Interplay of laser power and pore characteristics in selective laser melting of ZK60 magnesium alloys:A study based on in-situ monitoring and image analysis

This study offers significant insights into the multi-physics phenomena of the SLM process and the subsequent porosity characteristics of ZK60 Magnesium(Mg)alloys.High-speed in-situ monitoring was employed to visualise process signals in real-time,elucidating the dynamics of melt pools and vapour plumes under varying laser power conditions specifically between 40 W and 60 W.Detailed morphological analysis was performed using Scanning-Electron Microscopy(SEM),demonstrating a critical correlation between laser power and pore formation.Lower laser power led to increased pore coverage,whereas a denser structure was observed at higher laser power.This laser power influence on porosity was further confirmed via Optical Microscopy(OM)conducted on both top and cross-sectional surfaces of the samples.An increase in laser power resulted in a decrease in pore coverage and pore size,potentially leading to a denser printed part of Mg alloy.X-ray Computed Tomography(XCT)augmented these findings by providing a 3D volumetric representation of the sample internal structure,revealing an inverse relationship between laser power and overall pore volume.Lower laser power appeared to favour the formation of interconnected pores,while a reduction in interconnected pores and an increase in isolated pores were observed at higher power.The interplay between melt pool size,vapour plume effects,and laser power was found to significantly influence the resulting porosity,indicating a need for effective management of these factors to optimise the SLM process of Mg alloys.

In-situ AFM and quasi-in-situ studies for localized corrosion in Mg-9Al-1Fe-(Gd) alloys under 3.5 wt.% NaCl environment

Revealing the localized corrosion process of Mg alloy is considered as one of the most significant ways for improving its corrosion resistance.The reliable monitor should be high distinguishability and real-time in liquid environment.Herein,Mg-9Al-1Fe and Mg-9Al-1Fe-1Gd alloys were designed to highlight the impact of intermetallic on the corrosion behaviour.In-situ AFM with a special electrolyte circulation system and quasi-in-situ SEM observation were used to monitor the corrosion process of the designed alloys.SEM-EDS and TEM-SAED were applied to identify the intermetallic in the designed alloys,and their volta potentials were measured by SKPFM.According to the real-time and real-space in-situ AFM monitor,the corrosion process consisted of dissolution of anodicα-Mg phase,accumulation of corrosion products around cathodic phase and shedding of some fine cathodic phase.Then,the localized corrosion process of Mg alloy was revealed combined with the results of the monitor of corrosion process and Volta potential difference.

Development and Application of On-Line Corrosion Monitoring Device for Condenser Tube

This paper introduces the development and industrial application of an on-line corrosion monitoring device for condenser tubes. Corrosion sensors are made up of representative condenser tubes chosen by eddy current test, which enable the monitoring result to be consistent with the corrosion of actual condenser tubes. Localized corrosion rate of condenser tubes can be measured indirectly by a galvanic couple made up of tube segments with and without pits. Using this technology, corrosion problems can be found in time and accurately, and anticorrosive measures be made more economic and effective. Applications in two power plants showed the corrosion measurements are fast and accurate.

Technical development of operational in-situ marine monitoring and research on its key generic technologies in China

In China,operational in-situ marine monitoring is the primary means of directly obtaining hydrological,meteorological,and oceanographic environmental parameters across sea areas,and it is essential for applications such as forecast of marine environment,prevention and mitigation of disaster,exploitation of marine resources,marine environmental protection,and management of transportation safety.In this paper,we summarise the composition,development courses,and present operational status of three systems of operational in-situ marine monitoring,namely coastal marine automated network station,ocean data buoy and voluntary observing ship measuring and reporting system.Additionally,we discuss the technical development in these in-situ systems and achievements in the key generic technologies along with future development trends.

