The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing wit...The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing with HRB335 steel bars, i.e. coordination of strength and ductility, strain-aging sensibility, low temperature impact toughness, weld ability and high strain low cycle fatigue. The ductile-brittle transit temperatures of hot-rolled and strain-aged steel bars were evaluated as –17 °C and ?8 °C respectively, and the low temperature impact toughness of HRB400 steel bars remains to be improved. Transmission electron microscopy (TEM) and electron diffraction showed little vanadium existed in ferrite as VN, most of which existed in pearlite as alloy cementite which resulted in the declination of impact toughness. Methods were suggested to improve the anti- seismic properties of steel bars.展开更多
Taking the seamless tube plant of Baoshan Iron & Steel Complex in China as the background,we analyze the characters of hot rolling seamless steel tube:multi varieties,low volume,complicated production process,flex...Taking the seamless tube plant of Baoshan Iron & Steel Complex in China as the background,we analyze the characters of hot rolling seamless steel tube:multi varieties,low volume,complicated production process,flexible production routes.Then integrated scheduling problem for hot rolling seamless steel tube production is studied,which covers two key points;order-grouping problem and solution method for flowshop/jobshop scheduling problem.On the basis of these two problems,integrated scheduling decision system is developed.The design idea,function flow sheet,data processing method,and functional module of visualized human-computer interactive scheduling system implemented in seamless steel tube plant of Shanghai Baoshan Iron & Steel Complex are described into detail.Compared with manual system,the performance of system shows the applicability and superiority in several criteria.展开更多
The types and growth of various oxide scales formed during the different phases of the production of hotrolled strip steel products are reviewed. Similarities and differences between the "tertiary scale" on the surf...The types and growth of various oxide scales formed during the different phases of the production of hotrolled strip steel products are reviewed. Similarities and differences between the "tertiary scale" on the surface of carbon steels at high temperatures and the oxide scale on pure iron are compared. The micro-structural features of the "final oxide scale" on the surface of strip steels at room temperature as well as the relationship between these features and the position of the steel coil (plate) and the subsequent processes of recoiling, temper rolling and trimming, etc. are summarized. The actual oxide scales retained on the commercial hot-rolled strip steels at room temperature have been proposed to define as " quartus scale" for the first time. The micro-structural development and phase transformation of the initial "tertiary scale" during and after cooling and coiling are described. The reasons for the "tertiary scale" on carbon steels differing from the oxide scale formed on pure iron, and the major influencing factors in the formation of various types of "quartus scales" are analyzed from both thermodynamic and dynamic viewpoints. The development mechanism of " quartus scales" is discussed and the potential effects of the " quartus scale" state (thickness, constitution, structure and defects), on the rusting and pickling properties of commercial hot-rolled strip steel, as well as on the mechanical properties of oxide scales are analyzed.展开更多
Nb-Tihot-rolled TRIP-assisted steel with high plasticity and appropriate volume percentage of retained austenite based on fine ferrite grain have been developed in the experiment. The test results showed that niobium ...Nb-Tihot-rolled TRIP-assisted steel with high plasticity and appropriate volume percentage of retained austenite based on fine ferrite grain have been developed in the experiment. The test results showed that niobium tend to exist in solution state in matrix with less precipitation, and niobium-titanium could be precipitated in form of (Nb, Ti)C or (Nb, Ti) (C, N), which play an important role in increasing yield strength (from 495 MPa to 610 MPa). Besides, the retained austenite had a positive effect on improving the plasticity by transformation into martensite during tensile deformation.展开更多
In order to simplify production process and to decrease production cost of thicker cold-rolled iF steel sheets for deep drawing applications, a new hot-rolled IF steel sheet is developed through hot-rolling in or regi...In order to simplify production process and to decrease production cost of thicker cold-rolled iF steel sheets for deep drawing applications, a new hot-rolled IF steel sheet is developed through hot-rolling in or region. In this paper, properties, microstructures and precipitate morphology of hot-rolled iF steel sheets are described..展开更多
