Effect of ultrasonic vibration on Fe-containing intermetallic compounds of hypereutectic Al-Si alloys with high Fe content

The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.

Dry sliding wear behavior of rheocast hypereutectic Al-Si alloys with different Fe contents

The effect of iron content on wear behavior of hypereutectic Al?17Si?2Cu?1Ni alloy produced by rheocasting process was investigated. The dry sliding wear tests were carried out with a pin-on-disk wear tester. The results show that the wear rate of the rheocast alloy is lower than that of the alloy produced by conventional casting process under the same applied load. The fine particle-likeδ-Al4(Fe,Mn)Si2 and polygonalα-Al15(Fe,Mn)3Si2 phases help to improve the wear resistance of rheocast alloys. As the volume fraction of fine Fe-bearing compounds increases, the wear rate of the rheocast alloy decreases. Moreover, the wear rate of rheocast alloy increases with the increase of applied load from 50 to 200 N. For the rheocast alloy with 3% Fe, oxidation wear is the main mechanism at low applied load (50 N). At higher applied loads, a combination of delamination and oxidation wear is the dominant wear mechanism.

Effects of Mg content on primary Mg_2Si phase in hypereutectic Al-Si alloys

Hypereutectic Al-Si alloy with variant Mg contents were fabricated by casting,and the effects of Mg content on the microstructure of primary Mg2Si particles in hypereutectic Al-Si alloys were investigated.The results show that the volume fraction of primary Mg2Si particles increases linearly with raising the Mg content,but the average size of Mg2Si particles does not exhibit a corresponding change.When the Mg content is 3%,á1 0 0？ directions have the fastest growth velocity,so that Mg2Si particles are likely to form octahedron shape.When gradually increasing the Mg content,the distributions of Mg and Si atoms on the solid-liquid interface become inhomogeneous,which results in the formation of irregular octahedron structures.Finally,when the Mg content is about 10%,the morphology of primary Mg2Si particles changes from the octahedron shape into various complex structures with a large size.

Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P

The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.

Microstructure evolution and phase transformation of traditional cast and spray-formed hypereutectic aluminium-silicon alloys induced by heat treatment

Microstructural evolution and phase transformation induced by different heat treatments of the hypereutectic aluminium-silicon alloy, Al-25Si-5Fe-3Cu （wt%, signed as 3C）, fabricated by traditional cast （TC） and spray forming （SF） processes, were investigated by differential scanning calorimetry （DSC） and scanning electron microscopy （SEM） combined with energy dispersive X-ray spectroscopy and X-ray diffraction techniques. The results show that A17Cu2Fe phase can be formed and transformed in TC- and SF-3C alloys between 802-813 K and 800-815 K, respectively. The transformation from β-Al5FeSi to δ-Al4FeSi2 phase via peritectic reaction can occur at around 858-870 K and 876-890 K in TC- and SF-3C alloys, respectively. The starting precipitation temperature of δ-Al4FeSi2 phase as the dominant Fe-bearing phase in the TC-3C alloy is 997 K and the exothermic peak about the peritectic transformation of δ-Al4FeSi2→β-Al5FeSi is not detected in the present DSC experiments. Also, the mechanisms of the microstructural evolution and phase transformation are discussed.

Influence of high pressure and manganese addition on Fe-rich phases and mechanical properties of hypereutectic Al-Si alloy with rheo-squeeze casting

The influence of high pressure and manganese addition on Fe-rich phases(FRPs)and mechanical properties of Al-14Si-2Fe alloy with rheo-squeeze casting(RSC)was investigated.The semi-solid alloy melt was treated by ultrasonic vibration(UV)firstly,and then formed by squeeze casting(SC).Results show that the FRPs in as-cast SC alloys are composed of coarseβ-Al5(Fe,Mn)Si,δ-Al4(Fe,Mn)Si2 and bone-shapedα-Al15(Fe,Mn)3Si2 phases when the pressure is 0 MPa.With RSC process,the FRPs are first refined by UV,and then the solidification under pressure further causes the grains to become smaller.The peritectic transformation occurs during the formation ofαphase.For the alloy with the same composition,the ultimate tensile strength(UTS)of RSC sample is higher than that of the SC sample.With the same forming process,the UTS of Al-14Si-2Fe-0.8Mn alloy is higher than that of Al-14Si-2Fe-0.4Mn alloy.

