Mechanical and Electrical Properties of Some Sn-Zn Based Lead-Free Quinary Alloys

Although there are many lead-free soldering alloys on the market, none of them have ideal qualities. The researchers are combining binary alloys with a variety of additional materials to create the soldering alloys’ features. The eutectic Sn-9Zn alloy is among them. This paper investigated the mechanical and electrical properties of Sn-9Zn-x (Ag, Cu, Sb);{x = 0.2, 0.4, and 0.6} lead-free solder alloys. The mechanical properties such as elastic modulus, ultimate tensile strength (UTS), yield strength (YS), and ductility were examined at the strain rates in a range from 4.17 10−3 s−1 to 208.5 10−3 s−1 at room temperature. It is found that increasing the content of the alloying elements and strain rate increases the elastic modulus, ultimate tensile strength, and yield strength while the ductility decreases. The electrical conductivity of the alloys is found to be a little smaller than that of the Sn-9Zn eutectic alloy.

Effect of Strain Rate on Tensile Behavior of Sn-9Zn-xAg-ySb;{(x, y) = (0.2, 0.6), (0.2, 0.8), (0.6, 0.2), (0.8, 0.2)} Lead-Free Solder Alloys

The tensile properties of Sn-9Zn-xAg-ySb;{(x, y) = (0.2, 0.6), (0.2, 0.8), (0.6, 0.2), (0.8, 0.2)} lead-free solders were investigated. All the test samples were annealed at 150°C for 1 hour. The tests are carried out at room temperature at the strain rate of 4.17 × 10-3 s-1, 20.85 × 10-3 s-1, and 208.5 × 10-3 s-1. It is seen that the tensile strength increases and the ductility decrease with increasing the strain rate over the investigated range. From the strain rate change test results, the strain sensitivity values are found in the range of 0.0831 to 0.1455 due to the addition of different alloying elements.

Effects of phosphorus addition on the properties of Sn-9Zn lead-free solder alloy

This article explores tile effects of phosphorus addition on the wettability between Sn-9Zn solder alloy and Cu substrates, the oxidation behavior and the corrosion behavior of Sn-9Zn solder alloy. Spreading test was used to characterize the wettability of Sn-9Zn-xP solder alloys to Cu substrates. The oxidation and corrosion behaviors of Sn- 9Zn-xP solder alloys were determined by means of weight gaining, and secondary ion mass spectrometry was used to analyze the oxygen content. The role and mechanism of P in the solder alloys were also discussed. It is found that the addition of P can significantly improve the wettability of the solder alloys. Incorporating P into Sn-9Zn solder alloy obviously decreases the oxygen content and enhances the oxidation and corrosion resistance. Microstructure observations show that an appropriate amount of P can greatly refine coarse rod-like Zn-rich phases in Sn-gZn solder alloy.

Effect of cerium on microstructure and mechanical properties of Sn-Ag-Cu system lead-free solder alloys

The melting point, spreading property, mechanical properties and microstructures of Sn-3.0Ag-2.8Cu solder alloys added with micro-variable-Ce were studied by means of optical microscopy, scanning electron microscopy(SEM) and energy dispersive X-ray(EDX). The results indicate that the melting point of Sn-3.0Ag-2.8Cu solder is enhanced by Ce addition; a small amount of Ce will remarkably prolong the creep-rupture life of Sn-3.0Ag-2.8Cu solder joint at room temperature, especially when the content of Ce is 0.1%, the creep-rupture life will be 9 times or more than that of the solder joint without Ce addition; the elongation of Sn-3.0Ag-2.8Cu solder is also obviously improved even up to 15.7%. In sum, the optimum content of Ce is within 0.05%-0.1 %.

Effect of diode-laser parameters on shear force of micro-joints soldered with Sn-Ag-Cu lead-free solder on Au/Ni/Cu pad

Soldering experiments with Sn-3.5Ag-0.5Cu lead-free solder on Au/Ni/Cu pad were carried out by means of diode-laser and IR reflow soldering methods respectively.The influence of different heating methods as well as output power of diode-laser on shear force of micro-joints was studied and the relationship between the shear force and microstructures of micro-joints was analyzed.The results indicate that the formation of intermetallic compound Ag3Sn is the key factor to affect the shear force and the fine eutectic network structures of micro-joints as well as the dispersion morphology of fine compound Ag3Sn,in which eutectic network band is responsible for the improvement of the shear force of micro-joints soldered with Sn-Ag-Cu lead-free solder.With the increases of output power of diode-laser,the shear force and the microstructures change obviously.The eutectic network structures of micro-joints soldered with diode-laser soldering method are more homogeneous and the grains of Ag3Sn compounds are finer in the range of near optimal output power than those soldered with IR reflow soldering method,so the shear force is also higher than that using IR reflow soldering method.When the output power value of diode-laser is about 41.0 W,the shear force exhibits the highest value that is 70% higher than that using IR reflow soldering method.

