In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters （i.e. austenitizing temperature and time, and austempering temperature and ...In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters （i.e. austenitizing temperature and time, and austempering temperature and time） on microstructure and mechanical properties of LZQT500-7 ductile iron dense bars with 172 mm in diameter which were produced by horizontal continuous casting （HCC）. The results show that the major factors influencing the hardness of austempered ductile iron （ADI） are austenitizing temperature and austempering temperature. The fraction of retained austenite increases as the austenitizing and austempering temperatures increase. When austenitizing temperature is low, acicular ferrite and retained austenite can be efifciently obtained by appropriately extending the austenitizing time. The proper austmepering time could ensure enough stability of retained austenite and prevent high carbon austenite decomposition. The optimal mechanical properties of ADI can be achieved with the fol owing process parameters： austenitizing temperature and time are 866 ＆#176;C and 135 min, and austempering temperature and time are 279 ＆#176;C and 135 min, respectively. The microstructure of ADI under the optimal austempering process consists of ifne acicular ferrite and a smal amount of retained austenite, and the hardness, tensile strength, yield strength, elongation and impact toughness of the bars are HBW 476, 1670 MPa, 1428 MPa, 2.93%and 25.7 J, respectively.展开更多
Ductile iron bars(DIBs) with a diameter of 145 mm, used for plunger pump production, were made by the horizontal continuous casting(HCC). The microstructure of the samples cut at three locations with different distanc...Ductile iron bars(DIBs) with a diameter of 145 mm, used for plunger pump production, were made by the horizontal continuous casting(HCC). The microstructure of the samples cut at three locations with different distances away from the surface(~20 mm from the surface, half of the radius and the center of the HCCDIBs)were investigated. The mechanical properties were measured by tensile and torsion tests. Results show that after the spheroidization of graphite, the iron matrix incorporates the nodules of Format I, Size 8 close to the surface, Format I, Size 7 at the half of the radius from the surface, and Format II, Size 6 in the centre of the bar,according to the ASTM A247 standard. The content of pearlite in the matrix changes from 55%(~20 mm from the surface) to 70%(half of the radius) and 80%(the center of the HCCDIBs). The strengths in tension are 552, 607 and 486 MPa with the elongations of 12.5%, 10.5% and 5.8% in samples cut at these three locations from the surface to the centre, respectively. The strength in torsion is equal to 558, 551 and 471 MPa at corresponding torsion angles of 418°, 384° and 144° respectively to the same distance from the bar surface. Fracture in tension is manifested via crack propagation through the interface between graphite nodules and matrix(Mode I), while in torsion the fracture is caused by the shear of graphite nodules(Mode II). It is shown that the transition between two fracture modes is also dependent on the size of graphite nodule. Typically, fracture Mode I was observed for nodules of smaller diameter(less than 22.7 μm) and fracture Mode II was seen for nodules of greater diameter(more than 24.8 μm).展开更多
It is important to improve the comprehensive performance of the ductile iron bars(DIBs)for the cylinder block of the extra high pressure hydraulic plunger pump and accelerate the industrial application.In this work,th...It is important to improve the comprehensive performance of the ductile iron bars(DIBs)for the cylinder block of the extra high pressure hydraulic plunger pump and accelerate the industrial application.In this work,the LZQT600-3 DIBs with the diameter of 145 mm were prepared by the horizontal continuous casting(HCC)process,that is,LZQT600-3 HCCDIBs.The microstructure and room temperature tensile properties of different sections[left-edge(surface layer),left-1/2R(left half of the radius),and the center of the HCCDIBs]were studied.The results show that the spheroidization of LZQT600-3 HCCDIBs matrix from the left-edge,left-1/2R to the center is at nodulizing grade II and above.As the cooling rate gradually decreases from surface to the center of the HCCIBs,the number of spheroidized graphite is gradually reduced,the size is gradually increased,the shape factor is decreased,and the pearlite content and lamellate spacing are increased.Along the horizontal direction of the section,the hardness of the material is distributed symmetrically around the center of the HCCDIBs.In the vertical direction,the hardness distribution in the center of the HCCDIBs is asymmetrical due to the gravity during the solidification process.Therefore,the microstructure in the lower part of the section solidifies relatively quickly.The left-edge has the best tensile mechanical properties,and the ultimate tensile strength,yield tensile strength and elongation are 597.3 MPa,418.5 MPa and 9.6%,respectively.The tensile fracture belongs to the ductile-brittle hybrid fracture.The comprehensive performances of LZQT600-3 HCCDIBs meet the actual application requirements of ultra-high pressure hydraulic plunger pump cylinder.展开更多
基金financially supported by the fund of the Key Projects of Shaanxi Provincial International Technology Cooperation Plan(2013KW16)the Scientific Research Program funded by Shaanxi Provincial Education Department(2013JK0914)+2 种基金the State Key Laboratory of Solidifi cation Processing in NWPU(SKLSP201115)the Scientific Research Project of Xi'an University of Technology(2013CX004)the fund of the Key Laboratory of Electrical Materials and Infi ltration Technology of Shaanxi Province,China(2014)
文摘In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters （i.e. austenitizing temperature and time, and austempering temperature and time） on microstructure and mechanical properties of LZQT500-7 ductile iron dense bars with 172 mm in diameter which were produced by horizontal continuous casting （HCC）. The results show that the major factors influencing the hardness of austempered ductile iron （ADI） are austenitizing temperature and austempering temperature. The fraction of retained austenite increases as the austenitizing and austempering temperatures increase. When austenitizing temperature is low, acicular ferrite and retained austenite can be efifciently obtained by appropriately extending the austenitizing time. The proper austmepering time could ensure enough stability of retained austenite and prevent high carbon austenite decomposition. The optimal mechanical properties of ADI can be achieved with the fol owing process parameters： austenitizing temperature and time are 866 ＆#176;C and 135 min, and austempering temperature and time are 279 ＆#176;C and 135 min, respectively. The microstructure of ADI under the optimal austempering process consists of ifne acicular ferrite and a smal amount of retained austenite, and the hardness, tensile strength, yield strength, elongation and impact toughness of the bars are HBW 476, 1670 MPa, 1428 MPa, 2.93%and 25.7 J, respectively.
