Preparation of Laser Cladding Coating Undercooling Cu-based Alloy and Co on Non-equilibrium Solidification Structure

The effect of the gradient content of Co element on the solidification process of Cu-based alloy under deep under cooling conditions was explored.The non-equilibrium solidification structure of the under cooled alloy samples were analyzed.It is found that the rapidly solidified alloy has undergone twice grain refinement during the undercooling process.Characterization and significance of the maximum undercooling refinement structure of Cu60Ni35Co5 at T=253 K were analyzed.High-density defects were observed,such as dislocations,stacking faults networks,and twinning structures.The standard FCC diffraction pattern represents that it is still a single-phase structure.Based on the metallographic diagram,EBSD and TEM data analysis,it is illustrated that the occurrence of grain refinement under high undercooling is due to stress induced recrystallization.In addition,the laser cladding technology is used to coat Co-based alloy(Stellite12) coating on 304 stainless steel substrate;the microstructure of the coating cross-section was analyzed.It was found that the microstructure of the cross-section is presented as columnar crystals,planar crystals,and disordered growth direction,so that the coating has better hardness and wear resistance.By electrochemical corrosion of the substrate and coating,it can be seen that the Co and Cr elements present in the coating are more likely to form a dense passivation film,which improved the corrosion resistance of the coating.

Microstructure and Properties of AlCoCrFeNiTi High-Entropy Alloy Coatings Prepared by Laser Cladding

21-4N(5Cr21Mn9Ni4N)is extensively employed in the production of engine valves,operating under severe conditions.Apart from withstanding high-temperature gas corrosion,it must also endure the impact of cylinder explosion pressure.The predominant failure mode of 21-4N valves is abrasive wear.Surface coatings serve as an effective approach to prevent such failures.In this investigation,Laser cladding technology was utilized to fabricate AlCoCrFeNiTi high entropy alloy coatings onto the surfaces of 21-4N valves.According to the findings,the cladding zone has a normal dendritic microstructure,a good substrate-to-cladding layer interaction,and no obvious flaws.In terms of hardness,the cladding demonstrates an average hardness of 620 HV.The hardness has increased by 140%compared to the substrate.The average hardness of the cladding remains at approximately 520 HV even at elevated temperatures.Regarding frictional wear performance,between 400℃and 800℃,the cladding layer exhibits an average friction coefficient of 0.4,with the primary wear mechanisms being abrasive wear,adhesive wear,and a minor degree of plastic deformation.

Process Parameters Optimization of Laser Cladding for HT200 with 316L Coating Based on Response Surface Method

In order to improve the sealing surface performance of gray cast iron gas gate valves and achieve precise molding control of the cladding layer,as well as to reveal the influence of laser cladding process parameters on the morphology and structure of the cladding layer,we prepared the 316L coating on HT 200 by using Design-Expert software central composite design(CCD)based on response surface analysis.We built a regression prediction model and analyzed the ANOVA with the inspection results.With a target cladding layer width of 3.5 mm and height of 1.3 mm,the process parameters were optimized to obtain the best combination of process parameters.The microstructure,phases,and hardness variations of the cladding layer from experiments with optimal parameters were analyzed by the metallographic microscope,confocal microscope,and microhardness instrument.The experimental results indicate that laser power has a significant impact on the cladding layer width,followed by powder feed rate;scan speed has a significant impact on the cladding layer height,followed by powder feed rate.The HT200 substrate and 316L can metallurgically bond well,and the cladding layer structure consists of dendritic crystals,columnar crystals,and equiaxed crystals in sequence.The optimal process parameter combination satisfying the morphology requirements is laser power(A)of 1993 W,scan speed(B)of 8.949 mm/s,powder feed rate(C)of 1.408 r/min,with a maximum hardness of 1564.3 HV0.5,significantly higher than the hardness of the HT200 substrate.