As one of the important categories of hot-rolled products, hot-rolled steel plates for automobile applications generally undergo uniform corrosion or localized corrosion according to different environments of manufact...As one of the important categories of hot-rolled products, hot-rolled steel plates for automobile applications generally undergo uniform corrosion or localized corrosion according to different environments of manufacturing, transportation and/or storage of the plates. General corrosion often takes place on the surface of a plate in the exterior part of a package, and only reduces the thickness of the plate and slightly increases the roughness of the surface; however, localized corrosion on the surface of a plate inside the package is likely to result in the formation of pit-like defects on the substrate of the plate, which cannot be removed thoroughly by normal acid pickling or sand blasting, and affects the application of the plate. This research report analyzes the phenomena and characteristics of the rusting behavior of hot- rolled steel plates for automobile applications, and the influencing factors are summaried. The corresponding preventative measures are proposed.展开更多
The microstructure characteristics with super fine ferrite grain size less than 5mm, appropriate retained austenite fraction around 5.0% and or removable abundant dislocations have been obtained by controlled rolling ...The microstructure characteristics with super fine ferrite grain size less than 5mm, appropriate retained austenite fraction around 5.0% and or removable abundant dislocations have been obtained by controlled rolling and cooling, which leads to well balance com- prehensive properties with high tensile strength of 510 and 615MPa, high elongation of 40% and 27%, low ratio of yield strength to tensile strength 0.83 and 0.80, as well as low ductile- brittle transition temperature less than -80 and -70℃ for advanced aluminum hot-rolled TRIP steel and silicon hot-rolled TRIP steel, respectively.展开更多
Influence of thermo-mechanical controlled processing(TMCP),including two-stage rolling with laminar cooling,air cooling and ultra-fast cooling,on the microstructure and mechanical properties of three kinds of Nb-micro...Influence of thermo-mechanical controlled processing(TMCP),including two-stage rolling with laminar cooling,air cooling and ultra-fast cooling,on the microstructure and mechanical properties of three kinds of Nb-microalloeyed steels was investigated by hot-rolling experiment.Effect of chemistry compositions and microstructure on mechanical properties and the relationship between the multiphase microstructure' s formation with TMCP were analyzed.The results showed that the mixed microstructure containing ferrite,bainite,martensite and a small amount of retained austenite can be obtained by thermo-mechanical controlled processing.Size, quantity and distribution of the constituents(ferrite grain,bainite packet and M-A islands) significantly affect the mechanical properties of three kinds of Nb-microalloyed steels.Under the condition of similar TMCP parameters, there is a gradually decreasing tendency in tensile strength from high silicon Nb steel,high silicon Nb-Ti steel to low silicon Nb-Ti steel,and an opposite tendency in total elongation and product of tensile strength and ductility. Total elongation and product of tensile strength and ductility reach the maximum values(41%and 25256 MPa% respectively) for low silicon Nb-Ti steel.展开更多
The patenting process of three hot-rolled steels with carbon mass contents of 0.70%-0. 90% was studied. The effect of the quenching temperature on the cementite lamellar distance in the steel was evaluated on the basi...The patenting process of three hot-rolled steels with carbon mass contents of 0.70%-0. 90% was studied. The effect of the quenching temperature on the cementite lamellar distance in the steel was evaluated on the basis of microstructural characterization and mechanical property tests. The patenting treatment of high-carbon hot- rolled strip and its application in springs were discussed.展开更多
The critical transformation temperatures,A_(c1) and A_(c3),of a hot-rolled low-carbon titanium microalloyed steel were determined as a part of an examination of its phase-transformation behavior. Austenite decompositi...The critical transformation temperatures,A_(c1) and A_(c3),of a hot-rolled low-carbon titanium microalloyed steel were determined as a part of an examination of its phase-transformation behavior. Austenite decomposition during the continuous cooling of the titanium microalloyed steel was studied by heating it to 1 250 ℃,cooling it to 880 ℃,holding for 2 s,and then cooling it to room temperature at different cooling rates. The transformation kinetics( CCT curve) was characterized as well.展开更多
In this study, the welding technology of the hot-rolled extra-high-strength steel, BS960QC, has been comprehensively investigated. Analysis has been made on the weldability ,the different welding procedures ,the mecha...In this study, the welding technology of the hot-rolled extra-high-strength steel, BS960QC, has been comprehensively investigated. Analysis has been made on the weldability ,the different welding procedures ,the mechanical properties, and the fatigue properties, and a set of recommendation guidelines have been proposed for evaluating the welded joints of the extra-high-strength steel. The research and results indicate that the hot-rolled extra-high-strength steel, BS960QC,has good weldability and an excellent adaptability to welding procedures. Further,the excellent mechanical properties and fatigue properties of the welded joints ,which can be achieved by using optimized welding procedures, can completely meet the technical requirements of the construction machinery industry.展开更多
