Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with t...Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with the addition of Ga2S3, two main structural transformations were deduced ： the gradual enhancement of ethane- like structural units S3 Ge- GeS3 （ 250 cm ^- 1） and S3 Ga- GaS3 （270 cm ^- 1 ） and the appearance of charge imbalanced units [ Ga2 S2 （ S1/2 ）4 ]^2- and [Ga（ S1/2 ）4 ]^- . And this change of structural aspect seems to give as a clue to understanding the cause of the increased rare-earth solubility.展开更多
In this paper a new kind of mid - infrared fiber material is reported. The reflective coefficients (R) of glasses in the system Na2O - ZnO - GeO2-SiO2-PbO have been measured-the refractive index becomes less than unit...In this paper a new kind of mid - infrared fiber material is reported. The reflective coefficients (R) of glasses in the system Na2O - ZnO - GeO2-SiO2-PbO have been measured-the refractive index becomes less than unity at 1180 - 900cm-1 range because of the existence of anomalous dispersion. The optical losses of hollow waveguides were calculated,the predicted losses at 940cm-1are 0. 65 and 0. 081B/ m as the inner diameter of fiber is 0. 5 and 1. 0mm respectively. The glasses can be used as the cladding materials of hol-low waveguides for transmitting CO2 laser from the measurements of characteristic temperatures, coefficient of expansion and chemical durability.展开更多
文摘Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with the addition of Ga2S3, two main structural transformations were deduced ： the gradual enhancement of ethane- like structural units S3 Ge- GeS3 （ 250 cm ^- 1） and S3 Ga- GaS3 （270 cm ^- 1 ） and the appearance of charge imbalanced units [ Ga2 S2 （ S1/2 ）4 ]^2- and [Ga（ S1/2 ）4 ]^- . And this change of structural aspect seems to give as a clue to understanding the cause of the increased rare-earth solubility.
文摘In this paper a new kind of mid - infrared fiber material is reported. The reflective coefficients (R) of glasses in the system Na2O - ZnO - GeO2-SiO2-PbO have been measured-the refractive index becomes less than unity at 1180 - 900cm-1 range because of the existence of anomalous dispersion. The optical losses of hollow waveguides were calculated,the predicted losses at 940cm-1are 0. 65 and 0. 081B/ m as the inner diameter of fiber is 0. 5 and 1. 0mm respectively. The glasses can be used as the cladding materials of hol-low waveguides for transmitting CO2 laser from the measurements of characteristic temperatures, coefficient of expansion and chemical durability.