In this article, the synthesis and characterization of a novel fluoromonomer and its copolymer with acrylamide is reported. 2-perfluoroamyl-4-hydroxylquinoline 2 was synthesized from ethyl 2, 2-dihydroperfluoroheptano...In this article, the synthesis and characterization of a novel fluoromonomer and its copolymer with acrylamide is reported. 2-perfluoroamyl-4-hydroxylquinoline 2 was synthesized from ethyl 2, 2-dihydroperfluoroheptanoate in high yields. The monomer 4 was then synthesized from 2 in two steps readily in high yields. Synthesis and characterization of copolymers of acrylamide (AM) and the fluoromonomer were investigated. The composition and intrinsic viscosity of these copolymers were studied. It was found that the rheological properties of aqueous solutions of polyacrylamide were modified significantly when a small proportion of the fluoromonomer 4 was incorporated on investigating the viscosity-concentration profiles, pseudoplasticity of these solutions and the effect of the presence of surfactant. These results could be explained by the hydrophobic association of the fluorocarbon segments in the aqueous solutions of these copolymers.展开更多
Water-based drilling fluids can cause hydration of the wellbore rocks,thereby leading to instability.This study aimed to synthesize a hydrophobic small-molecule polymer(HLMP)as an inhibitor to suppress mud shale hydra...Water-based drilling fluids can cause hydration of the wellbore rocks,thereby leading to instability.This study aimed to synthesize a hydrophobic small-molecule polymer(HLMP)as an inhibitor to suppress mud shale hydration.An infrared spectral method and a thermogravimetric technique were used to characterize the chemical composition of the HLMP and evaluate its heat stability.Experiments were conducted to measure the linear swelling,rolling recovery rate,and bentonite inhibition rate and evaluate accordingly the inhibition performance of the HLMP.Moreover,the HLMP was characterized through measurements of the zeta potential,particle size distribution,contact angles,and interlayer space testing.As confirmed by the results,the HLMP could successfully be synthesized with a favorable heat stability.Furthermore,favorable results were found for the inhibitory processes of the HLMP on swelling and dispersed hydration during mud shale hydration.The positively charged HLMP could be electrically neutralized with clay particles,thereby inhibiting diffusion in the double electron clay layers.The hydrophobic group in the HLMP molecular structure resulted in the formation of a hydrophobic membrane on the rock surface,enhancing the hydrophobicity of the rock.In addition,the small molecules of the HLMP could plug the spaces between the layers of bentonite crystals,thereby reducing the entry of water molecules and inhibiting shale hydration.展开更多
A temperature-resistant, salt-tolerant polyacrylamide, hydrophobically associating polymer (HAP), was synthesized in the State Key Laboratory of Heavy Oil Processing. The rheological behavior of HAP solution was inv...A temperature-resistant, salt-tolerant polyacrylamide, hydrophobically associating polymer (HAP), was synthesized in the State Key Laboratory of Heavy Oil Processing. The rheological behavior of HAP solution was investigated by means of flow experiments in porous media and by using a HAAKE RS600 rheometer. The results of Nuclepore membrane filtration showed that filtration time increased sharply when the critical association concentration was reached. Shear rate had a greater impact on viscosity and shear stress with increasing HAP concentration. The HAP solution with a concentration of 100 mg/L (salinity 32,868 mg/L) exhibited negative thixotropy. However, at the same salinity the HAP solution showed thixotropy and its viscosity became greater when the polymer concentration increased to 1,500 mg/L. The flow experiments in cemented core samples indicated that the resistance factor and residual resistance factor of the HAP solution were 31.8 and 12 when polymer concentration and salinity were 1,500 mg/L, 32,868 mg/L at 85℃ respectively, which is favorable for flooding application. Such factors of partially hydrolyzed polyaerylamide 3530S were merely 3.14 and 1.71, so it could not be applied to polymer flooding in the oilfield with high temperature and high salinity.展开更多
