High-chromium vanadium-titanium magnetite all-pellet integrated burden optimization and softening-melting behavior based on flux pellets

High-chromium vanadium-titanium magnetite(HVTM)is a crucial polymetallic-associated resource to be developed.The allpellet operation is a blast furnace trend that aims to reduce carbon dioxide emissions in the future.By referencing the production data of vanadium-titanium magnetite blast furnaces,this study explored the softening-melting behavior of high-chromium vanadium-titanium magnetite and obtained the optimal integrated burden based on flux pellets.The results show that the burden with a composition of 70wt%flux pellets and 30wt%acid pellets exhibits the best softening-melting properties.In comparison to that of the single burden,the softening-melting characteristic temperature of this burden composition was higher.The melting interval first increased from 307 to 362℃and then decreased to 282℃.The maximum pressure drop(ΔPmax)decreased from 26.76 to 19.01 kPa.The permeability index(S)dropped from 4643.5 to 2446.8 kPa·℃.The softening-melting properties of the integrated burden were apparently improved.The acid pellets played a role in withstanding load during the softening process.The flux pellets in the integrated burden exhibited a higher slag melting point,which increased the melting temperature during the melting process.The slag homogeneity and the TiC produced by over-reduction led to the gas permeability deterioration of the single burden.The segregation of the flux and acid pellets in the HVTM proportion and basicity mainly led to the better softening-melting properties of the integrated burden.

Effect of titanium on the sticking of pellets based on hydrogen metallurgy shaft furnace:Behavior analysis and mechanism evolution

Direct reduction based on hydrogen metallurgical gas-based shaft furnace is a promising technology for the efficient and low-carbon smelting of vanadium-titanium magnetite.However,in this process,the sticking of pellets occurs due to the aggregation of metal-lic iron between the contact surfaces of adjacent pellets and has a serious negative effect on the continuous operation.This paper presents a detailed experimental study of the effect of TiO2 on the sticking behavior of pellets during direct reduction under different conditions.Results showed that the sticking index(SI)decreased linearly with the increasing TiO2 addition.This phenomenon can be attributed to the increase in unreduced FeTiO3 during reduction,leading to a decrease in the number and strength of metallic iron interconnections at the sticking interface.When the TiO2 addition amount was raised from 0 to 15wt%at 1100°C,the SI also increased from 0.71%to 59.91%.The connection of the slag phase could be attributed to the sticking at a low reduction temperature,corresponding to the low sticking strength.Moreover,the interconnection of metallic iron became the dominant factor,and the SI increased sharply with the increase in re-duction temperature.TiO2 had a greater effect on SI at a high reduction temperature than at a low reduction temperature.

Probing deactivation by coking in catalyst pellets for dry reforming of methane using a pore network model

Dry reforming of methane(DRM) is an attractive technology for utilizing the greenhouse gases(CO_(2) and CH_(4)) to produce syngas. However, the catalyst pellets for DRM are heavily plagued by deactivation by coking, which prevents this technology from commercialization. In this work, a pore network model is developed to probe the catalyst deactivation by coking in a Ni/Al_(2)O_(3) catalyst pellet for DRM. The reaction conditions can significantly change the coking rate and then affect the catalyst deactivation. The catalyst lifetime is higher under lower temperature, pressure, and CH_(4)/CO_(2) molar ratio, but the maximum coke content in a catalyst pellet is independent of these reaction conditions. The catalyst pellet with larger pore diameter, narrower pore size distribution and higher pore connectivity is more robust against catalyst deactivation by coking, as the pores in this pellet are more difficult to be plugged or inaccessible.The maximum coke content is also higher for narrower pore size distribution and higher pore connectivity, as the number of inaccessible pores is lower. Besides, the catalyst pellet radius only slightly affects the coke content, although the diffusion limitation increases with the pellet radius. These results should serve to guide the rational design of robust DRM catalyst pellets against deactivation by coking.

