Effects of Al_(2)O_(3)-SiO_(2) Raw Material Types on Properties of Anorthite Based Insulation Refractories

To optimize their Al_(2)O_(3)-SiO_(2) raw materials,anorthite based insulation refractories were prepared by the in-situ sintering process combined with the foaming method after sintering at 1350℃for 3 h,using green and pollution-free kaolin,kyanite,andalusite and sillimanite as Al_(2)O_(3)-SiO_(2) raw materials,respectively,and industrial CaCO_(3) as the CaO source.Effects of Al_(2)O_(3)-SiO_(2) raw material types on the physical properties,phase composition and microstructure were investigated.The results are as follows.All samples prepared by different Al_(2)O_(3)-SiO_(2) raw materials have hexagonal flake anorthite and a small amount of mullite and corundum.Their bulk density and thermal conductivity decrease in the order of using kaolin,andalusite,kyanite and sillimanite as the Al_(2)O_(3)-SiO_(2) raw material,but their apparent porosity increases.Moreover,in the sample with kaolin,the bonding between anorthite crystals on the pore walls is closer than that of the other samples,which is conducive to increasing the cold crushing strength.The bonding between anorthite crystals on pore walls gradually decreases in the order of using kyanite,andalusite and sillimanite as the Al_(2)O_(3)-SiO_(2) raw material,thus their cold crushing strength decreases accordingly.In comprehensive consideration,the properties of the sample from kyanite are the optimal.Its apparent porosity,thermal conductivity and cold crushing strength are 84.6%,0.141 W·m^(-1)·K^(-1) and 1.89 MPa,respectively.

Thermal Insulation Materials of Alumina Based Porous Ceramics

Significant energy saving effects can be made through the improvement of furnace refractories,especially the thermal insulation refractories. In this study,the preparation and the application of different alumina based porous ceramics were briefly introduced. Alumina based porous ceramics were prepared combined foaming method with gelcasting,sol- gel process or cement curing process. The influences of different preparation methods on the sintering shrinkage, porosity, phase composition, microstructure, compressive strength and thermal conductivity were discussed. Alumina based porous ceramics with relatively high strength and low thermal conductivity could be obtained through the above mentioned methods. Compared with the traditional lining materials,about 40% energy could be saved when they were used as the furnace wall.

Soliton mode-locked fiber laser based on topological insulator Bi2Te3 nanosheets at 2 μm

We reported diverse soliton operations in a thulium/holmium-doped fiber laser by taking advantage of a tapered fiber-based topological insulator（TI） Bi2Te3 saturable absorber（SA）.The SA had a nonsaturable loss of 53.5% and a modulation depth of 9.8%.Stable fundamentally mode-locked solitons at 1909.5 nm with distinct Kelly sidebands on the output spectrum,a pulse repetition rate of 21.5 MHz,and a measured pulse width of 1.26 ps were observed in the work.By increasing the pump power,both bunched solitons with soliton number up to 15 and harmonically mode-locked solitons with harmonic order up to 10 were obtained.To our knowledge,this is the first report of both bunched solitons and harmonically mode-locked solitons in a fiber laser at 2 μm region incorporated with TIs.

Dual-wavelength rectangular pulse erbium-doped fiber laser based on topological insulator saturable absorber

We reported on the generation of the dual-wavelength rectangular pulse in an erbium-doped fiber laser(EDFL)with a topological insulator saturable absorber.The rectangular pulse could be stably initiated with pulse width from 13.62 to 25.16 ns and fundamental repetition rate of 3.54 MHz by properly adjusting the pump power and the polarization state.In addition,we verified that the pulse shape of the dual-wavelength rectangular pulse can be affected by the total net cavity dispersion in the fiber laser.Furthermore,by properly rotating the polarization controllers,the harmonic mode-locking operation of the dual-wavelength rectangular pulse was also obtained.The dual-wavelength rectangular pulse EDFL would benefit some potential applications,such as spectroscopy,biomedicine,and sensing research.

A generation method of insulator region proposals based on edge boxes

High-quality insulator region proposals play important roles in the process of transmission line inspection images. A generation method of insulator region proposals based on edge boxes is proposed in this paper, and edge boxes are applied to the localization of insulators in inspection images creatively. We take a series of operations to generate insulator region proposals: K-means cluster is used on curvature scale space(CSS) points extracted from edge images, the most appropriate cluster number is chosen, and the circle is drawn on the insulator subclass. We consider the characteristics of insulators' edge images, and combine these characteristics with edge boxes. As a result, more insulator region proposals are displayed. The experimental results show that our method can effectively reduce the interference area, meanwhile, has high quality of region proposals with fast calculation speed.