A new electric arc furnace （EAF） steelmaking process with increasing hot metal charging ratio and improving slagging regime simultaneously was developed and applied in a 50 t electric arc furnace for more than a yea...A new electric arc furnace （EAF） steelmaking process with increasing hot metal charging ratio and improving slagging regime simultaneously was developed and applied in a 50 t electric arc furnace for more than a year at No. 1 Steelmaking Plant of Shanxi Taigang Stainless Corporation Limited. The essential fact of the new EAF steelmaking process was to charge hot metal in two portions or steps： firstly, 35wt%-40wt% hot metal was pretreated by blowing oxygen in a specially designed reactor for decar burization and improving hot metal temperature and melting premelted slag; secondly, 30wt% hot metal was charged into EAF with high basicity refining slags from ladle furnace （LF）-vacuum degassing furnace （VD） refining process. The results show that the hot metal charging ratio can reach to about 65wt%-70wt% for the new EAF steelrnaking process; meanwhile, the tap-to-tap time of a 50 t EAF can shorten by 5-10 min, the electricity consumption can decrease by 35-50 kW·h/t, the lime consumption can reduce by 10.5 kg/t of molten steel, and the content of harmful heavy metals in molten steel can be easily controlled to less than the upper limits of aimed steel specification or grade compared with the traditional EAF steelmaking process. In addition, the dephosphorization ability shows a slight strengthening, however, a small degree of lessening for desulphurization ability is observed for the new EAF steelmaking process, but the weakness of desulphurization ability cannot become an obstacle to its further application since a stronger desulphurization ability can be achieved during secondary refining of LF coupled with VD after EAF steelmaking process.展开更多
The foaming slag practice can effectively solve the problems existing in EAF smelting of stainless steel, such as high electrical consumption ,high refractory consumption and long tap to tap time. In this paper, theor...The foaming slag practice can effectively solve the problems existing in EAF smelting of stainless steel, such as high electrical consumption ,high refractory consumption and long tap to tap time. In this paper, theoretical analyses were made on the technical difficulties and development feasibility of the technology. Slag foaming experiments were performed in a 10t EAF where crude stainless steel with a Cr content of 13% - 15% and a carbon content of 1.5% - 2.5% was smelted and special foaming pellets were added to release additional gas for better foaming. Good foaming slag was observed with the electric arc fully covered by the foam when the content of Cr2O3 is between 7% - 12%. The industrial scale experiments were performed in a 110 t EAF by the use of the same foaming pellets. Compared with the traditional operation, these experiments resulted in better foaming effects.展开更多
文摘A new electric arc furnace （EAF） steelmaking process with increasing hot metal charging ratio and improving slagging regime simultaneously was developed and applied in a 50 t electric arc furnace for more than a year at No. 1 Steelmaking Plant of Shanxi Taigang Stainless Corporation Limited. The essential fact of the new EAF steelmaking process was to charge hot metal in two portions or steps： firstly, 35wt%-40wt% hot metal was pretreated by blowing oxygen in a specially designed reactor for decar burization and improving hot metal temperature and melting premelted slag; secondly, 30wt% hot metal was charged into EAF with high basicity refining slags from ladle furnace （LF）-vacuum degassing furnace （VD） refining process. The results show that the hot metal charging ratio can reach to about 65wt%-70wt% for the new EAF steelrnaking process; meanwhile, the tap-to-tap time of a 50 t EAF can shorten by 5-10 min, the electricity consumption can decrease by 35-50 kW·h/t, the lime consumption can reduce by 10.5 kg/t of molten steel, and the content of harmful heavy metals in molten steel can be easily controlled to less than the upper limits of aimed steel specification or grade compared with the traditional EAF steelmaking process. In addition, the dephosphorization ability shows a slight strengthening, however, a small degree of lessening for desulphurization ability is observed for the new EAF steelmaking process, but the weakness of desulphurization ability cannot become an obstacle to its further application since a stronger desulphurization ability can be achieved during secondary refining of LF coupled with VD after EAF steelmaking process.
文摘The foaming slag practice can effectively solve the problems existing in EAF smelting of stainless steel, such as high electrical consumption ,high refractory consumption and long tap to tap time. In this paper, theoretical analyses were made on the technical difficulties and development feasibility of the technology. Slag foaming experiments were performed in a 10t EAF where crude stainless steel with a Cr content of 13% - 15% and a carbon content of 1.5% - 2.5% was smelted and special foaming pellets were added to release additional gas for better foaming. Good foaming slag was observed with the electric arc fully covered by the foam when the content of Cr2O3 is between 7% - 12%. The industrial scale experiments were performed in a 110 t EAF by the use of the same foaming pellets. Compared with the traditional operation, these experiments resulted in better foaming effects.