Ballistic performance of titanium-based layered composites made using blended elemental powder metallurgy and hot isostatic pressing

Metal matrix composites tiles based on Ti-6Al-4V(Ti64)alloy,reinforced with 10,20,and 40(vol%)of either TiC or TiB particles were made using press-and-sinter blended elemental powder metallurgy(BEPM)and then bonded together into 3-layer laminated plates using hot isostatic pressing(HIP).The laminates were ballistically tested and demonstrated superior performance.The microstructure and properties of the laminates were analyzed to determine the effect of the BEPM and HIP processing on the ballistic properties of the layered plates.The effect of porosity in sintered composites on further diffusion bonding of the plates during HIP is analyzed to understand the bonding features at the interfaces between different adjacent layers in the laminate.Exceptional ballistic performance of fabricated structures was explained by a significant reduction in the residual porosity of the BEPM products by their additional processing using HIP,which provides an unprecedented increase in the hardness of the layered composites.It is argued that the combination of the used two technologies,BEPM and HIP is principally complimentary for the materials in question with the abilities to solve the essential problems of each used individually.

Effect of the capsule on deformation and densification behavior of nickel-based superalloy compact during hot isostatic pressing

The Shima yield criterion used in finite element analysis for nickel-based superalloy powder compact during hot isostatic pressing(HIP) was modified through uniaxial compression experiments. The influence of cylindrical capsule characteristics on FGH4096M superalloy powder compact deformation and densification behavior during HIP was investigated through simulations and experiments. Results revealed the simulation shrinkage prediction fitted well with the experimental shrinkage including a maximum shrinkage error of 1.5%. It was shown that the axial shrinkage was 1.7% higher than radial shrinkage for a cylindrical capsule with the size of ∮50 mm × 100 mm due to the force arm difference along the axial and radial direction of the capsule. The stress deviated from the isostatic state in the capsule led to the uneven shrinkage and non-uniform densification of the powder compact. The ratio of the maximum radial displacement to axial displacement increased from0.47 to 0.75 with the capsule thickness increasing from 2 to 4 mm. The pressure transmission is related to the capsule thickness, the capsule material performance, and physical parameters in the HIP process.

Effect of hot isostatic pressure on the microstructure and tensile properties of γ'-strengthened superalloy fabricated through induction-assisted directed energy deposition

The microstructure characteristics and strengthening mechanism of Inconel738LC(IN-738LC) alloy prepared by using induction-assisted directed energy deposition(IDED) were elucidated through the investigation of samples subjected to IDED under 1050℃ preheating with and without hot isostatic pressing(HIP,1190℃,105 MPa,and 3 h).Results show that the as-deposited sample mainly consisted of epitaxial columnar crystals and inhomogeneously distributed γ’ phases in interdendritic and dendritic core regions.After HIP,grain morphology changed negligibly,whereas the size of the γ’ phase became increasingly even.After further heat treatment(HT,1070℃,2 h + 845℃,24 h),the γ’ phase in the as-deposited and HIPed samples presented a bimodal size distribution,whereas that in the as-deposited sample showed a size that remained uneven.The comparison of tensile properties revealed that the tensile strength and uniform elongation of the HIP + HTed sample increased by 5% and 46%,respectively,due to the synergistic deformation of bimodal γ’phases,especially large cubic γ’ phases.Finally,the relationship between phase transformations and plastic deformations in the IDEDed sample was discussed on the basis of generalized stability theory in terms of the trade-off between thermodynamics and kinetics.

