Investigation and improvement of tiny spot defects on hot-dip galvanized automotive steel sheets

The causes of tiny spot defects on the surface of hot-dip galvanized automotive steel sheets were studied using scanning electron microscopy(SEM)and energy dispersive spectrometer(EDS),and effective control measures were introduced.The results show that rubbing against the top roller after galvanizing is easy due to the local thickness of tiny spot defect location coating;therefore,the surface morphology is different from the normal part.Three kinds of defects,namely zinc slag,small slivers,and pitting,are likely to cause local thickening of the coating after galvanizing,leading to the formation of tiny spots.Therefore,resolving the three types of defects can effectively control the generation of tiny spot defects.Among them,due to the hereditary nature of the small sliver defect,focusing on its control and supervision is necessary.

Recent development of UHSS and its hot-dip galvanizing processes in Baosteel

Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel products.Some milestones achieved by Baosteel automotive steel sheet were briefly reviewed.The current challenges in producing ultra-high strength steel(UHSS),especially hot-dip galvanized UHSS,were summarized.The most current advancements in UHSS and the corresponding hot-dip galvanizing processes were discussed.The galvanizability of Si-Mn-added QP steel and DP steel, Mn-added TWIP steel, and Al-added low-density steel has been improved by different techniques in Baosteel.

Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel

A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and then reheated to 450°C(process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel(DP600) was investigated using optical microscopy, scanning electron microscopy(SEM), transmission electron microscopy(TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength(YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient(n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength(UTS) and elongation(A80) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties(YS = 362 MPa, UTS = 638 MPa, A_(80) = 24.3%, n = 0.17) was obtained via process A.

Preparation and hot-dip galvanizing application of CeO_2/Zn nanocomposite

CeO2/Zn nanocomposite was fabricated by high-energy ball milling and subsequent hot-press sintering under vacuum. The produced nanocomposite powders and bulks were characterized using X-ray diffraction （XRD）, transmission electron microscopy （TEM） and scanning electron microscopy （SEM） with an energy dispersive X-ray spectrum （EDS）. The as-fabricated nanocomposite bulks were added successfully into the hot-dip galvanizing bath to improve the corrosion resistance of coatings. The results show that after milling for 120min, nano-sized CeO2 particles are distributed homogeneously on the surface of fine Zn particles to form spherical-like nanocomposite powder with narrow grain size distribution. The subsequent sintering does not lead to a dramatic grain growth, and the distribution of CeO2 nanoparticles in the composite bulk is also homogeneous. With the addition of as-prepared bulks, the corrosion resistance of the galvanized coatings is improved obviously. It provides a feasible route for adding CeO2 nanoparticles into the hot-dip galvanized coating.

Application of WC cermet sprayed composite coating in hot-dip galvanizing lines

With the rapid development of the automobile industry, the use of galvannealed and galvanized steel sheets in automobiles is on the rise. These sheets must meet very high surface quality requirements. The surface treatment of line rolls is known to have a great impact on strip quality. To prevent dusts such as zinc ash from pressing into the strip surface, we used a composite thermal spray surface treatment technique to treat rolls. The successfully developed tungsten carbide （WC） ＋ Ni-P composite plating technology improved the quality of the tungsten carbide thermally sprayed WC roll surface. This technique is also helpful to control defects such as adhered foreign materials in hot-dip galvanized automobile outer panel surfaces.

Innovative integrating of hot-dipped(aluminizing) galvanizing lines and engineering of related equipment

Based on the continuous hot(aluminizing) galvanizing lines and related non-standard equipment of Meishan Steel,this paper presents the main contents of such integrated engineering and designing of equipment for the two hot-dipped galvanizing lines,as well as innovative techniques and their features.Led by Cold Rolling Project Department of Meishan Steel,Baosteel Engineering and Technology Group Co.,Ltd. ,working as the responsible unit of this project,develops key technologies and integrates the system by combining the equipment design and development capacity of Baosteel Engineering,research and development capacity of Research Institute of Baosteel,process production and equipment maintenance experience of Cold Rolling Plant,Equipment Department and Manufacture Department of Baosteel Corporation.Core technologies of the two lines are developed and designed through original and integrated innovation and innovation after digestion,focusing on eight core techniques in process equipment,annealing furnace,fluid installation and EIC system.As a result of integration in key process equipment,industrial furnace and EIC control,the cold rolling hot dipped(aluminizing) galvanizing lines take on a new look and reach an annual capacity of 200 000 t galvanized products and 250 000 t galvanized aluminium base strips respectively.These two world advanced lines are able to produce hot-dipped galvanizing products with high quality surface and fine shape,such as household appliance board and senior construction board.As a result, the process and equipment technology of the lines have formed domestic intellectual property.Thus,the technology has reference value for self-integration and equipment technology innovation of similar lines.

