The fabrication of Fe2O3-MnO2-Co2O3-CuO system ceramics, and the composite system ceramics of transitional metal oxides-cordierite and transitional metal oxides-kaolinit are presented in this work. The research was ca...The fabrication of Fe2O3-MnO2-Co2O3-CuO system ceramics, and the composite system ceramics of transitional metal oxides-cordierite and transitional metal oxides-kaolinit are presented in this work. The research was carried out with the main attention to the infrared emissivity in the band of 8 similar to 14 mu m at room temperature, the microstructure of the ceramics and the relation between them. High infrared emissivities exceeding 0.9 in the band of 8 similar to 14 mu m at room temperature were gained in the transitional metal oxide ceramics and the composite system ceramics. It is suggested that the formation of inverse spinels and partially inverse spinels, such as Fe3O4, CoFe2O4, CuFe2O4 and CuMn2O4, is beneficial to the enhancement of the infrared emissivity of the transitional metal oxide ceramics. The transitional metal oxides play an important role in determining the infrared emissivity of the composite system ceramics.展开更多
Nowadays,it is a great challenge to reduce energy consumption and exhaust emission for human activities,in particular,high temperature industries.Among many efforts made to realize energy savings for high temperature ...Nowadays,it is a great challenge to reduce energy consumption and exhaust emission for human activities,in particular,high temperature industries.Among many efforts made to realize energy savings for high temperature furnaces and kilns,the use of high emissivity materials is considered to be an effective route to increase their thermal efficiency by enhancing heat transfer.Most materials with high refractoriness and superior chemical stability have weak infrared absorption and radiation properties;however,their emissivity in infrared regions（1 —25 μm） could be effectively increased by ion doping.This is attributed to three main mechanisms：1） distortion of the crystal lattice;2） increase of free carrier absorption; 3） formation of impurity energy level.In this paper,the development and advancement of various material systems with high emissivity including non-oxides and oxide based ceramics were reviewed.It is also suggested that the establishment of evaluation models or instruments for energy savings would be beneficial to design and application of high emissivity materials in various high-temperature environment.Furthermore,more efforts should be made on durability of high emissivity materials at high service temperatures and on the standardization of testing methods for emissivity.展开更多
A kind of far infrared radiation ceramics was prepared by using silicate minerals, calcium carbonate and silicon dioxide as main raw materials, and cerium nitrate as additive. The structure of the ceramics and far inf...A kind of far infrared radiation ceramics was prepared by using silicate minerals, calcium carbonate and silicon dioxide as main raw materials, and cerium nitrate as additive. The structure of the ceramics and far infrared radiation properties on the surface tension of water were characterized by X-ray diffraction, scanning electron microscopy, Fourier transform infrared spectroscopy and a tensiometer, respectively. It was showed that, after being sintered at 1160 ℃, the solid solution was formed by CeO2 and Fe2O3, thus the crystal parameters （c/a axis ratio） and interplanar spacing of Fe2O3 increased. The addition of cerium was regarded to improve the far infrared radiation of ceramics, and the maximum emissivity value in the range of 5-20 μm was 0.94. The surface tension of water gradually decreased with increasing radiation time.展开更多
In the present work, hybrid sintering technique which couples the resistive heating and microwave heating is employed to sinter infrared transparent La0.15Y1.85O3 to 99.2% of the theoretical density for the first time...In the present work, hybrid sintering technique which couples the resistive heating and microwave heating is employed to sinter infrared transparent La0.15Y1.85O3 to 99.2% of the theoretical density for the first time to the best of our knowledge. The presence of La3+ in the yttria matrix improves the hardness properties to a greater extent without affecting the transmittance properties, but there is a deterioration in the thermal properties of the sample. So we have limited our studies to La0.15Y1.85O3 which shows better optical, thermal, and hardness properties. The pellets fabricated from the ultra-fine nano powder with average particle size of ~12 nm synthesized by combustion technique and sintered at 1430 ℃ with an average grain size of 0.22 μm show ~80.1% transmittance in the UV–visible region and 81% in mid infrared region. For a comparative study of the optical, mechanical, and thermal properties, two other variants of sintering strategies namely conventional sintering and microwave sintering are also employed. A comprehensive analysis on the hardness reveals that the hardness of the pellets sintered via hybrid heating is 9.73 GPa and is superior to the pellets sintered using the other two techniques. The thermal conductivity of the sample is also analyzed in detail. The results clearly indicate that the La0.15Y1.85O3 ultra-fine nano powder synthesised by the single-step combustion method and sintered via microwave hybrid heating shows better transmittance properties without compromising the mechanical properties, and can be used very effectively for the fabrication of infrared transparent windows and domes.展开更多
基金The research is supported by the Foundation for Excellent Youth of Wuhan Science and Technology Commission and Opening Foundation of Stae Key Laboratory of Advanced Technology for Materials Synthesis and Process of Wuhan University of Technology.
