Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarbo...Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarboxylates water-reducing admixtures existed in the engineering application of were analyzed.At present the key for polycarboxylates application was to settle the compatibility between the water-reducing admixture and the cement and to keep the quality retention of this admixture.展开更多
An ability of aluminum-bearing substances-amorphous aluminum hydroxide, aluminum sulphate and basic aluminum sulphate to mitigate alkali-silica reactions in Portland cement mortars has been studied. At equivalent dosa...An ability of aluminum-bearing substances-amorphous aluminum hydroxide, aluminum sulphate and basic aluminum sulphate to mitigate alkali-silica reactions in Portland cement mortars has been studied. At equivalent dosages in terms of Al2O3, these substances are ranged in the following order in respect of inhibiting effect: Al(OH)1.78(SO4)0.61 ≥ Al2(SO4)3 > Al(OH)3. It is found that the plasticizing agents of the main types used in cement compositions have no influence on the inhibiting effect of aluminum-bearing admixtures. To control the setting time of cement paste, iron(II) sulphate may be used for partial substitution of Al2SO4·18H2O, and this operation is not influence on the results of ASR expansion test.展开更多
文摘Polycarboxylate water-reducing admixture possesses the capability which could meet with the comprehensive performance of high performance concrete used in passenger dedicated line engineering.The problems of polycarboxylates water-reducing admixtures existed in the engineering application of were analyzed.At present the key for polycarboxylates application was to settle the compatibility between the water-reducing admixture and the cement and to keep the quality retention of this admixture.
文摘An ability of aluminum-bearing substances-amorphous aluminum hydroxide, aluminum sulphate and basic aluminum sulphate to mitigate alkali-silica reactions in Portland cement mortars has been studied. At equivalent dosages in terms of Al2O3, these substances are ranged in the following order in respect of inhibiting effect: Al(OH)1.78(SO4)0.61 ≥ Al2(SO4)3 > Al(OH)3. It is found that the plasticizing agents of the main types used in cement compositions have no influence on the inhibiting effect of aluminum-bearing admixtures. To control the setting time of cement paste, iron(II) sulphate may be used for partial substitution of Al2SO4·18H2O, and this operation is not influence on the results of ASR expansion test.