Galvanic Skin Response—Extinction Biofeedback Training for Psychogenic Abdominal Pain: A Validation Protocol

Abdominal and pelvic pain of psychogenic origin is a widespread, disabling, difficult to identify, and often inadequately treated medical condition. This condition is often associated with poor quality of life due to high pain interference with daily activities. Cognitive behavioral psychological therapy and neuromodulation with biofeedback are validated therapies for the treatment of this condition. Aim of the present research work is the validation of a therapeutic protocol that involves the use of both techniques in combination. 20 patients diagnosed with psychogenic abdominal pain, of both sexes, aged between 18 and 60 years who had not benefited from pharmacological therapies were enrolled. 10 patients were randomly assigned to the control group (psychological treatment only), another 10 patients were assigned to the study group (neuromodulation with biofeedback-Galvanic skin response-extinction in combination with psychological therapy). For both groups, the pain score, interference of pain with daily living activities, pain relief, and the share of anxiety associated with the pain condition were evaluated (pre- and post-treatment). The patients who underwent the combined treatment achieved statistically significant better scores than patients in the control group, respectively −4.9 ± 0.9 vs −1.0 ± 0.4 for Pain;−5.1 ± 1.1 vs −0.9 ± 0.3 for Interference with life;−7.2 ± 3.7 vs −2.2 ± 2.1 for HAMA;4.6 ± 1.2 vs 1.1 ± 0.6 for Relief.

Growth and corrosion behavior of rare earth film on hot-dip galvanized steel

Hot-dip galvanized(HDG)steel sheets were treated for 30 s?24 h by the rare earth aqueous solution containing 20 g/L Ce(NO3)3·6H2O,and the growth behavior and corrosion resistance of the rare earth film were investigated by SEM,EDS,AES and NSS.The results reveal that the rare earth film becomes thick while the mass gain of the samples does not distinctly change due to the zinc dissolution with the increase of treatment time.The film grows up more quickly and is apt to cracking in the vicinity of zinc grain boundaries,and eventually the film partly warps and flakes off with increasing film thickness.The NSS results show that the corrosion resistance of the film is dominated by both the film thickness and the cracks.With increasing treatment time,the corrosion resistance of the film increases within 1 h due to the increased film thickness and decreases after 1 h because the cracking and flaking off gradually become dominant factor.

The Influence of Al on the Surface Properties of the Hot-dip Galvanized Melt

Wettability of Zn-Al alloy melt on the pure iron substrate at 450℃was studied.The effect of Al content(Zn,Zn-1Al,Zn-2Al,Zn-3Al,Zn-4Al,and Zn-5Al)on the wetting behavior and interfacial reaction was investigated by high-temperature contact angle measuring device and scanning electron microscope(SEM).The results show that,with the increase of Al content,the initial contact angle of the molten alloy on the substrate decreases gradually and the wettability increases gradually.Compared with the initial contact angle,the final contact angle is slightly reduced,because the Fe-Al inhibition layer is preferentially formed at the interface when adding Al to the alloy.The presence of Al will promote the occurrence of the reactive wetting,leading to an insignificant wetting spreading process,and the final contact angle negligibly differs from the initial contact angle.The adhesion work and charge density distributions of interface systems were calculated based on the first-principles.The results show that the adhesion work of the Fe/Zn and Fe/(Zn-Al)interface model is 2.0171 J/m^(2)and 13.7944 J/m^(2),respectively.The addition of Al greatly increases the adhesion work between alloy melt and iron substrate.Compared with the Zn-Fe and Al-Fe interface models,it can be seen that a significant charge migration phenomenon occurs between the interfaces.The amount of charge migration in the Al-Fe interface model is much larger than that in the Zn-Fe interface model,indicating that the bonding between Al-Fe atoms can occur more easily and the interaction between Al-Fe interfaces is stronger.This is also the reason why the addition of Al increases the adhesion work between interfaces.

Design of TRIP Steel With High Welding and Galvanizing Performance in Light of Thermodynamics and Kinetics

A new type of transformation induced plasticity （TRIP） steel with not only high strength and high ductility but also superior welding and galvanizing properties was designed and developed recently. Low carbon and low silicon content were preliminarily selected with the aim of meeting the requirements of superior quality in both welding and galvanizing. Phosphorus was chosen as one of the alloying elements, because it could reduce carbon activity in cementite and increase the stability of austenite. In addition, the possibility of phosphorus segregating at grain boundary was also discussed by thermodynamics as well as kinetics. Phase diagram was estimated at high temperature and the composition of the steel was then selected in the hyperperitectic range to avoid problems, which might occur in sheet steel continuous casting. Phase diagram in the inter.critical temperature was estimated for the steel to obtain the starting temperature of fast cooling. For understanding the minimum rate of fast cooling, pearlite growth kinetics was calculated with self-developed diffusion coefficients of elements in grain boundary. Overaging temperature was determined through the calculation of To temperature by both equilibrium and para-equilibrium assumptions, which was different from the current determination, which is only based on an equilibrium estimation.

