The tribological properties of isostatic graphite and carbon graphite under dry sliding and water lubricated conditions were studied.The friction test was conducted by using a pin-on-disc tribometer.The friction coeff...The tribological properties of isostatic graphite and carbon graphite under dry sliding and water lubricated conditions were studied.The friction test was conducted by using a pin-on-disc tribometer.The friction coefficient and the wear rate were employed to evaluate the tribological performances of the two materials,and wear morphology was used to analyze the wear mechanism.The results show that the friction coefficient of the isostatic graphite is larger than that of the carbon graphite under the dry sliding condition,and the wear rate is lower than that of the carbon graphite.Under the water lubricated condition,the friction coefficients and the wear rates of the isostatic graphite decrease obviously.The main wear form of the isostatic graphite is abrasive wear,while the main wear form of the carbon graphite is spalling wear.Finally,the tribological mechanism of the isostatic graphite under dry sliding and water lubricated conditions were systematically analyzed.展开更多
Isostatic graphite materials with 8%porosity and 14%porosity were prepared by the cold isostatic pressing process.Cavitation erosion resistance of the isostatic graphite was evaluated through cavitation tests in an ul...Isostatic graphite materials with 8%porosity and 14%porosity were prepared by the cold isostatic pressing process.Cavitation erosion resistance of the isostatic graphite was evaluated through cavitation tests in an ultrasonic vibration system.The volume loss and erosion morphology of the isostatic graphite were adopted to investigate the cavitation erosion resistance of the isostatic graphite.The cavitation test results show that after ultrasonic vibration of 14 h,the volume loss of the isostatic graphite materials with 8%porosity and 14%porosity are 35%and 46%of the carbon graphite material,respectively.The isostatic graphite material with 8%porosity exhibits an outstanding capability to resist cavitation erosion damage,and the cavitation erosion resistance of the isostatic graphite enhances with the decrease in porosity.The damage mechanism of isostatic graphite is brittle fracture attributed to the shock wave and micro jet.The isostatic graphite with low porosity exhibits excellent cavitation erosion resistance due to its fine graphite particles,homogeneous structure and high degree of hardness.展开更多
基金The National Natural Science Foundation of China(No.51635004,11472078)。
文摘The tribological properties of isostatic graphite and carbon graphite under dry sliding and water lubricated conditions were studied.The friction test was conducted by using a pin-on-disc tribometer.The friction coefficient and the wear rate were employed to evaluate the tribological performances of the two materials,and wear morphology was used to analyze the wear mechanism.The results show that the friction coefficient of the isostatic graphite is larger than that of the carbon graphite under the dry sliding condition,and the wear rate is lower than that of the carbon graphite.Under the water lubricated condition,the friction coefficients and the wear rates of the isostatic graphite decrease obviously.The main wear form of the isostatic graphite is abrasive wear,while the main wear form of the carbon graphite is spalling wear.Finally,the tribological mechanism of the isostatic graphite under dry sliding and water lubricated conditions were systematically analyzed.
基金The National Natural Science Foundation of China(No.51635004,11472078)。
文摘Isostatic graphite materials with 8%porosity and 14%porosity were prepared by the cold isostatic pressing process.Cavitation erosion resistance of the isostatic graphite was evaluated through cavitation tests in an ultrasonic vibration system.The volume loss and erosion morphology of the isostatic graphite were adopted to investigate the cavitation erosion resistance of the isostatic graphite.The cavitation test results show that after ultrasonic vibration of 14 h,the volume loss of the isostatic graphite materials with 8%porosity and 14%porosity are 35%and 46%of the carbon graphite material,respectively.The isostatic graphite material with 8%porosity exhibits an outstanding capability to resist cavitation erosion damage,and the cavitation erosion resistance of the isostatic graphite enhances with the decrease in porosity.The damage mechanism of isostatic graphite is brittle fracture attributed to the shock wave and micro jet.The isostatic graphite with low porosity exhibits excellent cavitation erosion resistance due to its fine graphite particles,homogeneous structure and high degree of hardness.