External organic carbon sources are needed to provide electron donors for the denitrification of wastewater with a low COD/NO_(3)^(-)-N(C/N)ratio,increasing the treatment cost.The economic strategy is to enhance the b...External organic carbon sources are needed to provide electron donors for the denitrification of wastewater with a low COD/NO_(3)^(-)-N(C/N)ratio,increasing the treatment cost.The economic strategy is to enhance the bioactivity and/or biodiversity of denitrifiers to efficiently utilize organic substances in wastewater.In this study,novel zero-valent iron(ZVI)composite carriers were prepared and implemented in a suspended carrier biofilm reactor to enhance the bioactivity and/or biodiversity of denitrifiers.At the influent C/N ratio of 4(COD was 179.5±5.0 mg/L and TN was 44.2±0.8 mg/L),COD and TN removal efficiencies were 85.1%and 66.4%,respectively,in the reactors filled with 3 wt%ZVI composite carriers.In contrast,COD and TN removal efficiencies were 70.4%and 55.3%,respectively,in the reactor filled with conventional high-density polyethylene(HDPE)biofilm carriers.The biofilm formation on the 3 wt%ZVI composite carriers was optimized due to its higher roughness(surface square roughness increased from 76.0 nm to 93.8 nm)and favorable hydrophilicity(water contact angle dropped to 72.5°±1.4°from 94.3°±3.2°)compared with the HDPE biofilm carriers.In addition,heterotrophic denitrifiers,Thauera and Dechloromonas,were enriched,whereas autotrophic denitrifiers,Raoultella and Thiobacillus,exhibited high relative abundance in the biofilm of ZVI composite carriers.The coexistence of heterotrophic denitrifiers and autotrophic denitrifiers on the surface of ZVI composite carriers provided mixotrophic metabolism of denitrification(including heterotrophic and iron-based autotrophic),thereby ensuring effective denitrification for wastewater with a low C/N ratio without external organic carbon source addition.展开更多
The effect of Ti （ C, N） on properties of low-carbon MgO - C bricks was investigated. The phase composition and the microstructure of the matrix of low-carbon MgO - C brick containing Ti （ C, N） were studied by XR...The effect of Ti （ C, N） on properties of low-carbon MgO - C bricks was investigated. The phase composition and the microstructure of the matrix of low-carbon MgO - C brick containing Ti （ C, N） were studied by XRD and SEM analysis together with EDS. The results showed that Ti （ C, N） distributed in the matrix of lowcarbon MgO - C brick uniformly after being treated at 1 600 ~C for 3 h in coke powder bed, and Ti （C, N） and MgO formed a solid solution. After the treatment at 1 600 ℃ for 3 h in coke powder bed, the bulk density and cold crushing strength of low-carbon MgO - C brick with Ti （ C, N） decreased, and the apparent porosity and linear change rate of specimens increased. The oxidation resistance of low-carbon MgO - C brick with Ti（ C, N） was superior to that of low-carbon MgO - C brick with no additives, but inferior to that of low-car- bon MgO - C brick with Al powder. The slag resistance of the specimen with Ti （ C, N） was excellent as well.展开更多
基金supported by National Science and Technology Major Project Water:Pollution Control and Treatment(No.2012ZX07202006)。
文摘External organic carbon sources are needed to provide electron donors for the denitrification of wastewater with a low COD/NO_(3)^(-)-N(C/N)ratio,increasing the treatment cost.The economic strategy is to enhance the bioactivity and/or biodiversity of denitrifiers to efficiently utilize organic substances in wastewater.In this study,novel zero-valent iron(ZVI)composite carriers were prepared and implemented in a suspended carrier biofilm reactor to enhance the bioactivity and/or biodiversity of denitrifiers.At the influent C/N ratio of 4(COD was 179.5±5.0 mg/L and TN was 44.2±0.8 mg/L),COD and TN removal efficiencies were 85.1%and 66.4%,respectively,in the reactors filled with 3 wt%ZVI composite carriers.In contrast,COD and TN removal efficiencies were 70.4%and 55.3%,respectively,in the reactor filled with conventional high-density polyethylene(HDPE)biofilm carriers.The biofilm formation on the 3 wt%ZVI composite carriers was optimized due to its higher roughness(surface square roughness increased from 76.0 nm to 93.8 nm)and favorable hydrophilicity(water contact angle dropped to 72.5°±1.4°from 94.3°±3.2°)compared with the HDPE biofilm carriers.In addition,heterotrophic denitrifiers,Thauera and Dechloromonas,were enriched,whereas autotrophic denitrifiers,Raoultella and Thiobacillus,exhibited high relative abundance in the biofilm of ZVI composite carriers.The coexistence of heterotrophic denitrifiers and autotrophic denitrifiers on the surface of ZVI composite carriers provided mixotrophic metabolism of denitrification(including heterotrophic and iron-based autotrophic),thereby ensuring effective denitrification for wastewater with a low C/N ratio without external organic carbon source addition.
文摘The effect of Ti （ C, N） on properties of low-carbon MgO - C bricks was investigated. The phase composition and the microstructure of the matrix of low-carbon MgO - C brick containing Ti （ C, N） were studied by XRD and SEM analysis together with EDS. The results showed that Ti （ C, N） distributed in the matrix of lowcarbon MgO - C brick uniformly after being treated at 1 600 ~C for 3 h in coke powder bed, and Ti （C, N） and MgO formed a solid solution. After the treatment at 1 600 ℃ for 3 h in coke powder bed, the bulk density and cold crushing strength of low-carbon MgO - C brick with Ti （ C, N） decreased, and the apparent porosity and linear change rate of specimens increased. The oxidation resistance of low-carbon MgO - C brick with Ti（ C, N） was superior to that of low-carbon MgO - C brick with no additives, but inferior to that of low-car- bon MgO - C brick with Al powder. The slag resistance of the specimen with Ti （ C, N） was excellent as well.