Hot-Dip Galvanized Sheet Production and Application

Hot-dip galvanized sheet is wildly used in construction,household appliances,ship,vehicle and vessel building and machinery,etc.In last ten years,with the development of automobile industry,the anti-eorrosion requirements for car body are increasingly strict,by which the rapid development in technology has been promoted.The application of hot-dip galvanized sheet,technological progress in production and some Chinese large units were introduced.

Corrosion behavior and mechanism of the automotive hot-dip galvanized steel with alkaline mud adhesion

The corrosion behavior and mechanism of hot-dip galvanized steel and interstitial-free （IF） substrate with alkaline mud adhesion were investigated by scanning electron microscopy （SEM）, X-ray diffraction （XRD）, electrochemical impedance spectroscopy （EIS）, and linear polarization. The results show that non-uniform corrosion occurs on the galvanized steel and IF substrate during 250 h with the mud adhesion. The corrosion products on the galvanized steel are very loose and porous, which are mainly ZnO, Zn5（OH）8C12·H2O and Zn（OH）2, and Fe-Zn alloy layer with a lower corrosion rate is exposed on the galvanized steel surface; however, the corrosion products on IF substrate are considerably harder and denser, whose compositions of rust are mainly FeOOH and Fe3O4, and several pits appear on their surface. The results of continuous EIS and linear polarization measurements exhibit a corrosion mechanism, that is, under activation control, the charge transfer resistances present different tendencies between the galvanized steel and IF substrate; in addition, the evolution of linear polarization resistances is similar to that of charge transfer resistances. The higher contents of dissolved oxygen and Cl^- ions in the mud play an important role in accelerating the corrosion.

Analysis of causes and influence factors of small black spot defects in hot-dip galvanized pure Zn products

In this study,the factors affecting the formation of small black spot defects on the surface of a hot-dip galvanized pure zinc strip are analyzed. These defects are primarily formed w hen the iron-aluminum inhibition layer is incompletely formed or fails to form or when foreign matter adheres to the surface or embeds in the zinc layer.The defects can be reduced by controlling the cleanliness and activity of the strip base before coating,regulating the zinc pot process parameters,and ensuring the cleanliness of the passline and workshop.

Roll Shape Setting Technology of Hot Galvanizing and Planishing Mill

A roll shape setting model was built for the hot galvanizing and planishing mill. The uniform transversal distributions of the front tension in the exit and the unit pressure were considered as the objective function. At the same time, the quality of the products, the stability of zinc layer, and the homogeneity of spangles were of considerable significance in the planishing process. The model was applied to the roll shape setting of the 1800 cold rolling 3# CGL hot galvanizing and planishing mill of Baosteel Co Ltd. After being planished, the flatness of a strip that was less than 6 I was more than 97%, and the flatness of others were less than 10 I; the pass percentage of the zinc lay- ers reached 100%.

Cracking of S235JR Cold-Deformed Steel during Galvanizing—Developing a Test to Evaluate and Predict the Effect of the Zinc Alloy Composition

This paper presents a study on the cracking of steel pieces during their galvanization in alloyed liquid zinc. An experimental design was developed to show the effect of the amount of the various alloying elements (Sn, Bi, Pb) on this phenomenon. The characterization of the effect was obtained by 1) deformation by three-point bending of a piece of steel with different levels of deflection;2) galvanizing and 3) observation and measurement of the cracks. A model of the critical deflection (deflection for crack starting) with the amounts of Sn, Pb, and Bi is presented and the predictions are described.

Evolution of appearance profile of hot-dip galvanized car-body steel sheet during deformation process

In recent years, the waterborne free intermediate coating process has been widely used in the automotive industry. Because the baking times and coating thickness are decreased, the surface covering capability of the painting process is reduced, which directly affects the appearance quality（ long-and short-wave values） of the body paint. Thus, there are correspondingly higher requirements for the white body surface profile prior to painting. The surface profile of the white body is mainly affected by the plate material, the surface profile, and the deformation process. So,the change rule for the surface profile during deformation of the steel plate is a key factor in coating appearance optimization. In this paper, we first analyze the typical deformation of the outer cover of a car body. Then ,we examine the change tendency of the surface profile of steel plates with respect to different deformation rates, specifically for a steel plate comprising a hot-dip galvanized bake-hardened steel sheet. Based on our analysis of the influence of the deformation on the coating appearance,we selected 3% ,5% ,and 8% deformation rates in this research. We found the roughness （Ra） value in the typical deformation range （3% -8% ） of the car body to exhibit a decreasing trend at first and then an increasing trend. The Ra value of the 8% deformation is not more than the original plate test value. When the Pc value of the original plate is in the lower range （ about 60）, it exhibits a slight increasing trend in the deformation process （3 % -8 % ）. And when the Pc value of the original plate is in the higher range （ about 120 ）, it exhibits no increasing trend in the deformation process （ 3% -8% ）. In contrast,the waviness （WCA） value in the car body＇s typical deformation range （3%-8%） shows a significant growth trend.

