An experimental study was carried out to assess the effects of silty sand on the CO 2 corrosion behavior of 1 wt% Cr (1Cr) and 3 wt% Cr (3Cr) tubing steel under 0.5 MPa CO 2 at 100°C and 1.5 m/s flow velocity.The...An experimental study was carried out to assess the effects of silty sand on the CO 2 corrosion behavior of 1 wt% Cr (1Cr) and 3 wt% Cr (3Cr) tubing steel under 0.5 MPa CO 2 at 100°C and 1.5 m/s flow velocity.The 1Cr and 3Cr specimens both suffered general corrosion,but the surface was coarser in the pure CO 2 corrosion environment.Under silty sand conditions,severe pitting corrosion occurred on the 1Cr specimens and some acicular pitting appeared on the 3Cr specimens.The average corrosion rates of 1Cr and 3Cr steels increased by factors of 3 and 1.6,respectively.The corrosion products were analyzed by scanning electron microscopy (SEM),energy dispersive spectroscopy (EDS),X-ray diffraction (XRD),and electrical impedance spectroscopy (EIS).The results show that silty sand acts as an inclusion in corrosion product films and reduces the homogeneity and density of the products,rather than abrading the corrosion film.Ion-diffusion channels may build up around the irregular silty sand;this would degrade the protective capabilities of the product films and aggravate corrosion.展开更多
基金supported by the National Science and Technology Major Project of China (2008ZX05024)
文摘An experimental study was carried out to assess the effects of silty sand on the CO 2 corrosion behavior of 1 wt% Cr (1Cr) and 3 wt% Cr (3Cr) tubing steel under 0.5 MPa CO 2 at 100°C and 1.5 m/s flow velocity.The 1Cr and 3Cr specimens both suffered general corrosion,but the surface was coarser in the pure CO 2 corrosion environment.Under silty sand conditions,severe pitting corrosion occurred on the 1Cr specimens and some acicular pitting appeared on the 3Cr specimens.The average corrosion rates of 1Cr and 3Cr steels increased by factors of 3 and 1.6,respectively.The corrosion products were analyzed by scanning electron microscopy (SEM),energy dispersive spectroscopy (EDS),X-ray diffraction (XRD),and electrical impedance spectroscopy (EIS).The results show that silty sand acts as an inclusion in corrosion product films and reduces the homogeneity and density of the products,rather than abrading the corrosion film.Ion-diffusion channels may build up around the irregular silty sand;this would degrade the protective capabilities of the product films and aggravate corrosion.