High corrosion and wear resistant electroless Ni–P gradient coatings on aviation aluminum alloy parts

A Ni–P alloy gradient coating consisting of multiple electroless Ni–P layers with various phosphorus contents was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were used to characterize the different Ni–P coatings’ morphologies, phase structures, elemental compositions, and corrosion protection. The gradient coating showed good adhesion and high corrosion and wear resistance, enabling the application of aluminum alloy in harsh environments. The results showed that the double zinc immersion was vital in obtaining excellent adhesion (81.2 N). The optimal coating was not peeled and shredded even after bending tests with angles higher than 90°and was not corroded visually after 500 h of neutral salt spray test at 35℃. The high corrosion resistance was attributed to the misaligning of these micro defects in the three different nickel alloy layers and the amorphous structure of the high P content in the outer layer. These findings guide the exploration of functional gradient coatings that meet the high application requirement of aluminum alloy parts in complicated and harsh aviation environments.

Homogenous coating of Li^(+)conductive Li_(5)AlO_(4)on single-crystalline nonstoichiometric Li_(1.04)Ni_(0.92)Al_(0.04)O_(2)for rechargeable lithium-ion batteries

Cobalt-free,nickel-rich LiNi_(1-x)Al_(x)O_(2)(x≤0.1)is an attractive cathode material because of high energy density and low cost but suffers from severe structural degradation and poor rate performance.In this study,we propose a molten salt-assisted synthesis in combination with a Li-refeeding induced aluminum segregation strategy to prepare Li_(5)AlO_(4)-coated single-crystalline slightly Li-rich Li_(1.04)Ni_(0.92)Al_(0.04)O_(2).The symbiotic formation of Li_(5)AlO_(4)from reaction between molten lithium hydroxide and doped aluminum in the bulk ensures a high lattice matching between the Ni-rich oxide and the homogenous conductive Li_(5)AlO_(4)that permits high Li^(+)conductivity.Benefiting from mitigated undesirable side reactions and phase evolution,the Li_(5)AlO_(4)-coated single-crystalline Li_(1.04)Ni_(0.92)Al_(0.04)O_(2)delivers a high specific capacity of220.2 mA h g^(-1)at 0.1 C and considerable rate capability(182.5 mA h g^(-1)at 10 C).Besides,superior capacity retention of 90.8%is obtained at 1/3 C after 100 cycles in a 498.1 mA h pouch full cell.Furthermore,the particulate morphology of Li_(1.04)Ni_(0.92)Al_(0.04)O_(2)remains intact after cycling at a cutoff voltage of 4.3 V,whereas slightly Li-deficient Li_(0.98)Ni_(0.97)Al_(0.05)O_(2)features intragranular cracks and irreversible lattice distortion.The results highlight the value of molten salt-assisted synthesis and Li-refeeding induced elemental segregation strategy to upgrade Ni-based layered oxide cathode materials for advanced Li-ion batteries.

Analysis of Coating Microstructure of Hot-Dip Aluminum of Deformed Low-Carbon Steel Containing Rare Earth

The coating microstructure of hot-dip aluminum (HDA) of deformed low-carbon steel containing RE was analyzed by metallography microscopy, TEM and XRD, and the forming mechanism was also discussed. The results show that, the Fe_2Al_5 phase, on whose subcrystal boundaries, Al particles with the size of 7～30 μm existing on parallel linear are, grows a strong orientation. And the spread activation energy of Al is 155.22 kJ·mol -1. In addition, the effects of deformation on coating microstructure of hot-dip aluminum and the function of RE were preliminarily analyzed.

