Micrcostructures of bulk and thin film YBa_2Cu_3O_(7-δ) superconductors were studied by using scanning elec-tron microscopy (SEM). It was confirmed that viscous technique processed bulk YBa_2Cu_3O_(7-δ) has a homoge...Micrcostructures of bulk and thin film YBa_2Cu_3O_(7-δ) superconductors were studied by using scanning elec-tron microscopy (SEM). It was confirmed that viscous technique processed bulk YBa_2Cu_3O_(7-δ) has a homoge-neous microstructure across the pellet diameter. Concerning the thin film, it was found that 2  ̄H ̄+ ion implanta-tion with a dose of 1× 10 ̄(12)cm ̄(-2) at 50 keV does not cause microstructural change of the film at a micrometrelevel. Combined with previous studies by using high resolution transmission electron microscopy, it appearsthat the structural modification is at an atomic scale.展开更多
文摘Micrcostructures of bulk and thin film YBa_2Cu_3O_(7-δ) superconductors were studied by using scanning elec-tron microscopy (SEM). It was confirmed that viscous technique processed bulk YBa_2Cu_3O_(7-δ) has a homoge-neous microstructure across the pellet diameter. Concerning the thin film, it was found that 2  ̄H ̄+ ion implanta-tion with a dose of 1× 10 ̄(12)cm ̄(-2) at 50 keV does not cause microstructural change of the film at a micrometrelevel. Combined with previous studies by using high resolution transmission electron microscopy, it appearsthat the structural modification is at an atomic scale.