Mesoporous materials with the highest surface area were synthesized by hydrothermal treatment from coal-measure kaolin using cetyltrimethylammonium bromide（CTAB）as template.The effect of several factors on surface a...Mesoporous materials with the highest surface area were synthesized by hydrothermal treatment from coal-measure kaolin using cetyltrimethylammonium bromide（CTAB）as template.The effect of several factors on surface area of products also had been discussed.The products were characterized by FT- IR,HRTEM and N 2 adsorption and desorption isotherm plot methods.There was typical structure as Si-O,Si- OH and Si-O-Si of mesoporous materials in the framework of synthesized materials;the pore size distributions of the products showed a sharp peak at 3.82 nm.The effect of hydrothermal treatment time and the amount of template on the specific surface area of mesoporous materials was important,when the Surf/Si=0.135,and hydrothermal time=12 h,and the surface area of the product reached up to 1 070 m2/g,which was higher than other products.展开更多
A direct synthesis method of preparing alkaline earth or transition metal oxides supporting mesoporous materials is reported. Distinguishing from those traditionaltechniques characterized by “synthesis at first and t...A direct synthesis method of preparing alkaline earth or transition metal oxides supporting mesoporous materials is reported. Distinguishing from those traditionaltechniques characterized by “synthesis at first and then modification”, this new method adds the precursor salts that have no perturbation in the strong acid synthetic system but easily form oxides after calcinations, into the initial syntheticmixture, performing the “synthesis” and “modification” in one-pot procedure.展开更多
A Y-zeolite-containing composite material with micro/mesoporous structure had been synthesized from kaolin by means of the in-situ crystallization method. The obtained samples were investigated by XRD and BET methods....A Y-zeolite-containing composite material with micro/mesoporous structure had been synthesized from kaolin by means of the in-situ crystallization method. The obtained samples were investigated by XRD and BET methods. Evaluation of catalytic activity of both the commercial Y-zeolite and the novel Y-zeolite-containing composite material was carried out in the pulse micro-chromatography platform with two probe molecules of different molecular sizes： VGO feedstock and 1,3,5 tri-isopropyl benzene. It was found that the Y-zeolite-containing composite material was richer in external surface and meso-/macro-pores; the Y-zeolite-containing composite material demonstrated a smaller rate of deactivation compared to the commercial Y-zeolite.展开更多
Mesoporous LiFePO4 microspheres were simply synthesized by a low temperature(130℃),template-free hydrothermal route using low cost LiOH,Fe(NO3)3 and NH4H2PO4 as starting raw materials.These microspheres are composed ...Mesoporous LiFePO4 microspheres were simply synthesized by a low temperature(130℃),template-free hydrothermal route using low cost LiOH,Fe(NO3)3 and NH4H2PO4 as starting raw materials.These microspheres are composed of densely aggregated LiFePO4 nanoparticles and filled with interconnected mesochannels,which demonstrates not only a high tap density(≥1.4 g cm-3),a high capacity of 150 mAh g-1(～90% of its theoretical capacity) at 0.5 C rate,but also a ≥ 80% utilization of its theoretical capacity at a high rate of 1 C.In addition,the hydrothermal synthesis developed in this work is simple and cost-effective,it may provide a new route for production of the LiFePO4 material in battery applications.展开更多
基金Funded by Social Development Plan of Jiangsu Department of the Science and Technology,Jiangsu,China(No.BS2007038)
文摘Mesoporous materials with the highest surface area were synthesized by hydrothermal treatment from coal-measure kaolin using cetyltrimethylammonium bromide（CTAB）as template.The effect of several factors on surface area of products also had been discussed.The products were characterized by FT- IR,HRTEM and N 2 adsorption and desorption isotherm plot methods.There was typical structure as Si-O,Si- OH and Si-O-Si of mesoporous materials in the framework of synthesized materials;the pore size distributions of the products showed a sharp peak at 3.82 nm.The effect of hydrothermal treatment time and the amount of template on the specific surface area of mesoporous materials was important,when the Surf/Si=0.135,and hydrothermal time=12 h,and the surface area of the product reached up to 1 070 m2/g,which was higher than other products.
文摘A direct synthesis method of preparing alkaline earth or transition metal oxides supporting mesoporous materials is reported. Distinguishing from those traditionaltechniques characterized by “synthesis at first and then modification”, this new method adds the precursor salts that have no perturbation in the strong acid synthetic system but easily form oxides after calcinations, into the initial syntheticmixture, performing the “synthesis” and “modification” in one-pot procedure.
文摘A Y-zeolite-containing composite material with micro/mesoporous structure had been synthesized from kaolin by means of the in-situ crystallization method. The obtained samples were investigated by XRD and BET methods. Evaluation of catalytic activity of both the commercial Y-zeolite and the novel Y-zeolite-containing composite material was carried out in the pulse micro-chromatography platform with two probe molecules of different molecular sizes： VGO feedstock and 1,3,5 tri-isopropyl benzene. It was found that the Y-zeolite-containing composite material was richer in external surface and meso-/macro-pores; the Y-zeolite-containing composite material demonstrated a smaller rate of deactivation compared to the commercial Y-zeolite.
基金supported by the National Basic Research Program of China (2009CB220103)
文摘Mesoporous LiFePO4 microspheres were simply synthesized by a low temperature(130℃),template-free hydrothermal route using low cost LiOH,Fe(NO3)3 and NH4H2PO4 as starting raw materials.These microspheres are composed of densely aggregated LiFePO4 nanoparticles and filled with interconnected mesochannels,which demonstrates not only a high tap density(≥1.4 g cm-3),a high capacity of 150 mAh g-1(～90% of its theoretical capacity) at 0.5 C rate,but also a ≥ 80% utilization of its theoretical capacity at a high rate of 1 C.In addition,the hydrothermal synthesis developed in this work is simple and cost-effective,it may provide a new route for production of the LiFePO4 material in battery applications.