Effects of microstructure characteristics on the tensile properties and fracture toughness of TA15 alloy fabricated by hot isostatic pressing

Powder hot isostatic pressing(HIP) is an effective method to achieve near-net-shape manufacturing of high-quality complex thinwalled titanium alloy parts, and it has received extensive attention in recent years. However, there are few reports about the microstructure characteristics on the strengthening and toughening mechanisms of powder hot isostatic pressed(HIPed) titanium alloys. Therefore, TA15powder was prepared into alloy by HIP approach, which was used to explore the microstructure characteristics at different HIP temperatures and the corresponding tensile properties and fracture toughness. Results show that the fabricated alloy has a “basket-like structure” when the HIP temperature is below 950℃, consisting of lath clusters and surrounding small equiaxed grains belts. When the HIP temperature is higher than 950℃, the microstructure gradually transforms into the Widmanstatten structure, accompanied by a significant increase in grain size. The tensile strength and elongation are reduced from 948 MPa and 17.3% for the 910℃ specimen to 861 MPa and 10% for the 970℃ specimen.The corresponding tensile fracture mode changes from transcrystalline plastic fracture to mixed fracture including intercrystalline cleavage.The fracture toughness of the specimens increases from 82.64 MPa·m^(1/2)for the 910℃ specimen to 140.18 MPa·m^(1/2)for the 970℃ specimen.Specimens below 950℃ tend to form holes due to the prior particle boundaries(PPBs), which is not conducive to toughening. Specimens above 950℃ have high fracture toughness due to the crack deflection, crack branching, and shear plastic deformation of the Widmanstatten structure. This study provides a valid reference for the development of powder HIPed titanium alloy.

Effect of hot isostatic pressing processing parameters on microstructure and properties of Ti60 high temperature titanium alloy

Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace.In order to obtain optimal processing parameters,the effects of hot isostatic pressing parameters on defects,composition uniformity,microstructure and mechanical properties of Ti60 cast high temperature titanium alloy were investigated in detail.Results show that increasing temperature and pressure of hot isostatic pressing can reduce defects,especially,the internal defects are substantially eliminated when the temperature exceeds 920℃or the pressure exceeds 125 MPa.The higher temperature and pressure can improve the microstructure uniformity.Besides,the higher pressure can promote the composition uniformity.With the temperature increases from 880℃to 960℃,α-laths are coarsened.But with increasing pressure,the grain size of prior-βphase,the widths ofα-laths andα-colony are reduced.The tensile strength of Ti60 alloy is 949 MPa,yield strength is 827 MPa,and the elongation is 11%when the hot isostatic pressing parameters are 960℃/125 MPa/2 h,which exhibits the best match between the strength and plasticity.

OBSERVATION OF DISLOCATION CONFIGURATIONS IN AGED ＆ DEFORMED NiAl ALLOY AFTER HOT ISOSTATIC PRESSING （HIP）

Observation of dislocation configurations was conducted for aged and compressive deformed (Ni64A136) FeMoB alloy after hot isostatic pressing (HIP). It isshown that short and straight parallel dislocations are present in the matrix of NiAI alloy.Long and tortuous dislocations and superdislocations appear in the 1%-deformed specimen. As the compressive strain increases to 2. 6%, high-densities dislocations appear inand between the deformation bands. The dislocations become tangled up in the specimencompressed to a strain of 6. 2 %.

Diffusion Bonding of Al6061 and Cu by Hot Isostatic Pressing

Diffusion bonding between Al and Cu was successfully performed by hot isostatic pressing(HIP). To improve the strength of diffusion bonding joint, pure nickel foils with different thickness were used as intermediate layer. Microstructure of the interface between Al and Cu was investigated by X-ray diffraction(XRD) technique, secondary electron microscopy(SEM), and nano-indentation tests. When the temperature was 500 ℃ and held for 3 h with a processing pressure of 50 MPa, Al and Cu could be bonded with its interface formed by several diffusion layers. With the addition of Ni interlayer, the diffusion of aluminum atoms was effectively hindered, and the interface became smoother. The tensile strength of bonded joints increases with increasing the thickness of Ni interlayer, which contributes to a reduction in the thickness of intermetallic compounds(IMCs) and well bonding quality of Al-Cu joints.

