Polypyrrole(PPy)is wildly used as electrode material in supercapacitors due to its high conductivity,low cost,ease of handling,and ease of fabrication.However,limited capacitance and poor cycling stability hinder its ...Polypyrrole(PPy)is wildly used as electrode material in supercapacitors due to its high conductivity,low cost,ease of handling,and ease of fabrication.However,limited capacitance and poor cycling stability hinder its practical application.After developing carboxylated cellulose nanocrystals(CNC-COO^(-))as immobile dopants for PPy to improve its cycling stability,we investigated the effect of different commonly used salts(KCl,NaCl,KBr,and NaClO_(4))as dopants during electrode fabrication by electropolymerization.The film’s capacitance increased from 160.6 to 183.4 F g^(-1)after adding a combination of KCl and NaClO_(4) into the electrodeposition electrolyte.More importantly,the porous and interconnected PPy/CNC-COO^(-)-Cl-(Cl O_(4)^(-))_0.5 electrode film exhibited an excellent capacitance of 125.0 F g^(-1)(0.78 F cm^(-2))at a high current density of 2.0 Ag^(-1)(20 m A cm^(-2),allowing charging in less than 1 min),increasing almost 204%over PPy/CNC-COO-films.A symmetric PPy/CNC-COO^(-)-Cl-(ClO_(4)^(-))_0.5 supercapacitor retained its full capacitance after 5000 cycles,and displayed a high energy density of 5.2 Wh kg^(-1)at a power density of 25.4 W kg^(-1)(34.5μWh cm^(-2) at 1752.3μW cm^(-2)).These results reveal that the porous structure formed by doping with CNC-COO-and inorganic salts opens up more active reaction areas to store charges in PPy-based films as the stiff and ribbon-like CNC-COO-as permanent dopants improve the strength and stability of PPy-based films.Our demonstration provides a simple and practical way to deposit PPy based supercapacitors with high capacitance,fast charging,and excellent cycling stability.展开更多
In this study,to better understand the reaction mechanism between inorganic salts and nitrocellulose,CaCO_(3) and Li_(2)CO_(3) were evaluated with respect to their effects on the thermal degradation of NC in nitrogen ...In this study,to better understand the reaction mechanism between inorganic salts and nitrocellulose,CaCO_(3) and Li_(2)CO_(3) were evaluated with respect to their effects on the thermal degradation of NC in nitrogen atmosphere using TG/DSC at three different heating rates(2,5,10 K/min).The numerical relationship between activation energy(E)and conversion rate was obtained by FWO and KAS method,and it was discovered that CaCO_(3) could improve the thermal stability of NC.Activation energy values were calculated by Kissinger method,and it was found that NC that contain Li2CO3had the highest activation energy while NC containing CaCO3had the lowest E value.By combining the thermal analysis data with Malek method,the most probable mechanism model of thermal degradation is obtained as Sesták-Berggren model,which expression is f(α)=α^(m)(1-α)^(n).As a result of this study,there are certain guiding principles that can be applied to the pyrolysis reaction model and to the actual production process of nitrocellulose.展开更多
Static experiments and dynamic displacement experiments were conducted to quantitatively determine the amount of precipitate generated by the CO_(2)-formation water reaction at different temperatures,pressures,and sca...Static experiments and dynamic displacement experiments were conducted to quantitatively determine the amount of precipitate generated by the CO_(2)-formation water reaction at different temperatures,pressures,and scaling ion concentrations during CO_(2) flooding in the Chang 8 block of Changqing Oilfield,the influence of precipitate on the physical properties of reservoirs was investigated,and the corresponding mathematical characterization model was established.The mathematical characterization equation was used to correct the numerical simulation model of E300 module in Eclipse software.The distribution pattern of inorganic salt precipitates during continuous CO_(2) flooding in Chang 8 block was simulated,and the influence of inorganic salt precipitates on oil recovery was predicted.The inorganic salt precipitate generated during CO_(2)-formation water reaction was mainly CaCO_(3),and the pressure difference and scaling ion concentration were proportional to the amount of precipitate generated,while the temperature was inversely proportional to the amount of precipitate.The rate of core porosity change before and after CO_(2) flooding was positively correlated with temperature and flooding pressure difference.The core porosity increase in the CO_(2)-formation water-core reaction experiment was always lower than that of CO_(2)-distilled water-core reaction experiment because of precipitation.The area around the production wells had the most precipitates generated with the injection of CO_(2).The oil field became poor in development because of the widely distributed precipitate and the recovery decreased to 33.45% from 37.64% after 20-year-CO_(2) flooding when considering of precipitation.展开更多
