Background: Effective polymerization of the composite resin is essential to obtain long term clinical success and has a great importance obtaining improved mechanical properties. The purpose of this study was to measu...Background: Effective polymerization of the composite resin is essential to obtain long term clinical success and has a great importance obtaining improved mechanical properties. The purpose of this study was to measure the effect of the light intensity of LED and QTH curing devices in relation to the light distances, on the hardness (KHN) of two light cure nano-resin composite. Material and Methods: The top and bottom surfaces of the two nanofill composite specimens were evaluated. Two LED and two QTH light curing devices were used at nine different distances. Light intensity was measured with two radiometers placed at these same distances from the curing tip. 360 pvc dies were prepared with circular cavity 3 mm in diameter and 2 mm thick. The tested materials were placed in each cavity. The different light curing distances were standardized by adding pvc spacers dies at different height matching the different distances. Top and bottom surface microhardness were evaluated with a Micro Hardness Tester in knoop hardness numbers (Kg/mm2). Data were statistically analyzed using: Three-way ANOVA, Tukey and Pearsons test. Results: It was revealed that there was a statistically significant difference in microhardness between the composites (p < 0.001), between the nine distances (p < 0.001) and between the four light curing devices (p < 0.001). Increasing the distance of the light source from composite resin, the light intensity and the microhardness values at the top and bottom surface decrease. LED light curing devices produced a greater microhardness results at the bottom surface of the specimens. The Filtek Ultimate nanocomposite (3 m) showed highest microhardness values on the top and bottom surfaces, polymerized with all four curing devices and all nine distances compared to Empress Direct nano composite (Ivoclar vivadent). Clinical significant: Even with high power LED curing light, the distance between the tip of the light source and the restoration surface should be as close as possible. In this study, Filtek Ultimate showed better results (highest microhardness values) than Empress Direct.展开更多
The purpose of this study was to use. a three-component photoinitiation system comprising 1wt% CQ （camphorquinone）, 2wt% DMAEMA （2-（dimethylamino） ethyl meth acrylate） and 2wt% ph^2I^＋PF6^- （diphenyliodonium h...The purpose of this study was to use. a three-component photoinitiation system comprising 1wt% CQ （camphorquinone）, 2wt% DMAEMA （2-（dimethylamino） ethyl meth acrylate） and 2wt% ph^2I^＋PF6^- （diphenyliodonium hexafluorophosphate） to initiate the copolymerization of the matrix resins which combine bisphenol-S-bis （3-methacrylate-2-hydroxy propyl） ether （BisS-GMA） with the expanding monomer unsaturated spiro orthoesters 2-methylene-l,4,6-tdspiro[4,4] nonane （MTOSN）, for minimizing the volumetric shrinkage that generally occurs during polymerization. It was hypothesized that MTOSN would expand volumetrically during polymerization under the three-component photoinitiator system and further reductions in volumetric shrinkage would be obtained. The performance study which consists of degree of conversion and condition of the ring-opening reactions of MTOSN, volumetric shrinkage and mechanical properties including tensile bond strength, compressive strength and Vicker＇s hardness were carried out respectively by Fourier transfer infrared, the dilatometer and the universal testing machine. The results supported that the dental composites based on the expanding monomer and three-component photoinitiator system engendered a greater decrease of volumetric shrinkage and better mechanieal properties.展开更多
目的比较玻璃离子水门汀与流动树脂垫底对深龋近髓磨牙充填后的疼痛及术后敏感性。方法120颗深龋近髓磨牙,随机分为对照组,玻璃离子水门汀组和流动树脂组,每组40颗患牙。对照组采用dycal护髓,玻璃离子水门汀组采用dycal护髓和玻璃离子...目的比较玻璃离子水门汀与流动树脂垫底对深龋近髓磨牙充填后的疼痛及术后敏感性。方法120颗深龋近髓磨牙,随机分为对照组,玻璃离子水门汀组和流动树脂组,每组40颗患牙。对照组采用dycal护髓,玻璃离子水门汀组采用dycal护髓和玻璃离子水门汀垫底,流动树脂组采用dycal护髓和流动树脂垫底,酸蚀粘接后,3组上层均加压充填3M ESPE Filtek^(TM)P60复合树脂。分别于修复后1天,1周,1个月,3个月采用疼痛程度标尺(Visual Analog scales,VAS)记录自觉疼痛程度,采用Ryge评价标准记录对压缩空气刺激的敏感性。结果术后1天、1周、1个月和3个月,对照组与两个实验组之间自觉疼痛程度上差异有统计学意义(P<0.05),各观察期两实验组之间自觉疼痛程度差异无统计学意义(P>0.05)。术后1天和1周,3组之间的术后敏感发生率差异无统计学意义(P>0.05),术后1个月和3个月,玻璃离子水门汀组和流动树脂组与对照组之间差异有统计学意义(P<0.05),而玻璃离子组与流动树脂组之间差异没有统计学意义(P>0.05)。结论在深龋近髓磨牙充填中,双垫底治疗可以降低术后疼痛以及敏感的发生,玻璃离子水门汀和流动树脂之间没有本质区别。展开更多
