Solidif ication and f luid f low analysis using computer simulation is a current common practice. There is also a high demand for thermal stress analysis in the casting process because casting engineers want to contro...Solidif ication and f luid f low analysis using computer simulation is a current common practice. There is also a high demand for thermal stress analysis in the casting process because casting engineers want to control the defects related to thermal stresses, such as large deformation and crack generation during casting. The riser system is an essential part of preventing the shrinkage defects in the casting process, and it has a great inf luence on thermal phenomena. The analysis domain is dramatically expanded by attaching the riser system to a casting product due to its large volume, and it makes FEM mesh generation diff icult. However, it is diff icult to study and solve the above proposed problem caused by riser system using traditional analysis methods which use single numerical method such as FEM or FDM. In this paper, some research information is presented on the effects of the riser system on thermal stress analysis using a FDM/FEM hybrid method in the casting process simulation. The results show the optimal conditions for stress analysis of the riser model in order to save computation time and memory resources.展开更多
Different types of polymer films were used in the combined in-mold decoration and microcellular injection molding(IMD/MIM)process.The multiphase fluid-solid coupled heat transfer model was established to study the the...Different types of polymer films were used in the combined in-mold decoration and microcellular injection molding(IMD/MIM)process.The multiphase fluid-solid coupled heat transfer model was established to study the thermal response at the melt filling stage in the IMD/MIM process.It was found that the temperature distributed asymmetrically along the thickness direction due to the changed heat transfer coefficient of the melt on the film side.When polyethylene terephthalate(PET)films were applied,the temperature of the melt-film interface increased faster and to be higher at the end of melt filling stage in comparison with the application of polycarbonate(PC)and thermoplastic polyurethane(TPU)films.And the effects of film types on the cellular structure,forming defects and mechanical properties of IMD/MIM parts were also studied experimentally.The results showed that the film types had no obvious effect on the cells size in the transition layer and the mechanical properties of the parts.Under certain film thickness,the offset distance of core layer was the largest with PET film used,while the offset distance was the smallest with TPU film used.And similar results were found for the warpage of the parts.However,an exactly opposite change occurred for the thickness of film-side transition layer and the bubble marks on the surface of the parts.展开更多
文摘Solidif ication and f luid f low analysis using computer simulation is a current common practice. There is also a high demand for thermal stress analysis in the casting process because casting engineers want to control the defects related to thermal stresses, such as large deformation and crack generation during casting. The riser system is an essential part of preventing the shrinkage defects in the casting process, and it has a great inf luence on thermal phenomena. The analysis domain is dramatically expanded by attaching the riser system to a casting product due to its large volume, and it makes FEM mesh generation diff icult. However, it is diff icult to study and solve the above proposed problem caused by riser system using traditional analysis methods which use single numerical method such as FEM or FDM. In this paper, some research information is presented on the effects of the riser system on thermal stress analysis using a FDM/FEM hybrid method in the casting process simulation. The results show the optimal conditions for stress analysis of the riser model in order to save computation time and memory resources.
基金financially supported by the National Natural Science Foundation of China(Nos.51801141 and 51605356)the 111 Project(No.B17034)+1 种基金the Innovative Research Team Development Program of Ministry of Education of China(No.IRT17R83)the Fundamental Research Funds for the Central Universities(No.WUT:2017IVB035)。
文摘Different types of polymer films were used in the combined in-mold decoration and microcellular injection molding(IMD/MIM)process.The multiphase fluid-solid coupled heat transfer model was established to study the thermal response at the melt filling stage in the IMD/MIM process.It was found that the temperature distributed asymmetrically along the thickness direction due to the changed heat transfer coefficient of the melt on the film side.When polyethylene terephthalate(PET)films were applied,the temperature of the melt-film interface increased faster and to be higher at the end of melt filling stage in comparison with the application of polycarbonate(PC)and thermoplastic polyurethane(TPU)films.And the effects of film types on the cellular structure,forming defects and mechanical properties of IMD/MIM parts were also studied experimentally.The results showed that the film types had no obvious effect on the cells size in the transition layer and the mechanical properties of the parts.Under certain film thickness,the offset distance of core layer was the largest with PET film used,while the offset distance was the smallest with TPU film used.And similar results were found for the warpage of the parts.However,an exactly opposite change occurred for the thickness of film-side transition layer and the bubble marks on the surface of the parts.