Removal of water contained in extra-viscous crude oil is quite difficult because of the high viscosity and high resins content of heavy oil.The microwave technology was introduced for the separation of water from high...Removal of water contained in extra-viscous crude oil is quite difficult because of the high viscosity and high resins content of heavy oil.The microwave technology was introduced for the separation of water from high-viscosity crude oil in the presence of sodium acetate.The decrease in zeta-potential of interface and the viscosity of crude oil are responsible for the accelerated separation of water under microwave irradiation.The influences of the concentration of sodium acetate in sample,irradiation pressure,irradiation time and irradiation power on the separation efficiency were investigated.The optimum technological condition for the refining process was determined.Upon treating the sample 1 (with a water concentration of 50%),the water removal rate was 98.44%,when the optimum conditions were identified to be a sodium acetate concentration of 2%,an irradiation pressure of 0.1 MPa,an irradiation time of 2 min,and an irradiation power of 225 W,with the recovery of sodium acetate reaching 97.88%.Upon treating the sample 2 (the concentration of water was 20%),the water removal rate was 93.85%,when the optimum conditions were determined to be a sodium acetate concentration of 3%,an irradiation pressure of 0.1 MPa,an irradiation time of 4 min,and an irradiation power of 375 W,with the recovery of sodium acetate reaching 93.54%.By using this method,the dehydration efficiency was increased rapidly.展开更多
The article is focused on the influence of inorganic salts on the adsorption of cationically modified starch to fibers. Results show that low concentrations of inorganic salts usually affect the process of adsorption ...The article is focused on the influence of inorganic salts on the adsorption of cationically modified starch to fibers. Results show that low concentrations of inorganic salts usually affect the process of adsorption in a positive way. Adsorption efficiency at higher concentrations, however, depends on the type of inorganic salts as well as the sequence of adding inorganic salts and starch to paper suspension.展开更多
The influence of salts on concrete durability,pore structure of cement pastes with inorganic salts,including CaCl2,NaCl,Na2SO4,NaNO2,Ca(NO3)2 and Ca(NO2)2,was studied through mercury intrusion porosimetry (MIP),and hy...The influence of salts on concrete durability,pore structure of cement pastes with inorganic salts,including CaCl2,NaCl,Na2SO4,NaNO2,Ca(NO3)2 and Ca(NO2)2,was studied through mercury intrusion porosimetry (MIP),and hydration degree of each paste was also tested.The results show that porosity of the paste with inorganic salt cured for 3 d or 28 d was related with its hydration degree.For the pore size distribution,the pores smaller than 50 nm in paste with salts cured for 3 d increased;the amount of pores larger than 100 nm increased because of the addition of Ca (NO3)2 at 3 d,but these coarse pores turned into fine pores and reduced significantly at 28 d;coarse pores lager than 1000 nm in cement pastes containing NaCl and Na2SO4 increased.展开更多
基金supported by the Research Foundation Flanders(grant 3E181170)supported by the China Scholarship Council(CSC,201806220066)。
文摘Polypyrrole(PPy)is wildly used as electrode material in supercapacitors due to its high conductivity,low cost,ease of handling,and ease of fabrication.However,limited capacitance and poor cycling stability hinder its practical application.After developing carboxylated cellulose nanocrystals(CNC-COO^(-))as immobile dopants for PPy to improve its cycling stability,we investigated the effect of different commonly used salts(KCl,NaCl,KBr,and NaClO_(4))as dopants during electrode fabrication by electropolymerization.The film’s capacitance increased from 160.6 to 183.4 F g^(-1)after adding a combination of KCl and NaClO_(4) into the electrodeposition electrolyte.More importantly,the porous and interconnected PPy/CNC-COO^(-)-Cl-(Cl O_(4)^(-))_0.5 electrode film exhibited an excellent capacitance of 125.0 F g^(-1)(0.78 F cm^(-2))at a high current density of 2.0 Ag^(-1)(20 m A cm^(-2),allowing charging in less than 1 min),increasing almost 204%over PPy/CNC-COO-films.A symmetric PPy/CNC-COO^(-)-Cl-(ClO_(4)^(-))_0.5 supercapacitor retained its full capacitance after 5000 cycles,and displayed a high energy density of 5.2 Wh kg^(-1)at a power density of 25.4 W kg^(-1)(34.5μWh cm^(-2) at 1752.3μW cm^(-2)).These results reveal that the porous structure formed by doping with CNC-COO-and inorganic salts opens up more active reaction areas to store charges in PPy-based films as the stiff and ribbon-like CNC-COO-as permanent dopants improve the strength and stability of PPy-based films.Our demonstration provides a simple and practical way to deposit PPy based supercapacitors with high capacitance,fast charging,and excellent cycling stability.
