Bulging Distortion of Austenitic Stainless Steel Sheet on the Partially Penetrated Side of Non-Penetration Lap Laser Welding Joint

Non-penetration laser welding of lap joints in austenitic stainless steel sheets is commonly preferred in fields where the surface quality is of utmost importance.However,the application of non-penetration welded austenitic stainless steel parts is limited owing to the micro bulging distortion that occurs on the back surface of the partial penetration side.In this paper,non-penetration lap laser welding experiments,were conducted on galvanized and SUS304 austenitic stainless steel plates using a fiber laser,to investigate the mechanism of bulging distortion.A comparative experiment of DC01 galvanized steel-Q235 carbon steel lap laser welding was carried out,and the deflection and distortion profile of partially penetrated side of the sheets were measured using a noncontact laser interferometer.In addition,the cold-rolled SUS304 was subjected to heat holding at different temperatures and water quenching after bending to characterize its microstructure under tensile and compressive stress.The results show that,during the heating stage of the thermal cycle of laser lap welding,the partial penetration side of the SUS304 steel sheet generates compressive stress,which extrudes the material in the heat-affected zone to the outside of the back of the SUS304 steel sheet,thereby forming a bulge.The findings of these experiments can be of great value for controlling the distortion of the partial penetrated side of austenitic stainless steel sheet during laser non-penetration lap welding.

Lap-Shear Performance of Weld-Bonded Mg Alloy and Austenitic Stainless Steel in Three-Sheet Stack-Up

With the growing interest in utilizing Mg and austenitic stainless steel(ASS)in the automotive sector,joining them together in three-sheet configuration is inevitable.However,achieving this task presents considerable challenges due to the large differences in their physical,metallurgical and mechanical properties.To overcome these challenges,the feasibility of using weld-bonding to join Mg alloy/ASS/ASS was investigated.The nugget formation,interface characteristics,microstructure and mechanical properties of the joints were investigated.The results show that the connection between the Mg alloy and upper ASS was achieved through the combined effect of the cured adhesive and weld-brazing in the weld zone.On the other hand,a metallurgical bond was formed at the ASS/ASS interface.The Mg nugget microstructure exhibited fine columar grains composed predominantly of primaryα-Mg grains along with a eutectic mixture ofα-Mg andβ-Mg17Al12.The nugget formed at the ASS/ASS interface consisted largely of columnar grains of austenite,with some equiaxed dendritic grains formed at the centerline of the joint.The weld-bonded joints exhibited an average peak load and energy absorption of about 8.5 kN and 17 J,respectively(the conventional RSW joints failed with minimal or no load application).The failure mode of the joints changed with increasing welding current from interfacial failure via the Mg nugget/upper ASS interface to partial interfacial failure(part of the Mg nugget was pulled out of the Mg sheet).Both failure modes were accompanied by cohesive failure in the adhesive zone.

Effect of Heat Sink and Cooling Mediums on Ferrite Austenite Ratio and Distortion in Laser Welding of Duplex Stainless Steel 2205

In order to control the ferrite and austenite percentage in duplex stainless steel welding, many researchers try to change the laser welding parameters and cooling medium, but ignore to study the influence of heat sink effect on weld strength. In this work, the effect of aluminium heat sink and varying cooling medium on the laser welding of duplex stainless steel (DSS) 2205 is studied. The 2 mm thick DSS sheets welded with pulsed Nd: YAG laser welding machine by varying the cooling medium (air and oil) and an aluminium plate used as a heat sink. The welded specimens tested for tensile strength, micro-hardness, distortion, microstructure and radiography analysis. The faster cooling rate in the oil quenching process enhances the ferrite percentage compared with air-cooled samples. But the faster cooling rate in oil quenching leads to more distortion and using aluminium as a heat sink influenced positively the distortion to a small extent. The lower cooling rate in air quenching leads to a higher tensile strength of the welded specimen. The objective of this work is to analyse experimentally the effect of cooling medium and heat sink in the mechanical and metallurgical properties of laser welded duplex stainless steel.