Effect of mixing rate and temperature on primary Si phase of hypereutectic Al-20Si alloy during control ed diffusion solidification(CDS) process

Controlled Diffusion Solidification(CDS) is a promising process relied on mixing two liquid alloys of precisely controlled chemistry and temperature in order to produce a predetermined alloy composition. In this study, the CDS was employed to prepare hypereutectic Al-20%Si(mass fraction) alloy using Al-30%Si and pure Al of different temperatures. The mixing rate was controlled using three small crucibles with a hole of different diameters in their bottom. The effect of mixing rate and temperature on the microstructure of the primary Si-phase during the mixing of molten Al and Al-30%Si was studied. The results showed that when the diameter of the small crucible bottom hole is 16 mm, a higher mass mixing rate 0.217 kg·s-1 would results in a lower stream velocity 0.414 m·s-1. Conversely a lower mass mixing rate 0.114 kg·s-1(the diameter of the small crucible bottom hole is 8 mm) would result in a higher fluid stream velocity 0.879 m·s-1. A lower mass mixing rate would be better to refine the primary Si than a higher mass mixing rate. Meanwhile, the morphology and distribution of primary Si could also be improved. Especially, when Al-30%Si alloy at 820 °C was mixed with pure Al at 670 °C in the case of a mass mixing rate of 0.114 kg·s-1 and a pouring temperature of 680 °C, the average size of the primary Si phase would be only 18.2 μm. Its morphology would mostly be octahedral and the primary Si would distribute uniformly in the matrix microstructure. The lower mass mixing rate(0.114 kg·s-1) will enhance the broken tendency of Al-30%Si steam and the mixing agitation of resultant melt, so the primary Si phase can be better refined.

Mechanical properties of hypereutectic Al-Si alloy by semisolid processing

Semisolid hypereutectic Al Si alloy billets were obtained by electromagnetic stirring, in which microstructure of primary silicon gets rounder and there are a large number of rosette α phases appearing. Compared with conventional gravity die casting alloys, the tensile strength and elongation of semisolid forming hypereutectic Al Si get obviously improved. Change of primary silicon morphology of semisolid hypereutectic Al Si alloy made by electromagnetic stirring is the main reason of better tensile strength, and a large number of rosette α phases precipitation is the main reason of better elongation.

Semi-solid processing of hypereutectic A390 alloys using novel rheoforming process

The feasibility of semi solid processing of hypereutectic A390 alloys using a novel rheoforming process was investigated. A combination of the swirl enthalpy equilibration device （SEED） process, isothermal holding using insulation and addition of solid alloy during swirling was introduced as a novel method to improve the processability of semi solid slurry. The effects of isothermal holding and the addition of solid alloy on the temperature gradient between the centre and the wall and on the formation of a（Al） particles were examined. In additional tests, phosphorus and strontium were added to the molten metal to refine the primary and eutectic silicon structure to facilitate semi solid processing. The results show that the combination of the SEED process with two additional processing steps can produce semi-solid A390 alloys that can be rheoprocessed. The microstructure reveals an adequate amount of non-dendritic a（Al） globules surrounded by liquid, which greatly improves the processability of semi-solid slurry.

Semi-solid characteristics and thixoforming of hypereutectic Al-Si alloy

Effects of processing parameters on microstructure evolutions by mechanical stirring, procedures for obtaining thixotropy in semi solid slurries, and procedure for thixoforging component, were investigated in hypereutectic Al Si alloy. It is shown that 605 ℃ was the proper temperature for stirring treatment of this alloy, at which the coarse and plate primary Si crystals were effectively changed to globular crystals with a mean diameter of 200 μm after 50 min stirring, that billets with excellent thixotropy were obtained after 50 min remelting at 575 ℃, in which solid fraction of matrix and primary Si crystals was about 60%, and that a perfect near net shape component of disc casting was obtained by thixoforging.

Microstructure Characteristics and Apparent Viscosity of Hypereutectic Al-24%Si Alloy Melt During Semi-solid State Stirring

The microstructural evolution and apparent viscosity of hypereutectic Al-24%Si alloy during semi-solid state shearing were studied with a Searte type viscometer. When the alloy melt was continuously stirred from 720 degreesC to eutectic temperature, the primary Si crystals were gradually changed from elongated platelets to near-spherical shapes. It was found that some nondendritic a-phase formed when the melt was stirred below 585 degreesC. The experiment showed that the semi-solid stirring had strong effect on inhibiting the anisotropic growth of Si crystals during solidification. The apparent viscosity of the alloy melt increased slowly with the decreasing of temperature before the formation of nondendritic alpha -phase, which caused the dramatic increase of apparent viscosity.