The Logistics of Production and Supply of Ag Pellets for Industrial Applications in Canada

In this work we analyze the supply of biomass from field to an in-land or port destination. The biomass is pelletized to increase its bulk density to extend its storage period and for ease of its transport. The pellet may be used for conversion to chemicals and animal bedding or for straight combustion. We analyzed supply chain in Saskatchewan where there are plenty of crop residues but widely dispersed and harvest seasons are short. We envisioned that the farmer collects bales from field and transports the bales to farmstead during the harvest season. The bales are then processed into pellets using small scale pellet equipment. A custom operator with expertise in pelletization may engage in handling and densifying the biomass. The business case for the mobile mill will be similar to the well established custom grain and forage harvesting operations. The pellets are stored in hopper bottom grain bins at the farmstead. From this point, the handling of pellets would be similar to the handling and marketing of grain. The farmer trucks a specified volume of pellets from farmstead to the nearest elevator where the pellets are transferred to larger bins or silos. Pellets are extracted from silos and loaded onto the rail cars. The Canadian freight rail companies (mainly CN) currently transport over 3 million dry tonne (dt) of wood pellets in rail cars. The pellets are hauled to marine ports on the West Coast or East Coast for export. The cost of delivering ag pellets to biorefinery or to the shipping port is $86.09/dt. This cost does not include the equivalent value of removing biomass from the farm (e.g. fertilizer replacement) and return on investment. The GHG emissions to produce and transport ag pellets add up to 185.9 kg of CO2 per dt of biomass. The cost of producing pellets without drying feedstock is $35.05/dt and the corresponding GHG for palletization amounts $146.30/dt.

Effect mechanism of aluminum occurrence and content on the induration characteristics of iron ore pellets

With the intensified depletion of high-grade iron ores,the increased aluminum content in iron ore concentrates has become unavoidable,which is detrimental to the pelletization process.Therefore,the effect mechanism of aluminum on pellet quality must be identified.In this study,the influence of aluminum occurrence and content on the induration of hematite(H)and magnetite(M)pellets was investigated through the addition of corresponding Al-containing additives,including alumina,alumogoethite,gibbsite,and kaolinite.Systematic mineralogical analysis,combined with the thermodynamic properties of different aluminum occurrences and the quantitative characterization of consolidation behaviors,were conducted to determine the related mechanism.The results showed that the alumina from various aluminum occurrences adversely affected the induration characteristics of pellets,especially at an aluminum content of more than 2.0wt%.The thermal decomposition of gibbsite and kaolinite tends to generate internal stress and fine cracks,which hinder the respective microcrystalline bonding and recrystallization between Fe2O3particles.The adverse effect on the induration characteristics of fired pellets with different aluminum occurrences can be relieved to varying degrees through the formation of liquid phase bonds between the hematite particles.Kaolinite is more beneficial to the induration process than the other three aluminum occurrences because of the formation of more liquid phase,which improves pellet consolidation.The research results can further provide insights into the effect of aluminum occurrence and content in iron ore concentrates on downstream processing and serve as a guide for the utilization of high-alumina iron ore concentrates in pelletization.

Simulation of deuterium pellet ablation and deposition in the EAST tokamak with HPI2 code

Pellet injection is a primary method for fueling the plasma in magnetic confinement devices.For that goal the knowledges of pellet ablation and deposition profiles are critical.In the present study,the pellet fueling code HPI2 was used to predict the ablation and deposition profiles of deuterium pellets injected into a typical H-mode discharge on the EAST tokamak.Pellet ablation and deposition profiles were evaluated for various pellet injection locations,with the aim at optimizing the pellet injection to obtain a deep fueling depth.In this study,we investigate the effect of the injection angle on the deposition depth of the pellet at different velocities and sizes.The ablation and deposition of the injected pellet are mainly studied at each injection position for three different injection angles:0°,45°,and 60°.The pellet injection on the high field side(HFS)can achieve a more ideal deposition depth than on the low field side(LFS).Among these angles,horizontal injection on the middle plane is relatively better on either the HFS or the LFS.When the injection location is 0.468 m below the middle plane on the HFS or 0.40 m above the middle plane of the LFS,it can achieve a similar deposition depth to the one of its corresponding side.When the pre-cooling effect is taken into account,the deposition depth is predicted to increase only slightly when the pellet is launched from the HFS.The findings of this study will serve as a reference for the update of pellet injection systems for the EAST tokamak.

Diffusion and reaction mechanism of limestone and quartz in fluxed iron ore pellet roasting process

