The effect of different tempering temperatures on the microstructure and mechanical properties of airquenched high boron white cast iron was studied.The results indicate that the high boron white cast iron comprises d...The effect of different tempering temperatures on the microstructure and mechanical properties of airquenched high boron white cast iron was studied.The results indicate that the high boron white cast iron comprises dendritic matrix and inter-dendritic M 2 B boride;and the matrix comprises martensite and pearlite.After quenching in the air,the matrix is changed into lath martensite;but only 1-μm-size second phase exists in the matrix.After tempering,another second phase of several tens of nanometers is found in the matrix,and the size and quantity increase with an increase in tempering temperature.The two kinds of second precipitation phase with different sizes in the matrix have the same chemical formula,but their forming stages are different.The precipitation phase with larger size forms during the austenitizing process,while the precipitation phase with smaller size forms during the tempering process.When tempered at different temperatures after quenching,the hardness decreases with an increase in the tempering temperature,but it increases a little at 450 ℃ due to the precipitation strengthening effect of the second phase,and it decreases greatly due to the martensite decomposition above 450 ℃.The impact toughness increases a little when tempered below 300 ℃,but it then decreases continuously owing to the increase in size and quantity of the secondary precipitate above 300 ℃.Considered comprehensively,the optimum tempering temperature is suggested at 300 ℃ to obtain a good combination of hardness and toughness.展开更多
Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently, the service life of the liner made from traditional materials, such as Hadfield steel and alloyed s...Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently, the service life of the liner made from traditional materials, such as Hadfield steel and alloyed steels, is typically less than ten months. Bimetal liner, made from high Cr white cast iron and carbon steel, has been successfully developed by using liquid-liquid composite lost foam casting process. The microstructure and interface of the composite were analyzed using optical microscope, SEM, EDX and XRD. Micrographs indicate that the boundary of bimetal combination regions is staggered like dogtooth, two liquid metals are not mixed, and the interface presents excellent metallurgical bonding state. After heat treatment, the composite liner specimens have shown excellent properties, including hardness 〉 61 HRC, fracture toughness ak 〉16.5 J.cm2 and bending strength 〉1,600 MPa. Wear comparison was made between the bimetal composite liner and alloyed steel liner in an industrial hematite ball mill of WISCO, and the results of eight-month test in wet grinding environment have proved that the service life of the bimetal composite liner is three times as long as that of the alloyed steel liner.展开更多
The structure and properties of high chromium white cast iron in different treatment states were studied. Using X ray diffraction method, observing their metallograph and measuring their microhardness, the phases inv...The structure and properties of high chromium white cast iron in different treatment states were studied. Using X ray diffraction method, observing their metallograph and measuring their microhardness, the phases involved in the iron were determined. The notch toughness, macrohardness and the fractograph of the samples are compared and their performance was determined, which mainly depends on the matrix structure. Relatively good comprehensive properties can be obtained in the tempering state. Improvements have been made on the commonly used tempering standard. Tempering for a short period at low temperature can improve the materials′ service performance obviously.展开更多
The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied.The results indicate that the fraction of retained austenite and...The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied.The results indicate that the fraction of retained austenite and the manganese distribution in as-cast alloys are controlled by manganese content.The manganese distribution in as-cast alloys is not homogeneous.The manganese content in carbide is higher than that in matrix.Whether the secondary hardening occurs or not and the peak hardness of secondary hardening is controlled by manganese content in retained austenite in as-cast structure.Higher manganese content can cause more retained austenite.The secondary hardening occurs in sub-critical treating process if the fraction of retained austenite is high.展开更多
The formulas proposed by J. Dodd and J. L. Parks for calculating the hardenability of high-Cr white cast iron under continuous cooling condition was recommended. For broader application, some supplements were made to ...The formulas proposed by J. Dodd and J. L. Parks for calculating the hardenability of high-Cr white cast iron under continuous cooling condition was recommended. For broader application, some supplements were made to the formula. Through tests on the half-cooling time of typical castings, the compositions of ideal alloys were precisely designed using the Dodd’s formula. Hardness testing of heat-treated castings showed that the designed compositions were correct. The application of castings demonstrated excellent abrasion resistance.展开更多
The valence electron structure of alloying austenite of 3C-15Cr high chromium white cast iron with different Mn contents from 1% to 6% is analyzed by BLD method and EET. Results show that the addition of Mn has major ...The valence electron structure of alloying austenite of 3C-15Cr high chromium white cast iron with different Mn contents from 1% to 6% is analyzed by BLD method and EET. Results show that the addition of Mn has major influence on the valence electron structure of the alloying austenite, especially on that of Fe-C, Fe-C-Cr and Fe-C-Cr-Mn unit cells of it. The effect becomes weak when Mn content is over 4%. Based on the effect of n~, F~~, the weighting of each unit cell and the degree of undercooling on phase transition of the aus- tenite, we can calculate the retained austenite content of as-cast structure of the high chromium white cast iron. The calculation results coincide well with those of the experiment. The phase transition characters of the austenite in high chromium white cast iron can be forecasted through valence electron structure analysis of alloying austenite by BLD method and EET on the basis of Fe-C-Cr equilibrium phase diagram.展开更多
The effect of austempering temperature on the microstructure and properties of a high chromium white cast iron was investigated with the Rietveld refinement method. The result shows that the upper bainite exists in th...The effect of austempering temperature on the microstructure and properties of a high chromium white cast iron was investigated with the Rietveld refinement method. The result shows that the upper bainite exists in the sampie austempered at 623 K and the martensite, lower bainite, M7C3, and retained austenite exist in the samples austempered at 563 K and 593 K. The relative content of the retained austenite increases with increasing the austemper- ing temperature from 563 K to 623 K. The higher hardness, impact toughness and impact abrasive wear resistance can be obtained for the specimen austempered at 593 K.展开更多
文摘The effect of different tempering temperatures on the microstructure and mechanical properties of airquenched high boron white cast iron was studied.The results indicate that the high boron white cast iron comprises dendritic matrix and inter-dendritic M 2 B boride;and the matrix comprises martensite and pearlite.After quenching in the air,the matrix is changed into lath martensite;but only 1-μm-size second phase exists in the matrix.After tempering,another second phase of several tens of nanometers is found in the matrix,and the size and quantity increase with an increase in tempering temperature.The two kinds of second precipitation phase with different sizes in the matrix have the same chemical formula,but their forming stages are different.The precipitation phase with larger size forms during the austenitizing process,while the precipitation phase with smaller size forms during the tempering process.When tempered at different temperatures after quenching,the hardness decreases with an increase in the tempering temperature,but it increases a little at 450 ℃ due to the precipitation strengthening effect of the second phase,and it decreases greatly due to the martensite decomposition above 450 ℃.The impact toughness increases a little when tempered below 300 ℃,but it then decreases continuously owing to the increase in size and quantity of the secondary precipitate above 300 ℃.Considered comprehensively,the optimum tempering temperature is suggested at 300 ℃ to obtain a good combination of hardness and toughness.