高温HIP对难熔金属显微组织与性能的影响

使用1800℃的高温HIP,研究了纯钨、钨镧、TZM和MHC等材料的微观组织和力学性能。试验发现:经过HIP1800处理后,钨镧合金的晶粒未发生明显变化,硬度高于纯钨;去应力状态的TZM和MHC钼合金性能差异在经过HIP1800后得到了消除,具有相似的显微组织和室温力学性能。

Effects of hot isostatic pressing temperature on casting shrinkage densification and microstructure of Ti6Al4V alloy

The Ti6Al4V alloy castings were produced by the investment casting process, and the hot isostatic pressing(HIP) was used to remove shrinkage from castings. The processing pressure and holding time for HIP were 150 MPa and 20 min, respectively. Four different HIP temperatures were tested, including 750 ℃, 850 ℃, 920 ℃ and 950 ℃. To evaluate the effects of temperature on densification and microstructure of Ti6Al4V alloy treated by HIP, non-destructive testing and metallographic observation was performed. The experimental results show that the shrinkage was completely closed at 920 ℃ and 950 ℃. The densification of Ti6Al4V alloy increased as the HIP temperature increased below 920 ℃. The lamel ae were more uniform, the thickness of lamel ae was obviously broadened and the structure was coarsen. Besides, the Norton creep equation was used to simulate the effect of different temperatures on the densification of Ti6Al4V alloy during HIP. The simulation results were in good agreement with the experimental results. It was also found that 920 ℃ is a suitable temperature for HIP for Ti6Al4V alloy.

Deformation Behavior of Hot Isostatic Pressing FGH96 Superalloy

The deformation behavior of hot isostatic pressing （HIP） FGH96 superalloy was characterized in the temperature range of 1000-1100 ℃ and strain rate range of 0. 001-0. 1 s^-1 using hot compression testing. The flow curves of HIP FGH96, superalloy during hot deformation was analyzed systematically. The results show that deformation temperature, strain rate and strain are the main influence factors on flow stress of HIP FGH96 superalloy during hot deformation. The flow stress displays a peak at a critical strain and then decreases with further increase in strain. For a given strain, the flow stress decreases with the increase of deformation temperature, and increases with the increase of strain rate. A mathematical model of these flow curves was established through regression analysis and taking the strain as a modification factor. The calculated stress values agree well with the experimental values.

Influence of hot isostatic pressing on microstructure,properties and deformability of selective laser melting TC4 alloy

The influence of different hot isostatic pressing regimes on microstructure,phase constitution,microhardness,tensile properties and deformability of TC4 alloy fabricated by selective laser melting(SLM)technology was studied.The results show that the microstructure of SLM TC4 alloy is composed of acicular martensiteα’phase,and the sample exhibits high microhardness and strength,but low plasticity.After hot isostatic pressing,acicular martensiteα’phase transforms intoα+βphase,and with the increase of hot isostatic pressing temperature and duration,αphase with coarse lath is gradually refined,and the proportion ofαphase is gradually reduced.Because of the change of phase constitution in SLM TC4 alloy after hot isostatic pressing,the grain refinement strengthening is weakened,the density of dislocation is reduced,so that both microhardness and tensile strength are decreased by around 20%,the elongation is increased by more than about 70%,even over 100%,compared with as-deposited TC4 alloy.When the hot isostatic pressing regime is 940°C/3 h/150 MPa,the tensile strength and the elongation achieve optimal match,which are about890 MPa and around 14.0%in both directions.The fracture mechanism of alloy after 940 oC/3 h/150 MPa HIP is dultile fracture.Hot isostatic pressing causes concave deformation of SLM TC4 alloy thin-walled frames,and the deformation degree increases with the increase of temperature.