Hot-Dip Coating of Lead-free Aluminum on Steel Substrates with Ultrasonic Vibration

Hot-dip coating has been practically employed in manufacturing zinc alloy coated steel sheets.However,it is difficult to coat aluminum alloy on a bulky steel substrate without sufficient preheating,because a rapidly solidified layer containing gas babbles is formed on a substrate surface.A variety of iron-aluminides are also formed at the interface of a steel and aluminum hot-dip coating system,which is the main difficulty in joining of steel with aluminum.Ultrasonic vibration was applied to a steel substrate during hot-dip coating of aluminum alloy to control a rapidly solidified layer and a brittle reaction layer.Hot dipping of columnar steel substrates into molten aluminum alloy （Al-2.7 mass fraction Si-4.6 mass fraction Sn） was carried out through the use of a Langevin oscillator with resonant frequency of 19.5 kHz.The application of ultrasonic vibration is quite effective to control a rapidly solidified layer and a surface oxide layer from a substrate surface by the sonocapillary effect based on a cavitation phenomenon,so that the intimate contact is achieved at the beginning of hot-dip coating.The application of ultrasonic vibration to hot-dipping is effective to control a reaction layer with less than 5 #m in thickness.An impact test exhibits that the good adhesive strength is approved in hot-dipped aluminum coatings with a thin reaction layer of approximately 5μm.

Microstructure and mechanical properties of twin-wire arc sprayed Ni-Al composite coatings on 6061-T6 aluminum alloy sheet

We have systematically studied the microstructure and mechanical properties of Ni-5wt%Al and Ni-20wt%Al composite coat- ings fabricated on 6061-T6 aluminum alloy sheet by twin-wire arc spraying under different experimental conditions. The abrasive wear be- havior and interface diffusion behavior of the composite coatings were evaluated by dry/wet rubber wheel abrasive wear tests and heat treat- ment, respectively. Experimental results indicate that the composite coatings exhibit features of adhesive wear. Besides, the Vickers micro- hardness of NiA1 and Ni3AI intermetallic compounds is relatively larger than that of the substrate, which is beneficial for enhancing the wear resistance. With the increase of annealing temperature and time, the interface diffusion area between the Ni-Al coating and the substrate gradually expands with the formation of NiAl3 and Ni2Al3 phases, and is controlled by diffusion of aluminum atoms. The grain growth ex- ponent n of diffusion kinetics of the Ni-Al coating, calculated via a high-temperature diffusion model at 400, 480, and 550℃, is between 0.28 and 0.38. This satisfies the cubic law, which is consistent with the general theoretical relationship of high-temperature diffusion.

Preparation technology and anti-corrosion performances of black ceramic coatings formed by micro-arc oxidation on aluminum alloys

In order to prepare ornamental and anti-corrosive coating on aluminum alloys, preparation technology of black micro-arc ceramic coatings on Al alloys in silicate based electrolyte was studied. The influence of content of Na2WO4 and combination additive in solution on the performance of black ceramic coatings was studied; the anticorrosion performances of black ceramic coatings were evaluated through whole-immersion test and electrochemical method in 3.5% NaCl solution at different pH value; SEM and XRD were used to analyze the surface morphology and phase constitutes of the black ceramic coatings. Experimental results indicated that, without combination additives, with the increasing of Na2WO4 content in the electrolyte, ceramic coating became darker and thicker, but the color was not black; after adding combination additive, the coating turned to be black; the black ceramic coating was multi-hole form in surface. There was a small quantity of tungsten existing in the black ceramic coating beside α-Al2O3 phase and β-Al2O3 phase. And aluminum alloy with black ceramic coating exhibited excellent anti-corrosion property in acid, basic and neutral 3.5% NaCl solution.

Effect of aluminum borate whisker coating on interface and mechanical properties of 6061Al matrix composites

Copper coating was deposited on the surface of aluminum borate whisker by an electroless plating method.This method was used to modify the interfacial property of squeeze-casting aluminum borate whisker reinforced 6061Al matrix composite.Interface observation indicates that the spinel reaction(MgAl2O4) is hindered by the copper coating,and the difference in interfacial reaction degree affects the tensile property and aging behavior of the composite.For the composite with less spinel reaction(MgAl2O4),its peak-aging process are postponed due to less depletion of magnesium.On the fracture surface of copper-coated composite dimples and fractures of whiskers are more,but on the fracture surface of uncoated composite pull-out of whiskers are more than that on the coated one.In uncoated composite the fracture generally originates from the near-interface-region.