Atmospheric Corrosion Monitoring of Field-exposed Q235B and T91 Steels in Zhoushan Offshore Environment Using Electrochemical Probes

This work aimed to in-situ monitor the atmospheric corrosion of steels exposed to Zhoushan offshore environment by using electrochemical noise（EN） technique. A portable EN monitoring system was established and two electrochemical probes（named as Q235 B and T91） were designed. Experimental results indicated that the noise resistance of T91 steel was higher than that of Q235 B steel, revealing that the corrosion resistance of T91 was higher than that of Q235 B. A 60-day monitoring result indicated that the noise resistance was well correlated with the weight loss data. Wavelet analyses results of EN data indicated that Q235 B underwent uniform corrosion and T91 suffered from localized corrosion, which was further confirmed by the surface observation. It is concluded that EN can be used as a new method to identify the corrosion form and corrosion resistance in atmospheric conditions.

Preparation and Properties of Embeddable Ag/Ag Cl Gelling Reference Electrode for Rebars Corrosion Monitoring in Concrete

Reference electrodes are a key part for corrosion monitoring and measurement of rebars in concrete. A reference electrode that can be buried in concrete is fabricated by using Ag/Ag Cl electrode and methyl cellulose gelling electrolyte. The stability, repeatability and anti-polarization of the reference electrode are investigated; the influences of the inner electrolyte loss, exterior OH- contamination, and temperature on the potential of the reference electrode are also investigated in this paper. The results show that the reference electrode has good stability, repeatability, and antipolarization. The influences of inner electrolyte loss, exterior OH- contamination, and temperature on the potential of the reference electrode are minimal. Therefore, it can be used for corrosion monitoring and measurement of rebars in concrete.

Preparation and performance of fluorescent sensing coating for monitoring corrosion of Al alloy 2024

A kind of fluorescent sensing coating was prepared for monitoring corrosion of aluminum alloys by incorporating phenylfluorone(PF) into acrylic paint as sensing material. The fluorescent dye PF reacts with aluminum ions on corroded aluminum substrate to occur fluorescence quenching observed in UV light. This paint system is sensitive to underlying corrosion processes through reacting with the Al3+ produced by anodic reaction accompanying corrosion. After a certain time, when the samples of Al alloy 2024 coated with PF-acrylic paint were immersed in 1 mol/L NaCl solution, fluorescence quenching spots can be seen with unaided eyes. With the development of corrosion process, the size of fluorescence quenching spots increases. Active corrosion areas on the sample surface were found under the fluorescence quenching spots by optical microscope. The corrosion areas can be observed more clearly by SEM, and many pits are found. This suggests that the fluorescence quenching spots are the sites of produced Al3+ by the anodic reaction of the local attack of the coated Al alloy substrate in the chloride solution and the corrosion process of the coated Al alloy can be monitored on-line by the sensing coating. The sensitivity of this coating system for detection of anodic reaction associated with corrosion was determined by applying constant charge current and measuring the charge, at which fluorescence quenching is detected in the coating with unaided eyes. Visual observation of coated samples can detect fluorescence change resulting from a charge corresponding to an equivalent hemispherical pit with approximate depth of 50 μm.

Corrosion monitoring system design for coating wire of steel in ocean

The monitoring system design used in anti-corrosion of coating wire of steel in ocean were concerned. A corrosion monitoring system adapting to corrosion observation of coating wire of steel was introduced in details, including design and choice of software and hardware. This system will play an important role in the collection, procession, demonstration, deposition and accident alarm of corrosion data of oceanic coating wire of steel.

Conductivity Method as a New Monitoring Technique for Corrosion and Corrosion Inhibition Processes of Zinc Metal

The electrical conductivity method was successfully applied as a new monitoring technique to monitor the corrosion and corrosion inhibition processes of zinc metal. Measurements of electrical conductivity at 20.0°C of three different corrosive solutions (HCl, NaOH, and NaCl) were performed with two different concentrations (0.10 and 1.00 M) containing zinc sheets in the absence and presence of four different concentrations of sodium lignosulfonate (1.0, 5.0, 10.0, and 20.0 mM). The analysis of curves that illustrates the changes in electrical conductivity of these solutions provides qualitative information about the strength of corrosion as well as the extent of corrosion inhibition behavior. The results obtained from electrical conductivity measurements revealed that sodium lignosulfonate was an effective corrosion inhibitor in acidic medium (for both 0.10 and 1.00 M HCl) in which it converted into lignosulfonic acid, but was less effective in salt and alkaline media.

