The paper describes the ries with high thermal shock development of brick seresistance and low creep rate for hot blast stove, including research target and research plan on the basis of analysis on how to enhance the...The paper describes the ries with high thermal shock development of brick seresistance and low creep rate for hot blast stove, including research target and research plan on the basis of analysis on how to enhance the thermal shock resistance and to lower creep rate of the bricks. Efforts have been made on the selection of starting materials such as corundum, mullite, andalusite and sillimanite etc., together with some measures taken on multi-grade formulation, homogenizing of the matrix of bricks and addition of some special additives. The results indicated that the bricks were with characteristics such as higher thermal shock resistance of 〉 30 cycles under quenching in water from 1000℃, and creep rate of 0. 2 under 1400℃ for 20 -50hrs with load of 0.2 MPa. Now a series of products of this kind have been developed and produced. The application of the products in Wuhan Iron and Steel Co. showed very prospective results. Now most of domestic large sized blast furnaces say ≥- 1000m^3, including those of Baoshan Iron and Steel Co. , have selected the series products made by Gongyi No. 5 Refractories Head Factory（GYWN） for their hot blast stoves.展开更多
The interactions of a spherical flame with an incident shock wave and its reflected shock wave in a confined space were investigated using the three-dimensional reactive Navier-Stokes equations, with emphasis placed o...The interactions of a spherical flame with an incident shock wave and its reflected shock wave in a confined space were investigated using the three-dimensional reactive Navier-Stokes equations, with emphasis placed on the effect of chemical reactivity of mixture on the flame distortion and detonation initiation after the passage of the reflected shock wave. It is shown that the spatio-temporal characteristics of detonation initiation depend highly on the chemi- cal reactivity of the mixture. When the chemical reactivity enhances, the flame can be severely distorted to form a reactive shock bifurcation structure with detonations initiating at different three-dimensional spatial locations. Moreover, the detonation initiation would occur earlier in a mixture of more enhanced reactivity. The results reveal that the detona- tions arise from hot spots in the unburned region which are initiated by the shock-detonation-transition mechanism.展开更多
In order to prolong the service life of castables for hot blast stove pipes,effects of SiO2 micropowder addition and aggregate kind on properties of castables for hot blast stove pipes,and properties of silica sol bon...In order to prolong the service life of castables for hot blast stove pipes,effects of SiO2 micropowder addition and aggregate kind on properties of castables for hot blast stove pipes,and properties of silica sol bonded castables were researched using homogenized bauxite,andalusite particles,andalusite fines,white fused corundum fines,α-Al2O3 micropowder,pure calcium aluminate cement,SiO2 micropowder,and silica sol as starting materials. The results show that：（1） as SiO2 micropowder addition increases,the shrinkage rate of fired specimens increases; BD increases firstly,reaches the highest at 4 mass%,and then decreases; CMOR and CCS of all specimens increase gradually; so the appropriate SiO2 micropowder addition is 4 mass%;（2） the specimens with bauxite aggregate have better CCS and volume stability,but specimens with andalusite aggregate have better thermal shock resistance;（ 3） for castables for hot blast stoves using silica sol as binder,the addition of pure calcium aluminate cement can decrease the linear change rate after treatment at 1 400℃ and can slightly enhance CCS and CMOR,but has very little influence on AP and BD; and the introduction of citric acid worsens the thermal shock resistance of specimens.展开更多
基金The paper was presented at the Unitecr’05,which was held in Orlando. USA on Nov.8~11,2005
文摘The paper describes the ries with high thermal shock development of brick seresistance and low creep rate for hot blast stove, including research target and research plan on the basis of analysis on how to enhance the thermal shock resistance and to lower creep rate of the bricks. Efforts have been made on the selection of starting materials such as corundum, mullite, andalusite and sillimanite etc., together with some measures taken on multi-grade formulation, homogenizing of the matrix of bricks and addition of some special additives. The results indicated that the bricks were with characteristics such as higher thermal shock resistance of 〉 30 cycles under quenching in water from 1000℃, and creep rate of 0. 2 under 1400℃ for 20 -50hrs with load of 0.2 MPa. Now a series of products of this kind have been developed and produced. The application of the products in Wuhan Iron and Steel Co. showed very prospective results. Now most of domestic large sized blast furnaces say ≥- 1000m^3, including those of Baoshan Iron and Steel Co. , have selected the series products made by Gongyi No. 5 Refractories Head Factory（GYWN） for their hot blast stoves.
基金supported by the National Natural Science Foundation of China (10972107)Open Fund of State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology (KFJJ12-4Y)Jiangsu Innovation Program for Graduate Education (CXLX11 0271)
文摘The interactions of a spherical flame with an incident shock wave and its reflected shock wave in a confined space were investigated using the three-dimensional reactive Navier-Stokes equations, with emphasis placed on the effect of chemical reactivity of mixture on the flame distortion and detonation initiation after the passage of the reflected shock wave. It is shown that the spatio-temporal characteristics of detonation initiation depend highly on the chemi- cal reactivity of the mixture. When the chemical reactivity enhances, the flame can be severely distorted to form a reactive shock bifurcation structure with detonations initiating at different three-dimensional spatial locations. Moreover, the detonation initiation would occur earlier in a mixture of more enhanced reactivity. The results reveal that the detona- tions arise from hot spots in the unburned region which are initiated by the shock-detonation-transition mechanism.
文摘In order to prolong the service life of castables for hot blast stove pipes,effects of SiO2 micropowder addition and aggregate kind on properties of castables for hot blast stove pipes,and properties of silica sol bonded castables were researched using homogenized bauxite,andalusite particles,andalusite fines,white fused corundum fines,α-Al2O3 micropowder,pure calcium aluminate cement,SiO2 micropowder,and silica sol as starting materials. The results show that：（1） as SiO2 micropowder addition increases,the shrinkage rate of fired specimens increases; BD increases firstly,reaches the highest at 4 mass%,and then decreases; CMOR and CCS of all specimens increase gradually; so the appropriate SiO2 micropowder addition is 4 mass%;（2） the specimens with bauxite aggregate have better CCS and volume stability,but specimens with andalusite aggregate have better thermal shock resistance;（ 3） for castables for hot blast stoves using silica sol as binder,the addition of pure calcium aluminate cement can decrease the linear change rate after treatment at 1 400℃ and can slightly enhance CCS and CMOR,but has very little influence on AP and BD; and the introduction of citric acid worsens the thermal shock resistance of specimens.
基金Projects(52161009,51961003)supported by the National Natural Science Foundation of ChinaProject(2022AAC03224)supported by the Natural Science Foundation of Ningxia,ChinaProject(XAB2022YW07)supported by the West Light Foundation of the Chinese Academy of Science。