons.The optimized CML-TENG delivered the highest open-circuit voltage(V_(oc))of 262 V and maximum instantaneous output power of 429 mW/m^(2).Pristine CH-TENG retained only 39%of its initial Voc at 70℃,whereas the optimized CM_(5)L_(3)-TENG retained 66%of its initial Voc.Our work provides a new strategy for suppressing the annihilation of triboelectric charges at high temperatures,thus boosting the development of self-powered sensing devices for application under hot conditions.
基金Project (No. 50334010) supported by the National Natural ScienceFoundation of China
文摘Effects of finishing rolling temperatures and reduction on the mechanical properties of hot rolled multiphase steel were investigated. Thermo-mechanical control processing (TMCP) was conducted by using a laboratory hot rolling mill, in which three different kinds of finishing rolling temperatures and reduction and various austempering times were applied. The results showed that polygonal ferrite, granular bainite and larger amount of stabilized retained austenite can be obtained by controlled rolling processes, and that the strain-induced transformation to martensite from the retained austenite can occur gradually when the steel is deformed during tensile test. Mechanical properties increase with decreasing finishing rolling temperature and increasing amount of deformation. The most TRIP (transformation induced plasticity) effect, and ultimate tensile strength (UTS), total elongation (TEL) and the product of ultimate tensile strength and total elongation (UTS×TEL) are obtained at 20 min.