Residual stress and welding distortion of Al/steel butt joint by arc-assisted laser welding-brazing

The thermo-elastic.plastic finite element method(FEM)is used to simulate the thermo-mechanical behavior of Al/steel tungsten inert gas(TIG)arc-assisted laser welding-brazing(A-LWB)butt joint.The influence of material nonlinearity,geometrical nonlinearity and work hardening on the welding process is studied,and the differences in the welding temperature field,residual stress and welding distortion by A-LWB and by single laser welding-brazing(SLWB)are analyzed.The results show that the thermal cycle,residual stress distribution and welding distortion by the numerical simulation are in good agreement with the measured data by experiments,which verifies the effectiveness of FEM.Compared with the SLWB,A-LWB can make the high-temperature distribution zone of weld in width direction wider,decrease the transverse tensile stress in the weld and reduce the distribution range of longitudinal tensile stress.And the welding deformation also decreases to some extent.

THRESHOLD STRESS INTENSITIES FOR HYDROGEN-INDUCED DELAYED FAILURE OF WELD METAL OF AUSTENITIC STAINLESS STEEL

It was found that hydrogen induced delayed failure could occur in 308L and 347L weld metals,and the threshold stress intensities of 308L and 347L welds were lower than that of 304L austenitic stainless steel.When dynamically charged under load on a single edge notched specimen,the threshold stress intensities of 308L,347L and 304L decrease with the increase in the diffusible hydrogen content C 0 and the experimental results are as follows:K ⅠH =85.2-10.7 ln C 0 (308L),K ⅠH =76.1-9.3 ln C 0 (347L),K ⅠH =91.7-10.1 ln C 0 (304L).The morphology of the hydrogen induced delayed fracture in the three materials are correlated with the K Ⅰ and C 0 values.

Microstructural evolution and mechanical properties of friction stir-welded C71000 copper–nickel alloy and 304 austenitic stainless steel

Dissimilar joints comprised of copper–nickel and steel alloys are a challenge for manufacturers in modern industries, as these metals are not thermomechanically or chemically well matched. The present study investigated the effects of tool rotational speed and linear speed on the microstructure and mechanical properties of friction stir-welded C71000 copper–nickel and 340 stainless steel alloys using a tungsten carbide tool with a cylindrical pin. The results indicated that a rotational-to-linear speed ratio of 12.5 r/mm did not cause any macro defects, whereas some tunneling defects and longitudinal cracks were found at other ratios that were lower and higher. Furthermore, chromium carbide was formed on the grain boundaries of the 304 stainless steel near the shoulder zone and inside the joint zone, directing carbon and chromium penetration toward the grain boundaries. Tensile strength and elongation percentages were 84% and 65% of the corresponding values in the copper–nickel base metal, respectively.

Application of response surface methodology to maximize tensile strength and minimize interface hardness of friction welded dissimilar joints of austenitic stainless steel and copper alloy

An attempt was made to optimize friction welding parameters to attain a minimum hardness at the interface and a maximum tensile strength of the dissimilar joints of AISI 304 austenitic stainless steel （ASS） and copper （Cu） alloy using response surface methodology （RSM）. Three-factor, five-level central composite design matrix was used to specify experimental conditions. Twenty joints were fabricated using ASS and Cu alloy. Tensile strength and interface hardness were measured experimentally. Analysis of variance （ANOVA） method was used to find out significant main and interaction parameters and empirical relationships were developed using regression analysis. The friction welding parameters were optimized by constructing response graphs and contour plots using design expert software. The developed empirical relationships can be effectively used to predict tensile strength and interface hardness of friction welded ASS-Cu joints at 95% confidence level. The developed contour plots can be used to attain required level of optimum conditions to join ASS-Cu alloy by friction welding process.

The comparison of multi-layer narrow-gap laser and arc welding of S32101 duplex stainless steel

Multi-layer narrow-gap welding of thick S32101 duplex stainless steel was conducted using laser welding with beam wobble process.The phase transition,grain size,phase proportion and crystal texture of welded joint were also studied and compared with gas metal arc welding process.The microhardness and tensile strength were measured and fracture surface was analyzed to evaluate the mechanical properties of welded joints.The results showed that beam wobble technology improved the misalignment of laser beam and filler wire in narrow groove and helped to avoid incomplete fusion defects.Compared to arc welding process,the groove size and heat input were reduced,while welding efficiency was increased.The faster cooling rate and lower temperature gradient of laser wobble welding favored grain refinement,while the austenite content in weld zone decreased.Both the beam wobble and swing arc were conducive to stir weld pool,optimizing the weld microstructure and joint formation.The microstructural variance in various weld passes was caused by the heat input and heat dissipation ability.The microhardness of laser welded joint was lower,while the tensile strength and elongation percentage were higher.The fracture surface of arc welded joint was featured with shallower dimples and cleavage steps.

