Manganese-doped Ba（0.925）Ca（0.075）TiO3 lead-free piezoelectric ceramics（abbreviated as BCT）with high mechanical quality factor were synthesized by conventional solid-state reaction method.The effects of excess B...Manganese-doped Ba（0.925）Ca（0.075）TiO3 lead-free piezoelectric ceramics（abbreviated as BCT）with high mechanical quality factor were synthesized by conventional solid-state reaction method.The effects of excess Ba on the crystal structure,microstructure,and electrical properties of the ceramics were systematically investigated.X-ray diffraction and Raman spectra revealed that Ca^2＋ions were pushed from Ba sites to Ti sites of BCT when 1.5 mol%extra Ba^2＋ions were added after sintering.The grain size of the ceramics was decreased by adding extra Ba^2＋ions.The mechanical quality factor and resistivity of the ceramics decreased dramatically when the excess Ba was more than 1.5 mol%.High piezoelectric coefficients（d（33）=150-190 pC/N）and high mechanical quality factors（Qm=1 000-1 200）were obtained in the ceramics when the excess of Ba was between 0.5 mol%and 1 mol%.These results indicated that the properties of BCT ceramics could be tailored by adjusting the content of Ba.展开更多
基金Funded by the National Natural Science Foundation of China(No.51672220)the 111 Program(No.B08040)of MOE+3 种基金the National Defense Science Foundation(No.32102060303)the Xi’an Science and Technology Foundation(Nos.2017XAKJCGZH-10 and 2017086CG-RC049-XBGY005)the Shaanxi Provincial Science Foundation(No.2017KW-018)the NPU Gaofeng Project(No.17GH020824)of China
文摘Manganese-doped Ba（0.925）Ca（0.075）TiO3 lead-free piezoelectric ceramics（abbreviated as BCT）with high mechanical quality factor were synthesized by conventional solid-state reaction method.The effects of excess Ba on the crystal structure,microstructure,and electrical properties of the ceramics were systematically investigated.X-ray diffraction and Raman spectra revealed that Ca^2＋ions were pushed from Ba sites to Ti sites of BCT when 1.5 mol%extra Ba^2＋ions were added after sintering.The grain size of the ceramics was decreased by adding extra Ba^2＋ions.The mechanical quality factor and resistivity of the ceramics decreased dramatically when the excess Ba was more than 1.5 mol%.High piezoelectric coefficients（d（33）=150-190 pC/N）and high mechanical quality factors（Qm=1 000-1 200）were obtained in the ceramics when the excess of Ba was between 0.5 mol%and 1 mol%.These results indicated that the properties of BCT ceramics could be tailored by adjusting the content of Ba.