Influences of complex modification of P and RE on microstructure and mechanical properties of hypereutectic Al-20Si alloy

P and RE complex modification of hypereutectic Al-Si alloys was conducted. The influences of P, RE content on the microstructure and mechanical properties of alloys were investigated. The complex modifications of P and RE make the coarse block primary silicon obviously refined and the large needle eutectic silicon modified to the fine fibrous or lamella ones. P mainly refines the primary silicon, but excess P is unfavorable to the refinement of primary silicon. RE can well refine the primary and eutectic silicon, but its modification effect on the eutectic silicon is more obvious. P can repress the modification of RE on the eutectic silicon. The alloys with the additions of 0.08% P and 0.60% RE have the optimal microstructure and the highest mechanical properties. Compared with the unmodified alloy, the primary silicon of alloys can be refined from 66.4 μm to 23.3 μm and the eutectic silicon can be refined from 8.3 μm to 5.2 μm. The tensile strength is improved from 256 MPa to 306 MPa and the elongation is improved from 0.35% to 0.48%.

Influence of rheo-diecasting processing parameters on microstructure and mechanical properties of hypereutectic Al-30%Si alloy

The effects of pouring temperature,vibration frequency,and the number of curves in a serpentine channel,on themicrostructure and mechanical properties of Al-30%Si alloy processed by rheo-diecasting(RDC)were investigated.The semisolidAl-30%Si alloy slurry was prepared by vibration serpentine channel pouring(VSCP)process in the RDC process.The results showthat the pouring temperature,the vibration frequency,and the number of the curves strongly affect the microstructure and mechanicalproperties of Al-30%Si alloy.Under experimental conditions of a pouring temperature of850°C,a twelve-curve copper channel anda vibration frequency of80Hz,the primary Si grains are refined into fine compact grains with average grain size of about24.6μm inthe RDC samples assisted with VSCP.Moreover,the ultimate tensile strength(UTS),elongation and hardness of the RDC sample are296MPa,0.87%and HB155,respectively.It is concluded that the VSCP process can effectively refine the primary Si grains.Therefinement of primary Si grains is the major cause for the improvement of the mechanical properties of the RDC sample.

Refinement and thermal analysis of hypereutectic Al-25%Si alloy

Refinement and thermal analysis of hypereutectic Al 25%Si alloy were investigated with scanning electron microscope (SEM) and differential scanning calorimeter (DSC). The results show that the average size of primary silicon in Al 25%Si alloy without and with phosphorus addition are 250 μm and 30 μm, respectively. But the primary and eutectic growth temperature is raised by about 17.3 ℃ and 4?℃ respectively due to phosphorus addition. The primary nucleation temperatures are 745.0 ℃ and 762.0 ℃ for untreated and treated samples and in addition, the enthalpy changes of primary and eutectic transformation are -261.0 J/g and -397.3 J/g without phosphorus addition, -294.2 J/g and -386.1 J/g with phosphorus addition, respectively. Otherwise the mechanisms of refinement and thermal transformation of Al 25%Si alloy in solidifying process are also discussed. [

Influence of hydrogen content on the behavior of grain reflnement in hypereutectic aluminum-silicon alloy

Dissolved hydrogen is harmful to mechanical properties of refinedhypereutectic aluminum-silicon alloys. In the present work, by using a stepped-form mold and thehydrogen-detecting instrument HYSCAN II, the relationship between the initial hydrogen content inthe melt and the refinement effect on the casting of hypereutectic aluminum-silicon alloy wasinvestigated. The experimental results show that the cooling rate, the hydrogen content and thegrain refinement effect are three interactive factors. When the hydrogen content is above 0.20mL/100 g and the cooling rate is lower than that in 50 mm-thick step, hydrogen dissolved in thealloy melt influences the grain refinement effect. With increasing the cooling rate, the criticalhydrogen content increases too. It is expected that much hydrogen in the melt make the netinterfacial energy larger than or equal to zero, resulting in the shielding of the particles AlPduring solidification and that the critical gas content is closely related to the critical radius ofembryo bubbles.