Activating Flux Design for Laser Weldingof Ferritic Stainless Steel

The behaviors of YAG laser welding process of ferritic stainless steel with activating fluxes were investigatedin this study. Some conventional oxides, halides and carbonates were applied in laser welding. The resultsshowed that the effect of oxides on the penetration depth was more remarkable. Most activating fluxes improved thepenetration more effectively at low power than that at high power. The uniform design was adopted to arrange theformula of multicomponent activating fluxes, showing that the optimal formula can make the penetration depth up to2.23 times as large as that without flux, including 50% ZrO2, 12.09% CaCO3, 10.43% CaO and 27.48% MgO. Throughthe high-speed photographs of welding process, CaF2 can minimize the plasma volume but slightly improve the penetrationcapability.

Laser Shock Processing of an Austenitic Stainless Steel and a Nickel-base Superalloy

An austenitic stainless steel 1Cr18Ni9Ti and a solid solution-strengthened Ni-base superalloy GH30 were shock processed using a Q-switched pulsed Nd-glass laser. Microstructure, hardness and residual stress of the laser shock processed surface were investigated as functions of laser processing parameters. Results show that high density of dislocations and fine deformation twins are produced in the laser shock processed surface layers in both the austenitic stainless steel and the nickel-base superalloy. Extensive strain-induced martensite was also observed in the laser shock processed zone of the austenitic steel. The hardness of the laser shock processed surface was significantly enhanced and compressive stress as high as 400 MPa was produced in the laser shock processed surface.

Effect of Laser Beam Welding Parameters on Microstructure and Properties of Duplex Stainless Steel

The present study is concerned with laser beam welding and its effect on size and microstructure of fusion zone then, on mechanical and corrosion properties of duplex stainless steel welded joints. In this regard, influence of different laser welding parameters was clarified. Both bead-on-plate and autogenously butt welded joints were made using carbon dioxide laser with a maximum output of 9 kW in the continuous wave mode. Welded joints were subjected to visual, dye penetrant and radiography tests before sectioning it for different destructive tests. Accelerated corrosion test was carried out based on tafel plot technique. The results achieved in this investigation disclosed that welding parameters play an important role in obtaining satisfactory properties of welded joint. High laser power and/or high welding speed together with adjusting laser focused spot at specimen surface have produced welded joints with a remarkable decrease in fusion zone size and an acceptable weld profile with higher weld depth/width ratio. Besides, acceptable mechanical and corrosion properties were obtained. Using nitrogen as a shielding gas has resulted in improving mechanical and corrosion properties of welded joints in comparison with argon shielding. This is related to maintaining proper ferrite/austenite balance in both weld metal and HAZ in case of nitrogen shielding. As a conclusion, laser power, welding speed, defocusing distance and type of shielding gas combination have to be optimized for obtaining welded joints with acceptable profile as well as mechanical and corrosion properties.

EFFECT OF LASER CLADDING ON HYDROGEN EMBRITTLEMENT RESISTANCE OF AUSTENITIC STAINLESS STEEL

A plasma spraying plus laser remelting technique has been performed. onaustenite stainless steel (22Cr-13Ni-5Mn ) with a newly developed hydrogen resistantcoating material. The results show that the surface cladding layer can effectively reducethe hydrogen content increasing of the stainless steel under the atmosphere of high pres-sure (30MPa), high temperature (300℃) and high purity (99. 995%) hydrogen andgreatly improve the hydrogen embrittlement resistance of the stain1ess steel. Throughanalysis of microstructure, a mechanism of hydrogen embrittlement resistance is presentedthat at room temperature, the surface oxidation films, both existing on the surface ofcoated and uncoated specimens, inhibit the adsorption and diffusion of hydrogen molecu-lae. However, at high temperature, it is the surface cladding layer with relatively low sol-ubility and Permeability for hydrogen that significantly reduces the amount of hydrogenentering into the interior of the material and improves its hydrogen embrittfement resis-tance.

