A specialised electrochemical measurement cell was plugged into a pilot water distribution system to simulate the pipe inner-wall corrosion. The linear polarisation resistance(LPR) technique and electrochemical impeda...A specialised electrochemical measurement cell was plugged into a pilot water distribution system to simulate the pipe inner-wall corrosion. The linear polarisation resistance(LPR) technique and electrochemical impedance spectroscopy(EIS) were measured in real time to study the variation of the corrosion rate(CR) and scale of cast iron. Three corrosion stages were observed according to the LPR analysis: an initial stage with significantly fluctuating CR, a developmental stage with slowly decreasing CR, and a stable stage with a low CR of approximately 0.157 5 mm·a^(-1). The EIS revealed that the scales with a compact outer layer and a porous inner layer finally formed in the stable stage, and the polarisation resistance was approximately 2 175 ?·cm^2. A physicochemical analysis of the scales showed that ferric oxides, oxyhydroxides and calcite made the outer layer compact and effectively limited the diffusion of oxygen through the scales, which resulted in a low CR.展开更多
By oxidation weight gain method, four groups of Fe-based superalloys with different content of chromium, aluminium and silicon were tested at 1 200 ℃ for 500 hours. According to the oxidation weight gains, the oxidat...By oxidation weight gain method, four groups of Fe-based superalloys with different content of chromium, aluminium and silicon were tested at 1 200 ℃ for 500 hours. According to the oxidation weight gains, the oxidation kinetic curves were plotted, and the equations were regressed by least square method and non-linear curve fitting. The effects of different scale compositions on the morphology and oxidation kinetic law were studied further by analysis of X-ray diffraction （XRD） and scanning electron microscope （SEM）. It is found that the compounded scale is composed of Cr2O3, Al2O3, SiO2 and FeCr2O4, with compact structure and fine grains, possessing complete oxidation resistance at 1 200 ℃, and the oxidation kinetic curve follows the power function of y=axb （a0, 0b1）. When the compounded scale lacks Al2O3 or SiO2, it becomes weak in oxidation resistance, but the oxidation kinetic curve still follows the power function with bigger parameter b. When Cr2O3 is absent, the kinetic curve shows two parts： the slow adding of oxidation weight gains at the beginning and the ascending line in the end. Such scale loses oxidation resistance completely.展开更多
A field study on the estimation and analysis of iron stability in drinking water distribution system was carried out in a city of China. The stability of iron ion was estimated by pC-pH figure. It was found that iron ...A field study on the estimation and analysis of iron stability in drinking water distribution system was carried out in a city of China. The stability of iron ion was estimated by pC-pH figure. It was found that iron ion was unstable, with a high Fe （OH）3 precipitation tendency and obvious increase in turbidity. The outer layer of the corrosion scale was compact, while the inner core was porous. The main composition of the scale was iron, and the possible compound constitutes of the outer scale were α-FeOH, γ-FeOOH, α-Fe2O3, γ-F2O3, FeCl3, while the inner were Fe3O4, FeCl2, FeCO3. According to the characteristics of the corrosion scale, it was thought that the main reason for iron instability was iron release from corrosion scale. Many factors such as pipe materials, dissolved oxygen and chlorine residual affect iron release. Generally, higher iron release occurred with lower dissolved oxygen or chlorine residual concentration, while lower iron release occurred with higher dissolved oxygen or chlorine residual concentration. The reason was considered that the passivated out layer of scale of ferric oxide was broken down by reductive reaction in a condition of low oxidants concentration, which would result more rapid corrosion of the nine and red water phenomenon.展开更多
Under far from equilibrium conditions, the formation mechanism of solid can be studied in terms of the dynamic scaling theory. The roughness and dynamic scaling behavior of the Fe-N thin films were studied by atomic f...Under far from equilibrium conditions, the formation mechanism of solid can be studied in terms of the dynamic scaling theory. The roughness and dynamic scaling behavior of the Fe-N thin films were studied by atomic force microscopy and grazing incidence X-ray scattering. The results indicate that the roughness of the surface increases with increasing sputtering time during the course of magnetron sputtering, and the surface exhibits a fractal characteristic. While the Fe-N films prepared by compound technology—combining magnetron sputtering with plasma based ion implantation are not in agreement with the fractal theory.展开更多
