Inconel 718 superalloys deposited by laser solid forming （LSF） were heat treated with solution treatment,intermediate heat treatment （IHT） and two-stage aging treatment in sequence （SITA heat treatment）.The effe...Inconel 718 superalloys deposited by laser solid forming （LSF） were heat treated with solution treatment,intermediate heat treatment （IHT） and two-stage aging treatment in sequence （SITA heat treatment）.The effect of IHT temperature on microstructure,tensile property and notch sensitivity of LSFed Inconel 718 superalloy at 500 ℃ were investigated.As-deposited columnar grains have transformed to equiaxed grains and the grains were refined due to the recrystallization during the SITA heat treatment.It is found that the size and amount of δ phase dispersed at grain boundaries decreased with the increasing of IHT temperature,and δ phase disappeared when the IHT temperature reached 1 020 ℃.The ultimate tensile strength （UTS） and yield strength （YS） of smooth samples increased to a maximum when the IHT temperature reached 980 ℃ and then decreased slightly to a minimum when the IHT temperature was 1 000 ℃,and followed by slight increasing again till the IHT temperature reached 1 020 ℃,resulted from the competition of precipitation strengthening effect of γ″ and γ＇ phase and the grain boundary weakening effect caused by the gradual disappearance of δ phase with increasing the IHT temperature.The notch sensitivity factor （qe） decreased but still greater than 1 as the IHT temperature increased,which is attributed to the decrease of the size and amount of δ precipitation.展开更多
The standard heat treatment of cast nickel base superalloy K403 is the solid solution treatment of 1210℃/4h, air cooling. It is very difficult to meet the requirements of Aviation Standard HB5155, in which the stre...The standard heat treatment of cast nickel base superalloy K403 is the solid solution treatment of 1210℃/4h, air cooling. It is very difficult to meet the requirements of Aviation Standard HB5155, in which the stress rupture life at 750℃ and 645MPa is longer than 50h. The results showed that the intermediate temperature stress rupture properties impaired by treatment of 1210℃/4h were due to precipitation of too small γ′ phase(<0.2μm) in grains and absence of the secondary carbides at grain boundaries. Microstructure containing the intergranular M6C carbides with envelope of γ′ and the residual coarse γ′ was obtained by means of 1180℃/4h treatment, therefore the stress rupture life was obviously increased to meet the demand of HB5155. The effect of γ′ size was also discussed from the view point of deformation mechanism in this paper.展开更多
The accumulative roll-bonding(ARB)process was applied on the strips of aluminum alloy 1050 in two processing conditions:cold ARB and warm ARB.The results of tensile tests and microhardness measurement show that the wa...The accumulative roll-bonding(ARB)process was applied on the strips of aluminum alloy 1050 in two processing conditions:cold ARB and warm ARB.The results of tensile tests and microhardness measurement show that the warm ARB process exhibits the lower tensile strength and microhardness,more homogeneous distribution of the microhardness,higher elongation,and especially superior planar isotropy of the tensile properties in comparison to the cold ARB,because of the intermediate heat treatment as well as the elevated temperature rolling in the warm ARB process.Furthermore,with increasing the cycles of both processes,the planar isotropy decreases progressively.展开更多
基金Funded by the Program for New Century Excellent Talents in University of China (No.NCET-06-0879)the National Natural Science Foundation of China (NSFC) (No.50971102)+2 种基金NPU Foundation for Fundamental Research(No.NPU-FFR-JC200808)the Fund of the State Key Laboratory of Solidification Processing (NPU) (Nos.16-TZ-2007 and 39-QZ-2009)supported by the Program of Introducing Talents of Discipline to Universities (No.08040)
文摘Inconel 718 superalloys deposited by laser solid forming （LSF） were heat treated with solution treatment,intermediate heat treatment （IHT） and two-stage aging treatment in sequence （SITA heat treatment）.The effect of IHT temperature on microstructure,tensile property and notch sensitivity of LSFed Inconel 718 superalloy at 500 ℃ were investigated.As-deposited columnar grains have transformed to equiaxed grains and the grains were refined due to the recrystallization during the SITA heat treatment.It is found that the size and amount of δ phase dispersed at grain boundaries decreased with the increasing of IHT temperature,and δ phase disappeared when the IHT temperature reached 1 020 ℃.The ultimate tensile strength （UTS） and yield strength （YS） of smooth samples increased to a maximum when the IHT temperature reached 980 ℃ and then decreased slightly to a minimum when the IHT temperature was 1 000 ℃,and followed by slight increasing again till the IHT temperature reached 1 020 ℃,resulted from the competition of precipitation strengthening effect of γ″ and γ＇ phase and the grain boundary weakening effect caused by the gradual disappearance of δ phase with increasing the IHT temperature.The notch sensitivity factor （qe） decreased but still greater than 1 as the IHT temperature increased,which is attributed to the decrease of the size and amount of δ precipitation.
文摘The standard heat treatment of cast nickel base superalloy K403 is the solid solution treatment of 1210℃/4h, air cooling. It is very difficult to meet the requirements of Aviation Standard HB5155, in which the stress rupture life at 750℃ and 645MPa is longer than 50h. The results showed that the intermediate temperature stress rupture properties impaired by treatment of 1210℃/4h were due to precipitation of too small γ′ phase(<0.2μm) in grains and absence of the secondary carbides at grain boundaries. Microstructure containing the intergranular M6C carbides with envelope of γ′ and the residual coarse γ′ was obtained by means of 1180℃/4h treatment, therefore the stress rupture life was obviously increased to meet the demand of HB5155. The effect of γ′ size was also discussed from the view point of deformation mechanism in this paper.
文摘The accumulative roll-bonding(ARB)process was applied on the strips of aluminum alloy 1050 in two processing conditions:cold ARB and warm ARB.The results of tensile tests and microhardness measurement show that the warm ARB process exhibits the lower tensile strength and microhardness,more homogeneous distribution of the microhardness,higher elongation,and especially superior planar isotropy of the tensile properties in comparison to the cold ARB,because of the intermediate heat treatment as well as the elevated temperature rolling in the warm ARB process.Furthermore,with increasing the cycles of both processes,the planar isotropy decreases progressively.