Results presented in this study contribute to investigation of the microstructure and mechanical properties of the hot-rolled Fe16Mn0.6C steel plates.The steel plates have been produced by being hot-rolled at temperat...Results presented in this study contribute to investigation of the microstructure and mechanical properties of the hot-rolled Fe16Mn0.6C steel plates.The steel plates have been produced by being hot-rolled at temperatures ranging from 1100℃ to 850℃ in seven passes to 97.5% reduction in thickness and then cooled in a furnace of 650℃.Some plates have been annealed at temperatures ranging from 300℃ to 1100℃ for 5min to 60min,and then followed by water quenching.There are annealing twins in the hot-rolled Fe16Mn0.6C steel.Fe16Mn0.6C steel presents similar ductile behavior as X-IPTM steel,but much higher elongation than commercial martensitic steel (MP) 1000,dual phase (DP) 980,and transformation induced plasticity (TRIP) 980 steels.Fe16Mn0.6C steel experiences γε (-α) transformation in some local regions,but remains mostly austenite during the entire deformation process.Fe16Mn0.6C steel with special mechanical properties can be produced by using the appropriate anneal technology.Twinning induced plasticity(TWIP) effect only occurs in the Fe16Mn0.6C steel annealed at temperature higher than 900℃.展开更多
In this work, the microstructure and the strain partitioning of lean duplex stainless steel 2101 (LDX 2101) during different hot-rolling processes are investigated by optical microscopy and electron-backscattered diff...In this work, the microstructure and the strain partitioning of lean duplex stainless steel 2101 (LDX 2101) during different hot-rolling processes are investigated by optical microscopy and electron-backscattered diffraction (EBSD). The results show that the LDX 2101 exhibits poor thermoplasticity at high temperature. The four-pass hot-rolled plates show fewer edge-cracking defects and superior thermoplasticity compared with the two-pass hot-rolled plates prepared at different temperature. The phase boundary is the weakest site in the LDX 2101. The cracks are initiated and propagated along the phase boundaries during the hot-rolling process. According to the EBSD analysis, the increase of the hot-rolling pass can dramatically improve the strain distribution in ferrite and austenite phases and promote the strain transmission in the constituent phases, thereby improving the coordinated deformation ability of the two phases. This effect further in- creases the thermoplasticity and reduces the formation of edge cracks in LDX 2101.展开更多
The non-vacuum roll bonding method of nickel plating on the base materials is put forward in accordance with the primary problems existed in the roll bonding of stainless/carbon steel. After nickel plating test on the...The non-vacuum roll bonding method of nickel plating on the base materials is put forward in accordance with the primary problems existed in the roll bonding of stainless/carbon steel. After nickel plating test on the base materials, the microstructure of nickel cladding is observed by scanning electron microscopy (SEM) at high, and room temperature, and the results show that the nickel cladding on base material can be protected from oxidation in the high temperature. Non-vacuum roll bonding tests of nickel plating on base materials are done by the roll bonding equipment, and the roll bonding plates of stainless/carbon steel are obtained. The microstructure and the elements distribution of non-vacuum roll bonding interface are analyzed by optical microscope (OM) and SEM. The results reflect that the nickel plating layer and the base materials bond well.展开更多
In this study, the matrix structure, state and composition of the mill scales of four typical domestically made 510L hot-rolled strips were observed and analyzed by means of optical microscopy (OM) ,scanning electro...In this study, the matrix structure, state and composition of the mill scales of four typical domestically made 510L hot-rolled strips were observed and analyzed by means of optical microscopy (OM) ,scanning electron microscopy (SEM) and X-ray diffraction (XRD). The corrosion behavior of the steels with and without mill scales were investigated by means of hot-humid corrosion tests under the condition of relative humidity ( RH ) of 95% at 50℃ and 70℃, respectively. The results show that the matrix structures, state, composition and thickness of mill scales vary in the strips. The rusting starting time of the specimens with scales is generally a bit longer than that of the specimens without scales, but their corrosion mass-gain is higher. For these two kinds of specimens ,their corrosion rate increases significantly with the increase of temperature. The rusting behavior of the 510L strips produced by various plants is different due to the variations of hot-rolling processes and designed chemical compositions. Various relevant aspects should be taken into account in the evaluation of the corrosion behavior of hot-rolled strips.展开更多