Herein we report on the deposition of transparent hydrophobic thin coatings by radio frequency plasma polymerization(PP) of perfluorooctyl ethylene(PFOE) in both pulsed and continuous wave(CW) modes.The chemical...Herein we report on the deposition of transparent hydrophobic thin coatings by radio frequency plasma polymerization(PP) of perfluorooctyl ethylene(PFOE) in both pulsed and continuous wave(CW) modes.The chemical compositions of the resulting PP-PFOE coatings were confirmed by means of Fourier transform infrared spectroscopy(FT-IR) and X-ray photoelectron spectroscopy(XPS).The thicknesses and surface morphologies of the coatings were examined using surface plasmon resonance spectroscopy and atomic force microscopy.The surface wetting properties and optical transmittance were measured using a water contact angle goniometer and UV-vis spectroscopy.The FT-IR and XPS data showed that the PP-PFOE coatings deposited in the pulsed mode had a higher retention of CF_2 groups compared to those from the CW mode.While the water contact angle of the freshly deposited PP-PFOE from the pulsed mode showed a decrease from 120 degrees to 111 degrees in the first two days,it then remained almost unchanged up to 45 days.The UV-vis data indicated that a PP-PFOE coating 30.6 nm thick had a light transmittance above 90%in the UV and visible ranges.The deposition rates under various plasma conditions are also discussed.展开更多
Hydrophobically associating water-soluble polymers (HPAP) have been synthesized from acrylamide(AM), acrylate (AA), 2-acrylamido-2-methyl propane sulfonic acid (AMPS) and hydrophobic monomer (AP) in aqueous solution...Hydrophobically associating water-soluble polymers (HPAP) have been synthesized from acrylamide(AM), acrylate (AA), 2-acrylamido-2-methyl propane sulfonic acid (AMPS) and hydrophobic monomer (AP) in aqueous solution by radical polymerization. New polymer drilling fluids are made up of HPAP, which is used as viscosifiers and encapsulation agents. Properties of this system are reported in this paper. Results indicate that this system has a high value of yield point to plastic viscosity (YP/PV≥0.7), high viscosity at a low-shear rate (LSRV≥30000mPa·s), excellent shear thinning behavior, good solid-carrying behavior, resistance to shear, good thermal stability (as high as 140℃) and salt resistance. The system has excellent behavior in high-density solution of NaCl and in calcium and magnesium rich saline solutions. Hence, HPAP also can be used in saltwater polymer drilling fluids.展开更多
To determine the template effect of hydrophobically associating copolymers(HACPs) on the morphology of nano/micro structures, six HACPs were synthesized and used as templates to biomimetically synthesize cuprous ox...To determine the template effect of hydrophobically associating copolymers(HACPs) on the morphology of nano/micro structures, six HACPs were synthesized and used as templates to biomimetically synthesize cuprous oxide(Cu2O), an important semiconductor. This experiment showed a clear relationship between the associating state of the HACP molecules and the morphology of the Cu2O particles. Cu2O hollow spheres were preferentially prepared when the HACP molecules were in an intramolecular associating state. Furthermore, a Cu2O hexapod was easily obtained when the HACP molecules were in an intermolecular associating state. The morphologies of the Cu2O crystals prepared in the presence of the HACPs also confirmed this result.展开更多
A hydrophilic/hydrophobic interpenetrating polymer network (IPN) of poly (vinyl alcohol) / polystyrene was prepared by conversion of the IPN of poly (vinyl acetate)/polystyrene. The hydrophilic/hydrophobic IPN w...A hydrophilic/hydrophobic interpenetrating polymer network (IPN) of poly (vinyl alcohol) / polystyrene was prepared by conversion of the IPN of poly (vinyl acetate)/polystyrene. The hydrophilic/hydrophobic IPN was characterized by FT-IR and DSC, and the swelling ratios of the IPN in different solvents were measured.展开更多
A fluorocarbon-modified ply( N-isopropylacrylamide) has been synthesized by copolymerization of N-isopropyl acrylamide with a small amount of acrylate or methacrylate containing a perfluoroalkyl group. It was found th...A fluorocarbon-modified ply( N-isopropylacrylamide) has been synthesized by copolymerization of N-isopropyl acrylamide with a small amount of acrylate or methacrylate containing a perfluoroalkyl group. It was found that the hydrophilicity of macromolecular backbone is an important factor to the solution properties of the copolymers and that hydrophobic association between fluorocarbon group is stronger than that between the corresponding hydrocarbon analogies. The viscosity of some of the copolymer solutions was very sensitive to temperature. It was dilatant at higher fluorocarbon comonomer content ( 0. 20–1.0 mol%) and was Newtonian at very low fluorocarbon comonomer content (0.03–0.2 mol%). Evidence for hydrophobic association of the fluorocarbon groups was obtained from the effects of adding NaCl and surfactants on the solution viscosity. The LC-ST properties of these copolymers were studied by DSC method and this was also found to be consistent with hydrophobic association between the fluorocarbons.展开更多