基金supported by the National Natural Science Foundation of China under grant No.50805109the Fundamental Research Funds for the Central Universities under grant No.2011-1a-023
文摘Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently, the service life of the liner made from traditional materials, such as Hadfield steel and alloyed steels, is typically less than ten months. Bimetal liner, made from high Cr white cast iron and carbon steel, has been successfully developed by using liquid-liquid composite lost foam casting process. The microstructure and interface of the composite were analyzed using optical microscope, SEM, EDX and XRD. Micrographs indicate that the boundary of bimetal combination regions is staggered like dogtooth, two liquid metals are not mixed, and the interface presents excellent metallurgical bonding state. After heat treatment, the composite liner specimens have shown excellent properties, including hardness 〉 61 HRC, fracture toughness ak 〉16.5 J.cm2 and bending strength 〉1,600 MPa. Wear comparison was made between the bimetal composite liner and alloyed steel liner in an industrial hematite ball mill of WISCO, and the results of eight-month test in wet grinding environment have proved that the service life of the bimetal composite liner is three times as long as that of the alloyed steel liner.
文摘The structure and properties of high chromium white cast iron in different treatment states were studied. Using X ray diffraction method, observing their metallograph and measuring their microhardness, the phases involved in the iron were determined. The notch toughness, macrohardness and the fractograph of the samples are compared and their performance was determined, which mainly depends on the matrix structure. Relatively good comprehensive properties can be obtained in the tempering state. Improvements have been made on the commonly used tempering standard. Tempering for a short period at low temperature can improve the materials′ service performance obviously.
文摘The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied.The results indicate that the fraction of retained austenite and the manganese distribution in as-cast alloys are controlled by manganese content.The manganese distribution in as-cast alloys is not homogeneous.The manganese content in carbide is higher than that in matrix.Whether the secondary hardening occurs or not and the peak hardness of secondary hardening is controlled by manganese content in retained austenite in as-cast structure.Higher manganese content can cause more retained austenite.The secondary hardening occurs in sub-critical treating process if the fraction of retained austenite is high.
文摘The formulas proposed by J. Dodd and J. L. Parks for calculating the hardenability of high-Cr white cast iron under continuous cooling condition was recommended. For broader application, some supplements were made to the formula. Through tests on the half-cooling time of typical castings, the compositions of ideal alloys were precisely designed using the Dodd’s formula. Hardness testing of heat-treated castings showed that the designed compositions were correct. The application of castings demonstrated excellent abrasion resistance.
文摘The valence electron structure of alloying austenite of 3C-15Cr high chromium white cast iron with different Mn contents from 1% to 6% is analyzed by BLD method and EET. Results show that the addition of Mn has major influence on the valence electron structure of the alloying austenite, especially on that of Fe-C, Fe-C-Cr and Fe-C-Cr-Mn unit cells of it. The effect becomes weak when Mn content is over 4%. Based on the effect of n~, F~~, the weighting of each unit cell and the degree of undercooling on phase transition of the aus- tenite, we can calculate the retained austenite content of as-cast structure of the high chromium white cast iron. The calculation results coincide well with those of the experiment. The phase transition characters of the austenite in high chromium white cast iron can be forecasted through valence electron structure analysis of alloying austenite by BLD method and EET on the basis of Fe-C-Cr equilibrium phase diagram.
基金Item Sponsored by Key Project on Natural Science for the Education Department of Anhui Province (2006KJ080A)
文摘The effect of austempering temperature on the microstructure and properties of a high chromium white cast iron was investigated with the Rietveld refinement method. The result shows that the upper bainite exists in the sampie austempered at 623 K and the martensite, lower bainite, M7C3, and retained austenite exist in the samples austempered at 563 K and 593 K. The relative content of the retained austenite increases with increasing the austemper- ing temperature from 563 K to 623 K. The higher hardness, impact toughness and impact abrasive wear resistance can be obtained for the specimen austempered at 593 K.