Composite hydrophilic coating for conditioner aluminum fins

To solve the so called “white rust” and ’water bridge" problems of the aluminum fins for heat exchanger of automobile air conditioner, aimed at nationalizing the art of hydrophilic coating technology, the choice of coating forming and curing materials was investigated. By measuring the water contact angle, SEM surface scanning and ingredients analysis of the coating, optimal parameters and composition are acquired. The coating forming mechanisms of the composition was also expatiated. The coating obtained has good hydrophilic and other properties.

A study on the effect of coating's sorption capacity on the porosity in lost foam aluminum alloy casting

Effects of coating constituent, coating density, coating layer thickness and temperature on coating sorption capacity for polystyrene decomposition products have been studied systematically. It has been found that the effect of attapulgite clay on sorption capacity is the largest among coating constituents. The sorption capacity of the coating with 2% attapulgite clay is elevated by 81%. The relationship between casting porosity and coating sorption capacity has been studied. It has been pointed out that higher coating sorption capacity for polystyrene decomposition products is helpful to decrease the casting porosity. Results also show that the sorption capacity of self-developed HW-1 coating for polystyrene decomposition products is as good as that of Ashland coating from America.

Low temperature bonding of LD31 aluminum alloys by electric brush plating Ni and Cu coatings

Soldering of LD31 aluminum alloys using Sn-Pb solder paste after electric brush plating Ni and Cu coatings was investigated. The technology of electric brush plating Ni and Cu was studied and plating solution was developed. The microstructure of the coatings, soldered joint and fracture face were analyzed using optic microscopy, SEM and EDX. The shear strength of soldered joint could reach as high as 26.83MPa. The results showed that reliable soldered joint could be obtained at 230℃, the adhesion of coatings and LD31 aluminum alloy substrate was high enough to bear the thermal process in the soldering.

Improving mechanical properties of AZ91D magnesium/A356 aluminum bimetal prepared by compound casting via a high velocity oxygen fuel sprayed Ni coating

In this paper,a Ni coating was deposited on the surface of the A356 aluminum alloy by high velocity oxygen fuel spraying to improve the performance of the AZ91D magnesium/A356 aluminum bimetal prepared by a compound casting.The effects of the Ni coating as well as its thickness on microstructure and mechanical properties of the AZ91D/A356 bimetal were systematically researched for the first time.Results demonstrated that the Ni coating and its thickness had a significant effect on the interfacial phase compositions and mechanical properties of the AZ91D/A356 bimetal.The 10μm’s Ni coating cannot prevent the generation of the Al-Mg intermetallic compounds(IMCs)at the interface zone of the AZ91D/A356 bimetal,while the Ni coating with the thickness of 45μm and 190μm can avoid the formation of the Al-Mg IMCs.When the Ni coating was 45μm,the Ni coating disappeared and transformed into Mg-Mg_(2)Ni eutectic structures+Ni_(2)Mg_(3)Al particles at the interface zone.With a thickness of 190μm’s Ni coating,part of the Ni coating remained and the interface layer was composed of the Mg-Mg_(2)Ni eutectic structures+Ni_(2)Mg_(3)Al particles,Mg_(2)Ni layer,Ni solid solution(SS)layer,Al_(3)Ni_(2) layer,Al_(3)Ni layer and sporadic Al_(3)Ni+Al-Al_(3)Ni eutectic structures from AZ91D side to A356 side in sequence.The interface layer consisting of the Mg-Ni and Al-Ni IMCs obtained with the Ni coating had an obvious lower hardness than the Al-Mg IMCs.The shear strength of the AZ91D/A356 bimetal with a Ni coating of 45μm thickness enhanced 41.4%in comparison with that of the bimetal without Ni coating,and the fracture of the bimetal with 45μm’s Ni coating occurred between the Mg matrix and the interface layer with a mixture of brittle fracture and ductile fracture.