Finite element simulation of real cavity closure in cast Ti6Al4V alloy during hot isostatic pressing

The healing behavior of shrinkage cavity inside the cast Ti6Al4V alloy during hot isostatic pressing(HIP)was investigated experimentally by interrupted hot isostatic pressing tests.The X-ray micro computed tomography was used to record the morphology changes before and after hot isostatic pressing.The two-dimensional geometry obtained by the microCT scan was used in simulation to study the evolution of the real shrinkage cavity during hot isostatic pressing.Shrinkage cavities,shrinkage porosity and small gas pores can be effectively eliminated under proper HIP conditions.The two-dimensional morphology in the simulation results agrees well with the experimental results.This study reveals that plastic deformation,creep and diffusion are the main mechanisms of cavity closure during hot isostatic pressing.In addition,the simplified elliptical pores with aspect ratios at different positions were used to replace the real pores to further study the factors affecting the position of dimples after HIP by simulation.It is found that the position of the dimples mainly depends on the aspect ratio of the elliptical pore and the distance between the pore surface and the external surface of the geometric model.

Combining Aluminum Heat Treat with Hot Isostatic Pressing: A Comparison of Structure, Properties, and Processing Routes for a Cast AI-Si-Mg Alloy

Bodycote researchers have successfully demonstrated that a T6 heat treatment can be integrated with Densal?, a proprietary, aluminum specific, hot isostatic pressing (HIP) process. In this combined operation, at least a portion of the solution heat treatment is conducted at elevated pressure. During development, two issues, adiabatic cooling during depressurization and a possible variation in the kinetics of homogenization resulting from conducting the solution heat treat at elevated pressure were perceived as factors which could alter the heat treat response from that seen in conventional processing. This paper reviews the results of experiments performed to Al-Si-Mg (A356.0) castings subjected to both combined and conventional processing routes. Results indicate that the combined HIP and heat treat process is an efficient means of achieving a microstructure characteristic of a conventionally T6 processed material while eliminating porosity within the casting. Further, the fatigue life of an A356.0 casting processed using the combined cycle can be improved by more than an order of magnitude over the as-cast and T6 treated component.

Simulation of pressure effects on hot isostatic pressing of stainless steel powder

To investigate the effects of pressure on the hot isostatic pressing(HIP) process of a stainless steel powder,density distribution and deformation of the powder at four different applied pressure levels were predicted and compared by using finite element method(FEM).Constitutive relations of porous compacts during HIP process were derived based on the yield criterion of porous metal materials.Thermo-mechanical coupling calculations were carried out by the MSC.Marc.Densification mechanisms were studied through evolutions of relative density,equivalent plastic strain and equivalent viscoplastic strain rate for compacts.The simulation results were also compared with experimental data.The results show that the densification rate and final density of compacts increase dramatically with the increase in the applied pressure level when it is below 100 MPa during HIP process,and the creep for compacts evolves into steady stage with the improvement of density.

Microstructure and mechanical properties of CuAgZn/GH909 diffusion bonded joint fabricated by hot isostatic pressing

The hot isostatic pressing-diffusion bonding(HIP-DB)was proposed to achieve the joining of CuAgZn and GH909 directly without an interlayer.The microstructure of joint was characterized by scanning electron microscope(SEM),energy dispersive spectrometer(EDS)and X-ray diffraction(XRD).The microhardness and shear strength were tested to investigate the mechanical properties of joint.The results showed that the interface was complete,and the joint was compact,uniform and free of unbonded defects.The maximum microhardness of joint was HV 443,higher than that of two base alloys,and the average shear strength of joint reached 172 MPa.It is concluded that a good metallurgical bonding between CuAgZn and GH909 can be obtained by HIP-DB with the process parameters of 700℃,150 MPa and 3 h.