To investigate the tensile deformation behavior of high strength anti-seismic steel with multi-phase microstructure,tensile tests with strains of 0.05,0.12 and 0.22 were performed at room temperature.Microstructure of...To investigate the tensile deformation behavior of high strength anti-seismic steel with multi-phase microstructure,tensile tests with strains of 0.05,0.12 and 0.22 were performed at room temperature.Microstructure of tested steels was observed by means of optical microscopy(OM),transmission electron microscopy(TEM)and scanning electron microscopy(SEM).Tensile mechanical properties of tested steels were obtained,and the influence of bainite content on deformation behavior was also discussed.Meanwhile,the deformation mechanism of steel with three kinds of microstructures of bainite,pearlite and ferrite was analyzed.Results show that tested steel with high volume fraction of bainite exhibits a continuous deformation behavior,and this may be attributed to a higher bainite volume fraction and a lower mobile dislocation density.The morphology of microstructure will influence the mechanical properties of tested steels.An increasing content of bainite can improve the tensile strength,but reduce the plasticity and toughness of the tested steels.In the deformation process of 0.039 Nb steel,the ferrite and bainite have priorities to deform,and the deformation exhibits co-deformation of all microstructures in the later stage of deformation.In the deformation process of 0.024Nb-0.032 Vsteel,the ferrite and pearlite have priorities to deform,and the deformation exhibits co-deformation of all microstructures in the later stage of deformation.展开更多
Heredity in the microstructure and mechanical properties of hot-rolled spring steel wire 60Si2MnA during heat treatment process was investigated comprehensively. The steel was isothermally transformed to obtain variou...Heredity in the microstructure and mechanical properties of hot-rolled spring steel wire 60Si2MnA during heat treatment process was investigated comprehensively. The steel was isothermally transformed to obtain various hot-rolled microstructure (pearlite fineness within the range of 140-510 nm) and mechanical properties, and followed by some quenching-tempering treatment. Afterwards, microstructure was characterized by optical microscopy, scanning electron microscopy and quantitative metallography, and mechanical properties were determined by tensile test. The results indicated that the hot-rolled microstructure with a coarsen pearlite structure had been changed after reheating, to a austenite microstructure with bigger and more uneven grain size, and finally to a coarsen tempered microstructure. And the average austenite grain size and standard deviation of its distribution in quenched microstructure were observed to depend linearly on the interlamellar spacing in hot-rolled microstructure. Besides, to obtain a good combination of the final strength and plasticity, an optimum value range (190-280 nm) of the interlamellar spacing had been determined for the interlamellar spacing in hot-rolled microstructure.展开更多
A new Ti-V-Mo complex microalloyed hot-rolled high-strength steel sheet was developed by controlling a thermo-mechanical controlled processing (TMCP) schedule, in particular with variants in coiling temperature. The...A new Ti-V-Mo complex microalloyed hot-rolled high-strength steel sheet was developed by controlling a thermo-mechanical controlled processing (TMCP) schedule, in particular with variants in coiling temperature. The effects of coiling temperature (CT) on various hardening mechanisms and mechanical properties of Ti-V-Mo complex mi- croalloyed high-strength low-alloy steels were investigated. The results revealed that the steels are mainly strengthened by a combined effect of ferrite grain refinement hardening and precipitation hardening. The variation in simulated coiling temperature causes a significant difference in strength, which is mainly attributed to different precipitation hardening increment contributions. When the CT is 600 ℃, the experimental steel has the best mechanical properties: ultimate tensile strength (UTS) 1000 MPa, yield strength (YS) 955 MPa and elongation (EL) 17%. Moreover, about 82 wt% of the total precipitates are nano-sized carbide particles with diameter of 1-10 nm, which is randomly dispersed in the ferrite matrix. The nano-sized carbide particles led to a strong precipitation hardening increment up to 310 MPa.展开更多
The controlled cooling technology following hot rolling process is a vital factor that affects the final micro- structure and mechanical properties of the hot-rolled transformation induced plasticity (TRIP) steels. ...The controlled cooling technology following hot rolling process is a vital factor that affects the final micro- structure and mechanical properties of the hot-rolled transformation induced plasticity (TRIP) steels. In the present study, low alloy C-Si-Mn TRIP steel was successfully fabricated by hot rolling process with a 4450 hot roiling mill. To maximize the volume fraction and stability of retained austenite of the steel, two different cooling methods (aircooling and ultra-fast cooling "AC-UFC" and ultrmfast cooling, air cooling and ultra-fast cooling "UFC-AC-UFC") were conducted. The effects of the cooling method on the microstructure of hot-rolled TRIP steel were investigated via optical microscope, transmission electron microscope and conversion electron Mossbauer spectroscope. The mechanical properties of the steel were also evaluated by conventional tensile test. The results indicated that ferrite and bainite in the microstructure were refined with the cooling method of UFC-AC-UFC. The morphology of retained austenite was also changed from small islands distributing in bainite district (obtained with AC-UFC) to granular shape locating at the triple junction of the ferrite grain boundaries (obtained with UFC-AC-UFC). As a result, the TRIP steel with a content of retained austenite of 11. 52%, total elongation of 32% and product of tensile strength and total elongation of 27 552 MPa·% was obtained.展开更多