Microstructure and tribological properties of laser cladding Fe-based coating on pure Ti substrate

Fe-based coating was produced on pure Ti substrate by the laser cladding technology. The composition and microstructure of the fabricated coating were analyzed by scanning electron microscopy （SEM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM） technique. The tribological properties were tested through sliding against AISI52100 steel ball at different normal loads and sliding speeds. Besides, the morphologies of the worn surfaces and wear debris were analyzed by scanning electron microscopy （SEM） and three dimensional （3D） non-contact surface mapping. The results show that the prepared Fe-based coating has a high hardness of about 860 HV0.2 and exhibits an average wear rate of （0.70-2.32）×10-6 mm3/（N-m）, showing that the Fe-based coating can greatly improve the wear resistance of pure Ti substrate. The wear mechanism of the coating involves moderate adhesive and abrasive wear.

Interface characteristics of Al_2O_3－13%TiO_2 ceramic coatings prepared by laser cladding

Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.

Corrosion behavior of Hastelloy C22 coating produced by laser cladding in static and cavitation acid solution

The Hastelloy C22 coatings on Q235 steel substrate were produced by high power diode laser cladding technique. Their corrosion behaviors in static and cavitation hydrochloric, sulfuric and nitric acid solutions were investigated. The electrochemical results show that corrosion resistance of coatings in static acid solutions is higher than that in cavitation ones. In each case, coating corrosion resistance in descending order is in nitric, sulfuric and hydrochloric acid solutions. Obvious erosion-corrosion morphology and serious intercrystalline corrosion of coating are noticed in cavitation hydrochloric acid solution. This is mainly ascribed to the aggressive ions in hydrochloric acid solution and mechanical effect from cavitation bubbles collapse. While coating after corrosion test in cavitation nitric acid solution shows nearly unchanged surface morphology. The results indicate that the associated action of cavitation and property of acid solution determines the corrosion development of coating. Hastelloy C22 coating exhibits better corrosion resistance in oxidizing acid solution for the stable formation of dense oxide film on the surface.

Microstructure and high temperature tribological behavior of laser cladding Ni60A alloys coatings on 45 steel substrate

The crack-free Ni60 A coating was fabricated on 45 steel substrate by laser cladding and the microstructure including solidification characteristics, phases constitution and phase distribution was systematically investigated. The high temperature friction and wear behavior of the cladding coating and substrate sliding against GCr15 ball under different loads was systematically evaluated. It was found that the coating has homogenous and fine microstructure consisting of γ（Ni） solid solution, a considerable amount of network Ni-Ni3 B eutectics, m^23C6 with the floret-shape structure and Cr B with the dark spot-shape structure uniformly distributing in interdendritic eutectics. The microhardness of the coating is about 2.6 times as much as that of the substrate. The coating produces higher friction values than the substrate under the same load condition, but the friction process on the coating keeps relatively stable. Wear rates of the coating are about 1/6.2 of that of the substrate under the higher load（300 g）. Wear mechanism of the substrate includes adhesion wear, abrasive wear, severe plastic deformation and oxidation wear, while that of the coating is merely a combination of mild abrasive wear and moderate oxidation wear.

Microstructure and mechanical properties of Ni-based composite coatings reinforced by in situ synthesized TiB_2 + TiC by laser cladding

A Ni-based composite coating reinforced by in situ synthesized TiB2 and TiC particles was fabricated on Ti6A14V by laser cladding. An attempt was made to correlate the thermodynamic predictions and experimental observation. The micro- structure and the microhardness profile across the coating were investigated by means of X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and a hardness tester. It is found that the coating mainly consists of a large number of reinforcements （black blocky TiB2, flower-like or equiaxial TiC, and fine acicular CrB） and the 7 matrix. The hardness of TiB2, TiC, and CrB reinforcements is much higher than that of the 7 matrix. The dispersive distribu- tion of such high hardness reinforcements causes the increase in hardness of the whole coating. The average value of the hard- ness is approximately Hv0.2 700 in the coating. The hardness of the coating is obviously higher than that of the substrate due to the dispersion strengthening of reinforcements.

