Effect of weld reinforcement on fatigue properties of A6N01 aluminum alloy welded joint

Fatigue properties of smooth and reinforcement A6N01 aluminum alloy welded joints were characterized in this paper. Based on measured S-lgN curves and fatigue fracture morphologies, effect of weld reinforcement on the fatigue property of the welded joint was studied. Results show that the weld toe is the weakness region of the reinforcement welded joint due to the stress concentration in this area, thus the fatigue fracture occurred at the weld toe for all the reinforcement welded joints; while the fatigue property of the smooth welded joint was improved due to remove of the weld reinforcement, and the welding defect was the key factor of the fatigue fracture, thus its fracture zones mainly located at welding zone and fusion line.

Determination of Water Diffusion Coefficients and Dynamics in Adhesive/Carbon Fiber Reinforced Epoxy Resin Composite Joints

To determinate the water diffusion coefficients and dynamics in adhesive/carben fiber reinforced epoxy resin composite joints, energy dispersive X-ray spectroscopy analysis（EDX） is used to establish the content change of oxy- gen in the adhesive in adhesive/carbon fther reinforced epoxy resin composite joints. As water is made up of oxygen and hydrogen, the water diffusion coefficients and dynamics in adhesive/carben fiber reinforced epoxy resin composite joints can be obtained from the change in the content of oxygen in the adhesive during humidity aging, via EDX analy-sis. The authors have calculated the water diffusion coefficients and dynamics in the adhesive/carbon fiber reinforced epoxy resin composite joints with the aid of beth energy dispersive X-ray spectroscopy and elemental analysis. The de- termined results with EDX analysis are almost the same as those determined with elemental analysis and the results al- so show that the durability of the adhesive/carbon fther reinforced epoxy resin composite joints subjected to silane cou- pling agent treatment is better than those subjected to sand paper burnishing treatment and chemical oxidation treat- ment.

Damage Failure Analysis of Z-Pins Reinforced Composite Adhesively Bonded Single-Lap Joint

In order to study themechanical properties of Z-pins reinforced laminated composite single-lap adhesively bonded joint under un-directional static tensile load,damage failure analysis of the joint was carried out bymeans of test and numerical simulation.The failure mode and mechanism of the joint were analyzed by tensile failure experiments.According to the experimental results,the joint exhibits mixed failure,and the ultimate failure is Z-pins pulling out of the adherend.In order to study the failure mechanism of the joint,the finite element method is used to predict the failure strength.The numerical results are in good agreement with the experimental results,and the error is 6.0%,which proves the validity of the numerical model.Through progressive damage failure analysis,it is found that matrix tensile failure of laminate at the edge of Z-pins occurs first,then adhesive layer failure-proceeds at the edge of Z-pins,and finally matrix-fiber shear failure of the laminate takes place.With the increase of load,the matrix-fiber shear failure expands gradually in the X direction,and at the same time,the matrix tensile failure at the hole edge gradually extends in different directions,which is consistent with the experimental results.

Experimental and Numerical Study on Mechanical Properties of Z-pins Reinforced Composites Adhesively Bonded Single-Lap Joints

The mechanical properties of Z-pins reinforced composites adhesively bonded single-lap joints(SLJs)under un-directional tension loading are investigated by experimental and numerical methods.Three kinds of joint configurations,including SLJs with three/two rows of Z-pins and“I”array of Z-pins,are investigated by tension test.The failure modes and mechanism of reinforced joints with different Z-pins numbers and alignment are analyzed,and the comparison is performed for the failure strengths of no Z-pins and Z-pins reinforced joints.According to experimental results,failure modes of three kinds of joints are all mixed failure.It turns out that the Z-pins are pulled out ultimately.The strength of joints of more Z-pins at the end of the overlap area is relatively bigger for the joint of the same Z-pins numbers.The strength of joints with Z-pins compared with non Z-pins joints is growing at 16%.Finally,the three-dimensional distribution of interfacial stress in the lap zone of three kinds of Z-pins reinforced joints is simulated,and the numerical results are in good agreement with the experimental results.It is effective that the numerical calculation of stress analysis is verified.

