La-doped Li3V2-xLax（PO4）3 （ x = 0.01, 0.02, and 0.03） cathode materials for lithium ion batteries were synthesized by the microwave-assisted carbothermal reduction method （MW-CTR）. The structures and properties ...La-doped Li3V2-xLax（PO4）3 （ x = 0.01, 0.02, and 0.03） cathode materials for lithium ion batteries were synthesized by the microwave-assisted carbothermal reduction method （MW-CTR）. The structures and properties of the prepared samples were investigated by X-ray diffraction （XRD） and electrochemical measurements. The results showed that all the three Li3V2-xLax（PO4）3 samples had the same monocfinic structures and sharper diffraction peaks of the crystal plane compared with those of the undoped Li3V2（PO4）3. The initial charge/discharge specific capacity, coulomb efficiency, and discharge decay rate of all the three Li3V2-xLax（PO4）3 samples were superior to those of the undoped Li3V2（PO4）3 sample, and the Li3V1.98La0.02（PO4）3 sample exhibited the best features among the three La-doped Li3V2-xLax（PO4）3 samples. Electrochemical impedance spectroscopy （EIS） demonstrated that the Li3V1.98Lao.02（PO4）3 sample had a lower charge transfer resistance and a higher Li ion diffusion coefficient compared with the undoped Li3V2 （PO4）3 sample.展开更多
基金supported by the Key Research Project of the Science and Technology Department of Jiangxi Province,China (2006)
文摘La-doped Li3V2-xLax（PO4）3 （ x = 0.01, 0.02, and 0.03） cathode materials for lithium ion batteries were synthesized by the microwave-assisted carbothermal reduction method （MW-CTR）. The structures and properties of the prepared samples were investigated by X-ray diffraction （XRD） and electrochemical measurements. The results showed that all the three Li3V2-xLax（PO4）3 samples had the same monocfinic structures and sharper diffraction peaks of the crystal plane compared with those of the undoped Li3V2（PO4）3. The initial charge/discharge specific capacity, coulomb efficiency, and discharge decay rate of all the three Li3V2-xLax（PO4）3 samples were superior to those of the undoped Li3V2（PO4）3 sample, and the Li3V1.98La0.02（PO4）3 sample exhibited the best features among the three La-doped Li3V2-xLax（PO4）3 samples. Electrochemical impedance spectroscopy （EIS） demonstrated that the Li3V1.98Lao.02（PO4）3 sample had a lower charge transfer resistance and a higher Li ion diffusion coefficient compared with the undoped Li3V2 （PO4）3 sample.