Abrasive wear behaviors of high velocity arc sprayed iron aluminum composite coatings

The High Velocity Arc Spraying （HVAS） technology was used to prepare Fe-Al composite coatings by the adding of different elements into cored wires to obtain different Fe-Al coatings. The added compounds do great effect on the properties of the composite coatings. The microstructures and abrasive wear performances of the coatings were assessed by transmission electron microscopy （TEM）, scanning electron microscopy （SEM）, and THT07-135 high temperature wear equipment. It was found that the adding of Cr3C2 can greatly increase the room temperature wear behavior, and Fe-Al/WC coatings have adapting periods at the beginning of wear experiment. With the rise of temperature, the wear resistance of Fe-AI/Cr3C2 coatings becomes bad from room temperature to 250℃, and then stable from 250℃ to 550℃; the wear resistance of Fe-Al/WC becomes well with the rise of temperature. The adding of Cr and Ni can also improve wear performances of Fe-Al composite coatings.

Effects of zincate treatment on adhesion of electroless Ni-P coating onto various aluminum alloys

The effects of alloying elements on zincate treatment and adhesion of electroless Ni-P coating onto various aluminum alloy substrates were examined.Surface morphology of zinc deposits in the 1st zincate treatment and its adhesion were changed depending on the alloying element.The zinc deposits in the 2nd zincate treatment became thinly uniform,and the adhesion between aluminum alloy substrate and Ni-P coating was improved irrespective of the alloying element.XPS analysis revealed the existence of zinc on the surface of each aluminum alloy substrate after the pickling in 5% nitric acid.This zinc on the surface should be an important factor influencing the morphology of zinc deposit at the 2nd zincate treatment and its adhesion.

Influence of oxidant KMnO_4 on film-forming process of rare earth metal conversion coating on LY12 aluminum alloy

A Cu/Al galvanic couple was established to study the influence of the oxidantKMnO_4 on the film-forming process of rare earth metal (REM) conversion coating on LY12 aluminumalloy. It is found that the galvanic couple simulative experiment accords with the actual immersion,and it can be substantially used to simulate the behavior of LY12 aluminum alloy in thefilm-forming process. It is showed that the formation of the coating is quickened in CeCl_3 solutioncontaining KMnO_4 compared with that not containing KMnO_4. XPS results reveal that the coatingformed on cathode is composed of oxide or hydroxide of Ce and Mn, so the mechanism of formation ofREM conversion coating changes when KMnO4 is added.

High temperature performance of arc-sprayed aluminum bronze coatings for steel

The high-temperature oxidation behavior of arc-sprayed aluminum bronze coatings on steel substrate was studied during isothermal exposures in air at 900 ℃. The surface morphologies and interface of the coatings after isothermal oxidation at 900 ℃ for different times were observed. The experiments showed that the coatings on steel substrate were not deteriorated and the substrate was protected well, being exposed to high temperatures up to 900 ℃ . The coatings withstood more than ten times thermal shock tests without any coating separation. The thermal expansion coefficient of the coatings was measured, revealing not much difference between it and that of steel substrate. After exposure at high temperature, the coatings were still adhered to steel substrate well. Isothermal mass gain of the coatings at elevated temperature in dry air was measured by means of a thermal balance and the oxidation behavior was evaluated by oxidation kinetic curves, exhibiting the oxidation kinetics curve accorded with a parabolic law. The parabolic rate constant of the oxidation kinetic curve is 1.02×10?9 g2·cm?4·s?1 for the first 60 min and from 150 min to 2 880 min the constant is 5.1×10?12 g2·cm?4·s?1.

Electrical resistivity of TiB_2/C composite cathode coating for aluminum electrolysis

The electrical resistivity of TiB2/C cathode composite coating at different temperatures was measured with the electrical conductivity test device; the effects of TiB2 content and kinds of carbonaceous fillers as well as their mean particle size on their electrical resistivities were investigated. The results show that electrical resistivity of the coating decreases with the increase of TiB2 content and the decrease of its mean particle size. When the mass fraction of TiB2 increases from 30% to 60%, the electrical resistivity of the coating at room temperature decreases from 31.2μΩ·m to 23.8μΩ·m. The electrical resistivity of the coating at 960℃ lowers from 76.1μΩ· m to 38.4μΩ·m with the decrease of TiB2 mean particle size from 12μm to 1μm. The kinds of carbonaceous fillers have great influence on the electrical resistivity of TiB2/C composite coating at 960℃, when the graphite, petroleum coke and anthracite are used as fillers, the electrical resistivities of the coating are 20.3μΩ·m, 53.7μΩ·m and 87.2μΩ·m, respectively. For the coating with petroleum coke filler, its electrical resistivity decreases with the increase of the mean particle size of petroleum coke filler. The electrical resistivity at 960℃ decreases from 56.2μΩ·m to 48.2μΩ·m with the mean particle size of petroleum coke increasing from 44μm to 1200μm. However, too big carbonaceous particle size has adverse influence on the abrasion resistance of coating. Its proper mean particle size is 420μm.