The increase to the proportion of fluxed pellets in the blast furnace burden is a useful way to reduce the carbon emissions in the ironmaking process.In this study,the interaction between calcium carbonate and iron ore powder and the mineralization mechanism of fluxed iron ore pellet in the roasting process were investigated through diffusion couple experiments.Scanning electron microscopy with energy dispersive spectroscopy was used to study the elements’diffusion and phase transformation during the roasting process.The results indicated that limestone decomposed into calcium oxide,and magnetite was oxidized to hematite at the early stage of preheating.With the increase in roasting temperature,the diffusion rate of Fe and Ca was obviously accelerated,while the diffusion rate of Si was relatively slow.The order of magnitude of interdiffusion coefficient of Fe_(2)O_(3)-CaO diffusion couple was 10^(−10) m^(2)·s^(−1) at a roasting temperature of 1200℃for 9 h.Ca_(2)Fe_(2)O_(5) was the initial product in the Fe_(2)O_(3)-CaO-SiO_(2) diffusion interface,and then Ca_(2)Fe_(2)O_(5) continued to react with Fe_(2)O_(3) to form CaFe_(2)O_(4).With the expansion of the diffusion region,the sillico-ferrite of calcium liquid phase was produced due to the melting of SiO_(2) into CaFe_(2)O_(4),which can strengthen the consolidation of fluxed pellets.Furthermore,andradite would be formed around a small part of quartz particles,which is also conducive to the consolidation of fluxed pellets.In addition,the principle diagram of limestone and quartz diffusion reaction in the process of fluxed pellet roasting was discussed.

高浓度甲状腺素对软骨细胞聚集体(pellets)体外形成软骨组织的作用

目的：药物浓度（100nM）甲状腺素对组织工程软骨形成的作用。方法：将软骨细胞聚集体分为常规培养组（DMED＋10％FBS）和100nM甲状腺素组（DMED＋10％FBS＋100nM甲状腺素），体外培养1、2和3周取材进行大体形态、组织学、二型胶原和十型胶原免疫组化染色和软骨特异基因PCR分析。结果：100nM甲状腺素组形成的软骨细胞聚集体的体积和湿重均明显低于常规培养组，甲苯胺兰、二型胶原（C01II）染色较常规培养组弱，软骨细胞特异基因的表达水平与常规培养组相似，软骨细胞肥大相关基因十型胶原（ColX）及基质金属蛋白酶13（MMP13）的表达较对照组减弱，成骨方向分化相关基因（ColI，Runx2）的表达与常规培养组相似。结论：高浓度甲状腺素能够抑制软骨细胞肥大，但同时也抑制了软骨细胞增殖和软骨细胞基质分泌。

An Innovative Process for Direct Reduction of Cold bound Pellets from Iron Concentrate with a Coal-based Rotary Kiln

Successfully developed an innovative process of direct reduction of cold bound pellets from iron ore concentrate with a coal based rotary kiln, in comparison with the traditional direct reduction of fired oxide pellets in coal based rotary kilns , possesses such advantages as: shorter flowsheet, lower capital investment, greater economic profit, good quality of direct reduced iron. The key technologies , such as the composite binder and corresponding feasible techniques were employed in practice. A mill utilizing this process and with an annual capacity of 50 thousand ton DRI has been put into operation.

Effect of carbon species on the reduction and melting behavior of boron-bearing iron concentrate/carbon composite pellets

Iron nugget and boron-rich slag can be obtained in a short time through high-temperature reduction of boron- bearing iron concentrate by carbonaceous material, both of which are agglomerated together as a carbon composite pellet. This is a novel flow sheet for the comprehensive utilization of boron-bearing iron concentrate to produce a new kind of man-made boron ore. The effect of reducing agent species （i.e., carbon species） on the reduction and melting process of the composite pellet was investigated at a laboratory scale in the present work. The results show that, the reduction rate of the composite pellet increases from bituminite, anthracite, to coke at temperatures ranging from 950 to 1300~C. Reduction temperature has an important effect on the microstructure of reduced pellets. Carbon species also affects the behavior of reduced metallic iron particles. The anthracite-bearing composite pellet melts faster than the bituminite- bearing composite pellet, and the coke-bearing composite pellet cannot melt due to the high fusion point of coke ash. With anthracite as the reducing agent, the recovery rates of iron and boron are 96.5% and 95.7%, respectively. This work can help us get a further understanding of the new process mechanism.

Effect of Cr2O3 addition on oxidation induration and reduction swelling behavior of chromium-bearing vanadium titanomagnetite pellets with simulated coke oven gas

The oxidation induration and reduction swelling behavior of chromium-bearing vanadium titanomagnetite pellets(CVTP)with Cr2O3 addition were studied,and the reduction swelling index(RSI)and compressive strength(CS)of the reduced CVTP with simulated coke oven gas(COG)injection were investigated.The results showed that the CS of the CVTP decreases and the porosity of the CVTP increases with increasing amount of Cr2O3 added.The Cr2O3 mainly exists in the form of(Cr,Fe)2O3 solid solution in the CVTP and as Fe-Cr in the reduced CVTP.The CS of the reduced CVTP increases and the RSI of the reduced CVTP decreases with increasing amount of Cr2O3 added.The limited aggregation and diffusion of metallic iron contribute to the formation of dense lamellar crystals,which leads to the slight decrease for reduction swelling behavior of reduced CVTP.This work provides a theoretical and technical basis for the utilization of CVTP and other Cr-bearing ores such as chromite with COG recycling technology.