文摘Background: Effective polymerization of the composite resin is essential to obtain long term clinical success and has a great importance obtaining improved mechanical properties. The purpose of this study was to measure the effect of the light intensity of LED and QTH curing devices in relation to the light distances, on the hardness (KHN) of two light cure nano-resin composite. Material and Methods: The top and bottom surfaces of the two nanofill composite specimens were evaluated. Two LED and two QTH light curing devices were used at nine different distances. Light intensity was measured with two radiometers placed at these same distances from the curing tip. 360 pvc dies were prepared with circular cavity 3 mm in diameter and 2 mm thick. The tested materials were placed in each cavity. The different light curing distances were standardized by adding pvc spacers dies at different height matching the different distances. Top and bottom surface microhardness were evaluated with a Micro Hardness Tester in knoop hardness numbers (Kg/mm2). Data were statistically analyzed using: Three-way ANOVA, Tukey and Pearsons test. Results: It was revealed that there was a statistically significant difference in microhardness between the composites (p < 0.001), between the nine distances (p < 0.001) and between the four light curing devices (p < 0.001). Increasing the distance of the light source from composite resin, the light intensity and the microhardness values at the top and bottom surface decrease. LED light curing devices produced a greater microhardness results at the bottom surface of the specimens. The Filtek Ultimate nanocomposite (3 m) showed highest microhardness values on the top and bottom surfaces, polymerized with all four curing devices and all nine distances compared to Empress Direct nano composite (Ivoclar vivadent). Clinical significant: Even with high power LED curing light, the distance between the tip of the light source and the restoration surface should be as close as possible. In this study, Filtek Ultimate showed better results (highest microhardness values) than Empress Direct.
基金Funded by the National Natural Science Foundation of China(No.50673065)
文摘The purpose of this study was to use. a three-component photoinitiation system comprising 1wt% CQ （camphorquinone）, 2wt% DMAEMA （2-（dimethylamino） ethyl meth acrylate） and 2wt% ph^2I^＋PF6^- （diphenyliodonium hexafluorophosphate） to initiate the copolymerization of the matrix resins which combine bisphenol-S-bis （3-methacrylate-2-hydroxy propyl） ether （BisS-GMA） with the expanding monomer unsaturated spiro orthoesters 2-methylene-l,4,6-tdspiro[4,4] nonane （MTOSN）, for minimizing the volumetric shrinkage that generally occurs during polymerization. It was hypothesized that MTOSN would expand volumetrically during polymerization under the three-component photoinitiator system and further reductions in volumetric shrinkage would be obtained. The performance study which consists of degree of conversion and condition of the ring-opening reactions of MTOSN, volumetric shrinkage and mechanical properties including tensile bond strength, compressive strength and Vicker＇s hardness were carried out respectively by Fourier transfer infrared, the dilatometer and the universal testing machine. The results supported that the dental composites based on the expanding monomer and three-component photoinitiator system engendered a greater decrease of volumetric shrinkage and better mechanieal properties.
文摘目的比较玻璃离子水门汀与流动树脂垫底对深龋近髓磨牙充填后的疼痛及术后敏感性。方法120颗深龋近髓磨牙,随机分为对照组,玻璃离子水门汀组和流动树脂组,每组40颗患牙。对照组采用dycal护髓,玻璃离子水门汀组采用dycal护髓和玻璃离子水门汀垫底,流动树脂组采用dycal护髓和流动树脂垫底,酸蚀粘接后,3组上层均加压充填3M ESPE Filtek^(TM)P60复合树脂。分别于修复后1天,1周,1个月,3个月采用疼痛程度标尺(Visual Analog scales,VAS)记录自觉疼痛程度,采用Ryge评价标准记录对压缩空气刺激的敏感性。结果术后1天、1周、1个月和3个月,对照组与两个实验组之间自觉疼痛程度上差异有统计学意义(P<0.05),各观察期两实验组之间自觉疼痛程度差异无统计学意义(P>0.05)。术后1天和1周,3组之间的术后敏感发生率差异无统计学意义(P>0.05),术后1个月和3个月,玻璃离子水门汀组和流动树脂组与对照组之间差异有统计学意义(P<0.05),而玻璃离子组与流动树脂组之间差异没有统计学意义(P>0.05)。结论在深龋近髓磨牙充填中,双垫底治疗可以降低术后疼痛以及敏感的发生,玻璃离子水门汀和流动树脂之间没有本质区别。