Microstructural characterization of titanium matrix composite coatings reinforced by in situ synthesized TiB + TiC fabricated on Ti6Al4V by laser cladding

Titanium-based composite coatings reinforced by in situ synthesized TiB and TiC particles between titanium and B4C were successfully fabricated on Ti6Al4V by laser cladding. Phase constituents of the coatings were predicted by thermodynamic calculations in the Ti-BnC-Al and Ti-B-C-Al systems, respectively, and were validated well by X-ray diffraction （XRD） analysis results. Microstructural and metallographic analyses were made by scanning electron microscopy （SEM） and electron probe micro-analysis （EPMA）. The results show that the coatings are mainly composed of α-Ti cellular dendrites and the eutecticum in which a large number of needle-shaped TiB and a few equiaxial TiC particles are embedded. C is enriched in α-Ti cellular dendrites and far exceeds the theoretical maximum dissolubility, owing to the extension of saturation during laser cladding. The coatings have a good metallurgical bond with the substrate due to the existence of the dilution zone, in which a great amount of lamella β-Ti grains consisting of a thin needle-shaped martensitic microstructure are present and grow parallel to the heat flux direction; a few TiB and TiC reinforcements are observed at the boundaries of initial β-Ti grains.

Effect of Y_2O_3 Content on Microstructure of Gradient Bioceramic Composite Coating Produced by Wide-Band Laser Cladding

To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And effect of Y2O3 content on gradient bioceramic composite coating was studied. The experimental results indicate that adding rare earth can refine grain. Different rare earth contents affect formation of HA and β-TCP in bioceramic coating. When the content of rare earth ranges from 0.4% to 0.6%, the active extent of rare earth in synthesizing HA and β-TCP is the best, which indicates that “monosodium glutamate” effect of rare earth plays a dominant role. However, when rare earth content is up to 0.8%, the amount of synthesizing HA and β-TCP in coating conversely goes down, which demonstrates that rare earth gradually losts its catalysis in manufacturing HA and β-TCP.

Microstructure of Cu-based Amorphous Composite Coatings on AZ91D Magnesium Alloy by Laser Cladding

To improve the sliding wear resistance of AZ91D magnesium alloy, Cu-based amorphous composite coatings made of CuaTTi34Zr11Nis and Cu47Ti34Zr11Ni8＋20 wt pct SiC powders were fabricated on AZ91D magnesium alloy by laser cladding, respectively. SEM （scanning electron microscopy）, EDS （energy dispersive X-ray spectroscopy）, XRD （X-ray diffraction） and TEM （transmission electron microscopy） techniques were employed to study the phases of the coatings. The results show that the coatings mainly consist of amorphous phase and different intermetallic compounds. The reason of formation of amorphous phase and the function of SiC particles were explained in details.

Superior corrosion resistance-dependent laser energy density in(CoCrFeNi)95Nb5 high entropy alloy coating fabricated by laser cladding

(CoCrFeNi)95Nb5 high entropy alloy(HEA)coatings were successfully fabricated on a substrate of Q235 steel by laser cladding technology.These(CoCrFeNi)95Nb5 HEA coatings possess excellent properties,particularly corrosion resistance,which is clearly superior to that of some typical bulk HEA and common engineering alloys.In order to obtain appropriate laser cladding preparation process parameters,the effects of laser energy density on the microstructure,microhardness,and corrosion resistance of(CoCrFeNi)95Nb5 HEA coating were closely studied.Results showed that as the laser energy density increases,precipitation of the Laves phase in(CoCrFeNi)95Nb5 HEA coating gradually decreases,and diffusion of the Fe element in the substrate intensifies,affecting the integrity of the(CoCrFeNi)95Nb5 HEA.This decreases the microhardness of(CoCrFeNi)95Nb5 HEA coatings.Moreover,the relative content of Cr2O3,Cr(OH)3,and Nb2O5 in the surface passive film of the coating decreases with increasing energy density,causing corrosion resistance to decrease.This study demonstrates the controllability of a high-performance HEA coating using laser cladding technology,which has significance for the laser cladding preparation of other CoCrFeNi-system HEA coatings.

