Corrosion performance and tribological behavior of diamond-like carbon based coating applied on Ni−Al−bronze alloy

The effect of diamond-like carbon(DLC)coating(fabricated by cathodic arc deposition)on mechanical properties,tribological behavior and corrosion performance of the Ni−Al−bronze(NAB)alloy was investigated.Nano-hardness and pin-on-plate test showed that DLC coating had a greater hardness compared with NAB alloy.Besides,the decrease in friction coefficient from 0.2 for NAB substrate to 0.13 for the DLC-coated sample was observed.Potentiodynamic polarization and EIS results showed that the corrosion current density decreased from 2.5μA/cm2 for bare NAB alloy to 0.14μA/cm2 for DLC-coated sample in 3.5 wt.%NaCl solution.Moreover,the charge transfer resistance at the substrate−electrolyte interface increased from 3.3 kΩ·cm2 for NAB alloy to 120.8 kΩ·cm2 for DLC-coated alloy,which indicated an increase in corrosion resistance due to the DLC coating.

Effect of N-ion implantation and diamond-like carbon coating on fretting wear behaviors of Ti6Al7Nb in artificial saliva

The tribology behaviors of Ti6Al7Nb,its alloy with N-ion implantation,and its alloy with diamond-like carbon(DLC)coating were investigated in artificial saliva.Fretting wear tests of untreated,N-ion implanted and DLC coated Ti6Al7Nb alloys plate against a Si3N4ball were carried out on a reciprocating sliding fretting wear test rig.Based on the analysis of X-ray diffraction,Raman spectroscopy,3-D profiler,SEM morphologies and frictional kinetics behavior analysis,the damage behavior of surface modification layer was discussed in detail.The results indicated that the fretting wear behavior of Ti6Al7Nb alloy with N-ion implantation was increased with the dose increase of the implanted nitrogen ions.Moreover,the DLC-coated Ti6Al7Nb alloy with low ion implantation could improve the fretting wear behavior greatly.In addition,the Ti6Al7Nb with DLC coating had better ncorrosion resistance due to the special compact structure.All results suggested that the Ti6Al7Nb with DLC coating had better wear resistance than that with N-ion implantation in artificial saliva.

Structure and Performance of TiC-containing Diamond-like Carbon Nanocomposite Coatings Deposited by Rectangular Cathodic Arc Ion-plating

TiC-containing diamond-like carbon （TiC-DLC） nanocomposite coatings were deposited by a rectangular cathodic arc ion-plating system using C2H2 as reacting gas. Raman spectroscopy and transmission electron microscopy analysis show that with increasing flow rate of C2H2, the structure of nanocomposite coatings changes from TiC nanograin-containing to graphite nanograin-containing DLC. The harness measurements show that the hardness decreases from 28 GPa to 18 GPa with increasing C2H2 flow rate. The scratch test show that a high critical load （〉40 N） was obtained and exhibited a good adhesion between the coating and the substrate. Wear experiment shows that the friction coefficient of TiC-DLC nanocomposite coatings decreases with increasing C2H2. A low friction coefficient of 0.07 was obtained at 480 sccm C2H2.

Development of Diamond-like Carbon Fibre Wheel

A unique diamond-like carbon (DLC) grinding wheel was developed, in which the DLC fibres were made by rolling Al sheets coated with DLC films and aligned no rmally to the grinding wheel surface by laminating Al sheets together with DLC fibres. In this paper, the formation process of DLC fibres and the fabrication process of a DLC fibre wheel were investigated. Many grinding experiments were also carried out on a precision NC plane milling machine using a newly developed DLC wheel. Grinding of specimens of silicon wafers, optical glasses, quartz, granites and hardened die steel SKD11 demonstrated the capabilities of nanometer surface finish. A smooth surface with a roughness value of Ra2.5 nm (Ry26 nm) was achieved.