Oxidation behavior of artificial magnetite pellets

The oxidation behavior of artificial magnetite pellets was investigated through measurements of the oxidation degree and mineralogical analysis. The results show that artificial magnetite pellets are much easier to oxidize than natural magnetite. The oxidation is controlled through two different reaction mechanisms. The oxidation of artificial magnetite is dominated by internal diffusion, with an activation energy of 8.40 kJ/mol, at temperatures less than 800°C, whereas it is controlled by chemical reaction, with a reaction activation energy of 67.79 kJ/mol, at temperatures greater than 800°C. In addition, factors such as the oxygen volume fraction and the pellet diameter strongly influence the oxidation of artificial magnetite: a larger oxygen volume fraction and a smaller pellet diameter result in a much faster oxidation process.

Numerical simulation of the direct reduction of pellets in a rotary hearth furnace for zinc-containing metallurgical dust treatment

A mathematical model was established to describe the direct reduction of pellets in a rotary hearth furnace （RHF）. In the model, heat transfer, mass transfer, and gas-solid chemical reactions were taken into account. The behaviors of iron metallization and dezincification were analyzed by the numerical method, which was validated by experimental data of the direct reduction of pellets in a Si-Mo furnace. The simulation results show that if the production targets of iron metallization and dezincification are up to 80% and 90%, respectively, the furnace temperature for high-temperature sections must be set higher than 1300~ C. Moreover, an undersupply of secondary air by 20% will lead to a decline in iron metallization rate of discharged pellets by 10% and a decrease in dezincing rate by 13%. In addition, if the residence time of pellets in the furnace is over 20 min, its further extension will hardly lead to an obvious increase in production indexes under the same furnace temperature curve.

Beneficiation of Titanium Oxides From Ilmenite by Self-Reduction of Coal Bearing Pellets

The study on the beneficiation of titanium oxides from Panzhihua ilmenites by reduction of coal bearing pellets was carried out. The iron oxides in pellets were efficiently reduced to metal iron, and titanium oxide slag beneficiated was separated from metal iron. The effect of temperature, flux and coal blending ratio on the reduction and separation was investigated, and rational parameters were determined. A new process for the beneficiation of titanium oxides by rotary hearth furnace （RHF） was proposed.

Preparation and in vitro-in vivo evaluation of intestinal retention pellets of Berberine chloride to enhance hypoglycemic and lipid-lowing efficacy

Berberine chloride(BBR) is a pharmacokinetic profile of drug with poor bioavailability but good therapeutic efficacy,which is closely related to the discovery of BBR intestinal target.The major aim of this paper is to develop BBR intestinal retention type sustained-release pellets and evaluate their in vivo and in vitro behaviors base on the aspect of local action on intestinal tract. Here,wet milling technology is used to improve dissolution and dissolution rate of BBR by decreasing the particle size and increasing the wettability. The pellets are prepared by liquid layer deposition technology,and then the core pellets are coated with Eudragit~?L30 D-55 and Eudragit~?NE30 D aqueous dispersion. The prepared pellets show high drug loading capacity,and the drug loading up to 93%. Meanwhile,it possesses significant sustained drug release effect in purified water which is expected to improve the pharmacokinetic behavior of BBR. The pharmacokinetics results demonstrate that the halflife of BBR was increased significantly from 24 h to 36 h and the inter-and intra-subject variability are decreased compared to commercial BBR tablets. The retention test results indicate that the pellet size and Eudragit~?NE30 D plays an important role in retention time of the pellet,and it is found that the pellets with small particle size and high Eudragit~?NE30 D coating content can stay longer in the intestine than the pellets with large particle size. All in all,BBR intestinal retention type pellets are prepared successfully in this study,and the pellets show satisfactory in vivo and in vitro behaviors.