Microstructure and Property Relationships in Resistance Spot Weld between 7114 Interstitial Free Steel and 304 Austenitic Stainless Steel

Due to the differences in physical, chemical and mechanical properties of the base metals, the resistance spot welding of dissimilar materials is generally more challenging than that of similar materials. The influence of the primary welding parameters affecting the heat input such as peak current on the morphology, microhardness, and tensile shear load bearing capacity of dissimilar welds between 304 grades austenitic and 7114 grade interstitial free steel has been investigated in this study. The optimum welding parameters producing maximum joint strength were established at a peak current of 9 kA, where the electrode force is kept 6×10^-5 Pa and weld time is kept constant 17 cycles, respectively. The primary cause of weakening the weldment is identified as the excessive grain growing region of heat affected zone （HAZ） in case of 7114 grade interstitial free steel.

Analysis on characteristics of laser induced plasma during laser welding of A304 stainless steel sheet

A group of the stainless steel laser welding was performed using continuous wave （CW） laser and pulsed laser. During the welding process the laser induced plasma behavior was recorded by high-speed video camera, while the plasma spectrum was acquired by the spectrometer. The plasma temperature was calculated based on the spectroscopic analysis of the optical emission and the results show that different output mode of laser source led to big difference of plasma temperature. The high-speed video images showed that the plasma was very steady and kept certain strength in CW laser welding, while the plasma erupted a little later after the laser peak arising during the pulsed laser welding. During a period of time about 2 ms just after the laser peak arising during the pulsed laser welding, much more laser energy reached the workpiece. This made the workpicce fully penetrated with a lower average power.

Hump formation mechanism in gas-jet-assisted keyhole laser welding of HR-2 stainless steel

Gas-jet-assisted keyhole laser welding offers the possibility of a breakthrough in the limitations of penetration depth in laser welding,which currently suffers from equipment restrictions.A gas jet of sufficient intensity to assist the keyhole should be used to obtain suppressed plasma,a deepened keyhole,and increased penetration depth.However,an excessively strong gas jet gives rise to humps.The incident angle of the keyhole-assisted gas jet is 60°,with a nozzle ahead of the laser beam.A series of experiments were carried out with different welding velocities and gas parameters by using HR-2 hydrogen-resistant stainless steel and a slab CO2 continuous-wave laser welding machine.The weld profiles can be categorized into four types,welds of traditional laser welding,welds of enhanced laser welding,undercut welds,and humping welds with increased gas pressure.A high-speed camera was employed in the experiments to monitor the formation of humps under an excessively strong gas jet.The results of analysis show that hump formation can be divided into six stages.Its main driving force is the intense turbulence of gas jet.There are two main reasons for hump formation：premature solidification of the molten pool caused by the large temperature gradient between the front and rear parts of the molten pool,and the emergence of a thin layer liquid bridge with one-directional flow under the enhanced cooling effect of excessively strong gas.

Welding of shape memory alloy to stainless steel for medical occluder

Dissimilar metal joining between NiTi shape memory alloy（SMA） and stainless steel was conducted.A cluster of NiTi SMA wires were first joined with tungsten inert gas（TIG） welding process,then the NiTi SMA TIG weld was welded to a stainless steel pipe with laser spot welding process.The microstructure of the welds was examined with an optical microscope and the elemental distribution in the welds was measured by electron probe microanalysis（EPMA）.The results show that TiC compounds dispersively distribute in the NiTi SMA TIG weld.However,the amount of TiC compounds greatly decreases around the fusion boundary of the laser spot weld between the NiTi SMA and stainless steel.Mutual diffusion between NiTi shape memory alloy and stainless steel happen within a short distance near the fusion boundary,and intermetallic compounds such as Ni3Ti＋（Fe,Ni）Ti appear around the fusion boundary.