Synergistic tribological effect between polyisobutylene succinimide-modified molybdenum oxide nanoparticle and zinc dialkyldithiophosphate for reducing friction and wear of diamond-like carbon coating under boundary lubrication

Organic molybdenum lubricant additive like molybdenum dialkyl dithiocarbamate(MoDTC)can cause wear acceleration of diamond-like carbon(DLC)coating coupled with steel under boundary lubrication,which hinders its industrial application.Therefore,polyisobutylene succinimide(PIBS),an organo molybdenum amide,was adopted to modify molybdenum oxide affording molybdenum polyisobutylene succinimidemolybdenum oxide nanoparticles(MPIBS-MONPs)with potential to prevent the wear acceleration of DLC coating.The thermal stability of MPIBS-MONPs was evaluated by thermogravimetric analysis.Their tribological properties as the additives in di-isooctyl sebacate(DIOS)were evaluated with MoDTC as a control;and their tribomechanism was investigated in relation to their tribochemical reactions and synergistic tribological effect with zinc dialkyldithiophosphate(ZDDP)as well as worn surface characterizations.Findings indicate that MPIBS-MONPs/ZDDP added in DIOS can significantly reduce the friction and wear of DLC coating,being much superior to MoDTC.This is because MPIBS-MONPs and ZDDP jointly take part in tribochemical reactions to form a composite tribofilm that can increase the wear resistance of DLC coating.Namely,the molybdenum amide on MPIBS-MONPs surface can react with ZDDP to form MoS2 film with excellent friction-reducing ability;and MPIBS-MONPs can release molybdenum oxide nanoparticle to form deposited lubrication layer on worn surfaces.The as-formed composite tribofilm consisting of molybdenum oxide nanocrystal,amorphous polyphosphate,and molybdenum disulfide as well as a small amount of Mo2C accounts for the increase in the wear resistance of DLC coating under boundary lubrication.

Tribological performance of hydrogenated diamond-like carbon coating deposited on superelastic 60NiTi alloy for aviation selflubricating spherical plain bearings

It is imperative to develop a novel matching of metallic substrate and self-lubricating coating for aircraft spherical plain bearing in a wide range of service conditions.As a new type of superelastic material,60NiTi alloy meets the performance requirements of aerospace bearing materials,but exhibits poor tribological performance,especially under the conditions of dry sliding friction.A Hydrogenated Diamond-Like Carbon(H-DLC)coating was deposited on the 60NiTi alloy to improve its tribological performance.The microstructure and mechanical behavior of the 60NiTi alloy and its H-DLC coating were explored.Results show that improvement of friction and wear performance of the H-DLC coating deposited on the 60NiTi substrate is mainly achieved by graphitization at the friction interface and the transfer film produced on the counterpart ball.The increased friction load leads to intensification of graphitization at the friction interface and formation of continuous and compact transfer film on the surface of the counterpart ball.

Experimental study on the feasibility of alternative materials for tilting pad thrust bearings operating in transition to mixed friction

In hydrodynamic bearings traditional bearing alloys:Babbitts and bronzes are most frequently utilized.Polymer sliding layers are sometimes applied as a valuable alternative.Hard diamond-like carbon(DLC)coatings,which are also considered for certain applications may show some advantages,as well.Although material selection is of secondary importance in a full film lubrication regime it becomes important in mixed friction conditions,which is crucial for bearings with frequent starts and stops.Experimental research aimed at studying the performance of fluid film bearings in the specific operating regime,including the transition to mixed friction,is described in the paper.The tests were carried out on four tilting pad bearings of different material compositions:Steel/bronze,DLC/steel,steel/polyether ether ketone(PEEK),and steel/Babbitt.The tests comprised stopping under load and reproduction of the Stribeck curve by decreasing rotational speed to very low values,and observing the changes of friction force during the transition to mixed friction regime.Analysis of the transition conditions and other results showed clear differences between the tested bearings,illustrating the feasibility of less popular material compositions for bearings operating in specific conditions.More specifically,the DLC/steel bearing was demonstrating superior performance,i.e.lower friction,transition to mixed friction occurring at higher load,and more stable performance at start-stop regime over the other tested bearings.