To improve the mechanical properties of AZ91D magnesium alloy,the submicrocrystal Al-Ti-B master alloy was prepared with copper mold inject casting method,and the influence of submicrocrystal Al-Ti-B master alloy on t...To improve the mechanical properties of AZ91D magnesium alloy,the submicrocrystal Al-Ti-B master alloy was prepared with copper mold inject casting method,and the influence of submicrocrystal Al-Ti-B master alloy on the microstructure and mechanical properties of AZ91D was investigated.Results show that,the distribution of Ti B_2 phase in submicrocrystal Al-Ti-B alloy is even and disperse,and the average size of Ti Al_3 phase is reduced from 10-30μm to～1μm.The properties of AZ91D refined with submicrocrystal Al-Ti-B master alloy are better than that with coarse-grained Al-Ti-B master alloy without copper mold inject casting.The tensile strength,elongation and Brinell hardness of AZ91D are increased by 10.6%,25%and 18.1%,respectively.Therefore,refinement of AZ91D with submicrocrystal Al-Ti-B that is obtained by copper mold inject casting is an effective method to improve its mechanical properties.展开更多
基金financially supported by the Science and Technology Research Project for Colleges and Universities of Hebei Province(ZD2014040)the Natural Science Foundation of Hebei Province(E2016202406)
文摘To improve the mechanical properties of AZ91D magnesium alloy,the submicrocrystal Al-Ti-B master alloy was prepared with copper mold inject casting method,and the influence of submicrocrystal Al-Ti-B master alloy on the microstructure and mechanical properties of AZ91D was investigated.Results show that,the distribution of Ti B_2 phase in submicrocrystal Al-Ti-B alloy is even and disperse,and the average size of Ti Al_3 phase is reduced from 10-30μm to～1μm.The properties of AZ91D refined with submicrocrystal Al-Ti-B master alloy are better than that with coarse-grained Al-Ti-B master alloy without copper mold inject casting.The tensile strength,elongation and Brinell hardness of AZ91D are increased by 10.6%,25%and 18.1%,respectively.Therefore,refinement of AZ91D with submicrocrystal Al-Ti-B that is obtained by copper mold inject casting is an effective method to improve its mechanical properties.