Effects of smelting parameters on the slag/metal separation behaviors of Hongge vanadium-bearing titanomagnetite metallized pellets obtained from the gas-based direct reduction process

Smelting separations of Hongge vanadium-bearing titanomagnetite metallized pellets（HVTMP）prepared by gas-based direct reduction were investigated,and the effects of smelting parameters on the slag/metal separation behaviors were analyzed.Relevant mechanisms were elucidated using X-ray diffraction analysis,FACTSAGE 7.0 calculations,and scanning electron microscopy observations.The results show that,when the smelting temperature,time,and C/O ratio are increased,the recoveries of V and Cr of HVTMP in pig iron are improved,the recovery of Fe initially increases and subsequently decreases,and the recovery of Ti O_2 in slag decreases.When the smelting Ca O/Si O_2 ratio is increased,the recoveries of Fe,V,and Cr in pig iron increase and the recovery of Ti O_2 in slag initially increases and subsequently decreases.The appropriate smelting separation parameters for HVTMP are as follows：smelting temperature of 1873 K;smelting time of 30–50 min;C/O ratio of 1.25;and Ca O/Si O_2 ratio of 0.50.With these optimized parameters（smelting time：30 min）,the recoveries of Fe,V,Cr,and Ti O_2 are 99.5%,91.24%,92.41%,and 94.86%,respectively.

Effect of magnesia on the compressive strength of pellets

The compressive strength of MgO-fluxed pellets was investigated before and after they were reduced. The porosity and pore size of green pellets, product pellets, and reduced pellets were analyzed to clarify how MgO affects the strength of the pellets. Experimental resuits show that when the MgO-bearing flux content in the pellets increases from 0.0wt% to 2.0wt%, the compressive strength of the pellets at ambient temperature decreases, but the compressive strength of the pellets after reduction increases. Therefore, the compressive strength of the pellets after reduction exhibits no certain positive correlation with that before reduction. The porosity and pore size of all the pellets （with different MgO contents） increase when the pellets are reduced. However, the increase in porosity of the MgO-fluxed pellets is relatively smaller than that of the traditional non-MgO-fluxed pellets, and the pore size range of the MgO-fluxed pellets is relatively narrower. The reduction swelling index （RSI） is a key factor for governing the compressive strength of the reduced pellets. An approximately reversed linear relation can be concluded that the lower the RSI, the greater the compressive strength of the reduced pellets is.

Gas-solid reduction kinetic model of MgO-fluxed pellets

The reduction process of MgO-fluxed pellets was investigated and compared with traditional acidic pellets in this paper. Based on the piston flow concept and experimental data, a kinetic model fitting for the gas-solid phase reduction of pellets in tubular reactors （blast furnace, BF） was built up, and the equations of reduction reaction rate were given for pellets. A series of reduction experiments of pellets were carried out to verify the model. As a result, the experimental data and calculated result were fitted well. Therefore, this model can well describe the gas-solid phase reduction process and calculate the reduction reaction rate of pellets. Besides, it can give a better explanation that the reduction reaction rate （reducibility） of MgO-fluxed pellets is better than that of traditional acidic pellets in BF.

Effects of Catalyst and Additive Containing Li, Na, or Ca on Reduction of Iron Oxide/Carbon Composite Pellets

The catalyst containing 0.69% (mass fraction) of Li+, Na+, or Ca2+ were synthesized, and the catalytic effect on the reduction of iron oxide/carbon composite pellets were investigated by comparing with that of additive at 850 degreesC. The effect of the catalyst was greater than that of the additive, it can be considered that catalyst promoted the formation of iron nucleus early on reduction processes of iron oxide/carbon composite pellets. In addition, both effects of catalyst and additive increased after added carbon powder into the pellets, but the extent of increase decreased when the carbon powder exceeded a suitable content (about 4%), this amount is less than that of carbon needed theoretically on the reduction from hematite to iron.

Effect of aluminum oxide on the compressive strength of pellets

Analytical-reagent-grade Al2O3 was added to magnetite ore during the process of pelletizing, and the methods of mercury intru-sion, scanning electron microscopy, and image processing were used to investigate the effect of Al2O3 on the compressive strength of the pellets. The results showed that, as the Al2O3 content increased, the compressive strength of the pellets increased slightly and then decreased gradually. When a small amount of Al2O3 was added to the pellets, the Al2O3 combined with fayalite （2FeO＆#183;SiO2） and the aluminosilicate （2FeO＆#183;2Al2O3＆#183;5SiO2） was generated, which releases some iron oxide and reduces the inhibition of fayalite to the solid phase of consolidation. When Al2O3 increased sequentially, high melting point of Al2O3 particles hinder the oxidation of Fe3O4 and the recrystallization of Fe2O3, making the internal porosity of the pellets increase, which leads to the decrease in compressive strength of the pellets.