Mechanical properties and microstructural evolution of the hot-rolled Fe-Mn-C-Si TWIP steel were investigated and the deformation mechanism was analyzed.The results showed that the tensile strength and elongation were...Mechanical properties and microstructural evolution of the hot-rolled Fe-Mn-C-Si TWIP steel were investigated and the deformation mechanism was analyzed.The results showed that the tensile strength and elongation were about 1050 MPa and 60%,respectively.The hot-rolled steel had high specific energy absorption and impact toughness between-120 ℃ and 20 ℃.Some inhomogeneous dislocation zones were observed in the undeformed steel.Lots of deformation twins and twin-dislocation interactions were observed in the deformed steel.TWIP effect was the major deformation mechanism for the excellent mechanical properties.展开更多
文摘The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing with HRB335 steel bars, i.e. coordination of strength and ductility, strain-aging sensibility, low temperature impact toughness, weld ability and high strain low cycle fatigue. The ductile-brittle transit temperatures of hot-rolled and strain-aged steel bars were evaluated as –17 °C and ?8 °C respectively, and the low temperature impact toughness of HRB400 steel bars remains to be improved. Transmission electron microscopy (TEM) and electron diffraction showed little vanadium existed in ferrite as VN, most of which existed in pearlite as alloy cementite which resulted in the declination of impact toughness. Methods were suggested to improve the anti- seismic properties of steel bars.
文摘Taking the seamless tube plant of Baoshan Iron & Steel Complex in China as the background,we analyze the characters of hot rolling seamless steel tube:multi varieties,low volume,complicated production process,flexible production routes.Then integrated scheduling problem for hot rolling seamless steel tube production is studied,which covers two key points;order-grouping problem and solution method for flowshop/jobshop scheduling problem.On the basis of these two problems,integrated scheduling decision system is developed.The design idea,function flow sheet,data processing method,and functional module of visualized human-computer interactive scheduling system implemented in seamless steel tube plant of Shanghai Baoshan Iron & Steel Complex are described into detail.Compared with manual system,the performance of system shows the applicability and superiority in several criteria.
文摘The types and growth of various oxide scales formed during the different phases of the production of hotrolled strip steel products are reviewed. Similarities and differences between the "tertiary scale" on the surface of carbon steels at high temperatures and the oxide scale on pure iron are compared. The micro-structural features of the "final oxide scale" on the surface of strip steels at room temperature as well as the relationship between these features and the position of the steel coil (plate) and the subsequent processes of recoiling, temper rolling and trimming, etc. are summarized. The actual oxide scales retained on the commercial hot-rolled strip steels at room temperature have been proposed to define as " quartus scale" for the first time. The micro-structural development and phase transformation of the initial "tertiary scale" during and after cooling and coiling are described. The reasons for the "tertiary scale" on carbon steels differing from the oxide scale formed on pure iron, and the major influencing factors in the formation of various types of "quartus scales" are analyzed from both thermodynamic and dynamic viewpoints. The development mechanism of " quartus scales" is discussed and the potential effects of the " quartus scale" state (thickness, constitution, structure and defects), on the rusting and pickling properties of commercial hot-rolled strip steel, as well as on the mechanical properties of oxide scales are analyzed.
文摘Nb-Tihot-rolled TRIP-assisted steel with high plasticity and appropriate volume percentage of retained austenite based on fine ferrite grain have been developed in the experiment. The test results showed that niobium tend to exist in solution state in matrix with less precipitation, and niobium-titanium could be precipitated in form of (Nb, Ti)C or (Nb, Ti) (C, N), which play an important role in increasing yield strength (from 495 MPa to 610 MPa). Besides, the retained austenite had a positive effect on improving the plasticity by transformation into martensite during tensile deformation.
