Thin-film composite (TFC) nanofiltration (NF) membranes were fabricated via the interfacial polymerization of piperazine (PIP) and 1,3,5-benzenetricart)oiiyl trichloride on polysulfone (PSf) support membranes blended ...Thin-film composite (TFC) nanofiltration (NF) membranes were fabricated via the interfacial polymerization of piperazine (PIP) and 1,3,5-benzenetricart)oiiyl trichloride on polysulfone (PSf) support membranes blended with K^+-responsive poly(N-isopropylacryamideco- acryloylamidobenzo-15-crown-5)(P(NIPAM-co- AAB15C5)). Membranes were characterized by attenuated total reflection Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, atomic force microscope, scanning electron microscope, contact angle, and filtration tests. The results showed that:(1) Under K^+-free conditions, the blended P(NIPAM-co-AAB15C5)/PSf supports had porous and hydrophilic surfaces, thereby producing NF membranes with smooth surfaces and low MgSO4 rejections;(2) With K^+ in the PIP solution, the surface roughness and water permeability of the resultant NF membrane were increased due to the K^+-induced transition of low-content P(NIPAM-co-AAB15C5) from hydrophilic to hydrophobic;(3) After a curing treatment at 95℃, the improved NF membrane achieved an even higher pure water permeability of 10.97 L·m^-2·h^-1 - bar1 under 200 psi. Overall, this study provides a novel method to improve the performance of NF membranes and helps understand the influence of supports on TFC membranes.展开更多
基金the National Natural Science Foundation of China (Grant No.51678377)Sichuan University Outstanding Youth Foundation (2015SCU04A35)+1 种基金Applied Basic Research of Sichuan Province (2017JY0238)Key Projects in the Science & Technology Program of Hainan Province (zdkj2016022).
文摘Thin-film composite (TFC) nanofiltration (NF) membranes were fabricated via the interfacial polymerization of piperazine (PIP) and 1,3,5-benzenetricart)oiiyl trichloride on polysulfone (PSf) support membranes blended with K^+-responsive poly(N-isopropylacryamideco- acryloylamidobenzo-15-crown-5)(P(NIPAM-co- AAB15C5)). Membranes were characterized by attenuated total reflection Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, atomic force microscope, scanning electron microscope, contact angle, and filtration tests. The results showed that:(1) Under K^+-free conditions, the blended P(NIPAM-co-AAB15C5)/PSf supports had porous and hydrophilic surfaces, thereby producing NF membranes with smooth surfaces and low MgSO4 rejections;(2) With K^+ in the PIP solution, the surface roughness and water permeability of the resultant NF membrane were increased due to the K^+-induced transition of low-content P(NIPAM-co-AAB15C5) from hydrophilic to hydrophobic;(3) After a curing treatment at 95℃, the improved NF membrane achieved an even higher pure water permeability of 10.97 L·m^-2·h^-1 - bar1 under 200 psi. Overall, this study provides a novel method to improve the performance of NF membranes and helps understand the influence of supports on TFC membranes.