Strength&Conduct of Reinforced Concrete Corner Joint under Negative Moment Effect

The aim of our study is to reveal the effect of steel reinforcement details,tensile steel reinforcement ratio,compressed reinforcing steel ratio,reinforcing steel size,corner joint shape on the strength of reinforced concrete Fc'and delve into it for the most accurate details and concrete connections about the behavior and resistance of the corner joint of reinforced concrete,Depending on the available studies and sources in addition to our study,we concluded that each of these effects had a clear role in the behavior and resistance of the corner joint of reinforced concrete under the influence of the negative moment and yield stress.A study of the types of faults that can be reinforced angle joints obtains details and conditions of crushing that are almost identical for all types of steel reinforcement details and the basic requirements for the acceptable behavior of reinforced concrete joints in the installations and the efficiency of the joint and this may help us to prepare for disasters,whether natural or other,as happens with tremors The floor and failure that may occur due to wrong designs or old buildings and the possibility of using those connections to treat those joints and sections in reinforced or unarmed concrete facilities to preserve the safety of humans and buildings from sudden disasters and reduce and reduce risks,as well as qualitative control over the production of concrete connections and sections free from defects to the extreme.

The contribution of steel wallposts to out-of-plane behavior of non-structural masonry walls

For years,non-structural masonry walls have received little attention by code developers and professional engineers.Recently,significant efforts have been made to shed more light on out-of-plane(OOP)behavior of non-structural masonry walls.In updated provisions of the Iranian seismic code,bed joint reinforcements(BJRs)and steel wallposts have been suggested for use.BJRs are horizontal reinforcements;steel wallposts are vertical truss-like elements intended to provide additional OOP restraints for a wall.The contribution of BJRs has previously been investigated by the authors.This study is devoted to investigating the contribution of steel wallposts to the OOP behavior of non-structural masonry walls.Using pre-validated 3D finite element(FE)models,the OOP behavior of 180 non-structural masonry walls with varying configurations and details are investigated.The OOP pressure-displacement curve,ultimate strength,the response modification factor,and the cracking pattern are among the results presented in this study.It is found that steel wallposts,especially those with higher rigidity,can improve the OOP strength of the walls.The contribution of wallposts in the case of shorter length walls and walls with an opening are more pronounced.Results also indicate that masonry walls with wallpost generally have smaller modification factors compared to similar walls without wallpost.

Experimental study on the seismic performance of masonry wall reinforced by cement mortar and polypropylene band

Since masonry structures are prone to collapse in earthquakes,a novel joint reinforcement method with a polypropylene band(PP-band)and cement mortar(CM)has been put forward.Compared with the common reinforcement methods,this method not only facilitates construction but also ensures lower reinforcement cost.To systematically explore the influence of joint reinforcement on the seismic performance of masonry walls,quasi-static tests were carried out on six specimens with different reinforcement forms.The test results show that the joint action of PP-band and CM can significantly improve the specimen′s brittle failure characteristics and enhance the integrity of the specimen after cracking.Compared with the specimen without reinforcement,each of the seismic performance indexes of the joint reinforced specimen had obvious improvement.The maximum increased rate about peak load and ductility of the joint reinforced specimen is 100.6%and 233.4%,respectively.

Laser welding process and strength enhancement of carbon fiber reinforced thermoplastic composites and metals dissimilar joint:A review

Carbon fiber reinforced thermoplastic composites(CFRTP)and metals hybrid structures have been widely used in aircraft lightweight manufacturing.However,due to the significant difference in physical and chemical properties between CFRTP and metals,there are lots of challenges to connect them with high quality.Laser welding has a good application prospect in CFRTP and metals connection,and a significant research progress has been made in the exploration of CFRTP-metal laser joining mechanism,joining process optimization,joining strength improvement and joining defects controlling.However,there are still some problems need to be solved for this technology application.In this paper,the research progress of CFRTP-metal laser joining was summarized in three major aspects:theoretical modeling and simulation analysis,process exploration and parameter optimization,joint performance improvement and process innovation.And,problems and challenges of this technology were discussed,and the outlook of this research was provided.

Energy efficiency enhancement in heterogeneous networks:a joint resource allocation approach

To support the drastic growth of wireless multimedia services and the requirements of ubiquitous access, numerous wireless infrastructures which consume enormous energy, such as macrocell, small cell, distributed antenna systems and wireless sensor networks, have been deployed. Under the background of environmental protection, improving the energy efficiency（EE） in wireless networks is becoming more and more important. In this paper, an EE enhancement scheme in heterogeneous networks（Het Nets） by using a joint resource allocation approach is proposed. The Het Nets consists of a mix of macrocell and small cells. Firstly, we model this strategic coexistence as a multi-agent system in which decentralized resource management inspired from Reinforcement Learning are devised. Secondly, a Q-learning based joint resource allocation algorithm is designed. Meanwhile, with the consideration of the time-varying channel characteristics, we take the long-term learning reward into account. At last, simulation results show that the proposed decentralized algorithm can approximate to centralized algorithm with low-complexity and obtain high spectral efficiency（SE） in the meantime.