Effect of hot extrusion process on microstructure and mechanical properties of hypereutectic Al-Si alloys

The hypereutectic Al-Si alloy was fabricated by hot extrusion process after solidified under electromagnetic stirring,and the microstructure and mechanical properties of the alloy were studied.The results show that the ultimate tensile strength and elongation of the alloy reached 229.5 MPa and 4.6%,respectively with the extrusion ratio of 10,and 263.2 MPa and 5.4%,respectively with extrusion ratio of 20.This indicates that the mechanical properties of the alloy are obviously improved with the increase of extrusion ratio.After hot extruded,the primary Si,eutectic Si,Mg2Si,AlNi,Al7Cu4Ni and Al-Si-Mn-Fe-Cr-Mo phases are refined to different extent,and the efficiency of refinement is obvious more and more with the increase of extrusion ratio.After T6 heat treatment,the sharp corners of these phases become passivated and roundish,and the mechanical properties are improved.The ultimate tensile strength of the extruded alloy after T6 heat treatment reaches 335.3 MPa with extrusion ratio of 10 and 353.6 MPa with extrusion ratio of 20.

Hydrogen Content and Porosity Behavior of Hypereutectic Aluminum-silicon Alloy with Phosphorus

By making castings that pick up gas from moisture in red sand molds,the porosity generated at different cooling rates was discussed during solidification of hypereutectic Al-25%Si alloy without and with phosphorus additions. The effect of phosphorus addition on hydrogen content in the melt was also studied. It was observed that the phosphorus addition made hydrogen content in alloy melts present a “see-saw' tendency.In addition to primary silicon refinement,the phosphorus promoted gas porosity formed not only in slowly cooled sections, but also in rapidly cooled sections. There was a small difference in density of full dense sample between P-refined and unrefined castings, with a larger density associated with phosphorous addition. The change of the surface tension seemed more reasonable to explain the mechanism of porosity behavior.

Modification effect of pure rare earth metal La on as-cast hypereutectic Al-17%Si alloys

The modification effect of La addition on the microstructural characteristics of hypereutectic Al 17%Si alloys was studied. Microstructures were examined using conventional optical microscopy and electron probe X ray microanalyzer. The morphology of Si crystal was evaluated by quantitative metallographical analysis. The results indicate that simultaneous modification to both primary and eutectic Si crystals is obtained by the addition of pure rare earth metal La in the hypereutectic Al 17%Si alloys while the optimal effect of La is obtained at a rather large scale. La begins to form intermetallic compound when its concentration exceeds approximately 1%, which appears as dark platelets in etched specimens. Electron probe X ray microanalysis experiment shows that La rich platelet could be represented as Al 1Si 2La 2 consisting of LaSi 2 and some unknown ternary Al x Si y La phase.

Effect of Nd on Microstructure and Mechanical Properties of Hypereutectic Al-25Si Alloy

The modification mechanism of Nd on Al-25Si alloy was studied. The result showed that pure Nd (0.3%) could significantly refine primary silicon in hypereutectic Al-25Si alloy. And the morphology of primary silicon was transformed from star-shaped to block and the size of primary silicon changed from 150～200 μm to 40～80 μm after modification. The morphology of silicon and elements presence was detected by means of SEM-EDS, XRD was carried out to detect the phase constitution before and after modification. It was found that no new phase formed and the lattice of silicon and aluminum increased after modification and most of Nd may exist as solids solute element of silicon and absorb on the surface of silicon. Mechanical property test results showed that after modification with 0.3% Nd, Tensile strength increased about 33% from 138 to 184 MPa, yield strength increased about 15% from 126 to 145 MPa, and elongation change was not obvious. The improvement of mechanical property should attribute to fine grain strength and purification of base metal after modification.

Modification mechanism of hypereutectic Al-Si alloy with P-Na addition

Effect of P-Na united modification on Al-22%Si-1.0%Cu-0.5%Mg-0.5%Mn alloy was studied. The results show that the refining effect of P-Na addition on primary silicon is superior to that of P and the former could modify eutectic silicon at the same time. Effects of P-Na modification on crystallization and microstructure of hypereutectic Al-Si alloys were studied with Electron-Scanning Microscope, Electron-Probe and X-ray diffractometer. The modification mechanism represents that on one hand, the primary silicon is refined by AlP as heterogeneous nucleus; on the other hand, when Na is added at the same time, P atoms are difficult to diffuse in the melt, and then enrichs on the growing faces of silicon phase. Moreover, a SiP compound was also discovered in Si crystals, which prevents the growth of silicon phase and refines the primary silicon.