基金Project supported by National Natural Science Foundation,Grant approval numbers 29472074 and 29632003
文摘In this article, the synthesis and characterization of a novel fluoromonomer and its copolymer with acrylamide is reported. 2-perfluoroamyl-4-hydroxylquinoline 2 was synthesized from ethyl 2, 2-dihydroperfluoroheptanoate in high yields. The monomer 4 was then synthesized from 2 in two steps readily in high yields. Synthesis and characterization of copolymers of acrylamide (AM) and the fluoromonomer were investigated. The composition and intrinsic viscosity of these copolymers were studied. It was found that the rheological properties of aqueous solutions of polyacrylamide were modified significantly when a small proportion of the fluoromonomer 4 was incorporated on investigating the viscosity-concentration profiles, pseudoplasticity of these solutions and the effect of the presence of surfactant. These results could be explained by the hydrophobic association of the fluorocarbon segments in the aqueous solutions of these copolymers.
基金The work is supported by the Integration and Testing of Safe and Fast Drilling and Completion Technologies for Complex Ultra-Deep Wells(2020F-46)Major Technology Field Test of Joint-Stock Company(Drilling and Production Engineering).Xuyang received the grant.
文摘Water-based drilling fluids can cause hydration of the wellbore rocks,thereby leading to instability.This study aimed to synthesize a hydrophobic small-molecule polymer(HLMP)as an inhibitor to suppress mud shale hydration.An infrared spectral method and a thermogravimetric technique were used to characterize the chemical composition of the HLMP and evaluate its heat stability.Experiments were conducted to measure the linear swelling,rolling recovery rate,and bentonite inhibition rate and evaluate accordingly the inhibition performance of the HLMP.Moreover,the HLMP was characterized through measurements of the zeta potential,particle size distribution,contact angles,and interlayer space testing.As confirmed by the results,the HLMP could successfully be synthesized with a favorable heat stability.Furthermore,favorable results were found for the inhibitory processes of the HLMP on swelling and dispersed hydration during mud shale hydration.The positively charged HLMP could be electrically neutralized with clay particles,thereby inhibiting diffusion in the double electron clay layers.The hydrophobic group in the HLMP molecular structure resulted in the formation of a hydrophobic membrane on the rock surface,enhancing the hydrophobicity of the rock.In addition,the small molecules of the HLMP could plug the spaces between the layers of bentonite crystals,thereby reducing the entry of water molecules and inhibiting shale hydration.
文摘A temperature-resistant, salt-tolerant polyacrylamide, hydrophobically associating polymer (HAP), was synthesized in the State Key Laboratory of Heavy Oil Processing. The rheological behavior of HAP solution was investigated by means of flow experiments in porous media and by using a HAAKE RS600 rheometer. The results of Nuclepore membrane filtration showed that filtration time increased sharply when the critical association concentration was reached. Shear rate had a greater impact on viscosity and shear stress with increasing HAP concentration. The HAP solution with a concentration of 100 mg/L (salinity 32,868 mg/L) exhibited negative thixotropy. However, at the same salinity the HAP solution showed thixotropy and its viscosity became greater when the polymer concentration increased to 1,500 mg/L. The flow experiments in cemented core samples indicated that the resistance factor and residual resistance factor of the HAP solution were 31.8 and 12 when polymer concentration and salinity were 1,500 mg/L, 32,868 mg/L at 85℃ respectively, which is favorable for flooding application. Such factors of partially hydrolyzed polyaerylamide 3530S were merely 3.14 and 1.71, so it could not be applied to polymer flooding in the oilfield with high temperature and high salinity.