基金The auLhors thank for the financial aid from Scienceamend of Shandong Province (No. Q98F05146)
文摘In order to simplify production process and to decrease production cost of thicker cold-rolled iF steel sheets for deep drawing applications, a new hot-rolled IF steel sheet is developed through hot-rolling in or region. In this paper, properties, microstructures and precipitate morphology of hot-rolled iF steel sheets are described..
文摘As one of the important categories of hot-rolled products, hot-rolled steel plates for automobile applications generally undergo uniform corrosion or localized corrosion according to different environments of manufacturing, transportation and/or storage of the plates. General corrosion often takes place on the surface of a plate in the exterior part of a package, and only reduces the thickness of the plate and slightly increases the roughness of the surface; however, localized corrosion on the surface of a plate inside the package is likely to result in the formation of pit-like defects on the substrate of the plate, which cannot be removed thoroughly by normal acid pickling or sand blasting, and affects the application of the plate. This research report analyzes the phenomena and characteristics of the rusting behavior of hot- rolled steel plates for automobile applications, and the influencing factors are summaried. The corresponding preventative measures are proposed.
文摘The microstructure characteristics with super fine ferrite grain size less than 5mm, appropriate retained austenite fraction around 5.0% and or removable abundant dislocations have been obtained by controlled rolling and cooling, which leads to well balance com- prehensive properties with high tensile strength of 510 and 615MPa, high elongation of 40% and 27%, low ratio of yield strength to tensile strength 0.83 and 0.80, as well as low ductile- brittle transition temperature less than -80 and -70℃ for advanced aluminum hot-rolled TRIP steel and silicon hot-rolled TRIP steel, respectively.
文摘Influence of thermo-mechanical controlled processing(TMCP),including two-stage rolling with laminar cooling,air cooling and ultra-fast cooling,on the microstructure and mechanical properties of three kinds of Nb-microalloeyed steels was investigated by hot-rolling experiment.Effect of chemistry compositions and microstructure on mechanical properties and the relationship between the multiphase microstructure' s formation with TMCP were analyzed.The results showed that the mixed microstructure containing ferrite,bainite,martensite and a small amount of retained austenite can be obtained by thermo-mechanical controlled processing.Size, quantity and distribution of the constituents(ferrite grain,bainite packet and M-A islands) significantly affect the mechanical properties of three kinds of Nb-microalloyed steels.Under the condition of similar TMCP parameters, there is a gradually decreasing tendency in tensile strength from high silicon Nb steel,high silicon Nb-Ti steel to low silicon Nb-Ti steel,and an opposite tendency in total elongation and product of tensile strength and ductility. Total elongation and product of tensile strength and ductility reach the maximum values(41%and 25256 MPa% respectively) for low silicon Nb-Ti steel.
文摘The patenting process of three hot-rolled steels with carbon mass contents of 0.70%-0. 90% was studied. The effect of the quenching temperature on the cementite lamellar distance in the steel was evaluated on the basis of microstructural characterization and mechanical property tests. The patenting treatment of high-carbon hot- rolled strip and its application in springs were discussed.
文摘The critical transformation temperatures,A_(c1) and A_(c3),of a hot-rolled low-carbon titanium microalloyed steel were determined as a part of an examination of its phase-transformation behavior. Austenite decomposition during the continuous cooling of the titanium microalloyed steel was studied by heating it to 1 250 ℃,cooling it to 880 ℃,holding for 2 s,and then cooling it to room temperature at different cooling rates. The transformation kinetics( CCT curve) was characterized as well.
文摘In this study, the welding technology of the hot-rolled extra-high-strength steel, BS960QC, has been comprehensively investigated. Analysis has been made on the weldability ,the different welding procedures ,the mechanical properties, and the fatigue properties, and a set of recommendation guidelines have been proposed for evaluating the welded joints of the extra-high-strength steel. The research and results indicate that the hot-rolled extra-high-strength steel, BS960QC,has good weldability and an excellent adaptability to welding procedures. Further,the excellent mechanical properties and fatigue properties of the welded joints ,which can be achieved by using optimized welding procedures, can completely meet the technical requirements of the construction machinery industry.