Formation of Bulk Intermetallic Compound AgaSn in Slowly-Cooled Lead-Free Sn-4.0 wt pct Ag Solders

Sn-Ag alloy system has been regarded as one of the most promising lead-free solder to substitute conventional Sn- Pb eutectic solder. But the formation of bulk Ag3Sn intermetallic compounds （IMCs） during reflow and post heat treatment significantly influences the performance of the solder joints. With an effort to clarify its microstructural evolution as a function of slow cooling rates, the fraction of bulk IMCs within the slowly solidified Sn-4.0 wt pct Ag solder was investigated by standard metallographic and compared with that detected by thermal analysis. It was found that the bulk IMCs fraction determined by thermal analysis corresponds quite well with the microstructure observation results. In accordance with the conventional solidification theory, the lower the applied cooling rate, the fewer the amount of bulk Ag3Sn IMCs formed in Sn-4.0 wt pct Ag alloy. In addition, Vickers hardness measurement results indicated that the relative coarse eutectic Ag3Sn IMCs distributing in the lamellar eutectic structure favored the improvement of the mechanical performance.

Mechanical properties of QFP micro-joints soldered with lead-free solders using diode laser soldering technology

Soldering experiments of quad flat package(QFP) devices were carried out by means of diode laser soldering system with Sn-Ag-Cu and Sn-Cu-Ni lead-free solders, and competitive experiments were also carried out not only with Sn-Pb eutectic solders but also with infrared reflow soldering method. The results indicate that under the conditions of laser continuous scanning mode as well as the fixed laser soldering time, an optimal power exists, while the optimal mechanical properties of QFP micro-joints are gained. Mechanical properties of QFP micro-joints soldered with laser soldering system are better than those of QFP micro-joints soldered with IR reflow soldering method. Fracture morphologies of QFP micro-joints soldered with laser soldering system exhibit the characteristic of tough fracture, and homogeneous and fine dimples appear under the optimal laser output power.

Effects of Ga,Al,Ag,and Ce multi-additions on the wetting characteristics of Sn-9Zn lead-free solder

An orthogonal method was used to evaluate the effects of Ga, Al, Ag, and Ce multi-additions on the wetting characteristics of Sn-9Zn lead-free solders by wetting balance method. The results show that the optimal loading of Ga, Al, Ag, and Ce was 0.2 wt.%, 0.002 wt.%, 0.25 wt.%, and 0.15 wt.%, respectively. Intermetallic compounds （IMCs） formed at the interface between Sn-9Zn-0.2Ga-0.002Al-0.25Ag- 0.15Ce solder and Cu substrate were investigated by scanning electron microscope （SEM） and energy dispersive spectroscopy （EDS） analysis. The SEM images illustrate that the IMCs can be divided into two portions from the substrate side to the solder side： a planar CusZns layer and an additional continuous scallop-like AgZn3 layer. The EDS analysis also shows that Ga segregates in the solder abutting upon the interface. X-ray photoelectron spectroscopy （XPS） and Auger electron spectroscopy （AES） of the surface components of Sn-9Zn-0.2Ga-0.002Al- 0.25Ag-0.15Ce solder indicate that Al aggregates at the surface in the form of Al203 protective fdm, which prevents the further oxidation of the solder surface. On the other hand, Ce aggregates at the subsurface, which may reduce the surface tension of the solder and improve the wettability in consequence.

Effects of cooling rates on microstructure and microhardness of lead-free Sn-3.5%Ag solders

The microstructure and microhardness of Sn-3.5%Ag solders were explored in the cooling rate ranging from 0.08 to 104 K/s. Under rapid cooling condition, the strong kinetic undercooling effect leads to the actual solidification process starting at the temperature lower than the equilibrium eutectic point, and the actual metastable eutectic point shifts to the higher Ag concentration. Hence, the higher the applied cooling rate is, the more the volume fraction of primary β-Sn crystal forms. At the same time, the separation of primary β-Sn crystal favors restraining the formation of bulk Ag3Sn intermetallic compounds (IMCs) in solder due to the mismatch crystalline orientation relationship, those Ag3Sn phase separating through the eutectic reaction could hardly cling to the primary β-Sn crystal and grow up. Additionally, the Vickers hardness test shows that fine β-Sn and spherical Ag3Sn phase in the rapidly solidified alloy strongly improves the microhardness of the Sn-3.5%Ag solder.