基金supported by the Tianjin Research Program of Application Foundation and Advanced Technology,China(No.12JCYBJC31700)the Program for New Century Excellent Talents in University,China(No.NCET-12-1064)
文摘Herein we report on the deposition of transparent hydrophobic thin coatings by radio frequency plasma polymerization(PP) of perfluorooctyl ethylene(PFOE) in both pulsed and continuous wave(CW) modes.The chemical compositions of the resulting PP-PFOE coatings were confirmed by means of Fourier transform infrared spectroscopy(FT-IR) and X-ray photoelectron spectroscopy(XPS).The thicknesses and surface morphologies of the coatings were examined using surface plasmon resonance spectroscopy and atomic force microscopy.The surface wetting properties and optical transmittance were measured using a water contact angle goniometer and UV-vis spectroscopy.The FT-IR and XPS data showed that the PP-PFOE coatings deposited in the pulsed mode had a higher retention of CF_2 groups compared to those from the CW mode.While the water contact angle of the freshly deposited PP-PFOE from the pulsed mode showed a decrease from 120 degrees to 111 degrees in the first two days,it then remained almost unchanged up to 45 days.The UV-vis data indicated that a PP-PFOE coating 30.6 nm thick had a light transmittance above 90%in the UV and visible ranges.The deposition rates under various plasma conditions are also discussed.
文摘Hydrophobically associating water-soluble polymers (HPAP) have been synthesized from acrylamide(AM), acrylate (AA), 2-acrylamido-2-methyl propane sulfonic acid (AMPS) and hydrophobic monomer (AP) in aqueous solution by radical polymerization. New polymer drilling fluids are made up of HPAP, which is used as viscosifiers and encapsulation agents. Properties of this system are reported in this paper. Results indicate that this system has a high value of yield point to plastic viscosity (YP/PV≥0.7), high viscosity at a low-shear rate (LSRV≥30000mPa·s), excellent shear thinning behavior, good solid-carrying behavior, resistance to shear, good thermal stability (as high as 140℃) and salt resistance. The system has excellent behavior in high-density solution of NaCl and in calcium and magnesium rich saline solutions. Hence, HPAP also can be used in saltwater polymer drilling fluids.
基金Supported by the National Natural Science Foundation of China(No. 51102219) and the Fundamental Research Funds for the Central Umversities of China(Nos.201113024, 41404010204).
文摘To determine the template effect of hydrophobically associating copolymers(HACPs) on the morphology of nano/micro structures, six HACPs were synthesized and used as templates to biomimetically synthesize cuprous oxide(Cu2O), an important semiconductor. This experiment showed a clear relationship between the associating state of the HACP molecules and the morphology of the Cu2O particles. Cu2O hollow spheres were preferentially prepared when the HACP molecules were in an intramolecular associating state. Furthermore, a Cu2O hexapod was easily obtained when the HACP molecules were in an intermolecular associating state. The morphologies of the Cu2O crystals prepared in the presence of the HACPs also confirmed this result.
基金supported by the National Natural Science Foundation of China(No.20474015)the Scientific Research Fund of Hunan Provincial Education Department(No.04A029).
文摘A hydrophilic/hydrophobic interpenetrating polymer network (IPN) of poly (vinyl alcohol) / polystyrene was prepared by conversion of the IPN of poly (vinyl acetate)/polystyrene. The hydrophilic/hydrophobic IPN was characterized by FT-IR and DSC, and the swelling ratios of the IPN in different solvents were measured.
基金Project (No. 29274100) supported by the National Natural Science Foundation of China.
文摘A fluorocarbon-modified ply( N-isopropylacrylamide) has been synthesized by copolymerization of N-isopropyl acrylamide with a small amount of acrylate or methacrylate containing a perfluoroalkyl group. It was found that the hydrophilicity of macromolecular backbone is an important factor to the solution properties of the copolymers and that hydrophobic association between fluorocarbon group is stronger than that between the corresponding hydrocarbon analogies. The viscosity of some of the copolymer solutions was very sensitive to temperature. It was dilatant at higher fluorocarbon comonomer content ( 0. 20–1.0 mol%) and was Newtonian at very low fluorocarbon comonomer content (0.03–0.2 mol%). Evidence for hydrophobic association of the fluorocarbon groups was obtained from the effects of adding NaCl and surfactants on the solution viscosity. The LC-ST properties of these copolymers were studied by DSC method and this was also found to be consistent with hydrophobic association between the fluorocarbons.