Microrolling experiments and uniaxial tensile tests of pure copper under different annealing conditions were carried out in this paper. The effects of grain size and reduction on non-uniform deformation, edge cracking...Microrolling experiments and uniaxial tensile tests of pure copper under different annealing conditions were carried out in this paper. The effects of grain size and reduction on non-uniform deformation, edge cracking, and microstructure were studied. The experimen- tal results showed that the side deformation became more non-uniform, resulting in substantial edge bulge, and the uneven spread increased with increasing grain size and reduction level. When the reduction level reached 80% and the grain size was 65 μm, slight edge cracks occurred. When the grain size was 200 μm, the edge cracks became wider and deeper. No edge cracks occurred when the grain size was 200 μm and the reduction level was less than 60%; edge cracks occurred when the reduction level was increased to 80%. As the reduction level increased, the grains were gradually elongated and appeared as a sheet-like structure along the rolling direction; a fine lamellar structure was obtained when the grain size was 20 lam and the reduction level was less than 60%.展开更多
To explain the reason why work hardening occurs in epoxy adhesive bonded zone of pure copper adherends after tensile shear strength testing, an elasto-plastic finite element model was established to analyze the effect...To explain the reason why work hardening occurs in epoxy adhesive bonded zone of pure copper adherends after tensile shear strength testing, an elasto-plastic finite element model was established to analyze the effect of different adherends thickness of 2mm and 4mm on the shear strength as well as the level of work hardening in copper adherends of single lap joint. The numerical simulation results show that the axial or equivalent stress overrun the yield strength of the pure copper adherend is the main reason why the work hardening occurs on the bonded zone of the adherends after the shear strength testing. The elasto-plastic finite element simulation results are agreed with the experimental ones. The thicker its adherends are, the more serious the work hardening is.展开更多
A continuous wave diode laser with an output power of 2.8 kW was used to join pure copper and 304 stainless steel with a thickness of 1 mm. The focused laser beam with a diameter of O. 8 mm was irradiated on the coppe...A continuous wave diode laser with an output power of 2.8 kW was used to join pure copper and 304 stainless steel with a thickness of 1 mm. The focused laser beam with a diameter of O. 8 mm was irradiated on the copper side of the butt joints. In process of laser welding, effects of processing primary parameters on tensile strength of the joints were investigated. The interfacial characterizations of the joints were investigated by metallographic microscope, scanning electron microscope （SEM） and energy dispersive X-ray spectroscope （EDS）. The results showed that the element diffusion and solution occur and metallurgical bonding was achieved between pure copper and 304 stainless steel. The maximum tensile strength of the joints was 209 MPa when the laser power of welding was 2. 4 kW and welding speed was 12 mm/s.展开更多
In the present study, pure iron/copper composite metal cladding was deposited onto carbon steel by tungsten inert gas welding. The study focused on interfacial morphological, microstructural, and mechanical analyses o...In the present study, pure iron/copper composite metal cladding was deposited onto carbon steel by tungsten inert gas welding. The study focused on interfacial morphological, microstructural, and mechanical analyses of the composite cladding layers. Iron liquid–solid-phase zones were formed at copper/steel and iron interfaces because of the melting of the steel substrate and iron. Iron concentrated in the copper cladding layer was observed to exhibit belt, globule, and dendrite morphologies. The appearance of iron-rich globules indicated the occurrence of liquid phase separation（LPS） prior to solidification, and iron-rich dendrites crystallized without the occurrence of LPS. The maximum microhardness of the iron/steel interface was lower than that of the copper/steel interface because of the diffusion of elemental carbon. All samples fractured in the cladding layers. Because of a relatively lower strength of the copper layer, a short plateau region appeared when shear movement was from copper to iron.展开更多
In a procedure for electrolytic dissolving pure copper and common brasses, the approximate electrochemical mole mass(k) of the sample was determined in accordance with the brand of the sample, a stitable electrolyte w...In a procedure for electrolytic dissolving pure copper and common brasses, the approximate electrochemical mole mass(k) of the sample was determined in accordance with the brand of the sample, a stitable electrolyte was selected to make the current efficiency equal to 100%, and then the dissolved mass of samples was calculated according to Faraday's law(m=klt).Three representative samples were sampled by the electrolytic dissolution method and the calculated dissolved amounts were equal to the values by weighing the anode.The cxperimental results of zinc and copper in the anode liquor are in agreement with certified values.展开更多