Laser Surface Modification of Lean-alloyed Austenitic Stainless Steel for Corrosion Resistance

In order to reduce the cost of the austenitic stainless steels(ASSs),the expensive austenite former(nickel) is often substituted by manganese.However,manganese is generally seen to have a detrimental effect on the corrosion resistance.In the present study,the feasibility of laser surface modification of a lean-alloyed ASS(FeCrMn) for enhancing pitting corrosion resistance was investigated.Laser surface modification of FeCrMn was successfully achieved by a 2.3 kW high power diode laser(HPDL).Cyclic polarization tests for FeCrMn after laser surface modification in 3.5% NaCl solution at 25 ℃ were performed by using a potentiostat.The pitting resistance of the laser-modified specimens was found to be significantly improved as reflected by the noble shift in pitting potential.This could be attributed to redistribution of manganese sulphide leading to a more homogenous and refined microstructure.Pitting corrosion resistance of the laser-treated FeCrMn followed by subsequent citric acid passivation was found to be further improved as reflected by the noble shift in pitting potential to 0.18 V.

Cracking Phenomenon in Spot Welded Joints of Austenitic Stainless Steel

The spot welds nugget cracking of austenitic stainless steel at temperatures between 700°C - 1010°C was investigated. Traditionally, the cracks have been observed around the spot nugget in welded temperature. Actually, these cracks are developed due to incomplete melting and inappropriate electrode pressure, which causes an expulsion of molten metal. These cracks start to grow and cause either the interface or plug fracture according to the loading type. In this work, the micro-cracks in the weld nugget were indicated for this type of steel at elevated temperature. Cracks appear in a certain range of temperature;about 700°C - 750°C. The cracks like defect and cavitations were presented. According to the fracture mechanics point of view, these cracks reduce the mechanical strength. Therefore, these cracks have to be taken into account with a certain precaution. Moreover, considering the working temperature and reducing the element may develop ferrite particles.

Friction welding influence on microstructure,microhardness and hardness behavior of CrNiMo steel(AISI 316)

For joining high Cr,Ni and Mo austenitic stainless steel(AISI 316)by direct drive friction welding(DDFW),with friction weld-ing conditions:rotation speed of 3000 r/min,friction time of 10 s,friction pressure of 130 MPa,forge time of 5 s and forge pressure of 260 MPa.The results of microstructure showed that the temperature at the interface reached 819℃while forge applied between 357-237℃,which subdivided welded joint into four distinct regions of highly plastically deformed zone(HPDZ),thermo-mechanically affected zone(TMAZ),heat affected zone(HAZ)and the base metal,with grain size about 10µm,100µm,90µm and 30µm respectively.These re-gions were created due to dynamic recrystallization(DRX)at the interface and thermo-mechanical deformation with heat diffusion in the neighboring regions.Whereas,high level of microhardness about 300 HV0.1 and hardness roughly 240 Hv10 at the interface due to HPDZ creation while low level of 240 HV0.1 for microhardness and moderately of 205 HV10 for hardness in neighboring regions.

Welding of nickel free high nitrogen stainless steel: Microstructure and mechanical properties

High nitrogen stainless steel(HNS) is a nickel free austenitic stainless steel that is used as a structural component in defence applications for manufacturing battle tanks as a replacement of the existing armour grade steel owing to its low cost, excellent mechanical properties and better corrosion resistance.Conventional fusion welding causes problems like nitrogen desorption, solidification cracking in weld zone, liquation cracking in heat affected zone, nitrogen induced porosity and poor mechanical properties.The above problems can be overcome by proper selection and procedure of joining process. In the present work, an attempt has been made to correlate the microstructural changes with mechanical properties of fusion and solid state welds of high nitrogen steel. Shielded metal arc welding(SMAW), gas tungsten arc welding(GTAW), electron beam welding(EBW) and friction stir welding(FSW) processes were used in the present work. Optical microscopy, scanning electron microscopy and electron backscatter diffraction were used to characterize microstructural changes. Hardness, tensile and bend tests were performed to evaluate the mechanical properties of welds. The results of the present investigation established that fully austenitic dendritic structure was found in welds of SMAW. Reverted austenite pools in the martensite matrix in weld zone and unmixed zones near the fusion boundary were observed in GTA welds. Discontinuous ferrite network in austenite matrix was observed in electron beam welds.Fine recrystallized austenite grain structure was observed in the nugget zone of friction stir welds.Improved mechanical properties are obtained in friction stir welds when compared to fusion welds. This is attributed to the refined microstructure consisting of equiaxed and homogenous austenite grains.