Monitoring of the Corrosion on a Steel Sheet-Pile Marine Breakwater by Systematic Thickness Measurements

In Quepos, Pacific of Costa Rica, it was finished on 2010 the first phase of a marina, including two mix breakwaters, with rubble mound （rocks and concrete units）, and 25 circular steel sheet piles cofferdam cells, filled with sand and gravel. The maintenance plan, considers tracking sheet pile corrosion, comparing ＂actual＂ against expected rates, checking structural limits, and programming countermeasures if accelerated corrosion is identified. Specific control sections, along the breakwaters, both inside and outside the basin, were established. In each section, thicknesses were measured every meter from the top of the steel cell to seabed using an ultrasonic equipment, and an underwater transducer. Both land crew, and divers for submerged portions, were used. The measurements campaigns are for several years from 2011 to 2016. Sectors of the breakwater with varied corrosion attack levels could be differentiated. Also, corrosion rates and lifespans were estimated, both general for the structures, and specific for each section and level. In turn, this allowed to identify maintenance priorities, defining sites where measures of corrosion protection should initiate, as well, to have confidence in the structural capacity and safety of the breakwaters.

Monitoring of the Corrosion on a Steel Sheet-pile Marine Breakwater by Systematic Thickness Measurements

In Quepos,Pacific of Costa Rica,it was finished on 2010 the first phase of a marina,including two mix breakwaters,with rubble mound(rocks and concrete units),and 25 circular steel sheet piles cofferdam cells,filled with sand and gravel.The maintenance plan,considers tracking sheet pile corrosion,comparing'actual'against expected rates,checking structural limits,and programming countermeasures if accelerated corrosion is identified.Specific control sections,along the breakwaters,both inside and outside the basin,were established.In each section,thicknesses were measured every meter from the top of the steel cell to seabed using an ultrasonic equipment,and an underwater transducer.Both land crew,and divers for submerged portions,were used.The measurements campaigns are for several years from 2011 to 2016.Sectors of the breakwater with varied corrosion attack levels could be differentiated.Also,corrosion rates and lifespans were estimated,both general for the structures,and specific for each section and level.In turn,this allowed to identify maintenance priorities,defining sites where measures of corrosion protection should initiate,as well,to have confidence in the structural capacity and safety of the breakwaters.

In-situ investigation of atmospheric corrosion behavior of bronze under thin electrolyte layers using electrochemical technique

The atmospheric corrosion behavior of bronze under thin electrolyte layer （TEL） with different thicknesses was monitored using cathodic polarization curves, open circuit potential （OCP） and electrochemical impedance spectroscopy （EIS）. Cathodic polarization result indicates that the cathodic limiting current density increases with decreasing the TEL thickness. EIS result shows that the corrosion rate increases with decreasing the TEL thickness at the initial stage because the corrosion is dominated by the cathodic process, whereas after long immersion time, the corrosion degree with the TEL thickness is in the sequence of 150 μm 〉 310 μm〉 10μm ≈ bulk solution 〉 57 μm. The measurements of OCP and EIS present in-situ electrochemical corrosion information and their results are in good agreement with that of physical characterizations.

Influences of rainfall infiltration on stability of accumulation slope by in-situ monitoring test

In order to improve the understanding of the fundamental mechanism of rainfall infiltration induced landslides in accumulation slope and to clarify some important characteristics of slope performance,artificial rainfall simulation tests and field synthetic monitoring were carried out on a typical accumulation slope of Shangrui Freeway in Guizhou Province,China.The monitoring results show that the most accumulation landslides caused by rainfall infiltration are shallow relaxation failure,whose deformation zone lies within the top 0-4 m soil layer.The deformation of slope gradually reduces from the surface,where the greatest deformation lies in,to the deep part of slope.The average percentage of infiltration during the first 2 h is 86%,and then it reduces gradually with time because of the increase of the surface runoff.The average percentage of infiltration drop to a relatively stable value(50%)after 6 h.Rainfall infiltration causes obvious increase of pore-water pressure,which may result in a reduction of shear strength due to a decrease in effective stress and wetting-induced softening.The double-effect of rainfall infiltration is the main reason of rainfall infiltration induced landslides in accumulation slope.