基金Supported by the National Natural Science Foundation of China(No.51278333)Specialized Research Fund for the Doctoral Program of Higher Education of China(No.20130032110032)
文摘A specialised electrochemical measurement cell was plugged into a pilot water distribution system to simulate the pipe inner-wall corrosion. The linear polarisation resistance(LPR) technique and electrochemical impedance spectroscopy(EIS) were measured in real time to study the variation of the corrosion rate(CR) and scale of cast iron. Three corrosion stages were observed according to the LPR analysis: an initial stage with significantly fluctuating CR, a developmental stage with slowly decreasing CR, and a stable stage with a low CR of approximately 0.157 5 mm·a^(-1). The EIS revealed that the scales with a compact outer layer and a porous inner layer finally formed in the stable stage, and the polarisation resistance was approximately 2 175 ?·cm^2. A physicochemical analysis of the scales showed that ferric oxides, oxyhydroxides and calcite made the outer layer compact and effectively limited the diffusion of oxygen through the scales, which resulted in a low CR.
基金Funded by Komatsu Ltd. of Japan (No. 31370011370804, Shandong University)the Friendly Joint Item between Shandong University & Komatsu Ltd
文摘By oxidation weight gain method, four groups of Fe-based superalloys with different content of chromium, aluminium and silicon were tested at 1 200 ℃ for 500 hours. According to the oxidation weight gains, the oxidation kinetic curves were plotted, and the equations were regressed by least square method and non-linear curve fitting. The effects of different scale compositions on the morphology and oxidation kinetic law were studied further by analysis of X-ray diffraction （XRD） and scanning electron microscope （SEM）. It is found that the compounded scale is composed of Cr2O3, Al2O3, SiO2 and FeCr2O4, with compact structure and fine grains, possessing complete oxidation resistance at 1 200 ℃, and the oxidation kinetic curve follows the power function of y=axb （a0, 0b1）. When the compounded scale lacks Al2O3 or SiO2, it becomes weak in oxidation resistance, but the oxidation kinetic curve still follows the power function with bigger parameter b. When Cr2O3 is absent, the kinetic curve shows two parts： the slow adding of oxidation weight gains at the beginning and the ascending line in the end. Such scale loses oxidation resistance completely.
文摘A field study on the estimation and analysis of iron stability in drinking water distribution system was carried out in a city of China. The stability of iron ion was estimated by pC-pH figure. It was found that iron ion was unstable, with a high Fe （OH）3 precipitation tendency and obvious increase in turbidity. The outer layer of the corrosion scale was compact, while the inner core was porous. The main composition of the scale was iron, and the possible compound constitutes of the outer scale were α-FeOH, γ-FeOOH, α-Fe2O3, γ-F2O3, FeCl3, while the inner were Fe3O4, FeCl2, FeCO3. According to the characteristics of the corrosion scale, it was thought that the main reason for iron instability was iron release from corrosion scale. Many factors such as pipe materials, dissolved oxygen and chlorine residual affect iron release. Generally, higher iron release occurred with lower dissolved oxygen or chlorine residual concentration, while lower iron release occurred with higher dissolved oxygen or chlorine residual concentration. The reason was considered that the passivated out layer of scale of ferric oxide was broken down by reductive reaction in a condition of low oxidants concentration, which would result more rapid corrosion of the nine and red water phenomenon.
文摘Under far from equilibrium conditions, the formation mechanism of solid can be studied in terms of the dynamic scaling theory. The roughness and dynamic scaling behavior of the Fe-N thin films were studied by atomic force microscopy and grazing incidence X-ray scattering. The results indicate that the roughness of the surface increases with increasing sputtering time during the course of magnetron sputtering, and the surface exhibits a fractal characteristic. While the Fe-N films prepared by compound technology—combining magnetron sputtering with plasma based ion implantation are not in agreement with the fractal theory.