EVOLUTION OF MICROSTRUCTURE OF Sn-Ag-Cu LEAD-FREE FLIP CHIP SOLDER JOINTS DURING AGING PROCESS

Flip chip bonding has become a primary technology that has found application in the chip interconnection process in the electronic manufacturing industry in recent years. The solder joints of the flip chip bonding are small and consist of complicated microstructures such as Sn solution, eutectic mixture, and intermetallic compounds （IMCs）, whose mechanical performance is quite different from the original solder bulk. The evolution of microstructure of the flip chip solder joints under thermal aging was analyzed. The results show that with an increase in aging time, coarsening of solder bulk matrix and AuSn4 IMCs occurred within the solder. The IMCs that are formed at the bottom side of the flip chip bond were different from those on the top side during the aging process. （Cu, Ni, Au）0Sn5 were formed at the interfaces of both sides, and large complicated （Au,Ni, Cu）Sn4 IMCs appeared for some time near the bottom interface after aging, but they disappeared again and thus （Cu,Ni, Au ）0Sn5 IMC thickness increased considerably. The influence of reflow times during the flip chip bonding （as-bonded condition） on the characteristics of interfacial IMCs was weakened when subjected to the aging process.

Influences of Ag and Au Additions on Structure and Tensile Strength of Sn-5Sb Lead Free Solder Alloy

It is important, for electronic application, to decrease the melting point of Sn-5Sb solder alloy because it is relatively high as compared with the most popular eutectic Pb-Sn solder alloy. Adding Au or Ag can decrease the onset melting temperature （233℃） of this alloy to 203,5℃ and 216℃, respectively. The results indicate that the Sn-5Sb-i.5Au alloy has very good ultimate tensile strength （UTS）, ductility, and fusion heat, which are better than both those of the Sn-5Sb-3.SAg and Sn-5Sb alloys. The formation of intermetallic compounds （IMCs） AuSn4 and Ag3Sn enhanced the SbSn precipitates in the solidification microstructure microstructure stability, while retained the formation of thus significantly improved the strength and ductility For all alloys, both UTS and yield stress （σy） increase with increasing strain rate and decrease with increasing temperature in tensile tests, but changes of ductility are generally small with inconsistent trends.

Parameter fitting of constitutive model and FEM analysis of solder joint thermal cycle reliability for lead-free solder Sn-3.5Ag

The experimental tests of tensile for lead-flee solder Sn-3.5Ag were performed for the general work temperatures range from 11 to 90 ℃ and strain rate range from 5 × 10^-5 to 2 × 10^-2s^-1, and its stress--strain curves were compared to those of solder Sn-37Pb. The parameters in Anand model for solder Sn-3.5Ag were fitted based on experimental data and nonlinear fitting method, and its validity was checked by means of experimental data. Furthermore, the Anand model was used in the FEM analysis to evaluate solder joint thermal cycle reliability. The results show that solder Sn-3.5Ag has a better creep resistance than solder Sn-37Pb. The maximum stress is located at the upper right comer of the outmost solder joint from the symmetric center, and thermal fatigue life is predicted to be 3.796 × 10^4 cycles under the calculated conditions.

Effects of rapid solidification on the microstructure and microhardness of a lead-free Sn-3.5Ag solder

A lead-free Sn-3.5Ag solder was prepared by rapid solidification technology. The high solidification rate, obtained by rapid cooling, promotes nucleation, and suppresses the growth of Ag3Sn intermetallic compounds （IMCs） in Ag-rich zone, yielding fine Ag3Sn nanoparticulates with spherical morphology in the matrix of the solder. The large amount of tough homogeneously-dispersed IMCs helps to improve the surface area per unit volume and obstructs the dislocation lines passing through the solder, which fits with the dispersion-strengthening theory. Hence, the rapidly-solidified Sn-3.5Ag solder exhibits a higher rnicrohardness when compared with a slowly-solidified Sn-3.5Ag solder.

Effect of Antimony Additions on Corrosion and Mechanical Properties of Sn-Bi Eutectic Lead-Free Solder Alloy

The goal of the present work is to investigate the effects of the addition of Sb (0, 3 and 6 wt%) on structure, melting, corrosion and mechanical properties of Sn-Bi eutectic solder alloys. The mechanical properties of the bulk Sn-Bi-Sb solders were higher as the amount of antimony increases, making compressive strength augment from 65 MPa to 100 MPa when 6 wt% Sb was incorporated to the Sn-Bi eutectic alloy. The three alloys presented a melting temperature that is smaller to the one exhibited by the eutectic alloy Sn-38Pb (Tm = 183°C). According to the electrochemical results, the addition of higher contents of Sb to the Sn-Bi eutectic alloy had a positive effect: it ennobled the Ecorr values.