Piezomagnetic In-situ Stress Monitoring and its Application in the Longmenshan Fault Zone

The relative change of in-situ stress is an inevitable outcome of differential movement among the crust plates. Conversely, changes of in-situ stress can also lead to deformation and instability of crustal rock mass, trigger activity of faults, and induce earthquakes. Hence, monitoring real-time change of in-situ stress is of great significance. Piezomagnetic in-situ stress monitoring has good and longtime applications in large engineering constructions and geoscience study fields in China. In this paper, the new piezomagnetic in-situ stress monitoring system is introduced and it not only has overall improvements in measuring cell＇s structure and property, stressing and orienting way, but also enhances integration and intelligence of control and data transmission system, in general, which greatly promotes installing efficiency of measuring probe and quality of monitoring data. This paper also discusses the responses of new piezomagnetic system in large earthquake events of in-situ stress monitoring station at Qiaoqi of Baoxing and Wenxian of Gansu. The monitoring data reflect adjustments and changes of tectonic stress field at the southwestern segment of and the northern area near the Longmenshan fault zone, which shows that the new system has a good performance and application prospect in the geoscience field. Data of the Qiaoqi stress-monitoring station manifest that the Lushan Earthquake did not release stress of the southwestern segment of the Longmenshan fault zone adequately and there still probably exists seismic risk in this region in the future. Combined with absolute in-situ stress measurement, carrying out long-term in-situ stress monitoring in typical tectonic position of important regions is of great importance for researchers to assess and study regional crust stability.

Mechanical strength and corrosion resistance of Al-additive friction stir welded AZ31B joints

Compared to other structural alloys,magnesium alloys have a relatively poor corrosion resistance and low mechanical strength,which can be further deteriorated when these alloys are subjected to joining processes using the existing joining methods.Herein,we propose for the first time an additive friction stir-welding(AFSW)using fine Al powder as an additive to improve the mechanical strength as well as corrosion resistance of AZ31B weld joints.AFSW is a solid-state welding method of forming a high-Al AZ31B joint via an in-situ reaction between pure Al powders filled in a machined groove and the AZ31B matrix.To optimize the process parameters,AFSW was performed under different rotational and transverse speeds,and number of passes,using tools with a square or screw pin.In particular,to fabricate a weld zone,where the Al was homogenously dispersed,the effects of the groove shape were investigated using three types of grooves:surface one-line groove,surface-symmetric grooves,and inserted symmetric grooves.The homogenous and defect-less AFS-welded AZ31B joint was successfully fabricated with the following optimal parameters:1400 rpm,25 mm/min,four passes,inserted symmetric grooves,and the tool with a square pin.The AFSW fully dissolved the additive Al intoα-Mg and in-situ precipitated Mg_(17)Al_(12)particles,which was confirmed via scanning electron microscopy,transmission electron microscope,and X-ray diffraction analyses.The microhardness,joint efficiency,and elongation at the fracture point of the AFS-welded AZ31B joint were 80 HV,101%,and 8.9%,respectively.These values are higher than those obtained for the FS-welded AZ31 joint in previous studies.The corrosion resistance of the AFS-welded AZ31B joint,evaluated via hydrogen evolution measurements and potentiodynamic polarization tests,was enhanced to 55%relative to the FS-welded AZ31B joint.

Design and feasibility analysis of a new completion monitoring technical scheme for natural gas hydrate production tests

As a prerequisite and a guarantee for safe and efficient natural gas hydrates(NGHs)exploitation,it is imperative to effectively determine the mechanical properties of NGHs reservoirs and clarify the law of the change in the mechanical properties with the dissociation of NGHs during NGHs production tests by depressurization.Based on the development of Japan’s two offshore NGHs production tests in vertical wells,this study innovatively proposed a new subsea communication technology-accurate directional connection using a wet-mate connector.This helps to overcome the technical barrier to the communication between the upper and lower completion of offshore wells.Using this new communication technology,this study explored and designed a mechanical monitoring scheme for lower completion(sand screens).This scheme can be used to monitor the tensile stress and radial compressive stress of sand screens caused by NGHs reservoirs in real time,thus promoting the technical development for the rapid assessment and real-time feedback of the in-situ mechanical response of NGHs reservoirs during offshore NGHs production tests by depressurization.