基金supported by the Key Research Foundation of Baoshan Iron & Steel Co.,Ltd.(No.D06EBEA207)
文摘Results presented in this study contribute to investigation of the microstructure and mechanical properties of the hot-rolled Fe16Mn0.6C steel plates.The steel plates have been produced by being hot-rolled at temperatures ranging from 1100℃ to 850℃ in seven passes to 97.5% reduction in thickness and then cooled in a furnace of 650℃.Some plates have been annealed at temperatures ranging from 300℃ to 1100℃ for 5min to 60min,and then followed by water quenching.There are annealing twins in the hot-rolled Fe16Mn0.6C steel.Fe16Mn0.6C steel presents similar ductile behavior as X-IPTM steel,but much higher elongation than commercial martensitic steel (MP) 1000,dual phase (DP) 980,and transformation induced plasticity (TRIP) 980 steels.Fe16Mn0.6C steel experiences γε (-α) transformation in some local regions,but remains mostly austenite during the entire deformation process.Fe16Mn0.6C steel with special mechanical properties can be produced by using the appropriate anneal technology.Twinning induced plasticity(TWIP) effect only occurs in the Fe16Mn0.6C steel annealed at temperature higher than 900℃.
基金financially supported by the National Natural Science Foundation of China (Nos. U1806220 and U1660114)
文摘In this work, the microstructure and the strain partitioning of lean duplex stainless steel 2101 (LDX 2101) during different hot-rolling processes are investigated by optical microscopy and electron-backscattered diffraction (EBSD). The results show that the LDX 2101 exhibits poor thermoplasticity at high temperature. The four-pass hot-rolled plates show fewer edge-cracking defects and superior thermoplasticity compared with the two-pass hot-rolled plates prepared at different temperature. The phase boundary is the weakest site in the LDX 2101. The cracks are initiated and propagated along the phase boundaries during the hot-rolling process. According to the EBSD analysis, the increase of the hot-rolling pass can dramatically improve the strain distribution in ferrite and austenite phases and promote the strain transmission in the constituent phases, thereby improving the coordinated deformation ability of the two phases. This effect further in- creases the thermoplasticity and reduces the formation of edge cracks in LDX 2101.
文摘The non-vacuum roll bonding method of nickel plating on the base materials is put forward in accordance with the primary problems existed in the roll bonding of stainless/carbon steel. After nickel plating test on the base materials, the microstructure of nickel cladding is observed by scanning electron microscopy (SEM) at high, and room temperature, and the results show that the nickel cladding on base material can be protected from oxidation in the high temperature. Non-vacuum roll bonding tests of nickel plating on base materials are done by the roll bonding equipment, and the roll bonding plates of stainless/carbon steel are obtained. The microstructure and the elements distribution of non-vacuum roll bonding interface are analyzed by optical microscope (OM) and SEM. The results reflect that the nickel plating layer and the base materials bond well.
文摘In this study, the matrix structure, state and composition of the mill scales of four typical domestically made 510L hot-rolled strips were observed and analyzed by means of optical microscopy (OM) ,scanning electron microscopy (SEM) and X-ray diffraction (XRD). The corrosion behavior of the steels with and without mill scales were investigated by means of hot-humid corrosion tests under the condition of relative humidity ( RH ) of 95% at 50℃ and 70℃, respectively. The results show that the matrix structures, state, composition and thickness of mill scales vary in the strips. The rusting starting time of the specimens with scales is generally a bit longer than that of the specimens without scales, but their corrosion mass-gain is higher. For these two kinds of specimens ,their corrosion rate increases significantly with the increase of temperature. The rusting behavior of the 510L strips produced by various plants is different due to the variations of hot-rolling processes and designed chemical compositions. Various relevant aspects should be taken into account in the evaluation of the corrosion behavior of hot-rolled strips.
基金funded by National Natural Science Foundation of China(51261009)
文摘To investigate the tensile deformation behavior of high strength anti-seismic steel with multi-phase microstructure,tensile tests with strains of 0.05,0.12 and 0.22 were performed at room temperature.Microstructure of tested steels was observed by means of optical microscopy(OM),transmission electron microscopy(TEM)and scanning electron microscopy(SEM).Tensile mechanical properties of tested steels were obtained,and the influence of bainite content on deformation behavior was also discussed.Meanwhile,the deformation mechanism of steel with three kinds of microstructures of bainite,pearlite and ferrite was analyzed.Results show that tested steel with high volume fraction of bainite exhibits a continuous deformation behavior,and this may be attributed to a higher bainite volume fraction and a lower mobile dislocation density.The morphology of microstructure will influence the mechanical properties of tested steels.An increasing content of bainite can improve the tensile strength,but reduce the plasticity and toughness of the tested steels.In the deformation process of 0.039 Nb steel,the ferrite and bainite have priorities to deform,and the deformation exhibits co-deformation of all microstructures in the later stage of deformation.In the deformation process of 0.024Nb-0.032 Vsteel,the ferrite and pearlite have priorities to deform,and the deformation exhibits co-deformation of all microstructures in the later stage of deformation.