基金the National Natural Science Foundation of China(NSFC,Grants No.52176114 and 52111530091)Jiangsu Funding Program for Excellent Postdoctoral Talent。
文摘In this study,to better understand the reaction mechanism between inorganic salts and nitrocellulose,CaCO_(3) and Li_(2)CO_(3) were evaluated with respect to their effects on the thermal degradation of NC in nitrogen atmosphere using TG/DSC at three different heating rates(2,5,10 K/min).The numerical relationship between activation energy(E)and conversion rate was obtained by FWO and KAS method,and it was discovered that CaCO_(3) could improve the thermal stability of NC.Activation energy values were calculated by Kissinger method,and it was found that NC that contain Li2CO3had the highest activation energy while NC containing CaCO3had the lowest E value.By combining the thermal analysis data with Malek method,the most probable mechanism model of thermal degradation is obtained as Sesták-Berggren model,which expression is f(α)=α^(m)(1-α)^(n).As a result of this study,there are certain guiding principles that can be applied to the pyrolysis reaction model and to the actual production process of nitrocellulose.
文摘Static experiments and dynamic displacement experiments were conducted to quantitatively determine the amount of precipitate generated by the CO_(2)-formation water reaction at different temperatures,pressures,and scaling ion concentrations during CO_(2) flooding in the Chang 8 block of Changqing Oilfield,the influence of precipitate on the physical properties of reservoirs was investigated,and the corresponding mathematical characterization model was established.The mathematical characterization equation was used to correct the numerical simulation model of E300 module in Eclipse software.The distribution pattern of inorganic salt precipitates during continuous CO_(2) flooding in Chang 8 block was simulated,and the influence of inorganic salt precipitates on oil recovery was predicted.The inorganic salt precipitate generated during CO_(2)-formation water reaction was mainly CaCO_(3),and the pressure difference and scaling ion concentration were proportional to the amount of precipitate generated,while the temperature was inversely proportional to the amount of precipitate.The rate of core porosity change before and after CO_(2) flooding was positively correlated with temperature and flooding pressure difference.The core porosity increase in the CO_(2)-formation water-core reaction experiment was always lower than that of CO_(2)-distilled water-core reaction experiment because of precipitation.The area around the production wells had the most precipitates generated with the injection of CO_(2).The oil field became poor in development because of the widely distributed precipitate and the recovery decreased to 33.45% from 37.64% after 20-year-CO_(2) flooding when considering of precipitation.
基金the financial support of Liaoning Province Education Department Project(2004D06)
文摘Removal of water contained in extra-viscous crude oil is quite difficult because of the high viscosity and high resins content of heavy oil.The microwave technology was introduced for the separation of water from high-viscosity crude oil in the presence of sodium acetate.The decrease in zeta-potential of interface and the viscosity of crude oil are responsible for the accelerated separation of water under microwave irradiation.The influences of the concentration of sodium acetate in sample,irradiation pressure,irradiation time and irradiation power on the separation efficiency were investigated.The optimum technological condition for the refining process was determined.Upon treating the sample 1 (with a water concentration of 50%),the water removal rate was 98.44%,when the optimum conditions were identified to be a sodium acetate concentration of 2%,an irradiation pressure of 0.1 MPa,an irradiation time of 2 min,and an irradiation power of 225 W,with the recovery of sodium acetate reaching 97.88%.Upon treating the sample 2 (the concentration of water was 20%),the water removal rate was 93.85%,when the optimum conditions were determined to be a sodium acetate concentration of 3%,an irradiation pressure of 0.1 MPa,an irradiation time of 4 min,and an irradiation power of 375 W,with the recovery of sodium acetate reaching 93.54%.By using this method,the dehydration efficiency was increased rapidly.
文摘The article is focused on the influence of inorganic salts on the adsorption of cationically modified starch to fibers. Results show that low concentrations of inorganic salts usually affect the process of adsorption in a positive way. Adsorption efficiency at higher concentrations, however, depends on the type of inorganic salts as well as the sequence of adding inorganic salts and starch to paper suspension.
文摘The influence of salts on concrete durability,pore structure of cement pastes with inorganic salts,including CaCl2,NaCl,Na2SO4,NaNO2,Ca(NO3)2 and Ca(NO2)2,was studied through mercury intrusion porosimetry (MIP),and hydration degree of each paste was also tested.The results show that porosity of the paste with inorganic salt cured for 3 d or 28 d was related with its hydration degree.For the pore size distribution,the pores smaller than 50 nm in paste with salts cured for 3 d increased;the amount of pores larger than 100 nm increased because of the addition of Ca (NO3)2 at 3 d,but these coarse pores turned into fine pores and reduced significantly at 28 d;coarse pores lager than 1000 nm in cement pastes containing NaCl and Na2SO4 increased.