Degradation of Phenol by Hydroxyl Radicals on Different Coating Lead Dioxide Electrodes

Lead dioxide electrodes on Ti substrates were prepared by thermal-deposition or electro-deposition. The amount of hydroxyl radicals generated at the electrodes prepared by the above-mentioned two methods was compared with that at the electrodes mingled with Bi or La prepared by electro-deposition. The experimental results indicate that the highest concentration of hydroxyl radicals generated by thermal-deposition, electro-deposition mingled with nothing, electro-deposition mingled with Bi or La was 0.781, 1.048, 1.838 or 2.044 μmol/L, respectively. When phenol was electrolyzed on the four electrodes at a current density of 30 mA/cm2, the removal efficiency of phenol after electrolysis for 1.5 h was 87.30%, 93.55%, 97.95% or 98.70%, TOC removal efficiency after electrolysis for 5 h was 86.76%, 94.26%, 98.53% or 99.60%, respectively. Through the degradation experiments of phenol, the amount of hydroxyl radicals was responsible for the removal efficiency of phenol. The electro-catalytic characteristics were investigated by SEM, the generation amount of hydroxyl radicals, the degradation degree of phenol and the stability and conductivity of the electrodes were also investigated. The experimental results indicate that the four electrodes all show good electro-catalytic characteristics; the electro-catalytic characteristics of the electrode mingled with La were superior to those of the other three ones, and the electrochemical degradation of phenol followed one-step reaction dynamics.

Comparison Between Performances of PbO_2 and F^--doped PbO_2 Anodes for Electrochemical Degradation of Aniline

The paper deals with the influence of anode material on the efficiency of degradation for organic pollutants in water system.The electrochemical performance of fluorine ion doped lead dioxide（F--PbO2） electrode for the degradation of aniline was compared with that of undoped lead dioxide（PbO2） electrode by ultraviolet-visible（UV-Vis） spectroscopy,linear voltammetry and other analytical methods,such as the measurement by chemical oxygen demand analyzer,high performance liquid chromatography and scanning electron micrography.It was shown that both PbO2 electrode and F--PbO2 electrode could make aniline be mineralized completely and have the same degradation course,but F--PbO2 electrode has much higher electrocatalytic activity than undoped PbO2 electrode for the electrochemical degradation of aniline.The experimental results confirm that F--PbO2 electrode has much higher potential for oxygen evolution than undoped PbO2 electrode.