Poly( glycolic acid-lactic acid)( PGLA) threadembedding material was modified by chitosan coating which could improve the rigidity,hydrophilicity and moisture absorption of the material,and produced better stimulation...Poly( glycolic acid-lactic acid)( PGLA) threadembedding material was modified by chitosan coating which could improve the rigidity,hydrophilicity and moisture absorption of the material,and produced better stimulation effect. Thus,this kind of thread-embedding materials which can be buried into acupuncture points to produce a long-time stimulation is popular in the acupuncture and moxibustion therapies. The variation tendencies of diameter,weight, hydrophilicity, and flexibility of the samples under the change of chitosan coating concentration,coating time and coating times were studied respectively. The results showed that the hydrophilicity,weight,and rigidity after coating rose in a certain range with the increase of coating time,coating times and coating concentration. The coating time had little influence on the diameter of fiber.展开更多
The PAL was synthesized with BA,MMA and some monomers containing carboxyl groups（for example,acrylic acid（AA） and methacrylic acid（MAA）） as co-monomers by semi-continuous seeded emulsion polymerization technique...The PAL was synthesized with BA,MMA and some monomers containing carboxyl groups（for example,acrylic acid（AA） and methacrylic acid（MAA）） as co-monomers by semi-continuous seeded emulsion polymerization technique.The influences of alkalinization temperature,the feeding manner of AA or MAA on the particles size,rheological properties and carboxyl distribution of the latex were discussed,and the rheological mechanism was analyzed.The experimental results show that the PAL system has preferable viscosity and particle size when the alkalinization temperature is 50 ℃.Different distribution of carboxyl group in the particles and different resultant rheological properties are obtained by different feeding manner of AA or MAA into the system.The TEM images show that the particle is a smooth globe with carboxyl group concentrating on the surface and stabilized with electric double layer and nonionic adsorbed layer.The concentration of carboxyl functional group on the surface of particles can be achieved by the specific polymerization technique.The rheologyical properties are determined by accretion of particle volume and variation of the two phase volume ratio resulted from the carboxyl group spreading layer.展开更多
基金Biomedical Textile Materials Science and Technology(111 Project),China(No.B07024)
文摘Poly( glycolic acid-lactic acid)( PGLA) threadembedding material was modified by chitosan coating which could improve the rigidity,hydrophilicity and moisture absorption of the material,and produced better stimulation effect. Thus,this kind of thread-embedding materials which can be buried into acupuncture points to produce a long-time stimulation is popular in the acupuncture and moxibustion therapies. The variation tendencies of diameter,weight, hydrophilicity, and flexibility of the samples under the change of chitosan coating concentration,coating time and coating times were studied respectively. The results showed that the hydrophilicity,weight,and rigidity after coating rose in a certain range with the increase of coating time,coating times and coating concentration. The coating time had little influence on the diameter of fiber.
基金Funded by the National Natural Science Foundation of China (No.50803017)
文摘The PAL was synthesized with BA,MMA and some monomers containing carboxyl groups（for example,acrylic acid（AA） and methacrylic acid（MAA）） as co-monomers by semi-continuous seeded emulsion polymerization technique.The influences of alkalinization temperature,the feeding manner of AA or MAA on the particles size,rheological properties and carboxyl distribution of the latex were discussed,and the rheological mechanism was analyzed.The experimental results show that the PAL system has preferable viscosity and particle size when the alkalinization temperature is 50 ℃.Different distribution of carboxyl group in the particles and different resultant rheological properties are obtained by different feeding manner of AA or MAA into the system.The TEM images show that the particle is a smooth globe with carboxyl group concentrating on the surface and stabilized with electric double layer and nonionic adsorbed layer.The concentration of carboxyl functional group on the surface of particles can be achieved by the specific polymerization technique.The rheologyical properties are determined by accretion of particle volume and variation of the two phase volume ratio resulted from the carboxyl group spreading layer.