文摘The fabrication of Fe2O3-MnO2-Co2O3-CuO system ceramics, and the composite system ceramics of transitional metal oxides-cordierite and transitional metal oxides-kaolinit are presented in this work. The research was carried out with the main attention to the infrared emissivity in the band of 8 similar to 14 mu m at room temperature, the microstructure of the ceramics and the relation between them. High infrared emissivities exceeding 0.9 in the band of 8 similar to 14 mu m at room temperature were gained in the transitional metal oxide ceramics and the composite system ceramics. It is suggested that the formation of inverse spinels and partially inverse spinels, such as Fe3O4, CoFe2O4, CuFe2O4 and CuMn2O4, is beneficial to the enhancement of the infrared emissivity of the transitional metal oxide ceramics. The transitional metal oxides play an important role in determining the infrared emissivity of the composite system ceramics.
基金Natural Science Foundation of China ( NSFC,Grant no. 51372255 )Beijing Natural Science Foundation ( BNSF,Grant no. 2131006 )+2 种基金International Science and Technology Cooperation Program of China ( Grant no. 2014DFR51010)External Cooperation Program of Chinese Academy of Sciences ( Grant no. GJHZ201310 )Open Foundation of State Key Laboratory of Advanced Refractories ( Grant no. 201401,Sinosteel Luoyang Institute of Refractories Research Co. ,Ltd. ) for the financial support
文摘Nowadays,it is a great challenge to reduce energy consumption and exhaust emission for human activities,in particular,high temperature industries.Among many efforts made to realize energy savings for high temperature furnaces and kilns,the use of high emissivity materials is considered to be an effective route to increase their thermal efficiency by enhancing heat transfer.Most materials with high refractoriness and superior chemical stability have weak infrared absorption and radiation properties;however,their emissivity in infrared regions（1 —25 μm） could be effectively increased by ion doping.This is attributed to three main mechanisms：1） distortion of the crystal lattice;2） increase of free carrier absorption; 3） formation of impurity energy level.In this paper,the development and advancement of various material systems with high emissivity including non-oxides and oxide based ceramics were reviewed.It is also suggested that the establishment of evaluation models or instruments for energy savings would be beneficial to design and application of high emissivity materials in various high-temperature environment.Furthermore,more efforts should be made on durability of high emissivity materials at high service temperatures and on the standardization of testing methods for emissivity.
基金Project supported by the National Key Technology R&D Program(2011BAE30B04)University Innovation Team Leader Training Program in Hebei Province(LJRC020)
文摘A kind of far infrared radiation ceramics was prepared by using silicate minerals, calcium carbonate and silicon dioxide as main raw materials, and cerium nitrate as additive. The structure of the ceramics and far infrared radiation properties on the surface tension of water were characterized by X-ray diffraction, scanning electron microscopy, Fourier transform infrared spectroscopy and a tensiometer, respectively. It was showed that, after being sintered at 1160 ℃, the solid solution was formed by CeO2 and Fe2O3, thus the crystal parameters （c/a axis ratio） and interplanar spacing of Fe2O3 increased. The addition of cerium was regarded to improve the far infrared radiation of ceramics, and the maximum emissivity value in the range of 5-20 μm was 0.94. The surface tension of water gradually decreased with increasing radiation time.
文摘In the present work, hybrid sintering technique which couples the resistive heating and microwave heating is employed to sinter infrared transparent La0.15Y1.85O3 to 99.2% of the theoretical density for the first time to the best of our knowledge. The presence of La3+ in the yttria matrix improves the hardness properties to a greater extent without affecting the transmittance properties, but there is a deterioration in the thermal properties of the sample. So we have limited our studies to La0.15Y1.85O3 which shows better optical, thermal, and hardness properties. The pellets fabricated from the ultra-fine nano powder with average particle size of ~12 nm synthesized by combustion technique and sintered at 1430 ℃ with an average grain size of 0.22 μm show ~80.1% transmittance in the UV–visible region and 81% in mid infrared region. For a comparative study of the optical, mechanical, and thermal properties, two other variants of sintering strategies namely conventional sintering and microwave sintering are also employed. A comprehensive analysis on the hardness reveals that the hardness of the pellets sintered via hybrid heating is 9.73 GPa and is superior to the pellets sintered using the other two techniques. The thermal conductivity of the sample is also analyzed in detail. The results clearly indicate that the La0.15Y1.85O3 ultra-fine nano powder synthesised by the single-step combustion method and sintered via microwave hybrid heating shows better transmittance properties without compromising the mechanical properties, and can be used very effectively for the fabrication of infrared transparent windows and domes.