Microstructure and properties of WC-12Co composite coatings prepared by laser cladding

A comprehensive study of the phase composition, microstructure evolution, microhardness and wear performance of WC-12 Co composite coatings fabricated by laser cladding using coaxial powder-feed mode was presented. It was shown that a combination of high scan speed and high laser energy density made WC on the edge of WC-12 Co composite powders partially melt in liquid Co and 304 stainless steel matrix, and then new carbides consisting of lamellar WC and herringbone M3 W3 C(M=Fe,Co) were formed. Meanwhile, WC-12 Co composite coatings with no porosity, cracks and drawbacks like decarburization were obtained, showing high densification and good metallurgical bonding with the substrate. Furthermore, a considerably high microhardness of HV0.3 1500-1600, low coefficient of friction of 0.55 and wear rate of(2.15±0.31)×10-7 mm3/(N·m) were achieved owing to the synergistic effect of excellent metallurgical bonding and fine microstructures of composite coating under laser power of 1500 W.

Microstructure,microhardness and corrosion resistance of laser cladding Ni−WC coating on AlSi5Cu1Mg alloy

The microstructure,microhardness,and corrosion resistance of laser cladding Ni−WC coating on the surface of AlSi5Cu1Mg alloy were investigated by scanning electron microscopy,X-ray diffraction,microhardness testing,immersion corrosion testing,and electrochemical measurement.The results show that a smooth coating containing NiAl,Ni_(3)Al,M_(7)C_(3),M_(23)C_(6)phases(M=Ni,Al,Cr,W,Fe)and WC particles is prepared by laser cladding.Under a laser scanning speed of 120 mm/min,the microhardness of the cladding coating is 9−11 times that of AlSi5Cu1Mg,due to the synergistic effect of excellent metallurgical bond and newly formed carbides.The Ni−WC coating shows higher corrosion potential(−318.09 mV)and lower corrosion current density(12.33μA/cm^(2))compared with the matrix.The crack-free,dense cladding coating obviously inhibits the penetration of Cl^(−)and H^(+),leading to the remarkedly improved corrosion resistance of cladding coating.

Pulsed Nd:YAG laser cladding of high silicon content coating on low silicon steel

A pulsed Nd：YAG （yttrium aluminum garnet） laser-based technique was employed to clad low silicon steel with preplaced Si and Fe mixed powders for high Si content. The surface morphology, microstructural evolution, phase composition, and Si distribution, within the obtained cladding coatings, were characterized by optical microscopy （OM）, field emission scanning electron microscopy （FE-SEM）, with associated energy dispersive spectroscopy （EDS）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. The microhardness was also measured along the depth direction of the specimens, A crack- and pore-free cladding coating through excellent metallurgical bonding with the substrate was successfully prepared on low silicon steel by means of optimized single-track and multi-track laser cladding. The phases of the coating are a-Fe, T-Fe, and FeSi. The high microhardness of the lasercladding zone is considered as an increase in Si content and as the refined microstructure produced by the laser treatment. The Si contents of the cladding coatings were about 5.8wt% in the single-track cladding and 6.5wt% in the multi-track cladding, respectively.

Ceramic-Metal Composite Coating by Laser Cladding

Four kinds of ceramics (silicon carbide, boron carbide, aluminum oxide and tungsten carbide) were added into Ni base self-fluxing alloy as reinforcing materials in order to obtain metalceramic composite coating by means of laser cladding. A lot of experiments have been carried out to test the processability of the four kinds of ceramics with different sizes and contents. The microstructures of sintered tungsten carbide (S-WC) and cast tungsten carbide (C-WC) reinforced Ni base alloy coatings were analysed, the distortion regulation of laser clad specimens was revealed. The wear resistance of the composite coating has been tested.

Fabrication and microstructure of Fe-based amorphous composite coatings by laser cladding

Fe-based amorphous composite coatings were fabricated on AISI 1045 steel by laser cladding. The results of the X- ray diffraction and transmission electron microscopy analyses .show the coating is composed of an amorphous phase in majority and a nanocrystaUine phuse in m,inority. Phase composition of the coating changes along the depth of the coating. The reasonable scanning speed for fabricating an amorphous composite coating is 3 500 mm/min when the laser power is 4 800 W and the laser beam diameter is 2 mm. If the scanning speed is lower than 3 500 mm/min, the intensity of the two main diffraction peaks in X-ray diffraction patterns of the coatings decreases with the scanning speeds increasing. At the same time, a broad halo peak emerges and enlarges. High laser power and fast scanning speed are the essential conditions of amorphization. The coating exhibits high microhardness.

