The interface formations of the heterojunctions concerning Ⅳ and Ⅱ Ⅵ semiconductors were studied via synchrotron radiation photoemission spectroscopy. Experimental results show that the overlayer growths of Si...The interface formations of the heterojunctions concerning Ⅳ and Ⅱ Ⅵ semiconductors were studied via synchrotron radiation photoemission spectroscopy. Experimental results show that the overlayer growths of Si or Ge on Ge, ZnSe and ZnS substrates are in compliance with an ideal two dimensional (2D) growth mode. However, deviations from 2D mode were also observed during the interfaces formation of Ge/CdTe and Si/CdTe, and are ascribed to large lattice mismatching and interfacial reaction.展开更多
The (100) texture of solidified fcc metals, caused by the preferential (100) dendrite growth, could be closeIy related to solid/melt interfaces which behave differently along different crystallographic orientation. Th...The (100) texture of solidified fcc metals, caused by the preferential (100) dendrite growth, could be closeIy related to solid/melt interfaces which behave differently along different crystallographic orientation. The stability and roughness of {111} and {100} solid/melt interfaces of fcc metals were investigated using a modified Temkin multi-layer model. It is demonstrated that {100}crystal/melt interface is more unstable and rougher than {111} interface. The effect of the stability of crystal/melt interface on the (100) texture formation in solidified fcc metals has been analysed and discussed.展开更多
Unconventional hydrocarbon reservoirs in layered formations,such as tight sandstones and shales,are continually being developed.Hydraulic fracturing is a critical technology for the high-efficiency development of hydr...Unconventional hydrocarbon reservoirs in layered formations,such as tight sandstones and shales,are continually being developed.Hydraulic fracturing is a critical technology for the high-efficiency development of hydrocarbon reservoirs.Understanding the stress field and stability of the formation interface is vital to understanding stress propagation,preferably before the growing hydraulic fracture contacts the formation interface.In this study,models are developed for computing the stress field of hydraulic fracture propagation near the formation interface,and the stress fields within and at the two sides of the formation interface are analyzed.Four failure modes of the interface under the impact of hydraulic fracture propagation in its vicinity are identified,and the corresponding failure criteria are proposed.By simulating the magnitude and direction of peak stress at different parameters,the failure mode and stability of the formation interface are analyzed.Results reveal that when the interface strength is weak,the formation interface fails before the growing hydraulic fracture contacts it,and its stability is significantly related to a variety of factors,including the type of formation interface,rock mechanical properties,far-field stress,structural parameters,distance between the hydraulic fracture and formation interface,and fracturing execution parameters.展开更多
The quantitative phase-field simulations were reviewed on the processes of solidification of pure metals and alloys.The quantitative phase-field equations were treated in a diffuse thin-interface limit,which enabled t...The quantitative phase-field simulations were reviewed on the processes of solidification of pure metals and alloys.The quantitative phase-field equations were treated in a diffuse thin-interface limit,which enabled the quantitative links between interface dynamics and model parameters in the quasi-equilibrium simulations.As a result,the quantitative modeling is more effective in dealing with microstructural pattern formation in the large scale simulations without any spurious kinetic effects.The development of the quantitative phase-field models in modeling the formation of microstructures such as dendritic structures,eutectic lamellas,seaweed morphologies,and grain boundaries in different solidified conditions was also reviewed with the purpose of guiding to find the new prospect of applications in the quantitative phase-field simulations.展开更多
文摘The interface formations of the heterojunctions concerning Ⅳ and Ⅱ Ⅵ semiconductors were studied via synchrotron radiation photoemission spectroscopy. Experimental results show that the overlayer growths of Si or Ge on Ge, ZnSe and ZnS substrates are in compliance with an ideal two dimensional (2D) growth mode. However, deviations from 2D mode were also observed during the interfaces formation of Ge/CdTe and Si/CdTe, and are ascribed to large lattice mismatching and interfacial reaction.
文摘The (100) texture of solidified fcc metals, caused by the preferential (100) dendrite growth, could be closeIy related to solid/melt interfaces which behave differently along different crystallographic orientation. The stability and roughness of {111} and {100} solid/melt interfaces of fcc metals were investigated using a modified Temkin multi-layer model. It is demonstrated that {100}crystal/melt interface is more unstable and rougher than {111} interface. The effect of the stability of crystal/melt interface on the (100) texture formation in solidified fcc metals has been analysed and discussed.
基金supported by National Natural Science Foundation of China (51704251)National Science and Technology Major Project of the Ministry of Science and Technology of China (2016ZX05006-002)。
文摘Unconventional hydrocarbon reservoirs in layered formations,such as tight sandstones and shales,are continually being developed.Hydraulic fracturing is a critical technology for the high-efficiency development of hydrocarbon reservoirs.Understanding the stress field and stability of the formation interface is vital to understanding stress propagation,preferably before the growing hydraulic fracture contacts the formation interface.In this study,models are developed for computing the stress field of hydraulic fracture propagation near the formation interface,and the stress fields within and at the two sides of the formation interface are analyzed.Four failure modes of the interface under the impact of hydraulic fracture propagation in its vicinity are identified,and the corresponding failure criteria are proposed.By simulating the magnitude and direction of peak stress at different parameters,the failure mode and stability of the formation interface are analyzed.Results reveal that when the interface strength is weak,the formation interface fails before the growing hydraulic fracture contacts it,and its stability is significantly related to a variety of factors,including the type of formation interface,rock mechanical properties,far-field stress,structural parameters,distance between the hydraulic fracture and formation interface,and fracturing execution parameters.
基金supported by National Natural Science Foundation of China(No.51174177)the Fund of the State Key Solidification Laboratory of Solidification Processing in Northwestern Polytechnical University(No.SKLSP 201714)
文摘The quantitative phase-field simulations were reviewed on the processes of solidification of pure metals and alloys.The quantitative phase-field equations were treated in a diffuse thin-interface limit,which enabled the quantitative links between interface dynamics and model parameters in the quasi-equilibrium simulations.As a result,the quantitative modeling is more effective in dealing with microstructural pattern formation in the large scale simulations without any spurious kinetic effects.The development of the quantitative phase-field models in modeling the formation of microstructures such as dendritic structures,eutectic lamellas,seaweed morphologies,and grain boundaries in different solidified conditions was also reviewed with the purpose of guiding to find the new prospect of applications in the quantitative phase-field simulations.