文摘Heredity in the microstructure and mechanical properties of hot-rolled spring steel wire 60Si2MnA during heat treatment process was investigated comprehensively. The steel was isothermally transformed to obtain various hot-rolled microstructure (pearlite fineness within the range of 140-510 nm) and mechanical properties, and followed by some quenching-tempering treatment. Afterwards, microstructure was characterized by optical microscopy, scanning electron microscopy and quantitative metallography, and mechanical properties were determined by tensile test. The results indicated that the hot-rolled microstructure with a coarsen pearlite structure had been changed after reheating, to a austenite microstructure with bigger and more uneven grain size, and finally to a coarsen tempered microstructure. And the average austenite grain size and standard deviation of its distribution in quenched microstructure were observed to depend linearly on the interlamellar spacing in hot-rolled microstructure. Besides, to obtain a good combination of the final strength and plasticity, an optimum value range (190-280 nm) of the interlamellar spacing had been determined for the interlamellar spacing in hot-rolled microstructure.
基金financially supported by the National Basic Research Program of China(No.2010CB630805)the National Natural Science Foundation of China(No.51201036)China Iron&Steel Research Institute Group(No.12060840A)
文摘A new Ti-V-Mo complex microalloyed hot-rolled high-strength steel sheet was developed by controlling a thermo-mechanical controlled processing (TMCP) schedule, in particular with variants in coiling temperature. The effects of coiling temperature (CT) on various hardening mechanisms and mechanical properties of Ti-V-Mo complex mi- croalloyed high-strength low-alloy steels were investigated. The results revealed that the steels are mainly strengthened by a combined effect of ferrite grain refinement hardening and precipitation hardening. The variation in simulated coiling temperature causes a significant difference in strength, which is mainly attributed to different precipitation hardening increment contributions. When the CT is 600 ℃, the experimental steel has the best mechanical properties: ultimate tensile strength (UTS) 1000 MPa, yield strength (YS) 955 MPa and elongation (EL) 17%. Moreover, about 82 wt% of the total precipitates are nano-sized carbide particles with diameter of 1-10 nm, which is randomly dispersed in the ferrite matrix. The nano-sized carbide particles led to a strong precipitation hardening increment up to 310 MPa.
基金Key Projects in National Science and Technology Pillar Program During the Eleventh Five-Year Plan Period of China(2006BAE03A08)
文摘The controlled cooling technology following hot rolling process is a vital factor that affects the final micro- structure and mechanical properties of the hot-rolled transformation induced plasticity (TRIP) steels. In the present study, low alloy C-Si-Mn TRIP steel was successfully fabricated by hot rolling process with a 4450 hot roiling mill. To maximize the volume fraction and stability of retained austenite of the steel, two different cooling methods (aircooling and ultra-fast cooling "AC-UFC" and ultrmfast cooling, air cooling and ultra-fast cooling "UFC-AC-UFC") were conducted. The effects of the cooling method on the microstructure of hot-rolled TRIP steel were investigated via optical microscope, transmission electron microscope and conversion electron Mossbauer spectroscope. The mechanical properties of the steel were also evaluated by conventional tensile test. The results indicated that ferrite and bainite in the microstructure were refined with the cooling method of UFC-AC-UFC. The morphology of retained austenite was also changed from small islands distributing in bainite district (obtained with AC-UFC) to granular shape locating at the triple junction of the ferrite grain boundaries (obtained with UFC-AC-UFC). As a result, the TRIP steel with a content of retained austenite of 11. 52%, total elongation of 32% and product of tensile strength and total elongation of 27 552 MPa·% was obtained.
文摘Mechanical properties and microstructural evolution of the hot-rolled Fe-Mn-C-Si TWIP steel were investigated and the deformation mechanism was analyzed.The results showed that the tensile strength and elongation were about 1050 MPa and 60%,respectively.The hot-rolled steel had high specific energy absorption and impact toughness between-120 ℃ and 20 ℃.Some inhomogeneous dislocation zones were observed in the undeformed steel.Lots of deformation twins and twin-dislocation interactions were observed in the deformed steel.TWIP effect was the major deformation mechanism for the excellent mechanical properties.