Results presented in this study contribute to investigation of the microstructure and mechanical properties of the hot-rolled Fe16Mn0.6C steel plates.The steel plates have been produced by being hot-rolled at temperat...Results presented in this study contribute to investigation of the microstructure and mechanical properties of the hot-rolled Fe16Mn0.6C steel plates.The steel plates have been produced by being hot-rolled at temperatures ranging from 1100℃ to 850℃ in seven passes to 97.5% reduction in thickness and then cooled in a furnace of 650℃.Some plates have been annealed at temperatures ranging from 300℃ to 1100℃ for 5min to 60min,and then followed by water quenching.There are annealing twins in the hot-rolled Fe16Mn0.6C steel.Fe16Mn0.6C steel presents similar ductile behavior as X-IPTM steel,but much higher elongation than commercial martensitic steel (MP) 1000,dual phase (DP) 980,and transformation induced plasticity (TRIP) 980 steels.Fe16Mn0.6C steel experiences γε (-α) transformation in some local regions,but remains mostly austenite during the entire deformation process.Fe16Mn0.6C steel with special mechanical properties can be produced by using the appropriate anneal technology.Twinning induced plasticity(TWIP) effect only occurs in the Fe16Mn0.6C steel annealed at temperature higher than 900℃.展开更多
基金supported by the Key Research Foundation of Baoshan Iron & Steel Co.,Ltd.(No.D06EBEA207)
文摘Results presented in this study contribute to investigation of the microstructure and mechanical properties of the hot-rolled Fe16Mn0.6C steel plates.The steel plates have been produced by being hot-rolled at temperatures ranging from 1100℃ to 850℃ in seven passes to 97.5% reduction in thickness and then cooled in a furnace of 650℃.Some plates have been annealed at temperatures ranging from 300℃ to 1100℃ for 5min to 60min,and then followed by water quenching.There are annealing twins in the hot-rolled Fe16Mn0.6C steel.Fe16Mn0.6C steel presents similar ductile behavior as X-IPTM steel,but much higher elongation than commercial martensitic steel (MP) 1000,dual phase (DP) 980,and transformation induced plasticity (TRIP) 980 steels.Fe16Mn0.6C steel experiences γε (-α) transformation in some local regions,but remains mostly austenite during the entire deformation process.Fe16Mn0.6C steel with special mechanical properties can be produced by using the appropriate anneal technology.Twinning induced plasticity(TWIP) effect only occurs in the Fe16Mn0.6C steel annealed at temperature higher than 900℃.