Effect of Post-weld Heat Treatment on Mechanical Characteristics of AZ31 Magnesium Alloy Welded Joints

Tungsten inert gas（TIG） welding was performed on 2.7 mm thick commercial extruded AZ31 B magnesium alloy plates. We investigated the effect of post-weld heat treatment（PWHT） on the microstructure, mechanical properties and precipitated phase of the weld joints. The results showed that during the annealing treatment（200 ℃-1 h, 250 ℃-1 h, 300 ℃-1 h, 350 ℃-1 h, 400 ℃-1 h, and 450 ℃-1 h）, the average grain size in the weld seam was the minimum after annealing at 400 ℃ for 1 hour, and then abnormally grew up after annealing at 450 ℃ for 1 hour. The mechanical properties enhanced when the joints were processed from 200 ℃-1 h to 400 ℃-1 h but sharply decreased with increasing annealing temperature. In contrast to the annealing treatment, solution treatment（250 ℃-10 h, 300 ℃-10 h, 350 ℃-10 h, 400 ℃-10 h, and 450 ℃-10 h） exhibited a better ductility but a slight deterioration in tensile strength. Especially speaking, no eutectic compounds（such as Mg17 Al12） were observed in the weld seam. The supersaturated Al atoms were precipitated in a coarse spherical shape dispersed in the weld seam. The precipitated Al atoms dissolved in the matrix substances at the condition（400 ℃-1 h） or（250 ℃-10 h）. The solution treatment caused grain coarsening and precipitated Al atoms dissolved in the weld seam substantially, which resulted in a drop in micro-hardness at the weld seam compared to the area of the annealed joints.

An Average Failure Index Method for the Tensile Strength Prediction of Composite Adhesive-bonded π Joints

An average failure index method based on accurate FEA was proposed for the tensile strength prediction of composite out-of-plane adhesive-bonded π joints. Based on the simple and independent maximum stress failure criterion, the failure index was introduced to characterize the degree of stress components close to their corresponding material strength. With a brief load transfer analysis, the weak fillers were prominent and further detailed discussion was performed. The maximum value among the average failure indices which were related with different stress components was filtrated to represent the failure strength of the critical surface, which is either the two curved upside surfaces or the bottom plane of the fillers for composite π joints. The tensile strength of three kinds of π joints with different material systems, configurations and lay-ups was predicted by the proposed method and corresponding experiments were conducted. Good agreements between the numerical and experimental results give evidence of the effectiveness of the proposed method. In contrast to the existed time-consuming strength prediction methods, the proposed method provides a capability of quickly assessing the failure of complex out-of-plane joints and is easy and convenient to be widely utilized in engineering.

Welding technique studies on the “West-East” pipeline project

This paper described the work of welding process design for the ＂ West-East＂ pipeline project, which is high pressure, large diameter and heavy wall thickness. According to the different geographical situation, climate, culture and the flexibility of the welding methods, this work recommended the semi-automatic process at the east and middle sections and automatic process at the west section of the pipeline project. The manual process is recommended on the tie-in joints and repairs. The double joint pipe and the 3 joint pipe are recommended at the water net place and some in-ditch welding place to reduce the welding volume. Also the special redesigned bevels are recommended for the automatic process and the semiautomatic process. Through all destructive tests, the results shows the welds are meet the requirements of related standards, specifications and design documents.

Microstructure and properties in dissimilar/similar weld joints between DP780 and DP980 steels processed by fiber laser welding

The microstructure and mechanical properties（strength, fatigue and formability） of dissimilar/similar weld joints between DP780 and DP980 steels were studied. The microstructure in fusion zone（FZ） was lath martensite（LM）, and alloying elements in the FZ were uniformly distributed. The hardness in the FZ of dissimilar weld joint was similar to the average value（375 HV） of the two similar weld joints. The microstructural evolution in heat affected zone（HAZ） of dissimilar/similar weld joints was as follows：LM（coarse-grained HAZ） →finer LM（fine-grained HAZ） →M-A constituent and ferrite（intercritically HAZ） →tempered martensite（TM） and ferrite（sub-critical HAZ）. Lower hardness in intercritically HAZ and sub-critical HAZ（softening zones） was observed compared to base metal（BM） in dissimilar/similar weld joints. The size of softening zone was 0.2-0.3 mm and reduction in hardness was ~7.6%-12.7% of BM in all the weld joints, which did not influence the tensile properties of weld joints such that fracture location was in BM. Formability of dissimilar weld joints was inferior compared to similar weld joints because of the softening zone, non-uniform microstructure and hardness on the two sides of FZ. The effect of microstructure on fatigue life was not influenced due to the presence of welding concavity.

Development and application of software packages in welding engineering

The weldabiUty of some material is analyzed with simple calculating program in this paper, and weldability testing data are shared through database system. The welding procedures are designed with help of expert systems, and the knowledge is shared among welding engineers. Not only the preparing progress of the welding documents is completed with database systems but also the complex decision on the necessity of the qualification test according to the present procedure qualification records （PQRs） and manufacture codes is made. Moreover, the artificial neural network （ANN） technique is proven to be one of the effective ways to predict mechanical properties of welded joints when there are enough tested data to train the models. Finally, the achievements in modeling microstructure of welded joints are introduced, especially in solid transformation and grain growth in both heat-affected zone （HAZ） and welded molten pool.