Observation of therapeutic effect of lamp irradiation combined with purple gromwell oil gauze on alleviating intestinal colic in patients

BACKGROUND Intestinal colic is a common complication in patients who have undergone radical surgery for colorectal cancer.Traditional Chinese medicine has advantages,including safety and stability,for the treatment of intestinal colic.Lamp irra-diation for abdominal ironing has been applied in the treatment of many gas-trointestinal diseases.Purple gromwell oil has the effects of clearing heat,cooling blood,reducing swelling,and relieving pain.RESULTS The general effective rate in the observation group was 95.00%,which was significantly higher than that in the control group(86.67%,P<0.05).Before treatment,there was no significant difference in the duration of symptoms between the groups(P>0.05).After 1,2,3,and 4 d of treatment,the duration of symptoms in both groups were decreased,and the duration in the observation group was significantly lower than that in the control group(96.54±9.57 vs 110.45±11.23,87.26±12.07 vs 104.44±11.68,80.45±16.21 vs 99.44±14.95,73.18±15.58 vs 92.17±14.20;P<0.05).After 1,3,5,and 7 d of treatment,the NRS scores in both groups were decreased,and the NRS scores in the observation group were significantly lower than those in the control group(3.56±0.41 vs 4.04±0.58,3.07±0.67 vs 3.74±1.02,2.52±0.76 vs 3.43±0.85,2.03±0.58 vs 3.03±0.82;P<0.05).There was no significant difference in the rate of adverse reaction occurrence between the groups(P>0.05).CONCLUSION The use of lamp irradiation combined with purple gromwell oil gauze in patients with intestinal colic after radical surgery for colorectal cancer can reduce symptom duration,alleviate intestinal colic,and improve treatment efficacy,and this approach is safe.It is worth promoting the use of this treatment in clinical practice.

Performance Analysis of Plant Shells/PVC Composites under Corrosion and Aging Conditions

To make full use of plant shellfibers(rice husk,walnut shell,chestnut shell),three kinds of wood-plastic com-posites of plant shellfibers and polyvinyl chloride(PVC)were prepared.X-ray diffraction analysis was carried out on three kinds of plant shellfibers to test their crystallinity.The aging process of the composites was conducted under 2 different conditions.One was artificial seawater immersion and xenon lamp irradiation,and the other one was deionized water spray and xenon lamp irradiation.The mechanical properties(tensile strength,flexural strength,impact strength),changes in color,water absorption,Fourier transform infrared spectroscopy(FTIR),and microstructures of the composites before and after the two aging experiments were analyzed.The results showed that the chestnut shell had the highest crystallinity,which was 42%.The chestnut shell/PVC composites had the strongest interface bonding,the least internal defects,and the best general mechanical properties among the three composites.Its tensile strength,bending strength and impact strength were 23.81 MPa,34.12 MPa,and 4.32 KJ·m^(-2),respectively.Comparing the two aging conditions,artificial seawater immersion and xenon lamp irradiation destroyed the quality of the combination of plant shellfibers and PVC,making the internal defects of the composites increase.This made the water absorption ability and changes in the color of the composites more obvious and led to a great decrease in the mechanical properties.The general mechanical properties of the chestnut shell/PVC composites were the best,but their water absorption ability changed more obviously.