Composition and hardness of mullite coatings formed with direct current power supply on LY12 aluminum alloy surface

The surface modification of aluminum and its alloys using plasma technology is increasingly being investigated. Thick ceramic coatings with high hardness on aluminum alloys can be prepared successfully using a micro-plasma oxidation （MPO） technique. In this work, the composition, microstructure and elemental distribution of ceramic coatings formed by MPO on LY 12 aluminum alloy and its hardness are investigated using XRD, EPMA and microhardness instruments. The results show that the ceramic coatings consist of mullite, γ-Al2O3 and a lot of amorphous matter. The content of silicon in the coatings increases from interface to the coatings, however, the content of aluminum decreases along this direction. The maximum hardness of ceramic coatings is up to 92 GPa.

Ambient temperature cured TiB_2 cathode coating for aluminum electrolysis

The concept of ambient temperature curable TiB 2 cathode coating was put forward, and the ambient temperature curable TiB 2 cathode coating was prepared successfully. Differing from the previous TiB 2 cathode coating solidified approximately at 200 ℃,the ambient temperature curable TiB 2 cathode coating can be solidified at room temperature, so the heating equipment is not necessary, which simplifies the preparation process and facilitates the industrial application of TiB 2 cathode coating. Many kinds of resin and curing agent were investigated. On the above mentioned basis, the ambient temperature curable TiB 2 cathode coating was prepared with furan resin 5 500 mixed with complex resins B as carbon binder and DXG1 as curing agent in 24 h. The results show that the properties of prepared coating are excellent, the electrical resistivity is 29.8 μΩ·m, the compressive strength is 33.6 MPa, which are all better than the relevant properties of partially graphitized cathode carbon block for aluminum electrolysis prescribed by the GB 8744 88. SEM morphologies show that the section morphology of the TiB 2 coating is unaltered during the electrolysis test, the TiB 2 coating can be used in aluminum electrolysis industry to save energy and prolong the life of aluminum electrolysis cell.

Corrosion behavior of sintered zinc-aluminum coating in NaCl solution

Sintered zinc aluminum coating (SZAC) was prepared using zinc flakes, aluminum flakes and CrO 3 as main raw materials. The corrosion behavior of SZAC in 3.5%NaCl solution was studied by means of SEM, EDS, EIS and so on. Results indicate that aluminum corroded in advance of zinc to produce speculate or spherical substances, which attaches to SZAC and adds mass to it. Corrosion production passivates metal powders in SZAC, causes E corr of SZAC to increase gradually, and causes the arising of the third time constant in EIS, which corresponds to the insulation of corrosion production.

Preparation and performance of a cold gas dynamic sprayed high-aluminum bronze coating

By mixing preheated high-aluminum bronze powders with different amounts of Al_2O_3 powder, a low-pressure cold-sprayed coating was prepared and sprayed onto a Cr12MoV steel substrate. The hardness of the coating and the bonding strength between the coating and the substrate were tested with a HV-1000 microhardness tester and a mechanical universal testing machine. The surface microstructure, cross-section and tensile fracture surface of the coating were observed with a scanning electron microscope(SEM). Correspondingly, the influences of the preheat treatment temperature of the bronze powder and the Al_2O_3 content on the coating performance were investigated. The results indicate that the hardness of bronze powders decreased and the coating deposition rate increased after the preheating treatment of the bronze powder. The Al_2O_3 content in the mixed powders contributed to the deformation of bronze powders during the spraying process. This trend resulted in varied performance of the coating.