Development of Cr-free anti-fingerprint hot-dip galvanized sheet for household appliances

China has become the maximum household appliances manufacturing base worldwide.It is a new challenge facing the steel industry to develop the low-cost and environment-friendly sheet for household appliance industry,so Cr-free anti-fingerprint hot-dip galvanized sheet for household appliances is the upgraded product which satisfies the requirement of China household appliance industry' s nuisanceless treatment.The paper discusses the technical key points of development on Cr-free anti-fingerprint galvanized sheet for household appliances,including the development of the Cr-free anti-fingerprint chemical and the production technology of Cr-free anti-fingerprint galvanized sheet for household appliances.The paper elaborates the main compositions,physical features and properties of the Cr-free anti-fingerprint chemical, surface quality control technology,anti-fingerprint coating quality control technology,influence of anti-fingerprint film weight on corrosion resistance,conductibility,high-temperature discolouration resistance,acid resistance,alkaline resistance and solvent resistance of Cr-free anti-fingerprint hot-dip galvanized sheet, influence of anti-fingerprint coating uniformity on paintability of the sheet,influence of strip surface roughness on corrosion resistance and conductivity of the sheet and influence of strip surface quality on corrosion resistance of the sheet.Adopting the suitable Cr-free anti-fingerprint chemical and the reasonable production process parameters,the properties of the Cr-free anti-fingerprint hot-dip galvanized sheet conform to the delivery technical norms and the Cr-free anti-fingerprint hot-dip galvanized sheet becomes the new material for household appliances such as computer case.

The new technical progress of hot dip galvanizing process without sink roll

In this paper,the recent state and problems of the sink roll in CGL are described.Several methods of increasing its operational life span are introduced,such as surface coating technology and sleeve material technology.Fundamentally they cannot solve the problems of surface quality caused by the contact between strip and roll.On this basis,the newly developed principle and solutions for hot dip galvanizing technology without sink roll are highly emphasized,they are Float Technology,Electromagnetic pump technology,Electromagnetic enclosed slot by high-frequency AC,Electromagnetic enclosed slot by high-frequency DC.A comparison among their functions and characteristics is made and the possibility of its application is also discussed.Finally it comes to a conclusion that electromagnetic enclosed slot represents the direction of a continuous hot-dip galvanizing steel strip in the the 21st century.It has a very broad application prospects.Baosteel Technology Center is focused on the research and development of this technology.As technology advances,industrial applications is possible.

Lead and Cadmium Distribution in Tubes of Galvanized Steel by Hot-Dip Used for Drinking Water Supply

The main objective of this work was to evaluate the presence of lead and cadmium in galvanized steel tubes by hot-dip used exclusively for drinking water supply.In this research,samples of galvanized tubes were removed from walls of residential buildings with 30 years of use.In the process of hot galvanizing,the manufacturing standards allow or for low cost conveniences,and the use of primary zinc ingot with 1.6%metallic impurities,such as lead and cadmium,is allowed,enabling the incorporation of these metals into the zinc coating deposited on the carbon steel.The associated corrosion of these tubes can release these toxic metals,contaminating the drinking water used by residents.The samples taken from the tubes were evaluated by a square-wave anodic stripping voltammetry technique,and the results for lead and cadmium suggested randomly distributed levels,indicating that the contents of these contaminants depend mainly on the quality of the added primary zinc and the operational conditions of the immersion bath.The metallographic evaluations performed on the samples of the galvanized tubes showed irregularities in thickness and even a lack of the zinc layer deposited on the carbon steel surface.These facts suggest that galvanized tubes should not be used for drinking water.

Simulation analysis of hot dip galvanizing process parameters based on orthogonal experimental design

An iron and steel company＇ s hot galvanizing technology was chosen as the object. An orthogonal experimental scheme with 5 factors of mixed level was designed, according to the various factors affecting the distribution of slag. For each scheme, the amount of slag and slag height in different orthogonal schemes by simulation were obtained with FLUENT software. Then, range and variance analyses were selected to compare the trend of slag height in the different process parameters of the hot dip galvanizing process. Finally, the optimal combination of the process parameters was obtained.