The corundum(α-alumina) core has been considered as a suitable candidate for investment casting of hollow, high pressure turbine engine airfoils due to its excellent properties. However, the efficiency of removing al...The corundum(α-alumina) core has been considered as a suitable candidate for investment casting of hollow, high pressure turbine engine airfoils due to its excellent properties. However, the efficiency of removing alumina cores in concentrated caustic solution cannot meet the needs of industrial production. In this paper, the effects of temperature and initial solution concentration on dissolution of α-alumina were studied by the classical weight-loss method. The fractal kinetic model was developed in order to describe α-alumina dissolution, assuming that the nonporous particles shrank during reaction process. The results show that the dissolution rate increases with increasing reaction temperature and initial solution concentration. Especially, the initial solution concentration has a significant influence on α-alumina dissolution rate at a higher reaction temperature. The activation energies decrease with increasing initial solution concentration, and the chemical reaction is the rate-controlling step.展开更多
This research investigates the mechanical and thermal properties of Morus alba combined with polylactic acid in comparison with other natural fibers. The study uses three different fiber and PLA compositions - 20%, 30...This research investigates the mechanical and thermal properties of Morus alba combined with polylactic acid in comparison with other natural fibers. The study uses three different fiber and PLA compositions - 20%, 30%, and 40% respectively - to produce composite materials. In addition, another composite with the same fiber volume is treated with a 4% NaOH solution to improve mechanical properties. The composites are processed by twin-screw extrusion, granulation, and injection molding. Tensile strength measurements of raw fibers and NaOH-treated fibers were carried out using a single-fiber tensile test with a gauge length of 40 mm. It was observed that the NaOH surface treatment increases the resistance against tensile loading and exhibited improved properties for raw fiber strands. The diameter of the fibers was measured using optical microscopy. During this research, flexural tests, impact tests, differential scanning calorimetry (DSC), and heat deflection temperature measurements (HDT) were conducted to evaluate the mechanical and thermal properties of the developed composite samples. The results indicate that the mechanical properties of NaOH-treated Morus alba-reinforced polylactic acid outperform both virgin PLA samples and untreated Morus alba samples.展开更多
基金financially supported by Special Project for High-end CNC Machine Tools and Basic Manufacturing Equipment of China(2012ZX04007-021)Liaoning Excellent Talents in University,China(LR2014004)
文摘The corundum(α-alumina) core has been considered as a suitable candidate for investment casting of hollow, high pressure turbine engine airfoils due to its excellent properties. However, the efficiency of removing alumina cores in concentrated caustic solution cannot meet the needs of industrial production. In this paper, the effects of temperature and initial solution concentration on dissolution of α-alumina were studied by the classical weight-loss method. The fractal kinetic model was developed in order to describe α-alumina dissolution, assuming that the nonporous particles shrank during reaction process. The results show that the dissolution rate increases with increasing reaction temperature and initial solution concentration. Especially, the initial solution concentration has a significant influence on α-alumina dissolution rate at a higher reaction temperature. The activation energies decrease with increasing initial solution concentration, and the chemical reaction is the rate-controlling step.
文摘This research investigates the mechanical and thermal properties of Morus alba combined with polylactic acid in comparison with other natural fibers. The study uses three different fiber and PLA compositions - 20%, 30%, and 40% respectively - to produce composite materials. In addition, another composite with the same fiber volume is treated with a 4% NaOH solution to improve mechanical properties. The composites are processed by twin-screw extrusion, granulation, and injection molding. Tensile strength measurements of raw fibers and NaOH-treated fibers were carried out using a single-fiber tensile test with a gauge length of 40 mm. It was observed that the NaOH surface treatment increases the resistance against tensile loading and exhibited improved properties for raw fiber strands. The diameter of the fibers was measured using optical microscopy. During this research, flexural tests, impact tests, differential scanning calorimetry (DSC), and heat deflection temperature measurements (HDT) were conducted to evaluate the mechanical and thermal properties of the developed composite samples. The results indicate that the mechanical properties of NaOH-treated Morus alba-reinforced polylactic acid outperform both virgin PLA samples and untreated Morus alba samples.