基金financially supported by the Shaanxi Provincial Science and Technology Achievement Transfer and Promotion Plan-absorb Achievement Transformation Project(No.2017CGZH-XNGJ-03)Shaanxi Provincial Education Department Scientific Research Program Project-service Local Special Industrialization Cultivation Project(No.17JF018)+1 种基金Xi'an Science and Technology Planning Project Science and Technology Innovation Guide Projects(No.201805037YD15CG21(19))Xi'an University of Technology Scientific and Technological Achievement Transformation Project-technical Requirement Solving Project of Enterprises(No.2018-1)
文摘Ductile iron bars(DIBs) with a diameter of 145 mm, used for plunger pump production, were made by the horizontal continuous casting(HCC). The microstructure of the samples cut at three locations with different distances away from the surface(~20 mm from the surface, half of the radius and the center of the HCCDIBs)were investigated. The mechanical properties were measured by tensile and torsion tests. Results show that after the spheroidization of graphite, the iron matrix incorporates the nodules of Format I, Size 8 close to the surface, Format I, Size 7 at the half of the radius from the surface, and Format II, Size 6 in the centre of the bar,according to the ASTM A247 standard. The content of pearlite in the matrix changes from 55%(~20 mm from the surface) to 70%(half of the radius) and 80%(the center of the HCCDIBs). The strengths in tension are 552, 607 and 486 MPa with the elongations of 12.5%, 10.5% and 5.8% in samples cut at these three locations from the surface to the centre, respectively. The strength in torsion is equal to 558, 551 and 471 MPa at corresponding torsion angles of 418°, 384° and 144° respectively to the same distance from the bar surface. Fracture in tension is manifested via crack propagation through the interface between graphite nodules and matrix(Mode I), while in torsion the fracture is caused by the shear of graphite nodules(Mode II). It is shown that the transition between two fracture modes is also dependent on the size of graphite nodule. Typically, fracture Mode I was observed for nodules of smaller diameter(less than 22.7 μm) and fracture Mode II was seen for nodules of greater diameter(more than 24.8 μm).
基金the support from the International Science and Technology Cooperation Program of Shaanxi Province(No.2023-GHZD-50)the Projects of Major Innovation Platforms for Scientific and Technological and Local Transformation of Scientific and Technological Achievements of Xi’an(No.20GXSF0003)+1 种基金the Projects of Major Scientific and Technological Achievements Local Transformation of Xi’an(No.2022JH-ZDZH-0039)the Higher Education Institution Discipline Innovation and Intelligence Base of Shaanxi Provincial(No.S2021-ZC-GXYZ-0011)。
文摘It is important to improve the comprehensive performance of the ductile iron bars(DIBs)for the cylinder block of the extra high pressure hydraulic plunger pump and accelerate the industrial application.In this work,the LZQT600-3 DIBs with the diameter of 145 mm were prepared by the horizontal continuous casting(HCC)process,that is,LZQT600-3 HCCDIBs.The microstructure and room temperature tensile properties of different sections[left-edge(surface layer),left-1/2R(left half of the radius),and the center of the HCCDIBs]were studied.The results show that the spheroidization of LZQT600-3 HCCDIBs matrix from the left-edge,left-1/2R to the center is at nodulizing grade II and above.As the cooling rate gradually decreases from surface to the center of the HCCIBs,the number of spheroidized graphite is gradually reduced,the size is gradually increased,the shape factor is decreased,and the pearlite content and lamellate spacing are increased.Along the horizontal direction of the section,the hardness of the material is distributed symmetrically around the center of the HCCDIBs.In the vertical direction,the hardness distribution in the center of the HCCDIBs is asymmetrical due to the gravity during the solidification process.Therefore,the microstructure in the lower part of the section solidifies relatively quickly.The left-edge has the best tensile mechanical properties,and the ultimate tensile strength,yield tensile strength and elongation are 597.3 MPa,418.5 MPa and 9.6%,respectively.The tensile fracture belongs to the ductile-brittle hybrid fracture.The comprehensive performances of LZQT600-3 HCCDIBs meet the actual application requirements of ultra-high pressure hydraulic plunger pump cylinder.