Studies on the Construction Parameter of an Artificial Occluded Cell for In-situ Inspection of the Propagation Rate of Localized Corrosion

An artificial localized corrosion system is assembled and some parameters related to the localized corrosion in active dissolution state (i.e., non-passive state) have been studied. The results showed that the developed electrochemical system can satisfactorily imitate a naturally formed localized corrosion and the coupling current can indicate the maximum localized propagating rate. In this artificial system, the anodic dissolution reaction followed the auto-catalytic mechanism. The localized corrosion current density was dependent on the area ratio R of the cathode to the occluded anode. While R was equal to or more than 6, the coupling current reached at a maximum value and did not alter with the increase in R-value. Therefore, R=7 is chosen as one of these optimum parameters used in constructing the system, with which the biggest galvanic current might be obtained. In contrast, the thickness of the polymer filler separating the occluded anode area from the bulk electrolyte solution and the volume of the occluded anode area did not affect the corrosion current obviously. They might affect the response time to approach a steady state.

Comparative investigation on copper atmospheric corrosion by electrochemical impedance and electrical resistance sensors

Electrochemical impedance(EIS)and thin electrical resistance(ER)sensors were invented for atmospheric corrosion measurement of copper(Cu)during cyclic wetting−drying/high−low temperature tests and field exposure tests.Three-month field exposure results showed that average corrosion rate of Cu measured by ER sensor was well in accordance with that by weight loss method.During cyclic wetting−drying test,EIS was proven to reflect sensitively time of wetting and drying on the surface of sensor.Although corrosion rate obtained from EIS had a similar tendency to that obtained from ER sensors,the former was more dependent on environmental humidity than the latter.When relative humidity was low than 60%,corrosion rate of Cu measured by EIS was much lower than that by weight loss method,mainly attributing to the fact that impedance sensor failed to detect corrosion current of interlaced Cu electrodes due to the breakdown of conductive passage composed of absorbed thin liquid film under low humidity condition.Promisingly,ER sensor was proven to be more suitable for atmospheric corrosion monitoring than electrochemical techniques because it could sensitively monitor thickness loss of Cu foil according to the Ohmic law,no matter how dry or wet the sensor surface is.

Non-contact and full-field online monitoring of curing temperature during the in-situ heating process based on deep learning

Online monitoring of the curing temperature field is essential to improving the quality and efficiency of the manufacturing process of composite parts.Traditional embedded sensor-based technologies have difficulty monitoring the full temperature field or have to introduce heterogeneous items that could have an undesired impact on the part.In this paper,a non-contact,full-field monitoring method based on deep learning that predicts the internal temperature field of composite parts in real time using surface temperature measurements of auxiliary materials is proposed.Using the proposed method,an average temperature monitoring accuracy of 97%is achieved in various heating patterns.In addition,this method also demonstrates satisfying feasibility when a stronger thermal barrier covers the part.This method was experimentally validated during the self-resistance electric heating process,in which the monitoring accuracy reached 93.1%.This method can potentially be applied to automated manufacturing and process control in the composites industry.

Microstructure, mechanical and corrosion properties of magnesium alloy bone plate treated by high-energy shot peening

To enhance the mechanical properties and corrosion resistance of magnesium alloys,high-energy shot peening(HESP)was used.According to the results,the in-situ surface nanocrystallization(ISNC)microstructure was fabricated on the magnesium alloy surface,and its formation mechanism was the coordination among twins,dislocations,subgrain boundary formation and dynamic recrystallization.Under the released surface stress of sample,the residual compressive stress and microhardness rose,thus enhancing compactness of the surface passivation film Mg(OH)2.Besides,the corrosion rate dropped by 29.2% in maximum.In the polarization curve,the maximum positive shift of the corrosion potential of sample was 203 mV, and the corrosion current density decreased by 31.25% in maximum.Moreover,the compression resistance and bending resistance of the bone plate were enhanced,and the maximum improvement rates were 18.2% and 23.1%,respectively.Accordingly,HESP significantly enhanced mechanical properties and corrosion resistance of magnesium alloys.