Microstructures and properties of Fe-Co-B-Si-Nb coating prepared by laser cladding and remelting

High power laser cladding of [ （ Fe0. 5 Co0. 5 ） 0. 75 B0. 2 Si0.05 ] 95. 7 Nb4. 3 powder mixture afier-remelting was performed to fabricate Fe-based metallic glass coating on the surface of steel of China Classification Society： Grade B （CCS-B）. Scanning electron microscopy （SEM）, X-ray diffraction （XRD）, transmission electron microscopy （TEM） with energy dispersive spectrometer （EDS）, Vickers hardness tester and corrosion resistance tester were employed to characterize microstructures and evaluate properties of this coating. According to the results of SEM, XRD and TEM, the cladding coating consisted of nanocrystalline embedded in amorphous phase. EDS data indicated that Nb segregated in the amorphous matrix. The results of hardness test revealed that the hardness of the top layer was higher than that of the inner layer of the coating. The coating exhibited excellent corrosion resistance in a 3.5% NaCl solution.

Microstructure and wear resistance of AlCrFeNiMo_(0.5)Si_(x) high-entropy alloy coatings prepared by laser cladding

In recent years,the coating prepared by laser cladding has attracted much attention in the field of wear research.In this work,AlCrFeNiMo_(0.5)Si_(x)(x=0,0.5,1.0,1.5,2.0)high-entropy alloy coatings were designed and prepared on Q235 steel by laser cladding.The effect of Si content on microstructure,microhardness and wear resistance of the coatings was studied in detail.The results indicate that the AlCrFeNiMo_(0.5)Si_(x) highentropy alloy coatings show an excellent bonding between substrate and the cladding layer.The AlCrFeNiMo_(0.5)Si_(x) coatings are composed of nano-precipitated phase with BCC structure and matrix with ordered B2 structure.With the addition of Si,the white phase(Cr,Mo)_(3)Si with cubic structure appears in the interdendritic,and the morphology of the coating(x=2.0)transforms into lamellar eutectic-like structures.The addition of Si enhances the microhardness and significantly improves the wear resistance of the coatings.As x increases from 0 to 2.0,the average hardness of the cladding zone increases from 632 HV to 835 HV,and the wear rate decreases from 1.64×10^(-5) mm^(3)·(N·m)^(-1) to 5.13×10^(-6) mm^(3)·(N·m)^(-1).When x≥1.5,the decreasing trend of the wear rate gradually slows down.The wear rates of Si1.5 and Si2.0 coatings are 5.85×10^(-6) mm^(3)·(N·m)^(-1) and 5.13×10^(-6) mm^(3)·(N·m)^(-1),respectively,which is an order of magnitude lower than that of Q235 steel.

Influence of Zirconia on Hydroxyapatite Coating on Ti-Alloy by Laser Cladding

Coating titanium alloy with the bioceramic material hydroxyapatite(HAP) has been used to improve the poor osteoinductive properties of pure titanium alloy. But in clinical applications, the mechanical failure of HAP-coated titanium alloy implant suffered at the interface of the HAP coatings and titanium alloy substrate will be a potential weakness in prosthesis. Yttria-stablized zirconia (YSZ) is expected to enhance the mechanical properties of the HAP coating and reduce the coefficient of thermal expansion difference between the coated layer and the substrate. These may reinforce the bonding strength between the coatings and the substrate. In this paper, HAP/YSZ composite coatings were cladded by laser. The effects of zirconia on the microstructure, mechanical properties and formation of tricalcium phosphate (TCP, Ca 3(PO 4) 2) of the HAP/YSZ composite coatings were evaluated. XRD, SEM and TEM were used to investigate the phase composition, microstructure and morphology of the coatings. The experimental results showed that adding YSZ in coatings was favorable to the composition and stability of HAP, and to the improvement of the adhesion strength, microhardness and microtoughness. A well uniform, crack-free coating of HAP/YSZ composites was formed on Ti-alloy substrate by laser cladding.