Failure Modes of Lead Free Solder Bumps Formed by Induction Spontaneous Heating Reflow

The shear failure modes and respective failure mechanism of Sn3.5Ag and Sn3.0Ag0.5Cu lead-free solder bumping on Au/Ni/Cu metallization formed by induction spontaneous heating reflow process have been investigated through the shear test after aging at 120℃ for 0, 1, 4, 9 and 16 d. Different typical shear failure behaviors have been found in the loading curves （shear force vs displacement）. From the results of interracial morphology analysis of the fracture surfaces and cross-sections, two main typical failure modes have been identified. The probabilities of the failure modes occurrence are inconsistent when the joints were aged for different times. The evolution of the brittle NiaSn4 and Cu-Ni-Au-Sn layers and the grains coarsening of the solder bulk are the basic reasons for the change of shear failure modes.

Effect of a Trace of Bi and Ni on the Microstructure and Wetting Properties of Sn-Zn-Cu Lead-Free Solder

The microstructure and melting behavior of Sn-9Zn-2Cu （SZC） lead-free solder with 3 wt pct Bi and various amount of Ni additions were studied. The wetting properties and the interracial reaction of Sn-Zn-Cu with Cu substrate were also examined. The results indicated that the addition of 3 wt pct Bi could decrease the melting point of the solder and Ni would refine the microstructure and the rod-shape Cu5Zn8 phase changed into square-shape （Cu, Ni）5Zn8 phase. The addition of Bi, Ni greatly improved the wettability of SZC solder. In addition, the interracial phase of the solders/Cu joint was typical planar Cu5Zn8 in SZC-3Bi-INi alloy.

Solderability and intermetallic compounds formation of Sn-9Zn-xAg lead-free solders wetted on Cu substrate

The eutectic Sn-9Zn alloy was doped with Ag （0 wt.%-1 wt.%） to form Sn-9Zn-xAg lead-free solder alloys. The effect of the addition of Ag on the microstructure and solderability of this alloy was investigated and intermetallic compounds （IMCs） formed at the solder/Cu interface were also examined in this study. The results show that, due to the addition of Ag, the microstructure of the solder changes. When the quantity of Ag is lower than 0.3 wt.%, the needle-like Zn-rich phase decreases gradually. However, when the quantity of Ag is 0.5 wt.%-1 wt.%, Ag-Zn intermetallic compounds appear in the solder. In particular, adding 0.3 wt.% Ag improves the wetting behavior due to the better oxidation resistance of the Sn-9Zn solder. The addition of an excessive amount of Ag will deteriorate the wetting property because the gluti- nosity and fluidity of Sn-9Zn-（0.5, 1）Ag solder decrease. The results also indicate that the addition of Ag to the Sn-Zn solder leads to the precipitation of ε-AgZn3 from the liquid solder on preformed interracial intermetallics （CusZn8）. The peripheral AgZn3, nodular on the Cu5Zn8 IMCs layer, is likely to be generated by a peritectic reaction L ＋ γ-Ag5Zns→AgZn3 and the following crystallization of AgZn3.

Wettability of Sn-Zn-Bi Based Lead-Free Solder with Rare Earths

Effect of different contents of La and Ga on the wettability and the mierostrueture of interface of Sn-8.9Zn- 2.7Bi trinary alloys was studied. The results show that different contents of La and Ga have significant effect on the wettability of Sn-Zn-Bi based lead-free solder under the condition of both atmosphere and nitrogen. By adding suitable amount of Ga, Cu and La to Sn-Zn-Bi solder, a new lead-free solder Sn-8.9Zn-2.7Bi- 1.0Ga-0.5Cu-0.2La with better wettability was prepared, which has a wetting angle of 25.1° to Cu.

Effects of Ni-Doping on Microstructures and Properties of Zn-20Sn High-Temperature Lead-Free Solders

In the present work, the effect of Ni doping on the microstructures and properties of Zn-20 Sn high temperature lead-free solder has been investigated. Interestingly,Ni was present as the form of Ni-Zn compounds in the microstructure of Zn-20 Sn-xNi alloy.When the Ni-doping amount was 0.2~0.4 wt.%, the presence of δ phase was found, and when the doping amoun was 0.8 wt.%, the presence of γ phase was observed. With the increase of Ni content, the liquidus temperature increased but the solidus temperature did not change obviously. In addition, the microhardness and electrical resistivities of Zn-20 Sn-xNi solder increased gradually. And the spreading area and shear strength increased firstly but decreased afterwards. When the content of Ni was 0.4 wt.%, the spreading area and shear strength of solder reached to be maximum. After the addition of 0.4 wt.% Ni, the microstructure of the interfacial intermetallic compound(IMC) layer of the interface didn't change, but the total thickness of the IMC layer reduced. The δ-phase was embedded in the grain boundary of ε-Cu Zn5, which hindered the diffusion of atoms. The thickness of IMC layer at the interface reduced, which led to the improvement of the shear strength of the interface.