The atom (Ag,Cu) diffusion behavior and the effect of technology on the interface of rolled Ag/Cu composite contact were investigated. The concentration of Ag and Cu atoms near the interface was determined with electr...The atom (Ag,Cu) diffusion behavior and the effect of technology on the interface of rolled Ag/Cu composite contact were investigated. The concentration of Ag and Cu atoms near the interface was determined with electron probe. The bonding strength of composite interface was tested and the fracture in tensile sample was observed by SEM. The results show that there was inter diffusion of Ag and Cu atoms on the interface, which formed compact layer with high bonding strength of 98 MPa. The practical application proved that the Ag/Cu composite interface is reliable.展开更多
Ag adsorptions at 0.25-3 monolayer （ML） coverage on a perfect TIC（001） surface and at 0.25 ML coverage on C vacancy are separately investigated by using the pseudopotential-based density functional theory. The pre...Ag adsorptions at 0.25-3 monolayer （ML） coverage on a perfect TIC（001） surface and at 0.25 ML coverage on C vacancy are separately investigated by using the pseudopotential-based density functional theory. The preferential adsorption sites and the adsorption-induced modifications of electronic structures of both the substrate and adsorbate are analysed. Through the analyses of adsorption energy, ideal work of separation, interface distance, projected local density of states, and the difference electron density, the characteristic evolution of the adatom-surface bonding as a function of the amount of deposited silver is studied. The nature of the Ag/TiC bonding changes as the coverage increases from 0.25 to 3 MLs. Unlike physisorption in an Ag/MgO system, polar covalent component contributes to the Ag/TiC interfacial adhesion in most cases, however, for the case of 1-3 ML coverage, an additional electrostatic interaction between the absorption layer and the substrate should be taken into account. The value of ideal work of separation, 1.55 J/m^2, for a 3-ML-thick adlayer accords well with other calculations. The calculations predict that Ag does not wet TIC（001） surface and prefers a three-dimensional growth mode in the absence of kinetic factor. This work reports on a clear site and coverage dependence of the measurable physical parameters, which would benefit the understanding of Ag/TiC（001） interface and the analysis of experimental data.展开更多
文摘The atom (Ag,Cu) diffusion behavior and the effect of technology on the interface of rolled Ag/Cu composite contact were investigated. The concentration of Ag and Cu atoms near the interface was determined with electron probe. The bonding strength of composite interface was tested and the fracture in tensile sample was observed by SEM. The results show that there was inter diffusion of Ag and Cu atoms on the interface, which formed compact layer with high bonding strength of 98 MPa. The practical application proved that the Ag/Cu composite interface is reliable.
基金Project supported by the National Basic Research Program of China (Grant No 2006CB605103)
文摘Ag adsorptions at 0.25-3 monolayer （ML） coverage on a perfect TIC（001） surface and at 0.25 ML coverage on C vacancy are separately investigated by using the pseudopotential-based density functional theory. The preferential adsorption sites and the adsorption-induced modifications of electronic structures of both the substrate and adsorbate are analysed. Through the analyses of adsorption energy, ideal work of separation, interface distance, projected local density of states, and the difference electron density, the characteristic evolution of the adatom-surface bonding as a function of the amount of deposited silver is studied. The nature of the Ag/TiC bonding changes as the coverage increases from 0.25 to 3 MLs. Unlike physisorption in an Ag/MgO system, polar covalent component contributes to the Ag/TiC interfacial adhesion in most cases, however, for the case of 1-3 ML coverage, an additional electrostatic interaction between the absorption layer and the substrate should be taken into account. The value of ideal work of separation, 1.55 J/m^2, for a 3-ML-thick adlayer accords well with other calculations. The calculations predict that Ag does not wet TIC（001） surface and prefers a three-dimensional growth mode in the absence of kinetic factor. This work reports on a clear site and coverage dependence of the measurable physical parameters, which would benefit the understanding of Ag/TiC（001） interface and the analysis of experimental data.