Influence of Hot Isostatic Pressing Temperature on the Microstructure and Properties of AlSi7Cu2Mg Alloys

The roles of hot isostatic pressing (HIP) temperatures (490 ℃/100 MPa/2 h,510 ℃/100 MPa/2 h,530 ℃/100 MPa/2 h) in the microstructure and properties of AlSi7Cu2Mg alloy step castings with three types wall thicknesses were studied.The experimental results show that HIP at 490 ℃ could effectively eliminate the internal closed porosity of the castings with a wall thickness of ≤40 mm,but for heavy castings (70 mm),even HIP at 530 ℃,a few loose defects remained inside the castings.Two types of incipient eutectics containing Al5Mg8Si6Cu2 and Al2Cu were observed in the samples that HIP at 530 ℃,which was responsible for the decrease of the tensile strength of the castings within the medium wall thickness (40 mm) compared with that HIP at 490 ℃.HIP could greatly reduce the difference of the tensile strength values of castings with wall thicknesses 17 mm and 70 mm from 117.93 MPa (without HIP) to 25.7 MPa (with HIP at 530 ℃).

Diffusion bonding of Ti−6Al−4V titanium alloy powder and solid by hot isostatic pressing

The Ti−6Al−4V(TC4)alloy powder and forged solid were diffusion bonded by hot isostatic pressing(HIP)to fabricate a powder−solid part.The microstructure of the powder−solid part was observed by scanning electron microscope(SEM).The microhardness and tensile tests were conducted to investigate the mechanical properties.The results showed that the powder compact was near-fully dense,and the powder/solid interface was tight and complete.The microhardness of the interface was higher than that of the powder compact and solid.The fractures of all powder−solid tensile specimens were on the solid side rather than at the interface,which indicated that a good interfacial strength was obtained.The tensile strength and elongation of the powder compact were higher than those of the solid.It is concluded that the HIP process can successfully fabricate high-quality Ti−6Al−4V powder−solid parts,which provides a novel near net shape technology for titanium alloys.

Compressive behavior of NiAl/(Cr,Mo)Hf alloy prepared by high-pressure die casting and hot isostatic pressing

The NiAl-28Cr-5.85Mo-0.15Hf alloy was prepared by high-pressure die casting (HPDC) and subsequent hot isostatic pressing(HIP), and tested for compressible strength and fracture behavior at 300-1 373 K. The results show that the elevated temperature 0.2% compressible yield strength as well as the room-temperature compressible fracture strain of as-HIP alloy are larger than those of the same alloy prepared by directional solidification (DS). It suggests that the fine structures with a homogeneous distribution of fine Cr (Mo) and Hf-rich phase created by high-pressure die casting lead to these improvements.

Effect of hot isostatic pressing nitrogen on the microstructure and properties of a Ti(C,N)-based cermet

The high-temperature, high-pressure hot isostatic pressing technology was used for depositing hard coatings on Ti（C, N）-based cermets. The rnicrostructure and properties of the sample were investigated using optical microscopy, scan- ning electron microscopy, X-ray diffraction, electron probe microanalysis, and microhardness tester. The results showed that the rich titanium and nitrogen in surface zone were induced by the heat treatment. The high nitrogen activity of the surface region was the driving force for outward transport of titanium and inward transport of tungsten in the cobalt binder. The toughness and hardness were improved and a hardness gradient was formed. It is the high-temperature, high-pressure N2 that enables closure of holes, thereby alleviating defects and prolonging tool life.

Microstructure Evolution and Mechanical Properties of Ti-25Ta Alloy Fabricated by Selective Laser Melting and Hot Isostatic Pressing

Ti-25Ta alloy samples were fabricated by selective laser melting,and the relative density,microstructure,microhardness and tensile properties of the as-built and hot isostatic pressing(HIP)-prepared samples were characterized.Results show that the track width and penetration depth are increased with the increase in laser power,and the surface morphology is improved.The maximum relative density improves from 95.31%to 98.01%after HIP process.Moreover,the microstructure is refined into the lath martensite and cellular grains with the increase in input power.After densification treatment,the subgrain coalescence occurs and high angle grain boundaries are formed.In addition,HIP process stabilizes the microhardness and enhances the tensile strength and elongation.