基金finically supported by the National Natural Science Foundation of China (No. 51474127)the Chinese Scholar Council (No. 201408210289)the Key Laboratory Open Project of Liaoning Province (USTLKFSY201504)
文摘Microrolling experiments and uniaxial tensile tests of pure copper under different annealing conditions were carried out in this paper. The effects of grain size and reduction on non-uniform deformation, edge cracking, and microstructure were studied. The experimen- tal results showed that the side deformation became more non-uniform, resulting in substantial edge bulge, and the uneven spread increased with increasing grain size and reduction level. When the reduction level reached 80% and the grain size was 65 μm, slight edge cracks occurred. When the grain size was 200 μm, the edge cracks became wider and deeper. No edge cracks occurred when the grain size was 200 μm and the reduction level was less than 60%; edge cracks occurred when the reduction level was increased to 80%. As the reduction level increased, the grains were gradually elongated and appeared as a sheet-like structure along the rolling direction; a fine lamellar structure was obtained when the grain size was 20 lam and the reduction level was less than 60%.
文摘To explain the reason why work hardening occurs in epoxy adhesive bonded zone of pure copper adherends after tensile shear strength testing, an elasto-plastic finite element model was established to analyze the effect of different adherends thickness of 2mm and 4mm on the shear strength as well as the level of work hardening in copper adherends of single lap joint. The numerical simulation results show that the axial or equivalent stress overrun the yield strength of the pure copper adherend is the main reason why the work hardening occurs on the bonded zone of the adherends after the shear strength testing. The elasto-plastic finite element simulation results are agreed with the experimental ones. The thicker its adherends are, the more serious the work hardening is.
文摘A continuous wave diode laser with an output power of 2.8 kW was used to join pure copper and 304 stainless steel with a thickness of 1 mm. The focused laser beam with a diameter of O. 8 mm was irradiated on the copper side of the butt joints. In process of laser welding, effects of processing primary parameters on tensile strength of the joints were investigated. The interfacial characterizations of the joints were investigated by metallographic microscope, scanning electron microscope （SEM） and energy dispersive X-ray spectroscope （EDS）. The results showed that the element diffusion and solution occur and metallurgical bonding was achieved between pure copper and 304 stainless steel. The maximum tensile strength of the joints was 209 MPa when the laser power of welding was 2. 4 kW and welding speed was 12 mm/s.
基金financially supported by the National Natural Science Foundation of China (No. 51575132)
文摘In the present study, pure iron/copper composite metal cladding was deposited onto carbon steel by tungsten inert gas welding. The study focused on interfacial morphological, microstructural, and mechanical analyses of the composite cladding layers. Iron liquid–solid-phase zones were formed at copper/steel and iron interfaces because of the melting of the steel substrate and iron. Iron concentrated in the copper cladding layer was observed to exhibit belt, globule, and dendrite morphologies. The appearance of iron-rich globules indicated the occurrence of liquid phase separation（LPS） prior to solidification, and iron-rich dendrites crystallized without the occurrence of LPS. The maximum microhardness of the iron/steel interface was lower than that of the copper/steel interface because of the diffusion of elemental carbon. All samples fractured in the cladding layers. Because of a relatively lower strength of the copper layer, a short plateau region appeared when shear movement was from copper to iron.
基金The projects was supported by the Pre-research Foundation of the National Basic Research Program (973 Program, grant No. 2004CCA07000)the Science and Technology Committee of Shanghai Municipality (Grant No. 04XD14008).
文摘In a procedure for electrolytic dissolving pure copper and common brasses, the approximate electrochemical mole mass(k) of the sample was determined in accordance with the brand of the sample, a stitable electrolyte was selected to make the current efficiency equal to 100%, and then the dissolved mass of samples was calculated according to Faraday's law(m=klt).Three representative samples were sampled by the electrolytic dissolution method and the calculated dissolved amounts were equal to the values by weighing the anode.The cxperimental results of zinc and copper in the anode liquor are in agreement with certified values.